F离子掺杂TiO2的性能研究

以NH4F为掺杂剂，采用溶胶-凝胶法制备F离子掺杂型TiO2光催化剂，对其进行XRD、XPS和PL表征，结果表明，F离子掺杂ToO2由于Ti—F配位体的形成而能抑制金红石相的生成，同时F离子掺杂能增加TiO2表面缺陷浓度并降低Ti2P键的结合能，另外，由于F离子能取代Ti—OH配位体而降低了表面羟基氧浓度．光催化研究结果表明，F离子掺杂提高了TiO2光催化活性近1．5倍．     

几种非金属矿物基陶瓷分离膜的制备和表征

多孔陶瓷膜的应用广泛，但是由于制造成本高，推广使用受到制约。为了降低多孔陶瓷的成本，并开发多孔陶瓷膜的新功能、新用途，本实验室以廉价非金属矿物（天然沸石、硅藻土和粉煤灰等)为原料，采用合适的制备工艺，以高温除尘和工业废水处理为主要研究方向，制备出新型的多孔陶瓷膜，并对其性能进行了表征。     

sol-gel法制备镉掺杂铁酸镧气敏材料

研究了气敏材料的制备条件、相组成、电导和气敏性能。结果表明:固溶体La1–xCdxFeO3(0≤x≤0.15)呈典型的p型半导体。270℃操作温度下,掺杂x(Cd2+)为25%的LaFeO3材料(700℃下热处理4h)对浓度为4.5×10–5mol·dm–3的C2H5OH的灵敏度达81.5。有望开发为一类新型的酒敏传感器。     

混凝-陶瓷膜微滤处理阴极电泳漆废水研究

提出用混凝与陶瓷膜微滤组合工艺处理阴极电泳漆废水的方法,研究了pH值对CODCr去除率的影响,操作压差、膜面流速对膜通量的影响,得到了适宜的操作条件和有效的膜清洗方法.结果表明:料液pH值为6.7时,混凝过程对CODCr去除率的贡献约63%,之后的微滤使废水中CODCr的去除率增加到85%.采用平均孔径为0.2μm的氧化锆膜,在膜面流速4.2 m/s,压差0.10 MPa,温度30℃,膜稳定通量约250 L/(m2.h),渗透液可作为涂装车间循环冲洗水用.混凝作为前处理过程有助于提高膜的渗透通量,降低膜污染,改善出水水质.     

YFe1-yCoyO3半导体气敏材料的制备和性能研究

用化学共沉淀法制备了YFe1-yCoyO3（0．0≤y≤0．05）固溶纳米晶微粉，并对其制备条件，物相组成，微结构，电导和气敏效应作了系统研究，结果表明，钴B位掺杂铁酸钇材料呈典型的P型半导体导电行为，同温下固溶体电导不仅大于纯相YFeO3的电导而且随湿度增加其电阻迅速下降，243℃下YFe0.9Co0.1O3传感器元件对乙醇有较高的灵敏度和良好的选择性，有望开发为一类新型C2H5OH3信息敏感材料。     

α－（Sb_xFe_（1－x））_2O_3半导体的固溶与导电机制的相关性

用化学共沉淀法，经热处理制得ｎ型半导体α－（ＳｂｘＦｅ１－ｘ）２Ｏ３．ＸＲＤ分析确证０≤ｘ≤０．２是固溶体．实验发现在ｘ≤０．０３区间内材料电阻降低幅度很大，而在ｘ＝０．０３～０．２区间的电阻却缓慢上升，根据体系中存在缺陷平衡，讨论其原因和导电机制；相应於此缺陷平衡的Ｓｂ３＋和Ｓｂ５＋的含量由ＸＰＳ分析予以证实．     

硅藻土多孔陶瓷的耐蚀性及酸/碱处理研究

采用注浆成型的方法制备硅藻土多孔陶瓷，对不同温度烧结样品的耐酸、碱腐蚀性进行了研究。材料的耐酸蚀性优于耐碱蚀性。硅藻土多孔陶瓷经过酸或碱处理后，微观结构和宏观性能会发生相应变化，也可利用这一特性通过酸或碱处理来控制瓷的微结构和过滤性能，碱处理样品、酸处理样和原始样品的氮气通量分别为1189、802和677m^3m^-2h^-1bar^-1。     

Microwave assisted synthesis,sinterability and properties of Ca-Zn co-doped LaCrO_3 as interconnect material for IT-SOFCs

The interconnect materials La0.7Ca0.3Cr1-xZnxO3-δ(x=0,0.01,0.03,0.05,0.07) were prepared by a microwave assisted sol-gel auto-ignition process.The crystalline structures of the samples were characterized by X-ray diffraction(XRD) and the lattice parameters were evaluated with Rietveld method.For Ca-Zn co-doped LaCrO3 with x=0.03,the sintering activity was improved,and the relative density came up to 96.5% for the sample sintered at 1300 oC for 10 h.The electrical conductivity of the samples was increased from 21.1 S/cm to the maximum of 70.9 S/cm at 650 oC in air,with the x content increasing from 0.01 to 0.03.However,with x further increasing,the electrical conductivity was decreased.The average thermal expansion coefficient(TEC) of the samples at RT-1000 oC in air was ca.10.0×10-6 K-1.All data indicated that the La0.7Ca0.3Cr1-xZnxO3-δ series ceramics would be potential candidate to be used as an interconnect materials for IT-SOFCs.     

以Ni-YSZ和Sm0.5Sr0.5Fe0.8Cu0.2O3-δ为电极的微管固体氧化物燃料电池的制备及电化学性能（英文）

分别以Ni-YSZ中空纤维为阳极和Sm0.5Sr0.5Fe0.8Cu0.2O3–δ–Sm0.2Ce0.8O1.9（SSFCu-SDC）为阴极制备了微管固体氧化物燃料电池（SOFC）。利用扫描电子显微镜（SEM）、电化学工作站表征了微管单电池的显微结构与电化学性能。SEM分析表明,采用相转化法制备的Ni-YSZ中空纤维阳极呈特殊的非对称结构,主要由中间海绵状结构和内外两侧的指孔状多孔结构构成。通过真空辅助浸渍涂覆法和与阳极共烧技术在阳极支撑体上制备了致密的YSZ电解质膜和SDC过渡层。分别采用湿氢为燃料和静态环境空气为氧化剂测定了制备的微管单电池在650～750℃时的电化学性能。结果表明,该微管单电池具有高的输出性能,在750、700℃和650℃时的最大功率密度分别可达到485.9、382.7mW/cm2和260.3mW/cm2。