天然橡胶/顺丁橡胶并用硫化胶的力学破坏机理

用扫描电子显微镜对天然橡胶／顺丁橡胶并用硫化胶的力学破坏机理进行了研究，结果表明试验样拉伸疲劳破坏断面具有拉伸断裂和屈挠龟裂的双重特征。白炭黑和Ｓｉ６９的加入使硫化胶的屈挠疲劳初始裂口形式发生变化。热氧老化使试样的拉伸断裂由韧性向脆性转化。     

The Microstructure of Solvent-Welding of PMMA

The microstructure of solvent-welding of PMMA has been investigated. The morphologies of shear, tensile, tear and cleavage fracture surfaces are observed. Effects of solubility parameter, elevated temperature, and cosolvent on the mechanical strength are studied. The solvents used are methanol, ethanol and DMF. The feature sizes of shear, tensile and tear fracture surfaces and the angle of the cleavage curve at the interface of PMMA can be employed to determine the mechanical strength qualitatively. Constituents of shear, tensile and tear fracture surfaces are tongues, long and narrow hackles, and equiaxed hackles, respectively. PMMA treated at high temperature showed enhanced mechanical strength. PMMA treated with 95% by volume ethanol yielded the best quality of adhesion. The solvent affected zone and the residual solvent are also discussed.     

加工条件对PP/芳纶复合材料横向拉伸性能的影响

对单向聚丙烯／芳纶纤维复合材料的横向拉伸性能进行了研究，讨论了压制时间、成型温度、成型压力，以及芳纶纤维的体积含量等对复合材料体系横向拉伸强度的影响。结果发现，随着压制时间、成型温度的增加，复合材料体系的横向拉伸强度提高；随成型压力的提高，复合材料的横向拉伸强度先升后降。此外，复合材料的横向拉伸强度随着芳烃纤维体积含量的增加而大幅度降低。     

Splicing of reinforcement bars with epoxy joints

The splicing of reinforcement bars in tension using epoxy-sleeve joints is described. The optimum length of the splicing sleeve required and the optimum bonding layer of epoxy resin in the joint were determined in direct tension tests. The performance of the epoxy-sleeve joint made to these optimum dimensions is then compared to that of a lap splice made according to the provisions of CP 110 in a beam flexure test. A sleeve length of 12 bar diameters and an optimum average thickness of 2 mm of the bonding layer of epoxy are shown to develop the full strength of the splices bar. Tensile reinforcement bars spliced using epoxy-sleeve joints are shown to perform satisfactorily as flexural reinforcement in beams and compare favourably with the standard CP 110 lap splice. Epoxy-sleeve joints are shown to produce stiffer beams and reduced crack width at the joints.     

纤维混掺超高性能混凝土抗冲磨与拉伸性能研究

为明确钢纤维-聚丙烯(PP)/聚乙烯醇(PVA)纤维混掺对超高性能混凝土(Ultra-High Performance Concrete,UHPC)抗冲磨和拉伸性能的影响,本文通过PP/PVA纤维与钢纤维混掺、长短PVA纤维混掺等方式,研究了UHPC抗冲磨性能,阐明了纤维混掺提升UHPC抗冲磨强度的作用机制;研究了不同掺量PVA纤维与钢纤维混掺对UHPC拉伸性能的影响,测试了UHPC拉伸应力-应变曲线,分析了纤维混掺对UHPC拉伸断裂能的影响。结果表明：在1.0%钢纤维的基础上添加0.2%~1.0%的PP/PVA纤维,能进一步提高UHPC的抗冲磨强度;纤维掺量相同时,钢-PP纤维混掺UHPC的抗冲磨性能整体上略优于钢纤维UHPC、钢-PVA纤维混掺UHPC和长短PVA纤维混掺UHPC;长短PVA纤维混掺时,长短纤维体积比为3∶1时UHPC抗冲磨强度最高。钢-PVA纤维混掺UHPC拉伸应力-应变曲线表现为应变软化,钢-PVA纤维混掺UHPC较钢纤维UHPC的抗拉强度略低,钢纤维比钢-PVA混掺纤维能更好地抑制微裂缝的萌生与扩展。     

