1.
In polymer modified cementitious materials, it is hard to set up a chemical connection between the added polymer and the cement moiety. In this study FS (functional silane) was adopted to form this connection as a bridge component which has the functional group forming bonds with polymer. To testify the connection between FS and cement moiety, Q2/Q1 ratio (Qx: intensity ratio) investigation was carried out by the means of quantitative solid state 29Si MAS NMR. The results show that the Q2/Q1 ratio has increased with the addition of FS which indicates that the silicon chain length has increased, and the quantity of silicon atoms at site of Q2, chain site, has enhanced, showing that the silicon atom of FS has connected to the silicon chain of cement moiety by the bond "-Si-O-Si-" formation. 相似文献
2.
早强磷硅酸盐水泥的制备和性能 总被引:23,自引:0,他引:23
以MgO含量较低的镁砂和粉煤灰为主要原料,制备了磷硅酸盐胶凝水泥(MPSC),研究力学性能.结果表明,磷硅酸盐水泥凝结快,早期强度高.掺入30%-50%的粉煤灰可明显地提高MPSC的早期和长期抗压强度,其中以粉煤灰掺量为40%效果最好.使用MgO含量较高而且颗粒较细的镁砂,制备出的水泥具有较高的强度.水泥石的水化产物以无定形为主,伴以少量的六水水化磷酸镁钾晶体.硬化水泥石中有许多未水化的镁砂,可作微集料.粉煤灰填充了反应物之间的空隙,使基体的密实度提高;粉煤灰参与水化反应提高了材料的胶凝性能. 相似文献
3.
4.
采用电阻率法研究水泥水化过程 总被引:39,自引:4,他引:35
用无接触电阻率测定仪测定了不同水灰比水泥浆基体的电阻率随时间变化的特征曲线ρ(t)-t,研究了普通硅酸盐水泥的水化特性。研究表明:基体电阻率ρ(t)是液相电阻率ρ0(t)和孔隙率φ的函数。实验结果说明:根据基体电阻率曲线的特征点将水泥水化过程划分为溶解期、诱导形成期和诱导期、凝结硬化期3个阶段。钙矾石包裹层的形成导致水化进入诱导期,渗透压导致包裹层的破裂,使水化进入凝结硬化期。溶解期电阻率的下降主要与水泥浆体中液相离子浓度的增加相关。诱导形成期和诱导期电阻率变化小,此时液相离子浓度和孔隙率的变化都较小,凝结硬化期电阻率的上升主要与水泥浆体孔隙率的下降相关。 相似文献
5.
6.
无机胶粘贴纤维布加固钢筋混凝土梁高温性能试验研究 总被引:2,自引:0,他引:2
常用的环氧树脂类有机粘结剂难以承受100℃以上的高温,采用无机粘结剂(MOC)来粘结纤维布加固钢筋混凝土结构,以期改善耐火性能。首先试验了这种无机粘结剂在常温下的各种性能,并对分别采用MOC和环氧树脂作为粘结剂的纤维布加固素混凝土小梁在常温下的受弯承载力进行了比较,证实用MOC作为粘结剂是可行的。随后进行了100℃~400℃间4种高温下MOC的各种性能试验,结果表明,在温度低于300℃时,MOC能保持较好的加固性能,当温度达到400℃时,MOC的各种性能下降很多,这主要是由其成份中结晶水损失过多所致。理论研究发现,混凝土的抗拉强度在300℃时也已降到原来的52%,使胶与混凝土的粘结强度降为原来的72%,因此,建议在使用MOC作为粘结剂时,碳纤维布外表面应采用防火涂层,使胶层处的温度小于300℃。 相似文献
7.
8.
9.
10.