BaTiO3基Au纳米颗粒复合薄膜的制备及其光学性质研究

采用溶胶-凝胶（sol-gel）方法，成功的将高体积面分比的Au纳米颗粒复合到BaTiO3的非晶薄膜中，并对其光学性质进行了研究。用XRD、TEM、椭偏仪、吸收光谱、光克尔效应OKE（Optical Kerr Effcet）方法对薄膜进行了表征和测试。从吸收光谱观察到表面等离子体共振SPR（Surface Plasma Resonance)峰随热处理温度升高而红移的现象。光学非线性测试表明薄膜具有高的三阶非线性极化率Χ^(3)和超快的响应时间。     

Effect of Strain Rate on Discontinuous Flow and Mechanical Characteristics of High-Nitrogenous Steel

Experimental study on the effect of strain rate on discontinuous flow and mechanical characteristics of the high-nitrogenous steel Kh23AG19F has been performed. Within the range of strain rates from 4.62 · 10^-5 to 1.85 · 10 ^-4 s^-1, discontinuous flow, reflected by serration on the tensile diagram, is chiefly determined by intergranular deformation mechanisms. Under strain rates over 1.85 · 10^-2 s^-1, combined deformation modes prevail, which cause a change in the character of discontinuous flow and transform a serrated tensile diagram into a wavy graph, with the yield stress of steel increased significantly.     

改性沥青新型磨耗层在高等级路面上的应用

从材料、适用范围、形成机理、经济分析、施工工艺五个方面，介绍了改性沥青新型磨耗层在高等级路面上的应用，并通过试验路的观察表明，改性沥青新型磨耗层具有快速排水、增加摩阻力、愈合原路面微裂缝和较强抗磨耗的功能，是处置高等级路面上常有的龟裂、网裂、脱皮、露骨、抗磨系数不足、渗水等病害较具推广价值的新型施工工艺。     

不同级配对微表处混和料性能的影响

微表处技术是一种性能优良的路面养护技术。首先检验了微表处用原材料的技术指标,在满足规范的要求下选择了三种不同级配,并对三种不同级配的微表处混和料的使用性能进行了比较。     

聚乙烯催化剂表面分形和多重分形特征

应用分形和多重分形理论研究了负载型聚乙烯催化剂(简称催化剂)表面形态。提出一种图片处理和计算过程更加完备的基于扫描电子显微镜照片的分形维数和多重分形谱计算程序,对4种催化剂进行分析计算。探讨了分形维数、多重分形谱相关参数与催化剂表面形态及与聚合活性的对应关系。实验结果表明,催化剂表面形态的复杂程度可以用表面分形维数来表征,聚合活性高的催化剂表面形态更加复杂,有更大的比表面积,对应的分形维数值也越大。催化剂表面分形维数的变化程度可以用多重分形谱来表征,聚合活性高的催化剂表面分形维数的跨度和分散程度更高。提出的分形维数和多重分形谱计算程序为催化剂的评定与设计提供了一种实用的手段。     

Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

润滑油用纳米TiO2的表面改性及自修复性能研究

采用油酸对纳米TiO2进行表面改性，使其稳定分散于基础油中。利用HQ-1摩擦磨损试验机考察纳米TiO2的自修复性能，并探讨其自修复机理。试验结果表明，经改性后的纳米TiO2粉体作为润滑添加剂具有良好的分散稳定性、减摩抗磨性和自修复性。     

高斜效率高功率850nm氧化限制型垂直腔面发射激光器

报道了MOCVD生长的高性能850nm氧化限制型垂直腔面发射激光器.研制出的氧化直径为9μm的激光器25℃时的斜效率和阈值电流分别为0.82mW/mA和2.59mA,激光器在23mA时输出16mW最大光功率.氧化直径为5μm的激光器25℃时的最小阈值电流为570μA,其最大饱和光功率为5.5mW.     

区域水土特性参数时空变异分布特征及相关分析

作者应用地质统计学原理与方法,在山东簸箕李引黄灌区开展大尺度区域水土特性参数时空变异性的研究,描述农田排水、地下水、表层土壤中含盐量的空间与时间变化分布趋势和特征,分析其间存在的相关关系。结果表明,在一个完整的水文循环年内,研究区域的水土特性参数之间具有相近的空间变异分布状态和特点,但却表现出不同的时间变异分布趋势与特征。农田排水和表层土壤的含盐量随季节变化的分布状态在灌区上、下游相对稳定,在中游却变化明显;地下水的盐分浓度在整个灌区的分布状况没有呈现出明显的时间变异性。在春季至初夏时段内,农田排水中含盐量的增加似乎对地下水水质的影响较小,而对表层土壤积盐状况影响较大。研究成果为灌区制定合理的水资源利用与农田水土管理策略提供了理论依据。