Microstructure and mechanical behavior of laser aided additive manufactured low carbon interstitial Fe49.5Mn30Co10Cr10C0.5 multicomponent alloy

Laser aided additive manufacturing(LAAM)was used to fabricate bulk Fe49.5Mn30Co10Cr10C0.5 interstitial multicomponent alloy using pre-alloyed powder.The room temperature yield strength(σy),ultimate tensile strength(σUTS)and elongation(εUST)were 645 MPa,917 MPa and 27.0％respectively.The as-built sample consisted of equiaxed and dendritic cellular structures formed by elemental segregation.These cellular structures together with oxide particle inclusions were deemed to strengthen the material.The other contributing components include dislocation strengthening,friction stress and grain bound-ary strengthening.The high εUTS was attributed to dislocation motion and activation of both twinning and transformation-induced plasticity(TWIP and TRIP).Tensile tests performed at-40℃and-130℃demonstrated superior tensile strength of 1041 MPa and 1267 MPa respectively.However,almost no twinning was observed in the fractured sample tested at-40℃and-130℃.Instead,higher fraction of strain-induced hexagonal close-packed(HCP)ε phase transformation of 21.2％were observed for fractured sample tested at-40℃,compared with 6.3％in fractured room temperature sample.     

Reduced texaphyrin: A ratiometric optical sensor for heavy metals in aqueous solution

We report here a water-soluble metal cation sensor system based on the as-prepared or reduced form of an expanded porphyrin, texaphyrin. Upon metal complexation, a change in the redox state of the ligand occurs that is accompanied by a color change from red to green. Although long employed for synthesis in organic media, we have now found that this complexation-driven redox behavior may be used to achieve the naked eye detectable colorimetric sensing of several number of less-common metal ions in aqueous media. Exposure to In(III), Hg(II), Cd(II), Mn(II), Bi(III), Co(II), and Pb(II) cations leads to a colorimetric response within 10 min. This process is selective for Hg(II) under conditions of competitive analysis. Furthermore, among the subset of response-producing cations, In(III) proved unique in giving rise to a ratiometric change in the ligand-based fluorescence features, including an overall increase in intensity. The cation selectivity observed in aqueous media stands in contrast to what is seen in organic solvents, where a wide range of texaphyrin metal complexes may be prepared. The formation of metal cation complexes under the present aqueous conditions was confirmed by reversed phase high-performance liquid chromatography, ultra-violet-visible absorption and fluorescence spectroscopies, and high-resolution mass spectrometry.     

以金属氧化物为原料改进燃烧法合成γ-LiAlO_2（英文）

提出一种合成γ-LiAlO_2的替代解决方案—改进燃烧法直接合成γ-LiAlO_2,并将其用于相对简单的反应体系中,原料为非氧化性化合物如Al_2O_3和LiOH,燃料为尿素。采用1:1、1.5:1和2:1的非化学计量Li/Al摩尔比,在900和1000°C下反应5 min,制备LiAlO_2,并对其组织和结构进行表征。考察Li/Al摩尔比对材料形貌和高γ射线辐照下材料稳定性的影响。结果表明,所得粉体的晶体结构为?-LiAlO_2和?-LiAlO_2,其取决于Li/Al摩尔比。因此,用该方法可以成功合成微砖状、多面体状和层状?-LiAlO_2,而无需任何后续处理。γ辐照结果表明,所得到的?-LiAlO_2不分解,只形成少量的Li_2CO_3;由此可以确定,辐照会导致固结,不利于氚的有效提取;结果证明,用燃烧法生产高纯度?-LiAlO_2不需要硝酸盐前驱体。     

大型水电工程前期准备延期的影响类型分析

讨论了成本考虑不足与水电工程项目施工前准备阶段延期的负面影响,以及发展中国家不能及时有效地交付项目与稀有资源浪费间的冲突。建议项目员工、开发商、政府官员和国际金融机构重视延期成本,找到成本与效益的平衡点。     

A boronic acid-based fluorescent hydrogel for monosaccharide detection

A boronic acid-based anthracene fluorescent probe was functionalised with an acrylamide unit to incorporate into a hydrogel system for monosaccharide detection. In solution, the fluorescent probe displayed a strong fluorescence turn-on response upon exposure to fructose, and an expected trend in apparent binding constants, as judged by a fluorescence response where D-fructose>D-galactose>D-mannose>D-glucose. The hydrogel incorporating the boronic acid monomer demonstrated the ability to detect monosaccharides by fluorescence with the same overall trend as the monomer in solution with the addition of D-fructose resulting in a 10-fold enhancement (≤0.25 mol/L).     

