闪光灯泵浦Nd3+:GGG激光特性研究

用闪光灯泵浦掺钕钆镓石榴石(Nd^3 ：GGG)激光晶体，研究了脉冲宽度0．5ms、1ms、1．5ms和2ms的放电泵浦下激光输出，实验获得了1．92J的最大激光能量．     

Study on Luminescence Properties of High-Density Phosphors BiTaO4∶Pr3+ and BiTaO4

The photoluminescence properties of BiTaO4∶Pr3+ and BiTaO4 at room temperature were studied, and the infrared transmission and diffusion reflection spectra of BiTaO4 were measured. The photoluminescence spectrum of BiTaO4 peaks at about 420, 440 and 465 nm. There has an obvious excitation band from 330 to 370 nm. The photoluminescence spectrum of BiTaO4∶Pr3+ consists of the characteristic emission of Pr3+, and its main peak is at 606 nm from 3P0→3H6 transition of Pr3+. Its excitation spectrum consists of the wide band with maximum at 325 nm, the wide band in the range of 375～430 nm, and the characteristic excitation of Pr3+. The bands at 325 nm and 375～430 nm may be from the absorption of the charge transfer transition of the tantalate group and defect energy levels in its forbidden band, respectively. There is energy transfer from host to Pr3+. Because both the host density and photoluminescence peak intensity of BiTaO4∶Pr3+ are superior to PbWO4, BiTaO4∶Pr3+ may be a potential heavy scintillator.     

Study on Luminescence Properties of High-Density Phosphors BiTaO4：Pr^3＋ and BiTaO4

The photoluminescence properties of BiTaO4:Pr^3 and BiTaO4 at room temperature were studied, and the infrared transmission and diffusion reflection spectra of BiTaO4 were measured. The photoluminescence spectrum of BiTaO4 peaks at about 420, 440 and 465nm. There has an obvious excitation band from 330 to 370nm. The photoluminescence spectrum of BiTaO4:Pr^3 consists of the characteristic emission of Pr^3 , and its main peak is at 606 nm from ^3P0→^3H6 transition of Pr^3 . Its excitation spectrum consists of the wide band with maximum at 325nm, the wide band in the range of 375-430nm, and the characteristic excitation of Pr^3 .The bands at 325nm and 375-430nm may be from the absorption of the charge transfer transition of the tantalate group and defect energy levels in its forbidden band, respectively.There is energy transfer from host to Pr^3 . Because both the host density and photoluminescence peak intensity of BiTaO4:Pr^3 are superior to PbWO4, BiTaO4:Pr^3 may be a potential heavy scintillator.     

热容模式下LD阵列泵浦Nd:GGG圆盘的温度场分析

为了研究Nd:GGG激光晶体圆盘在热容运行模式下的温度场分布及变化问题,根据实际情况建立物理模型进行了分析.从热传导微分方程出发,通过格林函数法求得激光器工作、冷却阶段晶体内部温度场的解析解,在一定程度上可以反映温度场的变化情况.数值计算了矩形LD光斑尺寸3 cm,泵浦功率8100 W、脉冲频率500 Hz、脉冲宽度0.2 ms条件下泵浦4 s后圆盘的温度场以及变化曲线,得到4 s末的最大应力已经达到晶体断裂极限的47%.采用280 K、290 K的温度分别对圆盘进行背面冷却时,需要60～70 s左右的冷却时间;当采用280 K对圆盘进行背面和侧面同时冷却时,冷却时间缩短到30 s左右.     

