FEM analysis of vacuum hot bulge forming of Hastelloy C-276 thin-walled cylindrical workpiece

A stress relaxation test has been carried out for Hastelloy C-276 at temperature of 800 ~C and initial stress level of 250 MPa. Based on the experimental stress relaxation curve, the relationship between creep strain rate and stress has been derived. Then, a set of creep constitutive equations has been built and the values of constants arising in the constitutive equations have been determined by fitting the creep strain rate-stress curve. Close agreement between computed results and experimental ones is obtained for stress relaxation data. The creep constitutive equation set has been integrated with the commercial FE （finite element） solver MSC.Marc via the user defined subroutine, CRPLAW, for the vacuum hot bulge forming process modelling of Hastelloy C-276 thin-walled cylindrical workpiece. The temperature field, the radius-direction displacement field and the stress-strain field are calculated and analyzed. Furthermore, the bulging dimension and the final internal diameter of workpiece are predicted and the test results verify the reliability of the finite element method.     

LC4铝合金高温变形规律的探讨

研究LC4铝合金的高温变形规律 ,拟合出具有较高精度的高温本构模型。并应用所开发的一套数值模拟软件系统 ,对LC4铝合金的高温压缩规律及压缩过程进行了分析。     

高压凝固对Al-Mg合金枝晶形态的影响

利用OLYMPUS光学显微镜研究了高压凝固对Al-9．6Mg合金枝晶形态的影响。结果表明，与常压下典型的破碎的粗大枝晶组织相比，高压凝固条件下，枝晶臂较完整，二次枝晶间距减小，并且大部分一次枝晶臂增长。从高压对成分过冷和热过冷的影响及溶质扩散角度探讨了枝晶形态的变化机理。高压这种极端凝固条件为改变合金的组织形态提供了一种新途径。     

Localized swelling of Fe-Cr-Ni alloy rollers in high-temperature applications

Localized swelling has been observed in 24Cr-24Ni-Nb steel transportation rollers used in the normalizing furnace of a plate mill after prolonged service at high temperature. Due to high localized thermal and mechanical stresses, the chromia layer formed on the roller surface ruptures, exposing the roller substrate to furnace oxygen. Oxidation of second-phase carbides results in the formation of carbon monoxide at very high partial pressure. This leads to formation of voids, leading in turn to localized swelling of the roller material.     

压铸模与铝合金金属间化合物的形成与分解

为了研究压铸模与铝合金金属间化合物的形成与分解过程，进行了热浸铝试验。试验结果表明金属间化合物的形成与分解是一个连续不断的循环过程，两者之间的相互关系导致了钢基的失效以及体积的减少。     

真空增压铸造技术及其应用前景

详细论述了真空增压铸造的技术原理、工艺特性及技术优点。结合铝合金铸件大型、复杂、薄壁、整体化和高气密性的发展趋势，针对性地分析了真空增压铸造技术推广应用的适应性，并提出了相应的技术对策。     

粉末冶金法浸入式发泡制作泡沫铝的试验研究

研究了浸入法制备泡沫铝的发泡新工艺以及工艺参数对发泡效果的影响，得出以工业纯铝粉和而H2粉为原料，制备气泡均匀、孔隙可控的泡沫铝的工艺参数为：浸入温度为680～760℃，浸入时间为10～30s，保温发泡时间为10～60s。研究结果表明，粉末冶金法浸入式发泡制备泡沫铝的效果好、结构均匀、TiH2利用率高，是一种有较好开发前景的新制备方法。     

NaCl水溶液中AZ91与A3钢的接触腐蚀

研究了NaCl水溶液中AZ9l镁合金与A3钢的接触腐蚀特性。试验结果表明，NaCl水溶液中，镁合金与A3钢接触时发生严重的接触腐蚀，腐蚀主要集中在镁合金与A3钢接触部附近；点蚀的平均孔深和腐蚀质量损失随NaCl浓度的增加和浸泡时间的延长而增加；镁合金接触腐蚀的主要腐蚀产物为Mg(OH)2，MgCO3和MgAl2O4，产物中还检测到因基体腐蚀而脱落的第二相Mgl7Al12。     

半连续铸造制备2024/3003梯度材料的研究

采用双流浇注半连续铸造方法制备了2024/3003铝合金梯度材料。研究了节流孔径和内浇包熔体温度两个工艺参数对铸件的成分分布，宏观组织和洛氏硬度的影响，结果表明，在保证铸造过程顺利进行的前提下，适当增大节流孔径和升高内浇包熔体温度都能增加铸件中内部合金的体积分数。合金的成分、宏观组织和力学性能之间的对应关系说明双流浇注半连续铸造方法制备2024/3003多元铝合金梯度材料是可行的。     

镁合金石墨砂型铸件表面氧化膜的组成与结构

利用XPS(X射线光电子能谱 )对镁合金石墨砂型铸造时的表面氧化膜进行了分析 ,探讨了表面氧化膜的组成与结构。结果表明 :镁合金表面氧化膜呈层状结构 ,主要由MgO和Mg(OH) 2 组成 ,由于表面氧化膜中有大量C原子的渗入 ,增加了致密度 ,使其具有较好的防护性能