AA7075高强铝合金热冲压流变行为本构模型对比研究

在热冲压过程中,AA7075高强铝合金板料经充分固溶后移入室温模具进行冲压成形并淬火。为表征AA7075铝合金在热冲压工艺中的变形行为,在温度200~480℃、应变速率0.01~10s-1范围内进行了高温拉伸试验。基于Arrhenius类型本构模型、Johnson-Cook模型以及Zerilli-Armstrong模型提出了多种修正本构模型,并应用实验所获流变曲线进行了拟合。提出的修正模型通过将模型参数表示为应变、应变速率及温度相关的多项式函数耦合了应变、应变速率及温度对流变应力的影响,并通过均方误差(MSE)以及相关系数R值对模型流变应力预测准确性进行了评价。结果表明,修正的Johnson-Cook模型能够更加准确的预测AA7075高温流变行为。     

生物基油对白炭黑填充天然橡胶胶料加工性能和硫化特性的影响

通常使用的石油基加工油,比如重质环烷油(HNO)和轻质环烷油(LNO)具有潜在的致癌性。本文研究了一种新型生物基油——茶籽油(TO)可能会成为通用加工油的替代品。在进行试验对比时,还选择了另外两种生物基油,分别是棕榈油(PO)和椰子油(CO)。试验结果表明,所有研究的生物基油的热稳定性均高于轻质环烷油(LNO),在白炭黑填充天然橡胶(NR)配方中,配合生物基油的混炼胶加工性能比添加石油基油的胶料更加优异。主要表现为:生物基油的热稳定性高,在相同混炼条件下,与添加石油基油的混炼胶相比,添加生物基油能够提高白炭黑与天然橡胶的混合效率,改善白炭黑在天然橡胶基质中的分散性,提高混炼胶的塑化效果。加工油的不同类型和用量对混炼胶的硫化特性影响很小。通过试验结果分析,所研究的TO、PO和CO生物基油很有可能成为石油基加工油的替代产品。     

Behavior of ZrO2-C Refractories in Thin-strip Casting of Steel

Zirconia graphite refractory is used as a core-nozzle in the thin-strip casting of steel. Post-mortem analysis of used refractory was performed in an effort to establish the failure mechanism. Corrosion behavior was studied against molten steel with Mn O- SiO 2based liquid inclusions. Corrosion of these materials involves dissolution and oxidation of graphite in the matrix followed by penetration of liquid slag leading to degradation of ZrO 2particles. Thermodynamic equilibrium calculations were performed to study this corrosion mechanism.     

Critical parameters near the ferromagnetic-paramagnetic phase transition in La0.67–xYxBa0.23Ca0.1MnO3 compounds（x=0.10 and x=0.15）

The critical properties of the mixed manganite La0.67–x Y x Ba0.23Ca0.1Mn O3 with x=0.10 and x=0.15 around the paramagnetic(PM)-ferromagnetic(FM) phase transition were investigated through various techniques. These involved modified Arrott plots, Kouvel-Fisher method and Widom scaling relation. Magnetic data, analyzed in the critical region, using the above methods, yielded the critical exponents for(x=0.10) La0.57Y0.10Ba0.23Ca0.1Mn O3(β=0.312±0.002 and γ=1.147±0.003 at T C=299.23±0.05 K). Moreover, the estimated critical exponents of(x=0.15) La0.52Y0.15Ba0.23Ca0.1Mn O3 were β=0.286±0.004 and γ=0.943±0.002 at T C=289.53±0.06 K. The critical exponents’ values were close to the theoretical values of 3D-Ising model and tricritical mean-field model. These results suggested that the present composition should be close to a tricritical point in the La0.67–x Y x Ba0.23Ca0.1Mn O3 phase diagram. Expressing the field dependence as ΔS M∝H n allowed us to establish a relationship between the exponent n and the critical exponents of the material and to propose a phenomenological universal curve for the field dependence of ΔS M.     

Separation of hematite from banded hematite jasper (BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.