高压胶带输送机控制方案探讨

通过分析胶带机设备在选矿系统中的作用和对电气控制的要求,以高压异步电动机的直接启动为基础,对高压胶带机的控制进行方案设计,包括胶带机的启动预告、启动控制、停机控制及故障检修等环节,以合理的方案满足胶带机的电气控制要求,保证设备正常运行。     

Yb,Er,Eu:YAP中红外激光晶体的生长与光谱特性

用提拉法成功生长出3种不同掺Eu3+浓度的优质Yb,Er,Eu:YAP激光晶体,并对其光谱特性进行了研究。测量了晶体在320~3 000nm波段内的吸收光谱,晶体在978nm附近有强的吸收峰和宽的吸收带。用波长为975nm的LD连续激光和OPO光参量脉冲激光激发分别获得了晶体的稳态和瞬态荧光光谱,采用单指数衰减拟合得到2.7~3.0μm激光上下能级寿命。与单掺Er:YAP晶体的光谱参数进行了比较,对Yb3+的敏化及Eu3+的退激活机理进行了分析。结果表明,Yb3+和Eu3+可分别作为Er3+的敏化剂和退激活剂,增宽978nm附近的吸收带和降低激光下能级(4I13/2)与上能级(4I11/2)寿命的比值(4.1,3.1和2.7);而在单掺Er:YAP晶体,下能级与上能级寿命的比值高达10.8,不利于激光性能的提高。因此,Yb,Er,Eu:YAP是一种更适合LD泵浦,有望实现低阈值、2.7~3.0μm高效率激光输出的新型激光晶体。     

Nd3 :Gd3Ga5O12激光晶体的吸收与发光

测量了用提拉(CZ)法生长的Nd3+Gd3Ga5O12(NdGGG)激光晶体室温时的吸收光谱,其中在806 nm处的吸收系数最大(α＝5.12 cm-1),吸收截面为4.03×10-20 cm2.用806 nm激发分别得到室温和10 K时的荧光光谱和荧光寿命,其中在1.06 μm附近晶体的荧光发射强度最强,2种温度时的峰值发射截面分别为1.7×10-19 cm2和1.9×10-19 cm2.0.6 at%和1.0 at%2种Nd3+掺杂浓度的晶体,室温时的荧光寿命分别为251 μs和240 μs,10 K温度时分别为253 μs和241 μs.与NdYAG晶体的荧光寿命、浓度猝灭效应和发射截面进行了比较,对结果进行了分析与讨论.     

最小二乘法计算晶格参数

最小二乘法是求解精确晶格参数的基本方法.讨论了使用和不使用校正函数情形下的科恩最小二乘法,给出了所有晶系的法方程、晶格参数、误差估计的计算公式,以及计算晶格参数、校正函数参数的阻尼最小二乘迭代算法,该方法具有普适性,有大的收敛范围和快的收敛速度.作为应用例子,计算了数个不同晶系晶体的晶格参数,说明最小二乘法是获得高精度晶格参数的计算方法;用阻尼最小二乘法计算了ChuG校正函数的参数,表明该方法是获得校正函数参数的有效方法.     

高精度磁测在内蒙古阿拉善盟雅布赖地区1:5万区域矿产地质调查中的应用

在内蒙古自治区阿拉善盟雅布赖地区开展了1:5万高精度磁测,对磁测数据采用滤波、化极、延拓、导数换算、小波断裂分析等处理,对磁异常进行分析研究,对区内岩性界线、断裂构造进行划分,直接或间接发现多个矿化点,为研究区内以铜、铁、镍、金为主的矿产成矿规律和圈定成矿预测区及找矿靶区提供了地球物理信息。同时指出了高精度磁测在区域地质填图、断裂构造研究及区域成矿预测方面的作用。     

Nd3+:Gd3Ga5O12单晶的能级和晶体场计算

测试了Nd3+:GGG单晶在可见和近红外波段的吸收光谱,并分析指认了它的实验能级,通过从头计算的DV-Xa方法计算得到了它的晶体场参数和旋轨耦合参数。用Nd3+:GGG在77K和300K的156个、88个实验能级,拟合了它的自由离子参数和晶体场参数,均方根误差（即拟合精度）σ分别为15.79和 11.48 cm-1。结果表明晶体场参数的拟合结果和从头计算值符合的很好。最后比较了拟合得到的Nd3+:GGG和已报道Nd3+:YAG 的自由离子参数和晶体场参数。