粉末注射成形硬质合金异形件热脱脂工艺的研究

对硬质合金异形件表带注射成形的热脱脂工艺进行了研究 ,根据喂料的热失重曲线确定了热脱脂的四个阶段 ,并确定了理论预脱脂曲线 ,然后采用实验对该预脱脂曲线进行校正和条件优化 ,得出较理想的实际热脱脂曲线 ;研究了不同热脱脂工艺对硬质合金碳含量控制的影响 ,研究结果表明 ,使用露点低、氧含量低的氢气热脱脂气氛、选择合适的保温温度以及保温时间都能较有效地控碳。     

Prediction of powder characteristics of uniform NiO precursor prepared by homogeneous precipitation

Uniform NiO precursor particles were prepared by homogeneous precipitation in the presence of urea. Optimal discrimination plan, one of the chemical pattern recognition techniques, was applied to analyze the experimental data and the quantitative relationships among the process parameters and powder characteristics of the obtained particles were determined. It proves that the model fits well with the experimental results and it is quite effective to guide the process design. Based on the above results, an improved La Mer model and the reasonable formation mechanism of the particles are proposed.     

C／C复合材料开孔孔隙度和比表面积对其氧化性能的影响

选用光学显微结构为光滑层沉积热解炭、试样的石墨化度近似相等（约为37%）的A，B，C，D，E5个不同开孔孔隙度和比表面积的C/C复合材料试样（孔隙度和比表面积分别为PA=14.03%,SA=1.463m^2/g；PB=18.01%,SR=2.701m^2/g,PC=24.65%,SC=3.594m^2/g,PD=12.07%,SD=6.527m^2/g,pe=15.79%,se=6.722m^2/g)在氧气流中进行变温氧化实验，具有不同比表面积和孔隙度的试样F，G，H，（PF=15.66%,SF=6.026m^2/g,PC=18.32%,SC=3.573m^2/g，PH=12.16%,SH=2.262m^2/g）在氧气流中进行等温氧化实验；具有不同比表面积和相同孔隙度的试样I，J（P1=13.61%,S1=0.8535m^2/g，P1=13.60%，S1=0.4293m^2/g）在马弗炉中进行静态空气氧化实验，结果表明：试样的比表面积控制了氧化进度，而与材料孔隙度无直接关系；氧化优先发生在纤维/基体和基体/基体界面，随后沿着界面间裂纹进行。     

ZnS光电材料制备技术的研究进展

ZnS作为一种性能优良的光学，电学和光电一体化材料，具有极大的应用价值，综合概述了ZnS粉末，块状材料和薄膜等各种材料的制备方法，阐述并讨论了水热合成法，均匀沉淀法，溶胶－凝胶法，化学气相沉积法，溅射法等不同方法的特点，并着重论述了ZnS粉末和薄膜，特别是在纳米粉末和纳米晶薄膜制备技术方面的研究进展。     

金属-Al2O3陶瓷基复合材料的研究现状及应用前景

Al2O3陶瓷是一种重要的抗氧化、抗腐蚀的高温结构陶瓷材料.但由于其烧结活性低,难以烧结致密,脆性大,在应用上受到限制.在Al2O3陶瓷中引入延性金属第二相和采用纳米材料可大大提高其烧结活性,不仅能使金属增韧,而且也能使陶瓷具有一定的导电、导热性,从而扩大了它在微电子行业中的应用.在此,作者综述了国内外近几年来对纳米金属-Al2O3陶瓷的研究现状,指出了其应用前景.     

Influence of microcrystalline wax on properties of MIM multi-component was matrix binder

The properties of PW-EVA-HDPE binder with the addition of MW were studied.It shows that the addition of MW from 1% to 20%(mass fraction)causes an increase in the tensile strength and a decrease in shrinkage of the binder.After blending PW with MW,the crystallation behavior of wax base changes,which results in fine grain for the binder and more isotropic microstructure for the feedstock.The powder loading capacity increases and homogeneity of feedstock becomes better.The reason of the modification is also discussed.     

Ti和TiH2与Al反应合成TiAl的研究

对采用ＤＳＣ、ＸＲＤ和ＳＥＭ３种方法分别由Ｔｉ和ＴｉＨ２粉末与Ａｌ粉末（５２％Ｔｉ和４８％Ａｌ）反应合成ＴｉＡｌ合金的过程及其机理进行了分析和探讨。Ｔｉ与Ａｌ，ＴｉＨ２与Ａｌ均需在Ａｌ转化为液态后才能进行剧烈的反应，但ＴｉＨ２与Ａｌ的反应是由ＴｉＨ２脱氢所产生的高活性Ｔｉ参与的，因而它们反应较完全，生成的ＴｉＡｌ相对量较高。随着反应的进行及Ａｌ元素的均匀化，反应初期生成的较不稳定的ＴｉＡｌ３相和αＴｉ相将消失，反应生成物由ＴｉＡｌ相和少量Ｔｉ３Ａｌ相构成     

金属注射成形技术的研究现状

金属注射成形 (MIM)已成为国际粉末冶金领域发展迅速 ,最有前途的一种新型近净成形技术。本文综述了MIM技术的研究现状 ,指出了MIM的发展趋势     

Fe-2Ni金属注射成形工艺研究

采用金属粉末注射成形工艺(MIM)制备Fe-2Ni合金。选择了5种石蜡基粘结剂,结果表明,由多组元聚合物组成的粘结剂注射成形性能好,热脱脂后无缺陷,样品形状保持完整。列举最佳工艺参数及烧结合金的机械性能。     

聚合物/无机物纳米复合材料研究现状

纳米材料是继单组分材料，复合材料和梯度材料之后的第四代材料，聚合物／无机物纳米复合材料的研究已成为当今高分子化学与物理，无机化学和材料化学等诸多交叉学科的前沿领域，聚合物和无机物在纳米及分子水平上的复合，将使各自的优势得到最充分的体现，简要概述了聚合物／无机物纳米复合材料的制备方法，结构与性能及其应用。