Re-evaluation of Radiation-Energy Transfer to an Extraction Solvent in a Minor-Actinide-Separation Process Based on Consideration of Radiation Permeability

ABSTRACT

Absorbed-dose estimation is essential for evaluation of the radiation tolerance of minor-actinide-separation processes. We propose a dose-evaluation method based on radiation permeability, with comparisons of heterogeneous structures seen in the solvent-extraction process, such as emulsions forming in the mixture of the organic and aqueous phases. A demonstration of radiation-energy-transfer simulation is performed with a focus on the minor-actinide-recovery process from high-level liquid waste with the aid of the Monte Carlo radiation-transport code PHITS. The simulation results indicate that the dose absorbed by the extraction solvent from alpha radiation depends upon the emulsion structure, and that from beta and gamma radiation depends upon the mixer-settler-apparatus size. Non-negligible contributions of well-permeable gamma rays were indicated in terms of the plant operation of the minor-actinide-separation process.     

An efficient manufacturing method for I-shaped cross-sectional CFRP beam with arbitrary arrangement of carbon fiber using electro-activated resin molding

Abstract

The I-shaped cross-sectional beam of CFRP (CFRP I-beam) is usually manufactured by the continuous protrusion method. Carbon fibers can only be arranged in the longitudinal direction. The CFRP I-beam with arbitrary arrangement of carbon fiber was manufactured with applying the electro-activated deposition molding method. The carbon fiber fabric was immersed in the deposition solution and energized, epoxy resin precipitated around carbon fiber and impregnated. The resin-impregnated fabric was installed to the mold, and the CFRP I-beam was fabricated. The CFRP I-beam was subjected to three-point bending tests, and the relationship between load-deflection was simulated by finite-element analysis.     

A feasibility study of a direct-mapping parallel processing method to solve linear equations in load-flow calculation

With the growing size and complexity of power systems, system analysis—such as transients calculation—takes much time. Hence, fast calculation methods are required. Although parallel processing is a hopeful method, there have been difficulties in the parallel solution of linear equations which appear in power-flow calculations by the Newton-Raphson method. This paper aims at the fast calculation of the power-flow problem by means of parallel processing. In order to improve the suitability to the parallel solution of the differential equation in transients calculation, we assume the use of a direct-mapping parallel processing machine to map directly the network of a power system onto a network of processors. Under this assumption, we propose a new parallel-processing-oriented method in which the linear equation is solved by linear iterations between nodes with Aitken acceleration. We simulate the method on three model power systems and compare this Parallel Iterative Method (PIN) with a Parallel Direct Method (PDM) which uses the banded matrix according to the number of operations required. As a result, we can expect that PIM may solve linear equations faster than PDM with m processors, although the PIM might be inferior to the PDM with m × m processors, where m denotes the half-band width of the banded matrix.     

Generation of adaptive gait patterns for quadruped robot with CPG network including motor dynamic model

This paper describes the generation of adaptive gait patterns using new Central Pattern Generators (CPGs) including motor dynamic models for a quadruped robot under various environments. The CPGs act as the flexible oscillators of the joints and adjust joint angles to required values. The CPGs are interconnected with each other and sets of their coupling parameters are adjusted by a genetic algorithm so that the quadruped robot can realize stable and adequate gait patterns. Generation of gait patterns results in the formation of the CPG networks suitable for the formation of not only a straight walking pattern but also of rotating gait patterns. Experimental results demonstrate that the proposed CPG networks are effective for the automatic adjustment of the adaptive gait patterns for the tested quadruped robot under various environments. Furthermore, the target tracking control based on image processing is achieved by combining the general gait patterns. © 2006 Wiley Periodicals, Inc. Electr Eng Jpn, 155(1): 35–43, 2006; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.20225     

Poly(L‐lactide). X. Enhanced surface hydrophilicity and chain‐scission mechanisms of poly(L‐lactide) film in enzymatic,alkaline, and phosphate‐buffered solutions

