Mass transfer in polycrystalline ytterbium monosilicate under oxygen potential gradients at high temperatures

Mass transfer in polycrystalline Yb₂SiO₅ wafers with precise composition control was evaluated and analyzed by oxygen permeation experiments at high temperatures using an oxygen tracer. Oxygen permeation proceeded due to mutual grain boundary diffusion of oxide ions and Yb ions without synergistic effects such as acceleration or suppression. The oxygen shielding properties of Yb₂SiO₅ were compared with those of the other line compounds such as Yb₂Si₂O₇ and Al₂O₃ based on the determined mass transfer parameters. It was found that the more preferentially an oxide ion diffuses in the grain boundary compared to the interior of the grain, the greater the effect of suppressing the movement of the oxide ion by applying an oxygen potential gradient becomes.     

Theoretical estimation of dielectric loss of oxide glasses using nonequilibrium molecular dynamics simulations

To theoretically explore amorphous materials with a sufficiently low dielectric loss, which are essential for next-generation communication devices, the applicability of a nonequilibrium molecular dynamics simulation employing an external alternating electric field was examined using alkaline silicate glass models. In this method, the dielectric loss is directly evaluated as the phase shift of the dipole moment from the applied electric field. This method enabled us to evaluate the dielectric loss in a wide frequency range from 1 GHz to 10 THz. It was observed that the dielectric loss reaches its maximum at a few THz. The simulation method was found to qualitatively reproduce the effects of alkaline content and alkaline type on the dielectric loss. Furthermore, it reasonably reproduced the effect of mixed alkalines on the dielectric loss, which was observed in our experiments on sodium and/or potassium silicate glasses. Alkaline mixing was thus found to reduce the dielectric loss.     

Systematic packaging design tools integrating functional and environmental consequences on product life cycle: Case studies on laundry detergent and milk

This study presents systematic packaging design tools integrating functional and environmental consequences on product life cycle. To design packaging for sustainability, the trade-offs between functional and environmental aspects of packaging throughout the product life cycle should be considered. However, it is difficult for packaging designers to understand the overall trade-offs because the extent of the design consequences on the entire life cycle of packaging and its contents is unclear. We developed two tools for packaging design: the Life Cycle Association Matrix (LCAM) and the Function Network Diagram (FND). The following three steps, based on literature reviews and interviews with industrial experts, were applied. Firstly, we listed the product functions and design variables related to the functions as the attributes allocated to the product life cycle. Secondly, the attributes were connected appropriately based on causal relationships. Lastly, we identified the factors to support decision making in the packaging design procedure. As a result, the LCAM depicts the design consequences on the life cycle, and the FND determines the stakeholders affected by the design consequences. Two case studies were demonstrated to analyze the trade-offs by using our tools. In the case studies, a liquid laundry detergent bottle and a milk carton were redesigned. The tools identified the design consequences and stakeholders affected by the redesign of the usability and protective function for the detergent and milk cases, respectively. The results showed the significance of understanding the design consequences on the product life cycle by integrating the functional and environmental aspects.     

Volumetric Change and Surface Properties of Temperature-Sensitive Polyvinylalcohol (PVA) Hydrogel

Polyvinylalcohol (PVA) polymer gel is a temperature sensitive polymeric gel, with a critical transition temperature (with H₂O) of 310 K. At higher than 310 K, this temperature sensitive polymer gel shrinks because of discharging water, whereas at lower temperatures, the gel swelled because of absorbing water. The reversibility of the gel's volume change was confirmed by temperature swing. The adsorption behavior of an organic compound onto the PVA polymer gel in water was tested at various temperatures. The amount of adsorbed organic compound increased remarkably at temperatures higher than about 310 K. Then, it was confirmed that the organic compound in PVA polymer gel could be reversibly adsorbed and desorbed by a temperature change between 293 and 323 K. The mechanism of adsorption of the organic compound onto the PVA polymer gel could be explained by hydration and dehydration of polymer gel.     

Generation of gas bubbles in microflow using micropipette with ultrasound

Ultrasound was applied to a micropipette micromixer to improve dispersion of gas and liquid in a microchannel. Flow visualization using a high-speed camera was performed to examine the effect of ultrasonic irradiation on bubble generation in the microchannel. Basically, nitrogen gas was injected using a (0.5 µm ID) glass micropipette into ethanol flowing in a rectangular (100 µm×200 µm) microchannel on polydimethylsiloxane (PDMS). Gas and liquid flow rates were regulated using mass flow controllers. At aflow condition that is typical of bubbly flow, ultrasound was transmitted into the microchannel using a piezo-electric (PZT) transducer over a range of operating voltages (2 to 200 Vp-p) and frequencies (50 to 60 kHz). Images captured during the action of the PZT transducer indicate that bubble formation is influenced by ultrasound. When subjected to ultrasound above 50 Vp-p and at the resonant frequency of the PZT transducer, bubbles formed that were smaller and closer together, signifying enhanced shearing of the gas at the micropipette tip by the liquid. The observation of gas slugs occurring sooner might be attributed to the coalescence of gas bubbles that became closely spaced.     

