Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

Novel Bi-Doped Amorphous SnOx Nanoshells for Efficient Electrochemical CO2 Reduction into Formate at Low Overpotentials

Engineering novel Sn-based bimetallic materials could provide intriguing catalytic properties to boost the electrochemical CO₂ reduction. Herein, the first synthesis of homogeneous Sn_1−xBi_x alloy nanoparticles (x up to 0.20) with native Bi-doped amorphous SnO_x shells for efficient CO₂ reduction is reported. The Bi-SnO_x nanoshells boost the production of formate with high Faradaic efficiencies (>90%) over a wide potential window (−0.67 to −0.92 V vs RHE) with low overpotentials, outperforming current tin oxide catalysts. The state-of-the-art Bi-SnO_x nanoshells derived from Sn_0.80Bi_0.20 alloy nanoparticles exhibit a great partial current density of 74.6 mA cm⁻² and high Faradaic efficiency of 95.8%. The detailed electrocatalytic analyses and corresponding density functional theory calculations simultaneously reveal that the incorporation of Bi atoms into Sn species facilitates formate production by suppressing the formation of H₂ and CO.     

Achieving Rich and Active Alkaline Hydrogen Evolution Heterostructures via Interface Engineering on 2D 1T‐MoS2 Quantum Sheets

Large‐scale production of hydrogen from water‐alkali electrolyzers is impeded by the sluggish kinetics of hydrogen evolution reaction (HER) electrocatalysts. The hybridization of an acid‐active HER catalyst with a cocatalyst at the nanoscale helps boost HER kinetics in alkaline media. Here, it is demonstrated that 1T–MoS₂ nanosheet edges (instead of basal planes) decorated by metal hydroxides form highly active ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ heterostructures, which significantly enhance HER performance in alkaline media. Featured with rich ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ sites, the fabricated 1T–MoS₂ QS/Ni(OH)₂ hybrid (quantum sized 1T–MoS₂ sheets decorated with Ni(OH)₂ via interface engineering) only requires overpotentials of 57 and 112 mV to drive HER current densities of 10 and 100 mA cm^?2, respectively, and has a low Tafel slope of 30 mV dec^?1 in 1 m KOH. So far, this is the best performance for MoS₂‐based electrocatalysts and the 1T–MoS₂ QS/Ni(OH)₂ hybrid is among the best‐performing non‐Pt alkaline HER electrocatalysts known. The HER process is durable for 100 h at current densities up to 500 mA cm^?2. This work not only provides an active, cost‐effective, and robust alkaline HER electrocatalyst, but also demonstrates a design strategy for preparing high‐performance catalysts based on edge‐rich 2D quantum sheets for other catalytic reactions.     

基于SoC的多轴驱控一体化平台设计

随着FPGA技术和电力电机技术的发展,FPGA+ARM的集成方式已经成为FPGA的发展方向.针对一体化多轴运动控制与驱动的特点,选用了集成双核ARM CPU与FPGA结合的Xilinx Zynq-7020全可编程System-on-chip(SoC)作为硬件平台,一个ARM CPU完成多轴的位置环、速度环和电流环的算法以及多轴轨迹生成,能同时完成伺服高级算法如谐振等,另一个ARM CPU完成交互功能,发挥FPGA高速运算的功能,完成6轴电流环流水线控制以及双采样双更新电流环算法.提高了系统整体带宽,实现多轴ns级同步精度以实现更精确的位置轨迹,驱控一体内部数据通过共享内存以及高速内部总线的方式进行交换,其传输速度更快、传输信息更加丰富.     

Mineralization of Para-Chlorobenzoic Acid in Water by Cobalt-Incorporated MCM-41 Catalyzed Ozonation

Cobalt-incorporated MCM-41(Co-MCM-41) was used as a heterogeneous catalyst for the ozonation of para-chlorobenzoic acid (p-CBA) in aqueous solution. Cobalt oxide supported on MCM-41(Co/MCM-41) was synthesized for comparison. Their textural properties were elucidated by various characterization techniques to understand the relationship between surface texture and catalytic activity. TOC removal at 60 min reached 91% with Co-MCM-41, 83% with Co/MCM-41 and only 52% with ozone alone, respectively. Observations from diffuse reflection spectroscopy demonstrated that different metal phases were formed in these cobalt-modified molecular sieves samples. Radical scavenger experiments indicated the formation of hydroxyl radicals that were responsible for the effective degradation of p-CBA. An integrated approach to the catalytic mechanism was proposed by considering the variation of pH in the course of ozonation as well as its subsequent influence on the dissociation of targeted compounds and surface charge of the catalyst. In the reusability experiments, the reused Co-MCM-41 was able to regain the same catalytic capability as the fresh one within 5 cycles. X-ray photoelectron spectroscopy results indicated that a part of Co²⁺ was oxidized to Co³⁺ after oxidation reaction.     

微型步进马达线架组自动卷线设备设计

微型步进马达线圈组卷线上下料基本靠手动作业,效率低下,同时因工人技术水平的不同造成产品品质不稳定的问题多发.为此专门设计了微型步进马达线圈组自动卷线及上下料设备.通过结合现阶段的先进工业技术,采用振动盘分离区分进料,多机构并联三菱PLC及威纶人机界面触摸屏研发了此微型步进马达线圈组自动上下料及卷线设备.通过该设备实现了微型步进马达因工人不足导致产能减少和品质多发问题,减少企业成本,提升产品品质.     

Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.