Improved hydration resistance of CaO granules via sol-processed metal oxide protective layers

Well-sintered CaO granules with hydration resistance are very important for the manufacturing and application of CaO-containing refractories. CaO granules with sol-processed metal oxide protective layers were prepared by granulation and surface treatment. The obtained results indicated that the usage of nano sol greatly improved the hydration resistance of CaO granules, especially when the CaO granules were treated by alumina sol. The promoting effect of nano sols in the sintering processes improved the density of CaO granules. Nanoparticles reacted with lime at lower temperature and a new phase was formed uniformly in the treated layer, which promoted densification of the treated layer. The grain size of CaO granules in the treated layer was increased obviously with the promotion of sintering. Moreover, nanoparticles were favorable for the formation of direct bonding between CaO grains by decreasing the dihedral angle.     

复合溶胶–凝胶一锅法制备锂离子电池氧化亚硅/碳复合负极材料

采用复合溶胶–凝胶法结合后续热处理,制备了具有包埋结构的氧化亚硅/碳(SiO_x/C)复合负极材料。扫描电子显微镜分析结果表明:氧化亚硅纳米颗粒嵌入在无定形碳中。电化学性能测试表明:SiO_x/C复合材料具有较高的比容量、优异的循环稳定性和倍率性能。材料在0.1 A/g的电流密度下100次循环后的可逆比容量为710 m A·h/g,容量几乎无衰减;在1.6 A/g的电流密度下,可逆比容量为380 m A·h/g。优异的电化学性能是由于材料的包埋结构能有效地缓冲SiO_x充放电过程中的体积膨胀,保证材料的结构完整性和电化学循环稳定性。     

负载型TiO2纳米薄膜电极光电催化氧化甲醇的研究

介绍了负载不同晶型TiO2薄膜电极的制备，并研究了聚乙二醇加入量、活化条件等对不同晶型、不同形貌、不同粒径纳米TiO2薄膜电极的光电催化活性的影响。结果表明：聚乙二醇加入量有一最佳值；且纳米级锐钛矿型TiO2和金红石型TiO2分别经600℃和400℃煅烧后，光电催化性能最好；粒径越小催化活性越高．当粒径小于25nm时，可显示出量子尺寸效应。     

钠基膨润土对硅溶胶涂料悬浮性的影响

硅溶胶涂料以其良好的工艺性能在熔模铸造领域得到越来越广泛的应用，但在实际使用过程中该涂料也存在着悬浮性不良等问题，影响到涂料实际使用。分析了改善硅溶胶涂料悬浮性的机理，以及硅溶胶涂料悬浮性与流杯粘度及涂片厚度等工艺性能之间的关系。采用钠基膨润土改善硅溶胶涂料的悬浮性，并取得了良好效果。     

基于荧光多元猝灭响应原理膜传感器测定正己烷中的噻吩

用溶胶 凝胶法制备光纤化学传感器测定正己烷中噻吩的浓度 ,在 1 0 .6～ 2 6 5μg/mL浓度范围内与lg(F0 /F) )成线性 ,相关系数为 0 .9984。检出限为 1 0 .6 μg/mL ,该方法的平均回收率为 1 0 5.0± 7.7%。     

电泳沉积氧化铝陶瓷涂层的制备及耐腐蚀性能

以氧化铝溶胶为前驱体,采用电泳沉积和低温煅烧法在低碳钢基体上制备了氧化铝陶瓷涂层,并对其成分、表面形貌及耐蚀性进行了研究。结果表明,将低碳钢片置于以乙醇作为分散介质的0.45mol/L氧化铝溶胶中,在60V恒电位下沉积180s后,再于马弗炉中700°C下煅烧5min,所制得的氧化铝陶瓷涂层在2mol/L盐酸溶液中具有良好的耐蚀性。     

硅载生物吸附剂的制备及性能研究

通过酵母细胞自溶得到中空细胞壁。以硅酸乙酯为原料,制备硅溶胶,通过溶胶-凝胶法制备了粒径为250~600μm的硅载细胞壁生物吸附剂S-1。以环氧氯丙烷交联细胞壁生物吸附剂S-2为对照,比较两者对Ag+的吸附性能。并研究了S-1对Pb2+,Cd2+,Cu2+,Zn2+的吸附性能。结果S-1的吸附强度明显高于S-2,但两者的吸附容量相当。S-1对Ag+及其它金属离子具有较高的吸附强度,对Pb2+和Cd2+具有较大的吸附容量。吸附是由于酵母细胞壁上的多糖对金属离子的螯合作用。     

Sol—Gel法制备有机—无机复合光致变色膜

本文讨论了用ｓｏｌ－ｇｅｌ法在有机改性ＳｉＯ２基体中于室温下俘陷有机染料如螺吡喃或螺恶嗪，制备出具有光致变色功能的有机－无机复合膜。该膜层在可见光区的最大吸收峰位于６２０ｍｎ处。     

有机-无机复合型建筑用封闭底漆的制备

采用硅溶胶、耐碱型苯丙乳液、云母粉、二氧化钛等颜填料制备有机-无机复合型建筑用非透明封闭底漆，以对比测试方法重点对其附着力、耐碱、抗渗透等性能进行验证，同时探讨了乳液、颜填料的选择因素以及硅溶胶对体系的作用和影响。     

纳米结构TiO2/SiO2的制备、结构与光催化性能

用自组装技术合成了纳米TiO2包覆的SiO2粒子.其中TiO2胶体通过溶胶-凝胶方法得到.讨论了不同晶型负载TiO2的合成条件及光催化性.样品经IR,SEM,XRD等进行表征.实验结果表明:SiO2粒子表面的纳米TiO2具有较好的均匀性;TiO2的含量随覆盖层的增加而增多;组装两层样品具有较大的比表面;经100℃干燥可得到不同晶型的纳米TiO2,且锐钛矿型含量较高的纳米TiO2组装粒子具有较好的光催化性能,