InxGa1−xAs ohmic contacts to n-type GaAs with a tungsten nitride barrier

Significant reduction of the contact resistance of In_0.7Ga_0.3As/Ni/W contacts (which were previously developed by sputtering in our laboratory) was achieved by depositing a W₂N barrier layer between the Ni layer and W layer. The In_0.7Ga_0.3 As/Ni/W₂N/W contact prepared by the radio-frequency sputtering technique showed the lowest contact resistance of 0.2 Ωmm after annealing at 550°C for 10 s. This contact also provided a smooth surface, good reproducibility, and excellent thermal stability at 400°C. The polycrystalline W₂N layer was found to suppress the In diffusion to the contact surface, leading to improvement of the surface morphology and an increase in the total area of the In_xGa−As between metal and the GaAs substrate. These improvements are believed to reduce the contact resistance.     

An automatic torque ripple compensation system for direct drive motors

A serious problem in motion control is the occurrence of torque ripple. Since a direct drive (DD) motor with a magnet rotor uses a rare-earth magnet, the torque ripple is more serious than that of conventional servomotors. This paper presents an auto-compensation of torque ripple using a software-implemented torque observer. The frequency and amplitude of torque ripple can be obtained in the controller by using the estimated torque from an observer, and the autonomous generation of a compensating current component for a torque ripple is possible. The proposed algorithm has been verified by experiments.     

Three-dimensional display of the bronchi using helical CT

The purpose of this study was to evaluate the clinical usefulness of three-dimensional (3D) images of the bronchi obtained using helical CT. Thirteen patients with lung cancer, one with tracheal diverticulum, and one with bronchial amyloidosis were examined. The CT scanner employed was the Toshiba Xforce. The helical CT scan cycle consisted of 20 continuous rotations, each requiring 1.5 sec, for a total scanning time of 30 sec. Scans were obtained using a 5-mm X-ray beam width, a 5-mm/1.5 sec couchtop sliding speed, and a 2-mm reconstruction interval. 3D images were reconstructed using a CEMAX VIPstation. The optimal lower and upper threshold CT values for 3D images of the bronchi were -650 and -100 HU, respectively, and 3D images clearly depicted endobronchial lesions. Cartilage crescents were also demonstrated, but longitudinal and circular mucosal folds could not be visualized. In conclusion, 3D images of the bronchi acquired using helical CT were useful in evaluating endobronchial lesions.     

Graphite formation on Ni film by chemical vapor deposition

Thin film formation of graphite by chemical vapor deposition using 2-methyl-1,2′-naphthyl ketone as a starting material was carried out on Ni film substrates. On Ni films directly deposited on quartz glass, the graphite films were obtained when the Ni film thickness was above 1 000 Å and above 5 000 Å at 700 °C and 1 000 °C, respectively. Depositions on thinner Ni film substrates comprise amorphous carbon (a-C) or graphite tubes which was owing to the thermal coagulation of the Ni film into droplets. On the other hand, graphite film was obtained on the Ni film with thickness 10 Å when a-C was inserted between the Ni film and the quartz glass. The coagulation of the Ni film is considered to be avoided by inserting a-C layer.     

Power swing analysis in a future metropolitan electric power system on a contingent trip of cryogenic high-power cables

A cryogenic power cable is expected to be capable of carrying bulk power as a main transmission line in a future metropolitan electric power system. It is important to establish a strategy of how to sustain power supply when such a highly densified power supply route trips from the network due to contingency. It is proposed here that the bulk power transmitted by the cryogenic cable could be distributed into the parallel conventional transmission lines by suitable circuit breaker operations in the system. In this process, power-flow routes are forced to be changed with a remarkable modification in the system configuration. In this paper, the power swings associated with the large power-flow change following contingent faults are analyzed by means of a transient network analyzer. It is found that the proposed system modification could be realized without any harmful power swing if the parameters in generators as well as in control devices have conventional magnitudes. It is shown also by simulations that the margin to occurrence in an unstable power swing is left sufficient even if the parameters deviate somewhat from the present magnitudes.