The modification behaviour for Si implanted PET

Polymeric solids have low density, high ability to form intricate shapes, versatile electronic properties and low manufacturing cost. However their uses are still limited by their inherent softness and unexpected dielectric properties. In order to enhance their electrical and mechanical properties, ion implantation techniques have been explored[1—3]. Recent studies have shown that ion implantation is very effective for improving surface properties of polymers such as surface hardness and wear…     

钼离子注入硅薄层硅化钼的合成

用大束流密度的钼金属离子注入硅，能够直接合成性能良好的薄层硅化物。随着束流密度的增加，硅化钼生长，薄层硅化物的方块电阻Ｒｓ明显下降，当束流密度为０．５Ａ／ｍ＾２时，Ｒｓ达到上值９０Ω，说明连续的硅化物已经形成。Ｘ衍射分析结果表明，注入层中形成了３种硅化钼Ｍｏ３Ｓｉ、Ｍｏ５Ｓｉ３和ＭｏＳｉ２。经过９００℃退火后，Ｒｓ下降至４Ω，电阻率可小到０．１６μΩ．ｍ，说明硅化钼薄层质量得到了进一步的改善。大束     

岩石中稀土元素中子活化分析时Na、Sc、Fe Cr等干扰元素的去除

稀土元素的分离、分析,在地球化学、宇宙化学、环境化学等学科中起着极为重要的作用。近年来,国内外利用高分辨率γ谱仪中子活化分析法测定岩石中稀土元素的报道很多,虽然对放射化学分析流程都在不同程度上有所改进,但对超基性岩石中大量存在的~(24)Na、~(46)Sc、~(59)Fe和~(51)Cr等核素的去除,解决被测元素γ谱之间相互干扰(包括重峰干扰和康普顿本底干扰)     

钨和碳双注入H13钢抗磨损和抗腐蚀特性

首次研究了钨和碳双注入对抗磨损和抗腐蚀特性的影响，研究了抗磨损和抗腐蚀相生成的条件，以及这些相对抗磨损和抗腐蚀特性的作用，并对其改进机理进行了讨论。实验结果表明，钨和碳双注入H13钢可注入层中形成超饱和的钨和碳原子浓度。因此在注入层中形成钨的碳化物WC和W2C相，合金相Fe2W和Fe2W6C等，这些弥散相不但可以使注入具有钨和碳单注入的特性，所以能进一步地提高H13钢的抗腐蚀性，随着W和C注入剂量的增加，抗磨损和抗腐蚀特性进一步提高，抗磨损特性可改善2倍，双注入样品抗腐蚀特性也有明显也提高，如样品W5C8的腐蚀电流峰值密度Jp经55个周期腐蚀后，其值是H13钢Jp的1／26.7-1/33.3，而钨样品C5W5经过88个周期腐蚀后，其值是H13钢的1／16－1／20。     

高能Si~+注入Sl-GaAs形成n型埋层

本文报导0.6～5MeV高能Si~+离子注入LEC半绝缘GaAs的快速退火效果,在950℃温度下退火5秒得到最佳电特性.采用多能量叠加注入已制备出平均深度在1.2μm,厚约1.7μm的n~+深埋层,载流子浓度为3～5×10~(17)cm~(-3).在近表面单晶层上作成了性能良好的肖特基接触,其势垒高度约为0.7V.     

0.5—7.5MeV高能磷离子注入硅中剖面分布及剖面迭加

本文对磷离子能量在0.5—7.5MeV、剂量在2.0×10~(12)—1.0×10~(13)/cm~2范围内注入硅中的载流子剖面进行了研究,发现在此条件下,n型磷载流子剖面是由两个只有不同偏差σ_(tront)(σ前)和σ_(back)(σ后)的高斯分布相连接组成的。根据实验所得剖面特性,提出了多次迭加形成平坦剖面的方法。用这种方法结合SiO_2膜屏蔽和调整注入离子能量、剂量,能够获得各种有特殊要求的载流子浓度剖面。为了得到好的可控性和可重复性,采用了瞬态退火技术。透射电镜分析表明:在我们所用退火条件下,剩余缺陷并未出现。这种迭加注入已应用于特种器件研制中,试制出的产品获得令人满意的结果。     

