硅藻土墙体材料试验研究

硅藻土经预处理后比表面积增加，孔结构改善，强度活性显著提高。由此可研制生产强度大于10MPa、容重小于1000kg／m3的轻质高强多功能墙体材料。本文还进一步研究了水泥和石灰掺量对制品强度的影响规律以及提高耐久性的措施。     

偏高岭土对羟乙基甲基纤维素改性砂浆性能影响

分别以0%,5%,10%,15%(质量分数)的偏高岭土等量取代羟乙基甲基纤维素改性砂浆中的水泥,通过调节用水量控制浆体稠度,研究偏高岭土对新拌及硬化砂浆性能的影响.结果表明:随偏高岭土取代量增加,水胶比提高,新拌砂浆在保持良好保水性及施工性的同时,凝结时间偏长的现象得到改善;偏高岭土能明显提高硬化砂浆的抗压强度和抗渗性能,并使硬化砂浆的孔径分布得到优化,但偏高岭土对硬化砂浆抗折强度的影响相对较小;偏高岭土取代量由5%提高到15%时,硬化砂浆干燥收缩值降低.当偏高岭土取代量为10%时,硬化砂浆能获得最佳的性能.     

粉煤灰加气混凝土抗拉强度及轴拉应力—应变关系的研究

本文对容重500kg/m~3的粉煤灰加气混凝土的劈裂抗拉强度、轴拉强度、极限轴拉应变值、极限轴拉应力、抗拉弹性模量等项性能及它们之间的相互关系,作了较系统的试验研究,这对于研究和改善加气混凝土的材性以及设计和施工都是十分重要的。     

粉煤灰加气混凝土结晶度、孔结构与制品性能的关系

本文通过扫描电镜和X—射线衍射图谱,分析了水化产物及其结晶度对制品性能的影响,以及碳化前后水化产物和组织结构的变异。并就孔结构对强度和耐久性的影响作了探讨。     

蒸压粉煤灰加气砼砌块建筑裂缝成因研究

试验研究表明;粉煤灰加气砼墙体开裂的主要原因在于制品的干燥收缩和温度变形。当制品含水率小于5%时,干湿循环变形显得十分重要。墙体粉刷后,碳化对其影响很小,针对上述结果,作者提出了一些相应的改进措施。     

pH值对凝胶中对羟基苯甲酸:Tb3+配合物形成及发光特性的影响

在有机改性凝胶中共掺对羟基苯甲酸和TbCl3制备了对羟基苯甲酸Tb3+配合物掺杂的有机改性凝胶,研究了pH值对有机改性凝胶中对羟基苯甲酸Tb3+配合物的形成及其发光性质,结果表明在不同的凝胶中,pH值对发光性质的影响差异较大,在由TEOS水解缩聚形成的SiO2凝胶中,随pH值增加,对羟基苯甲酸和TbCl3样品的发光强度逐渐增强,表明凝胶中对羟基苯甲酸Tb3+配合物的逐渐形成.但在50%TEOS和50%GPTMS水解缩聚形成的有机改性凝胶中,样品的发光强度随pH值的升高逐渐下降.     

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

The influence of superplasticizer(SP) on the early age drying shrinkage of cement paste with the same consistency was investigated. To conduct the test, which lasted for 72 hours, three paste mixtures were used for comparison. The 72 hours early age drying shrinkage staring from the initial setting time was measured by a clock gauge. The pore size distribution was measured by Mercury Intrusion Method. The surface tension of capillary simulation liquid and mass loss of paste were also measured. The experimental results showed that the addition of SP increased the early drying shrinkage greatly. The ratios of water evaporation and the total free water in mixtures added with SPs showed great differences. SPs fined the capillary pores of paste, and the volume of pore with diameter within 50 nm was well consistent with shrinkage rate. The addition of SPs did not raise the capillary liquid surface tension. It showed that with the volume of pore with diameter within 50 nm and the ratio of water evaporation and the total free water a tolerable shrinkage result of paste added with SP could be predicted, and the elastic modulus could have an influence on the early shrinkage. These results have never been proposed before.     

海洋环境下矿物外加剂对水泥胶砂抗腐蚀性能的影响研究

研究了各种不同种类和掺量的矿物外加剂对水泥胶砂试块抗海水腐蚀性能的影响。矿物外加剂选用了粉煤灰、矿粉、硅灰和膨胀剂，快速腐蚀试验方法采用半浸烘循环法。试验中测定了不同配比的水泥胶砂试件在快速腐蚀条件下的抗折强度、抗压强度变化以及Cl^-渗透深度和Cl^-扩散系数。并对试验结果进行了对比说明和机理分析。     

混凝土多孔砖砌体力学性能及应用

本文试验研究了混凝土多孔砖砌体力学性能。试验结果表明，MU15的多孔砖，当采用M10的混合砂浆砌筑时，砌体轴心抗压强度、抗剪强度及通缝和齿缝抗弯拉强度均高于同强度等级的烧结多孔砖，且远高于《砌体结构设计规范》(GBJ50003—2001)中烧结多孔砖砌体的标准值和设计值要求。多项试点工程表明，除因吸水率较小、粉刷掉灰相对较多外，其他性能均与烧结多孔砖相似，是一种适合我国现状、可推广应用的新型墙体材料。     

砌筑砂浆的改性分析和试验研究

新型墙体材料的广泛使用使得传统普通砂浆的局限性凸现。采用聚合物微粉和高效减水剂对传统普通砂浆进行合理改性，不仅不会降低砂浆的抗压和抗折强度，还会大幅度提高砂浆的粘结强度，从而使解决目前所面临的新型墙体材料砌体开裂的问题成为可能。