UHPC的轴拉性能与裂缝宽度控制能力研究

为研究3种类型超高性能混凝土(ultra-high performance concrete,简称UHPC)的轴拉应力-应变曲线及其裂缝宽度控制能力,包括高应变强化UHPC、低应变强化UHPC和应变软化UHPC.采用轴拉试验方法测试狗骨头形试件,得到UHPC的轴拉应力-应变曲线和缝宽-应变曲线.试验结果表明:高应变强化UHPC和低应变强化UHPC的轴拉应力-应变曲线均包括弹性段、应变强化段和应变软化段,应变软化UHPC只有弹性段和应变软化段;UHPC应变强化段和应变软化段的转折点是裂缝缓慢扩展和迅速扩展的临界点;提高UHPC的极限拉伸应变,即延长其应变强化段,有助于提高其裂缝宽度控制能力;高应变强化UHPC拉伸应变在0.42%之前,其裂缝宽度均小于0.05 mm.对比C50混凝土(极限应变、极限强度分别为0.012%、2.3 MPa),高应变强化UHPC优异的裂缝宽度控制能力避免了结构设计中受正常使用状态裂缝宽度验算限制的影响,同时可在钢筋屈服前与其全程协同工作,这使得钢筋增强高应变强化UHPC在某些需要对裂缝宽度进行严格控制的结构类型中具有很高的应用价值.     

拉伸变形对AA6016铝合金汽车外板再结晶组织及性能的影响

为优化冲压成形工艺,研究了不同拉伸形变量对T4P态AA6016冷轧薄板再结晶、析出行为、烘烤硬化性及断裂方式的影响规律.采用与气垫炉生产线类似的新型热处理设备,对合金进行固溶处理,预时效后室温停放,获得T4P态合金.以单向拉伸模拟板材局部冲压成形过程,采用金相显微镜、扫描电镜和透射电镜,对合金再结晶组织、拉伸断口以及位错进行观察,并结合DSC测定和拉伸性能测定,对合金析出行为及力学性能表征.结果表明:随拉伸形变量增加,局部晶粒有被拉长的趋势;形变可抑制GP区溶解,并促进强化相析出;烘烤硬化性随形变增加而减弱;形变较小时,烘烤前后断裂方式均为塑性断裂,而形变较大时,烘烤前合金更加趋向于解理断裂,烘烤后解理断裂趋势减弱.     

地聚物砂浆高温后抗拉和粘结性能及退化机理

为考察地聚物砂浆在有耐高温要求的混凝土结构加固领域的应用可行性,开展了常温下和高温后地聚物砂浆的抗拉强度试验以及地聚物砂浆与普通水泥砂浆及普通混凝土基体的粘结性能试验,并与普通水泥砂浆的抗拉及粘结性能进行试验比较;通过热重分析-差示扫描量热分析(TG-DSC),探究了地聚物砂浆的高温强度退化机理.试验结果表明:地聚物砂浆与水泥砂浆及混凝土之间的常温粘结强度分别达2.15 MPa及1.7 MPa,经300℃高温后残余粘结强度仍有1.5 MPa左右,远高于普通水泥砂浆的粘结强度;超过300℃以后地聚物砂浆的强度急剧退化,这主要是因地聚物砂浆高温脱水、微观结构遭受破坏引起.基于上述试验结果,可将地聚物砂浆用于300℃以下高温环境的混凝土结构修补加固.     

拉压变形对B(N)掺杂碳纳米管Al吸附性能的影响

为了研究(5,5)碳纳米管的B(N)环状掺杂效应,以及拉压变形对B(N)环状掺杂碳纳米管Al吸附性能的影响,采用基于密度泛函理论的平面波赝势和广义梯度近似方法,对B(N)环状掺杂碳纳米管Al吸附模型进行了几何优化,计算了B(N)环状掺杂碳纳米管的形成能,并确定了Al原子的最稳定吸附位置.结果表明,B(N)环状掺杂(5,5)碳纳米管的结构较为稳定.B(N)环状掺杂可以增加碳纳米管与Al之间的吸附能;一定范围内的拉伸和压缩变形则会降低碳纳米管与Al之间的大部分吸附能.     

芦荟纤维与粘胶纤维物理性能测试与分析

对芦荟纤维与粘胶纤维的拉伸性质、摩擦和抱合性质、卷曲弹性、耐热性和热稳定性进行了测试与分析。结果表明:芦荟纤维的断裂强度比粘胶高,芦荟纤维的断裂伸长率比粘胶低;芦荟纤维粘胶的静摩擦因数小于粘胶纤维的静摩擦因数;粘胶纤维间的抱合力比芦荟纤维间的抱合力大,但芦荟纤维的平滑性比粘胶纤维要好。粘胶纤维的卷曲数、卷曲率、卷曲弹性回复率和残留卷曲率均小于芦荟纤维。