钛注入钢退火中纳米相镶嵌结构的形成和表面强化

透射电子显微镜观察表明,经过Ti注入的钢,表面形成了直径为3.5～20nm的FeTi_2相,镶嵌在注入层中,其平均直径为8nm。靶温在400℃注入时,这些纳米相出现在位错和晶界处。这种镶嵌的结构具有很强的抗磨损特性和抗腐蚀特性。经过退火后,这种结果将发生变化。在350～500℃退火20min后,其结构没有明显的变化,但是注入层的硬度得到了明显的提高。经过500℃退火后,表面硬度最高。说明退火能有效地增强表面强化效果。当退火温度为750℃和1000℃时,位错和晶界消失,纳米相平均直径分别增加到10 nm和15 nm。其平均密度分别为8.8×10~(10)/cm~2和6.5×10~(10)/cm~2。注入硬度明显下降,说明基体软化。     

The corrosion behavior of nano-meter embedded phase in Ti implanted H13 steel

On the SEM micrographs of Ti implanted H13 steel, a tree-branch-like structure can be observed. Further investigation with TEM shows that the newly tormed composition is a formation of nann-meter FeTi_2 phase in Ti implanted layer. The layer with a relatively high corrosion resistance has been formed in Ti implanted H13 steel with this structure.The results of electrochemical measurement show that the corrosion current density decreases obviously with an increase of ion dose. The corrosion current density in Ti implanted steel with a dose of 1.3×10~(18)/cm~2 is 8-20 times less than that of Ti implanted steel with a dose of 6×10~(17)/cm~2. The corrosion behavior of Ti implanted steel with a dose of 6×10~(17)/cm~2 could be further improved as the sample was annealed at 500℃ for 20 min and the corrosion current density decreases by 48-80 times compared to that of non-implanted samples. The corrosion trace was not observed on the annealing sample by SEM, after multi-sweep cyclic voltammetry of 40 cycles     

C和W注入H13钢纳米结构和抗腐蚀特性

用多次扫描电位法研究了C和W单独及双注入H13钢对抗腐蚀特性的影响、抗腐蚀相生成的条件及其对抗腐蚀特性的作用,对改性机理进行了讨论.实验结果表明,碳、钨单独和双注入H13钢钨和碳可在注入层超饱和分布,特征为类高斯分布.双注入可在注入层中形成弥散的碳化钨WC和W2C、中间相Fe2W、铁钨碳化物FeW3C、Fe6W6C和铁的碳化物Fe5C3,Fe3C,Fe2C等.其形状为丝状纳米相,丝状相沿样品法线生长.这种结构使注入层强化,增强了表面抗腐蚀特性;钨和碳双注入同时具有钨和碳单注入的优势,能更有效地提高H13钢的抗腐蚀性,随着W和C注入剂量的增加,抗腐蚀特性逐步增强;样品W5C5的Jp经55个周期腐蚀后,约为H13钢Jp的1/30.     

C+W+C离子注入H13钢复合钝化层的抗腐蚀特性

用多次扫描电位法研究了C＋W＋C离子注入H13钢的结构和相变及其对抗腐蚀特性的影响,研究了抗腐蚀相生成的条件以及这些相对抗腐蚀特性的作用,并对其改性机理进行了讨论。实验结果表明,W离子和C离子多重离子注入H13钢可在注入层中形成超饱和浓度的W和C原子分布,分布形状为类高斯分布;并可在注入层中形成钨的碳化物WC和W2C相、合金相Fe2W和Fe6W6C等,这些弥散相不但可以使注入层强化,而且也可使表面钝化,从而增强了表面抗腐蚀特性;W和C双重离子注入具有W和C单离子注入的特性,可进一步提高H13钢的抗腐蚀特性,随着W重离子和C重离子注入剂量的增加,抗腐蚀特性进一步增强。样品C3W3C3的Jp经50个周期腐蚀后,其值比H13钢的Jp下降了60％,而C3W3的Jp比H13钢的Jp下降了47％。C3W3C3的Jp比C3W3的Jp小34％。扫描电子显微镜观察表明,腐蚀后抗腐蚀的钝化层依然存在。