我国铸造有色合金及其特种铸造技术发展现状

结合我国在铸造有色合金领域的发展概况,从合金发展、应用和有色合金熔体技术以及特种铸造在有色合金中的应用角度,分析了五十年来我国在该领域所取得的成绩和存在的问题,以引起广大科技工作者和生产技术人员对这方面自主创新的重视,不断提高铸造有色合金的技术水平,扩大其应用领域。     

Microstructure and mechanical properties of high strength as—cast Ti—15—3 alloy

The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as-cast Ti-15-3 alloy prepared by induction skull melting method were investigated.Results show that the microstructure of as-cast Ti-15-3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate.After solution treatment and different ageing treatment,alpha phase precipitates in grains interior as well as in grain boundaries.Due to the modification of the precipitate phase,the tensile stength and elongation of the alloy are improved simultaneously.A good combination of the values of 1.406GPa of σb and 4.5% of δ was obtained,which will be satisfied the use of this kind of alloy in critical areas.     

钛合金冷坩埚电磁约束铸造工艺研究

针对液态下化学性质相对活泼的钛合金,采用冷坩埚技术对电磁约束铸造工艺过程进行了试验研究,考察了工艺条件对成形坯件表面质量和内部组织的影响.结果表明:试样抽拉速度变化对表面质量和宏观组织的影响明显,加热功率虽然对组织变化影响不大,但对表面质量影响较为显著.通过优化工艺,可以获得既有较光滑铸造表面又具有一次定向凝固组织的钛合金铸件.讨论了铸造过程裂纹和组织缺陷的形成机理,获得到了表面光滑无裂纹,宏观组织为柱状晶的钛合金大尺寸圆坯.     

A357合金中铁的有害影响

在工业生产条件下熔炼Ａ３５７合金，易使合金增铁。铁在Ａ３５７合金中主要形成三种金属互化物；汉字状α相，板片状β相和粗大π相。Ｔ６处理后，β相基本上不发生变化，π相则固溶于α－Ａｌ中。合金含铁量增加使β相增多，使合金的伸长率急剧下降。     

Ti-47Al-1.2Ce合金显微组织及富稀土相的形貌

采用水冷铜坩埚真空感应熔炼炉制备了Ti-47Al-1.2Ce合金.通过XRD,SEM,EMPA和TEM等测试方法,研究了Ce对TiAl基合金显微组织的影响以及富稀土相的形貌.实验结果表明,铸态Ti-47Al-1.2Ce合金由等轴晶组成,富稀土相主要以椭球形存在于晶内和以网状存在于晶界;稀土元素的加入,可以减小TiAl相的单胞体积,细化合金晶粒尺寸和层片间距.     

冷坩埚熔铸技术的研究及开发现状

综述了冷坩埚技术的原理和特点、目前的研究及开发现状。冷坩埚具有无污染，可熔化高熔点金属，制备的材料组织均匀等优点。冷坩埚技术在以下领域得到广泛的研究和应用：与熔化技术相结合能高纯均匀熔炼活性金属，通过起熔材料能制备陶瓷材料；与连铸技术相结合能进行冷坩埚电磁连铸技术，提高铸锭表面质量，改善内部组织；与定向凝固和连铸技术相结合的冷坩埚定向凝固技术已成功进行钛合金的定向凝固；与多晶硅制备技术相结合能连续制备多晶硅，杂质含量少；与雾化沉积技术相结合的冷坩埚雾化沉积技术具有熔化合金种类多、适用范围广的优点。冷坩埚的自身特点决定了其必将更受重视和广阔发展前景。     

Equivalent heat transfer coefficient at casting/Cu mould interface and temperature field simulation

1　INTRODUCTIONThesolidifiedmicrostructuresofalloysdependontheirsolidifyingprocesswhoseprimarycharacteristicsarethetemperaturedropofthesuperheatedmeltandthere leaseofthelatentheat.Sothestudyontheheattransferduringthesolidificationprocessistheessentialprobleminthesolidificationtheorystudy .Theresearchersworkingonthenumericalsimulationofthesolidificationprocessallknowthattheinterfacialheattransfercoefficientatthecasting/mouldisavariablechangingwithtime .Thusthedeterminationoftheinterfacialh…     

硅对压铸模与铝合金相互作用的影响

为了研究压铸模与铝合金的相互作用 ,探讨Si对压铸模与铝铸件焊合倾向性的影响 ,进行了热浸铝试验。试验结果表明 ,模具钢在纯铝熔体中热浸时 ,主要形成Fe2 Al5相层和针片状的FeAl3 相 ,Fe2 Al5相是反应扩散的主导相。模具钢在A3 80合金中热浸时 ,主要形成FeSiAl3 和Fe2 Al5两种相层。由于Si降低了Al在FeSiAl3 相层中的活度 ,减少了从铝熔体向Fe2 Al5相供应的铝原子数 ,从而抑制了Fe2 Al5相的快速生长。因而 ,Si减弱了铝合金熔体与模具钢间的相互作用 ,从而降低压铸合金的焊合倾向性。热浸温度降低 ,Si对Fe2 Al5相层生长的抑制作用减弱     

电磁铸造移动磁场发生器磁场分布规律及其作用分析

研究了用于电磁铸造的移动磁场发生器上磁场强度变化及其对金属产生的力的作用.结果表明,磁感应强度分量By和Bz的变化趋势相反.By的存在使金属流动充型过程中产生表面凹坑型缺陷,Bz明显提高金属液流动速度,而在提高充型能力的同时,会使金属液流前端截面减小而形成反向充填,引发冷隔缺陷.铁磁性上模可以减弱By、增强Bz,提高表面质量.金属在移动磁场中受到的力与其投影面积有关,而且存在临界投影面积,小于该临界值后,电磁力不足以拉动该金属.     

过滤净化对LD10合金热轧板材疲劳性能的影响

一、前言随着现代航空和宇航工业的发展,不但要求变形铝合金制品有很高的强度,而且要有很高的抵抗疲劳断裂扩展的能力。否则,尽管合金材料强度很高,但综合性能不佳,就极易发生毁灭性的低应力脆断事故,这样的教训在国内外所见不少。近二十年来,人们用电子显微镜