表面活性剂后处理对YAG∶Ce~(3+)荧光粉发光特性的影响

采用固相法制备YAG∶Ce3+黄色荧光粉,以油酸、聚乙二醇、十二烷基磺酸钠和十二烷基硫酸钠等表面活性剂作为后处理剂,考察其种类、浓度和性质等对荧光粉发光性能的影响,进一步对浸泡温度以及浸泡时间等工艺条件进行了对比研究,并通过荧光光谱和扫描电子显微镜等手段对处理前后YAG∶Ce3+荧光粉的发光性能、表面形貌和老化性能等方面进行了表征和分析。结果表明,YAG∶Ce3+荧光粉的最佳后处理工艺条件为:十二烷基硫酸钠较为理想,经2.4%十二烷基硫酸钠处理后,YAG∶Ce3+荧光粉的发光强度约提高8.4%,浸泡温度为50℃,浸泡时间为60 min。     

Vishay推出新款高发光强度功率MiniLED

正日前,Vishay Intertechnology,Inc.宣布,推出采用超小尺寸2.3mm×1.3 mm×1.4mm SMD封装的新系列功率Mini LED——VLM×234..系列。该系列器件采用了最先进的AllnGaP技术,具有非常高的亮度,典型发光强度为3500mcd,在70mA下的最大发光强度达到4900mcd,热性能优于前一代LED。此次发布的高发光强度LED的结/环境的热阻低至325K/W,功率耗散高达200mW,从而能够采用70mA的高驱动电流。器件的小尺寸和高发光强度使其非常适合汽车应用,且     

Vishay推出采用独特SurfLight表面发射器技术的新款850nm红外发射器

Vishay Intertechnology,Inc.日前宣布推出两款采用该公司的SurfLight表面发射器技术制造的850nm红外(IR)发射器VSMY7852X01和VSMY7850X01。VSMY7852X01和VSMY7850X01采用高功率LittleStar?封装,占位为6.0mm×7.0mm     

LED灯具照明在改造工程中的应用

本文通过对LED照明产品的分析论述,结合某改造工程实例,介绍了LED照明灯具改造方案的实施及效果,分析总结了节能效益和社会效益。     

Vishay推出采用小尺寸0402 ChipLED封装的多色彩新型超亮LED

Vishay Intertechnology,Inc.光电子产品部发布新VLMx1500-GS08系列采用小型表面贴装0402 ChipLED封装的大红、浅橙、黄、嫩绿、蓝色和白色的超亮LED。VLMx1500-GS08系列器件的尺寸为1.0×0.5 mm,高0.35 mm,180mcd的发光强度实现了超群亮度。VLMx1500-GS08系列中的蓝色和白色LED使用高效InGaN技术,大红、浅橙、黄色和嫩绿色器件使用最先进的AllnGaP     

稀土发光材料的水热法合成及其发光强度

采用水热合成法成功制备出了掺铕CaF2、SrF2和BaF2,并探究了同浓度稀土离子掺杂的CaF2、SrF2和BaF2的发光能力的强弱,得出同浓度稀土离子掺杂的CaF2、SrF2和BaF2中CaF2的发光能力最强.此外,还通过荧光光度计对不同浓度的CaF2的发光强度进行了探究,发现随掺杂稀土离子浓度的增加,掺铕CaF2的发光强度增强.     

EXAFS study of cation reordering in NaYF4：Yb3＋,Tb3＋ up-conversion luminescence materials

The NaYF4：yb3＋,Tb3＋ （Xyb： 0.20, XTb： 0.04） materials were prepared using the co-precipitation method, lne as-preparea material was washed either with or without water in addition to ethanol and thereafter annealed for 5 h at 500℃. This resulted in materials with moderate or very high up-conversion luminescence intensity, respectively. The structural study carried out with X-ray powder diffraction revealed microstrains in the rare earth （R） sublattice that were relaxed for the material with very high up-conversion intensity thus decreasing energy losses. The local structural details were investigated with R LⅢ and Y K edge ex- tended X-ray absorption fine structure （EXAFS） using synchrotron radiation. Around 10 tool.% of the Yb3＋ ions were found to occupy the Na site in the material with very high up-conversion intensity. These Yb species formed clusters with the Tb3＋ ions occupying the regular Na/R sites. Such clustering enhanced the energy transfer between Yb3＋ and Tb3＋ thus intensifying the up-conversion emission.     

PbF2:Gd晶体的发光强度与发光均匀性研究

以Ｘ射线荧光光谱分析为手段,测试了用Ｂridgman方法生长的ＰbF2:Gd晶体中Ｇd离子沿生长方向的分布。发现该晶体在Ｘ射线激发下的发光强度与Ｇd在ＰbF2晶体中的含量变化均从结晶开始端至结晶结束端逐渐降低,表明ＰbF2:gD晶体的发光是不均匀的。这种不均匀性源于Ｇd离子在ＰbF2晶体中的分布不均匀性,通过在ＰbF2:Gd晶体中掺入一定量的碱金属离子,可以比较有效地改善Ｇd离子在ＰbF２晶体中的不均匀分布,使晶体的发光均匀性和透光率得到明显提高,其中以Ｎa离子的均匀化效果为最好,推测Ｎa离子的作用是消除了ＰbF2:Gd晶体中因子Ｇd离子的掺杂而造成的间隙Ｆ离子,从而使晶体中的缺陷浓度大大降低。     

瓷器热释光高温信号特征研究

对32个不同时代和地点的瓷器进行了热释光高温信号的检测,结果表明,除4个古瓷器和现代瓷器没有热释光高温信号外,其它古瓷器都有明显的高温信号,而且都呈单峰,但发光强度和高温峰的位置各不相同,古瓷器对于人工β,α辐照有较好的响应。     

关于测试距离对机动车前照灯发光强度影响的研究

本文介绍在三个不同测试距离下(1m、3m和10m)进行机动车前照灯远光发光强度的测试及试验结果,并通过理论分析得出结论,即选择10m的距离最为合适。