Effect of annealing treatment on electrochemical property of LiNi0.5Mn1.5O4 spinel

LiNi0.5Mn1.5O4 was prepared under different cooling conditions. The electrochemical properties of LiNi0.5Mn1.5O4 prepared under different cooling conditions were investigated. The results show that LiNi0.5Mn1.5O4 synthesized with or without annealing treatment has similar X-ray diffraction patterns that can be indexed to cubic spinel structure. The mass loss occurring above 650℃ during the heating process can be mostly gained during the cooling process. LiNi0.5Mn1.5O4 synthesized with an annealing treatment exhibits almost one voltage plateau at around 4.7 V and higher capacity with a quick fading upon cycling, whereas LiNi0.5Mn1.5O4 synthesized without annealing treatment shows two voltage plateaus at around 4.1 and 4.7 V and superior capacity retention upon cycling both at rates of 1/7C and 1 C, though the capacity is not high.     

薄壁金刚石钻头的研制和在电熔锆刚玉耐火材料中的应用

电熔锆刚玉砖具有高硬度、耐高温、耐磨损、抗腐蚀等特点,因而成为玻璃熔窑的关键筑炉材料.文章通过复合电镀方法研制和生产薄壁金刚石钻头.在研制过程中,对金刚石钻头的胎体配方进行了优化,确定了电镀工艺参数,分析了金刚石参数等对钻进过程的影响,采用混目金刚石扩大了钻头的适用范围,提高了钻头的自锐性.研制的电镀薄壁金刚石钻头用于钻进锆刚玉砖耐火材料,其平均使用寿命达到6m,钻进时效为1.5m.使用结果表明胎体配方、工艺流程和电镀参数是合理的,电镀金刚石薄壁钻头是最适合钻进电熔锆刚玉砖的金刚石工具,加工后的锆刚玉砖具有精确的几何形状和高光洁度的表面.     

锂离子电池电解液过充添加剂的行为

制备了3种1 mol/L LiPF6电解液,溶剂组成分别为:1)碳酸乙烯酯,碳酸二甲酯和碳酸甲乙酯;2)碳酸乙烯酯,碳酸二甲酯,碳酸甲乙酯和4%联苯;3)碳酸乙烯酯,碳酸二甲酯,碳酸甲乙酯和4%环己基苯.采用线性电压扫描法、锂循环效率法、锂离子电池的循环性能法和3 C倍率过充的方法测试了联苯与环己基苯电解液过充添加剂的行为.结果表明:环己基苯是一种较实用的锂离子电池电解液过充添加剂,环己基苯的电化学稳定性比联苯的高,环已基苯的氧化电势为4.72 V(vs Li/Li ),联苯的为4.54 V(vs Li/Li );以1 mA电流循环20次后,联苯的铂电极锂循环效率为15.7%,环己基苯的为59.3%;锂离子电池以1 C循环150次后,环己基苯的容量保持率为88%,联苯的为76.3%.环己基苯与联苯添加剂都改善了锂离子电池的耐过充性能,且两者的效果十分接近.     

BK992萃取除铜净化硫酸镍钴溶液

以BK992为萃取剂,从废镍合金硫酸溶液中萃取分离铜,研究了pH值、相比(O/A)、BK992浓度和萃取时间对萃取的影响,确定了BK992萃取铜的优化条件.结果表明:BK992的萃铜速度很快,随着pH值升高,铜萃取率增大,但当pH大于4.0时,镍钴损失较大;相比越大,萃取分离效果越好;BK992浓度的影响也较大,随着BK992浓度增加,铜分配比增大.室温下BK992萃取铜的最佳工艺条件:BK992浓度为20%,相比O/A为1:2,水相初始pH为3.0,萃取时间为10 min.在优化条件下,待处理液的一级萃取率达93.06%,20%BK992萃铜的饱和容量为17.30 g/L;一级反萃率达91.79%,铜净传递量为15.88 g/L.     

