Citrate-Gel Synthesis and Luminescent Properties of α-Zn3 （PO4）2 Doped with Eu^3＋

By using inorganic salts as raw materials and citric acid as complexing agent, α-Zn3(PO4)2 and Eu^3 doped α-Zn3( PO4)2 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), TG - DTA, FF - IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500℃ and pure α-Zn3(PO4)2 phase is obtained at 800℃. And the results of XRD reveal that Eu^3 exists as EuPO4 in the powder. In the phosphor powders, the Eu^3 shows its characteristic red-orange(592 nm, ^5D0 -^7F1) emission and has no quenching concentration.     

建筑外墙渗漏的防治措施

当前建筑领域内新技术的普及以及操作人员素质的提高却相当缓慢,造成了设计不重视施工、管理跟不上施工、规范落后于施工等现象的出现。并由此带来的外墙渗漏等质量问题,本文对常见渗漏部位及成因进行了分析。     

Citrate-Gel Synthesis and Luminescent Properties of α-Zn3(PO4)2 Doped with Eu3+

By using inorganic salts as raw materials and citric acid as complexing agent, α-Zn3(PO4)2 and Eu3 doped α-Zn3(PO4)2 phosphor powders were prepared by a citrate-gel process. X-ray diffraction(XRD), TG-DTA, FT-IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 ℃ and pure α-Zn3(PO4)2 phase is obtained at 800 ℃. And the results of XRD reveal that Eu3 exists as EuPO4 in the powder. In the phosphor powders, the Eu3 shows its characteristic red-orange(592 nm, 5D0-7F1) emission and has no quenching concentration.