SHS技术发展的概况

本文概括介绍了SHS技术原理、工艺特点及研究现状,并提出了SHS工艺存在的问题及今后研究的重点。     

Chemical States of Lanthanum in Carbonized La2O3-Mo Thermionic Cathode Materials

The chemical reaction between lanthanum oxide and molybdenum carbide was studied by thermodynamic calcu-lation, thermal analysis and in-situ X-ray Photoelectron Spectroscopy. The theoretical results show that at the environment allowing for the evaporation of lanthanum, such as in high vacuum, La2O3 in the La2O3-Mo materials can be reduced to metallic lanthanum by molybdenum carbide (Mo2C). To confirm the conclusion, many analysis methods such as XRD, SPS, and TG-DTA were taken. The experimental results show that the chemical state of lanthanum changes during heat-ing. It was proved, for the first time, that reacted metallic lanthanum appears at the surface of this kind of material at high temperature.     

双金属旋锻制取空心钨片及钨管的工艺研究

为了满足汽车点火器接点用空心钨片(具有加工形变组织)及套管用小直径厚壁钨管的需要,本文研制了一种制备钨钼双金属棒材并溶去钼芯制取小直径空心圆钨片和小直径厚壁钨管的新工艺。用于汽车点火器接点的空心钨片是由切割双金属棒材成圆片后,用配制的溶液溶去钼芯而制得。套管则是切取一定长度的钨钼棒材,用通电自身加热法熔去钼芯制得。     

稀土镧、钇对蓝色氧化钨氢还原的影响

借助于ＳＥＭ、Ｘ射线衍射技术及ＩＰＰ粉末粒度仪等系统地研究了稀土镧、钇对蓝色氧化钨（ＢＯ）氢还原的影响。结果表明：稀土元素镧、钇在蓝色氧化钨的还原钨粉中以氧化物及钨酸盐形式存在；还原后所得的钨粉颗粒大多为规则形状的多面体；稀土镧、钇和铝相似，强烈地抑制ＢＯ氢还原钨粉颗粒的长大，而且钇的作用更为显著。     

镧钼丝组织结构和性能的研究

对掺杂镧的钼粉、坯条、棒料及不同温度退火的丝料的性能及组织结构分析表明：掺杂粉中的镧以硝酸镧、氧化镧及镧钼氧化物的形态存在，坯条、棒料及丝材中的镧以氧化斓的形态存在。丝材中呈纤维状的氧化镧在１６００℃开始分裂成粒子串。微量镧能显著提高钼的再结晶温度，并形成长宽比大的晶粒，且能提高其塑性和高温抗蠕变性能，高镧钼可改善其高温再结晶后的低温脆性，并具有很好的电子发射性能。     

钪系阴极基体的研究

采用氧化钪与钨机械混合、氧化钨与钪盐水溶液固液掺杂法制备了氧化钪-钨基体，采用扫描电镜及原位俄歇电子能谱方法研究了基体中钪的分布及阴极基体的抗离子轰击性能。结果表明，采用液固法制备的烧结体，氧化钪分布均匀，这样的结构有利于钪的扩散和补充，原位俄歇轰击实验结果表明，阴极基体具有良好的耐高温和耐离子轰击性。     

Durability experiment on anti-electron-bombardment of RE2O3-Mo secondary emission material

A durability test to determine anti-bombardment sensitivity of multi-RE2 O3-Mo secondary emission material was carried out and the variation of maximum secondary emission coefficient (δmax) was monitored at regular intervals. After the experiment, the cathode was analyzed with SEM, EDS and XRD techniques. The results show that δmax of multi-RE2O3-Mo cermets cathode heated to 1 100 ℃ under electron bombardment of 300 W/cm2 reaches the peak of 3.35 at 200 h. After 500 h of bombardment, the maximum secondary-electron-yield curve stabilizes. The δmax value of the cathode remains at about 2.5 after 1 000 h and represents a good anti-bombardment property. The high δmax value of the cathode is related with formation of an enriched Y2 O3 layer on the surface under high temperature and with the amount of La2 O3 particles in the shape of nanometer distributed on the surface. Under the experimental conditions, the drop of δmax value may be caused by the reduction of La2 O3 content and the porous layer resulted from evaporation of MoO2, which is formed when Mo at the surface is oxidized.     

家用微波炉磁控管用碳化La2O3-Mo阴极

研究了家用微波炉磁控管碳化La2 O3 Mo阴极 ,参照碳化ThO2 W阴极磁控管的制作工艺 ,成功实现了La2 O3 Mo阴极的碳化以及碳化La2 O3 Mo阴极磁控管的去气、激活。碳化La2 O3 Mo阴极的微波能量输出功率为 5 0 0W ,而同类型的碳化ThO2 W阴极磁控管的额定微波能量输出为 90 0W。通过分析认为 ,碳化La2 O3 Mo阴极磁控管微波输出能量不足的主要原因在于碳化La2 O3 Mo阴极材料本身的电子发射能力不足。     

叠层加压SPS烧结制备梯度硬质合金

采用叠层加压SPS烧结法制备致密的YG10/YG20梯度结构硬质合金。通过调整WC粒度和添加微量元素B来调整烧结温度,使含钴量低的粉末与含钴量高的粉末的烧结温度相近。研究了烧结温度对致密度、组织形貌、显微硬度和断裂韧性的影响,分析了沿梯度截面上C,Co,W等成分、显微硬度的变化及YG10/YG20界面的结合情况。结果表明:原始WC粒度为1μm的YG10+0.05%B混合粉末和9μm的YG20混合粉末都能在1100℃~1160℃烧结致密,相对密度达到99%以上,晶粒尺寸均匀,梯度界面结合良好,没有开裂现象。低钴端的硬度达到了15500MPa~16000MPa,高钴端的硬度为11100MPa;在294N载荷的作用下低钴端的断裂韧性为12.62MPa·m1/2,而高钴端在这一载荷的作用下没有出现裂纹,断裂韧性较高,从而实现了硬质合金一端具有高硬度,另一端具有良好的韧性的有机结合。     

6T51高频加热电子管用碳化La2O3—Mo阴极的研究

研究了应用于6T51发射管中的碳化La2O3-Mo阴极的制作工艺及电子发射性能，在碳化钍钨阴极的实践基础上，实现了La2O3-Mo阴极的碳化以及碳化La2O3-Mo阴极6T51管的去气和阴极激活。对比碳化钍钨阴极，分析了碳化La2O3-Mo阴极6T51管的发射能力，认为目前碳化La2O3-Mo阴极研究的发射量最高水平只达到钝钨阴极的下限值，还不具备取代碳化Th-W阴极的条件，由于碳化Th-W阴极6T51管设计时所选取的阴极发射能力富余量相当大，经过严格的去气，老练处理，碳化La2O3-Mo阴极基本上满足6T51测试的要求，但其发射稳定性不好，发射寿命也不容易掌握，论述了La元素消耗或碳化层消耗是两个影响碳化La2O3-Mo阴极发射稳定性的因素。