Preparation and Characterization of Red Luminescent Ca_(0.8)Zn_(0.2)TiO_3∶ Pr~(3+), Na~+ Nanophosphor

Pr dopedalkalineearthmetaltitanateswithper ovskitestructurehaverecentlybeenthesubjectof manyinvestigations.Thisisbecauseoftheirhigh chemicalstability,strongandsharpredemission,and longafterglowluminescence[1～13].CaTiO3∶Pr3+,asa relativelynewluminescencematerialofthatcategory,andexhibitsredcathodoluminescencelocatedatthe CIEcoordinate[8]ofx=0.680andy=0.311,very closeto“idealred”ofNTSC(NationalTelevision StandardsCommittee).Inaddition,itisapromising redlongpersistencephosphor,whichmayp…     

碳酸盐前驱体和CS_2硫化制备SrY_2S_4∶Eu~(2+)红色荧光粉及其表征

以Sr2+,Y3+和Eu3+的混合硝酸盐溶液为阳离子溶液,以(NH4)2CO3为沉淀剂,共沉淀法制备了碳酸盐前驱体,TG-DSC分析结果表明,随着(NH4)2CO3浓度的升高,前驱体组成由碱式碳酸盐向正盐转变。以CS2为硫化剂,高温煅烧前驱体合成了SrY2S4∶Eu2+红色荧光粉。XRD表明前驱体经800℃处理得到纯相SrY2S4。荧光光谱和SEM研究表明在[Sr(NO3)2+Eu(NO3)3]∶[Y(NO3)3]∶[(NH4)2CO3]=0.25∶0.50∶2.00(摩尔比)条件下制备前驱体,然后1050℃煅烧4 h所得荧光粉的发光强度最大,粒径小于1μm,粒子形貌呈椭球。Eu2+在SrY2S4基质中的最佳掺杂摩尔分数是0.6%。     

CaTiO_3∶Pr~(3+)的合成及发光特性

本文采用高温团相反应合成TCaTiO3∶Pr3+红色发光材料、报道了Pr3+激活的CaTiO3的光谱特征及长余辉特性，并与CaS∶Eu的光谱特性及长余辉进行了比较。CaTiO3∶Pr3+将是一种具有广泛用途的新材料     

Sr_4Al_(14)O_(25)∶Eu,Nd夜光粉的晶体结构

通过对 Ｓｒ４ Ａｌ１４ Ｏ２５∶ Ｅｕ , Ｎｄ 夜光粉 样品的 Ｘ 射线衍射 分析,确 定其是一 混晶结 构。 Ｅｕ ２ ＋取代基质 中 Ｓｒ２ ＋ 的位 置, Ｎｄ３ ＋ 取代 Ａｌ３ ＋ 的位置 。通过 扫描电 镜测定 了样 品的 外观 形貌 和颗 粒级配。     

前驱体法制备Ca0.8Zn0.2TiO3:Pr3+荧光粉及其发光性能

采用前驱体微波加热法、电阻加热法和传统的高温固相法等不同方法制备了Ca0.8Zn0.2TiO3Pr3+荧光粉,以 TG-DSC、XRD、荧光光谱和粒度分析为表征手段,比较了不同方法制备Ca0.8Zn0.2TiO3Pr3+的发光性质.XRD测定结果表明, 前驱体微波加热法和电阻加热法制备的样品可使反应温度低200℃,但材料的晶体化程度不高.TG-DSC的测定结果表明,前驱体在加热达到700℃以上才完全失重.荧光光谱和粒度分析的测定结果表明,与传统的高温固相法制备的荧光粉相比, 前驱体微波加热法和电阻加热法制备的荧光粉具有发光增强和颗粒细小均匀的特点,但微波加热法更为简单.     