Attempts were carried out to enhance the surface hydrophilicity of poly(L ‐lactide), that is, poly(L ‐lactic acid) (PLLA) film, utilizing enzymatic, alkaline, and autocatalytic hydrolyses in a proteinase K/Tris–HCL buffered solution system (37°C), in a 0.01N NaOH solution (37°C), and in a phosphate‐buffered solution (100°C), respectively. Moreover, its chain‐scission mechanisms in these different media were studied. The advancing contact‐angle (θ_a) value of the amorphous‐made PLLA film decreased monotonically with the hydrolysis time from 100° to 75° and 80° without a significant molecular weight decrease, when enzymatic and alkaline hydrolyses were continued for 60 min and 8 h, respectively. In contrast, a negligible change in the θ_a value was observed for the PLLA films even after the autocatalytic hydrolysis was continured for 16 h, when their bulk M_n decreased from 1.2 × 10⁵ to 2.2 × 10⁴ g mol^?1 or the number of hydrophilic terminal groups per unit weight increased from 1.7 × 10^?5 to 9.1 × 10^?5 mol g^?1. These findings, together with the result of gravimetry, revealed that the enzymatic and alkaline hydrolyses are powerful enough to enhance the practical surface hydrophilicity of the PLLA films because of their surface‐erosion mechanisms and that its practical surface hydrophilicity is controllable by varying the hydrolysis time. Moreover, autocatalytic hydrolysis is inappropriate to enhance the surface hydrophilicity, because of its bulk‐erosion mechanism. Alkaline hydrolysis is the best to enhance the hydrophilicity of the PLLA films without hydrolysis of the film cores, while the enzymatic hydrolysis is appropriate and inappropriate to enhance the surface hydrophilicity of bulky and thin PLLA materials, respectively, because a significant weight loss occurs before saturation of θ_a value. The changes in the weight loss and θ_a values during hydrolysis showed that exo chain scission as well as endo chain scission occurs in the presence of proteinase K, while in the alkaline and phosphate‐buffered solutions, hydrolysis proceeds via endo chain scission. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1628–1633, 2003     

Fracture toughness of silica particulate‐filled epoxy composite

The relationship between the postcuring conditions and fracture toughness on three silica particulate‐filled epoxy composites was investigated. The glass transition temperature, T_g, and the fragility parameter, m, derived from the thermo‐viscoelasticity, were used to characterize the composites, which were postcured under various conditions. The glass transition temperature and fragility both depended on both of the curing conditions and the volume fraction of silica particles. The glass transition temperature increased with the postcuring time and temperature, while the fragility generally decreased as the volume fraction increased. There was no direct correlation between the glass transition temperature and fragility. The fracture toughness depended on both the glass transition temperature and fragility. The composites with a high glass transition temperature and low fragility had high fracture toughness. These results indicate that the glass transition temperature and fragility are useful parameters for estimating the fracture toughness of the silica particulate‐filled epoxy composites. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 2261–2265, 2002     

Electrochemical formation of AlN in molten LiCl-KCl-Li3N systems

Electrochemical formation of aluminum nitride was investigated in molten LiCl-KCl-Li₃N systems at 723 K. When Al was anodically polarized at 1.0 V (versus Li⁺/Li), oxidation of nitride ions proceeded to form adsorbed nitrogen atoms, which reacted with the surface to form AlN film. The obtained nitrided film had a thickness of sub-micron order. The obtained nitrided layer consisted of two regions; the outer layer involving AlN and aluminum oxynitride and the inner layer involving metallic Al and AlN. When Al electrode was anodically polarized at 2.0 V, anodic dissolution of Al electrode occurred to give aluminum ions, which reacted with nitride ions in the melt to produce AlN particles (1-5 μm of diameter) of wurtzite structure.     

Back‐channel‐etched thin‐film transistor using c‐axis‐aligned crystal In–Ga–Zn oxide

Our crystalline In–Ga–Zn oxide (IGZO) thin film has a c‐axis‐aligned crystal (CAAC) structure and maintains crystallinity even on an amorphous base layer. Although the crystal has c‐axis alignment, its a‐axis and b‐axis have random arrangement; moreover, a clear grain boundary is not observed. We fabricated a back‐channel‐etched thin‐film transistor (TFT) using the CAAC‐IGZO film. Using the CAAC‐IGZO film, more stable TFT characteristics, even with a short channel length, can be obtained, and the instability of the back channel, which is one of the biggest problems of IGZO TFTs, is solved. As a result, we improved the process of manufacturing back‐channel‐etched TFTs.     

Preparation of poly(thiophene-alt-pyrrole) bearing chiral LC group

ABSTRACT

Preparation of poly(thiophene-alt-pyrrole bearing mesogen) was carried out with Migita–Kosugi–Stille coupling type polycondensation with an aid of Pd(0) complex catalyst. The resultant polymer shows lyotropic liquid crystallinity with good film-forming property. The smectic fan-shaped texture is maintained after completion of evaporation of solvent from the polymer solution. The cast film having liquid crystal (LC) order shows light emission function upon irradiation of excitation light at 460 nm. The polymer shows LC domain emission. Mechanical orientation allows to yield LC domain aligned film with band structure. Chiral mesogenic side chain induces π-conjugated main chain helicity from distance in molecular level.