以江西区域内典型红黏土边坡为研究对象,基于岩土非饱和渗流理论,建立红黏土边坡有限元计算模型,对4种典型降雨工况下红黏土边坡稳定性进行分析。结果表明,降雨强度、降雨持续时间均是影响红黏土边坡稳定性的重要因素;前期为常态时,边坡各参数指标均维持在初始稳定状态;降雨开始后,边坡安全系数呈减小态势,岩土体强度和稳定性降低,边坡中土体的孔隙水压力变大,体积含水量升高;越接近地表的土体降雨入渗响应越强烈,边坡不同位置处土体的降雨入渗影响程度依次为:坡肩>坡顶>坡面>坡脚>坡底;降雨入渗和互渗过程具有明显的滞后性,越靠近地表,孔隙水压力短期内变化越明显;土体干湿循环对边坡稳定性整体表现为负作用,且作用效果不可逆。     

铸造Al-5Cu合金准固态断裂行为的研究

采用SEM观察手段并结合EDX分析 ,在合金的准固态区 ,通过观察Al 5Cu Mn合金准固态拉伸和热裂应力测试试样的断口形貌 ,研究了Ti、Ce等合金元素及其交互作用对Al 5Cu Mn合金准固态断裂行为的影响及其影响机理。通过对试验合金准固态力学性能的测试和大量SEM断口的观察分析研究 ,结果表明 ,Al 5Cu Mn中添加Ti元素可明显提高合金抗热裂能力 ,主要是由于其良好的细化晶粒效果 ;适量Ce元素的加入 ,不仅可细化晶粒 ,而且其在晶间富集形成的化合物还可有效改善低熔点共晶反应在准固态区的力学行为 ,对减小热裂倾向非常有利 ;Ti和Ce的综合作用对合金抗热裂水平的提高比单一元素更有效 ;热裂的产生首先表现为枝晶枝臂的屈服 ,其后的扩展则表现为脆性断裂占优的穿晶、沿晶混合型特征     

Research of quasi-solid fracture behavior of casting Al-4.5Cu alloys

The influencing mechanisms of elements Ti and Ce and their interactions on fracture behaviors of casting alloys Al-4.5Cu-0.6Mn were studied by observing tensile fracture behavior in quasi-solid zone under SEM and EDX instruments.The results indicate that the resistance stress against hot cracking can be improved obviously by addition of Ti, because of its grain refining function. It is also found that, when Ce is added into the alloys, besides its effect in refining crystalline, the mechanical behavior of lower melting point eutectic phase in quasi-solid zone can be improved efficiently by some compounds with Ce formed and deposited between dendrites. Therefore, a coiligating effect of Ti and Ce on improving resistance stress against hot cracking is more efficient than that only single alloy element is applied. When hot cracking occurs, grains yield at first, and then crack spreads. Both inter-grain and trans-grain fractures are observed, but the major fracture manner is brittleness.     

Au—9Ni—8In合金表面铟离子注入层的微观组织与性能的研究

利用透射电镜观察Au-9Ni-8In合金表面In~+注入后的微观组织,并分析有关性能的变化。研究结果表明,In~+注入使合金表层晶粒细化,晶格畸变,位错密度降低;表层组织的变化使合金的表层显微硬度提高,摩擦和磨损性能得到改善。     

Research on the creep damage and interfacial failure of dissimilarmetal welded joint between 10Cr9Mo1 VNbN and 12Cr1MoV steel

0　IntroductionAnewmodified 9Cr Mosteel (SA2 13T91orT91)pos sessesimprovedhightemperaturestrength ,excellentductili ty ,weldability ,heatfatigueproperties .Therefore ,T91hasbeenwidelyusedinelectricpower,petrochemicalplant,nu clearpowerstation ,andsoon[1～3] .Itisappliedtothefinalstagesofsuperheatersandreheatersinfossil firedpowerplants .However,lowalloypearlitesteel(12Cr1MoV)isstillusedintheearlierstages .Thus,therearealotofdissimilarmetalweldedjoints (DMWJs)betweenSA2 13T91and12Cr1Mo…     