Synthesis and characterization of LiNi0.45Co0.10Mn0.45O2 cathode for lithium ion batteries

1INTRODUCTIONAdvanced rechargeable lithium ion batteriesare attractive for use in consumer electronic andelectric vehicle(EV)application because of a fa-vorable combination of voltage,energy density,cycling performance,and have been developed rap-idly worldwide during the past decade[1,2].LiCoO2has been widely used as a cathode material in com-mercial lithiumion battery because it is reasonableeasy to synthesize and shows a stable discharge ca-pacity[3].But due to its high cost and toxic…     

钴酸锂的再生及其电化学性能

采用提取的含少量Co3O4的LiCoO2为原料,在不同温度下合成正极材料LiCoO2,烧结时间为12 h,并采用XRD和SEM技术研究合成的LiCoO2的晶相结构与微观形貌。结果发现:烧结温度对LiCoO2的晶体结构影响较大,烧结温度越高,LiCoO2的层状结构发育越完整。循环伏安曲线很好地反映了再生LiCoO2的脱/嵌锂行为。将LiCoO2样品做成电池进行电化学检测,结果发现,烧结温度为850℃的样品首次放电容量为151mA.h/g,30次循环之后,放电容量仍有141mA.h/g,表现出良好的电化学性能。     

三峡永久船闸导垂孔施工用电镀金刚石钻头的研制

为了满足导垂孔施工孔径大、垂直精度高（扎斜允许偏差在1‰以内）的要求，本文采用复合电镀技术研制出大口径会刚石钻头，所用胎体材料为镍钴合金，钻进金刚石的品级为MBD8、MBD10，其中MBD10占总量的60％，金刚石粒度分别为40／45、45／50、50／60、60／70，各种粒度的比例（质量比）分别为20％、30％、35％、15％。电镀金刚石钻头在室温下进行，pH值在3～5之间，电流密度在0．5—0．9A／dm^2范围内。文章还提出了基体设计和强化方案，分析了钢体、金刚石参数、胎体对钻进过程的影响，采用混目金刚石扩大了钻头的适用范嗣，提高了钻头的自锐性。使用结果表明：胎体配方、工艺流程、电镀参数和钢体强化没汁是合理的，研制的电镀金刚石钻头在二峡永久船闸倒垂孔钻进中，其平均使用寿命达到16米，钻进时效为0．3～0．5m．     

锂离子电池用石墨材料的结构与性能研究

研究了锂离子电池用石墨材料的结构与物理及化学特性对其电化学性能的影响。采用XRD、BET、ICP、激光粒径分析等方法 ,对多种典型石墨样品的结构、比表面积、杂质含量、粒径分布进行了表征分析。随着石墨颗粒粒径的增大 ,石墨试样的比表面积减小。电化学性能测试表明 :在石墨材料的石墨化度非常接近的情况下 ,粒径和比表面积对电化学性能的影响较为突出 ,粒径较大及比表面积较小的石墨材料具有较好的充放电性能。试样D具有较高的可逆容量 ( 2 62mAh/g)和较低的不可逆容量损失 ( 85mAh/g) ,首次充放电效率为 75 .5 % ,适用作锂离子电池负极的原材料     

正极材料LiNi0.5Mn0.5O2的合成及其性能研究

用共沉淀法制备镍锰氢氧化物前驱体,并通过高温固相反应在800℃空气气氛下煅烧12h合成锂离子蓄电池正极材料LiNi0.5Mn0.5O2,研究了冷却速度和升温制度对材料电化学性能的影响。结果表明,在500℃预处理5h,800℃煅烧完毕立即从炉中取出,环境温度下在空气中冷却,得到的样品比容量能达到180mAh·g-1,材料在2.5～4.6V范围内循环时性能不佳,当采用恒流/恒压模式,在2.5～4.3V范围内,材料具有良好的循环性能。     

中间相炭材料包覆天然石墨球

以煤焦油为原料在天然石墨球表面包覆一层中间相炭材料制备出一种复合炭材料.研究了天然石墨球加入量对复合炭材料电化学性能的影响.结果表明:随着天然石墨球添加量的减小,复合炭材料的充放电容量增加,首次充放电效率减小.在200 mL煤焦油中加入70 g天然石墨时所制备的复合炭材料经700℃热处理2 h后性能最佳,可逆比容量达378 mAh/g,充放电效率为91.3%.复合炭材料的循环性能得到了充分改善,30个周期容量保持率97.04%.