Preparation and Characterization of Red Luminescent Ca0.8 Zn0.2 TiO3 ： Pr3 ＋ , Na^＋ Nanophosphor

Nanophosphor with the nominal composition of Ca0.8 Zn0.2 TiO3 ： Pr3 ＋ , Na^＋ （CZTOPN） was synthesized at relatively low temperature by the sol-gel method. Metal ions were dispersed by citric acid in ethylene glycol solvent and then react with Ti（OC4H9）4 to form sol and gel. The decomposition process of the precursor, and crystallization and particle size of CZTOPN were examined by thermal analysis （TG-DSC）, powder X-ray diffraction （XRD）, and scan election microscopy （SEM）. Results of TG-DSC and XRD reveal that the composition of Ca0.8 Zn0.2 TiO3 ： Pr3 ＋ , Na^＋ changes with the sintering temperature. SEM data indicate that the diameter of particles is under 50 nm even if the sintering temperature increases to 1000 ℃. In contrast to a solid state reaction, the excitation spectra of samples synthesized by the sol-gel method shift blue about 10 nm and the emission intensity at 617 nm increases significantly.     

碳酸盐前驱体和CS2硫化制备SrY2S4:Eu2+红色荧光粉及其表征

以Sr2＋, Y3＋和Eu3＋的混合硝酸盐溶液为阳离子溶液, 以（NH4）2CO3为沉淀剂, 共沉淀法制备了碳酸盐前驱体, TG-DSC分析结果表明, 随着（NH4）2CO3浓度的升高, 前驱体组成由碱式碳酸盐向正盐转变. 以CS2为硫化剂, 高温煅烧前驱体合成了SrY2S4：Eu2＋红色荧光粉. XRD表明前驱体经800 ℃处理得到纯相SrY2S4. 荧光光谱和SEM研究表明在[Sr（NO3）2＋Eu（NO3）3]：[Y（NO3）3]：[（NH4）2CO3]=0.25：0.50：2.00（摩尔比）条件下制备前驱体, 然后1050 ℃煅烧4 h所得荧光粉的发光强度最大, 粒径小于1 μm, 粒子形貌呈椭球. Eu2＋在SrY2S4基质中的最佳掺杂摩尔分数是0.6%.     

长江中游荆江流域环境演变及 两湖平原盆地形成过程

通过区域地质调查资料和地球卫星遥感解译技术对长江中游荆江流域及两湖平原盆地进行环境演变及形成过程的综合研究,揭示了华中地块在全球新构造运动中发生的拉分运动对地表过程的影响,阐明了流域水系和区域环境及平原盆地的同步演化关系,探讨了山-盆-原-江-湖-河耦合系统及环境演化的地球动力学机制。     

Ca1-nBanS:Cu+,Eu2+的合成及其光谱特征

研究了Ｃｕ＋,Ｅｕ２＋共激活的Ｃａ１－ｎＢａｎＳ的发光性质、余辉特性、基质组份Ｃａ／Ｂａ摩尔比与发光性质的关系．随着基质中Ｂａ含量的增加,Ｃｕ＋的蓝区发射带（４１６ｎｍ附近）及Ｅｕ２＋的红区发射带（６３０ｎｍ附近）均逐渐向绿区移动,且蓝光与红光的相对发射强度发生变化．实验证明,Ｃａ１－ｎＢａｎＳ：０．００５Ｃｕ＋,０．００１Ｅｕ２＋是一种红、蓝发射强度可调的单基双能光转换材料．     

柴达木盆地沙下盐湖的发现及意义

根据地球卫星遥感影象、地物谱测定以及地貌景观、古水系演化和地面地质调查等资料的综合研究表明,柴达木盆地察尔汗盐湖矿区北部外围地带存在一种新的成因类型的盐湖－沙下盐湖。通过对其主体物质结构和成盐环境的初步分析,认为其主要成盐方式呈现为复式成盐建造系统,为在我国广大内陆盆地寻找同一类型的地下卤水矿产资源提供了科学依据,具有理论意义和经济价值。