Kernel-based adversarial attacks and defenses on support vector classification

While malicious samples are widely found in many application fields of machine learning, suitable countermeasures have been investigated in the field of adversarial machine learning. Due to the importance and popularity of Support Vector Machines (SVMs), we first describe the evasion attack against SVM classification and then propose a defense strategy in this paper. The evasion attack utilizes the classification surface of SVM to iteratively find the minimal perturbations that mislead the nonlinear classifier. Specially, we propose what is called a vulnerability function to measure the vulnerability of the SVM classifiers. Utilizing this vulnerability function, we put forward an effective defense strategy based on the kernel optimization of SVMs with Gaussian kernel against the evasion attack. Our defense method is verified to be very effective on the benchmark datasets, and the SVM classifier becomes more robust after using our kernel optimization scheme.     

直流PWM伺服系统的一种新型控制器

文章设计了一种新型的直流PWM自适应变结构控制器，并且采用了非线性反馈技术，理论分析与实验表明该系统获得良好的快速性、准确性和鲁棒性。     

Preparation and properties of polymer-encapsulated phthalocyanine blue pigment via emulsion polymerization

Polymer-encapsulated phthalocyanine blue pigment dispersion was prepared with a polymerizable dispersant by emulsion polymerization method, and the effect of preparation conditions on the particle size of dispersion was investigated. Dynamic light scattering measurement demonstrated that allyloxy nonyl-phenoxypropanolpolyoxyethyleneetherammonium sulfonate (ANPS) was suitable for phthalocyanine blue pigment modification. The polymer-encapsulated phthalocyanine blue pigment dispersion with the small particles was obtained when the mass ratio of ANPS to phthalocyanine blue pigment, styrene (St) to phthalocyanine blue pigment, and ammonium persulfate (APS) to St was about 0.2, 0.2, and 0.01, respectively. Transmission electron microscopy (TEM), Fourier transforms infrared spectra (FTIR) and thermogravimetric analyses (TGA) provided supporting evidences for the encapsulation of phthalocyanine blue pigment with the formed copolymer. The polymer-encapsulated phthalocyanine blue pigment dispersion showed excellent stabilities to freeze–thaw treatment and centrifugal force.     

Mechanism and properties of coloured nanoscale SiO2 prepared from silica and reactive dyes

KH560‐modified SiO₂ was prepared using tetraethyl orthosilicate (TEOS) and γ‐(2,3‐epoxypropoxy) propytrimethoxysilane (KH560) by the sol–gel method and then coloured with CI Reactive Blue 4 (X‐BR) to prepare coloured nanoscale SiO₂. The antisolvent performance and the results of cross‐polarisation/magic angle spinning ¹³C nuclear magnetic resonance and Fourier transform infrared spectroscopy showed that the reaction of X‐BR with KH560‐modified SiO₂ is a two‐step process: X‐BR is firstly adsorbed by KH560‐modified SiO₂ via van der Waals forces, and then nucleophilic substitution occurs between dichloro triazine and the epoxy group. The grafting ratio of X‐BR on KH560‐modified SiO₂ reached 95% under optimum conditions, i.e. a mass ratio of KH560 to TEOS of 20%, a temperature of 40 °C, a pH of 8.5, and a reaction time of 5 h. X‐ray diffraction analysis and transmission electron microscopy showed that the coloured nanoscale SiO₂ was amorphous, with a mean diameter of 216 nm. Experimental application showed that the coloured nanoscale SiO₂ had excellent stability to solvents and alkaline solution, and the absorptive capacity of the coloured nanoscale SiO₂ in the 200–400 nm region was higher than that of X‐BR. The light fastness of the coloured nanoscale SiO₂ reached 5–6 grade.