Class I hydrophobin Vmh2, a peculiar surface active and versatile fungal protein, is known to self‐assemble into chemically stable amphiphilic films, to be able to change wettability of surfaces, and to strongly adsorb other proteins. Herein, a fast, highly homogeneous and efficient glass functionalization by spontaneous self‐assembling of Vmh2 at liquid–solid interfaces is achieved (in 2 min). The Vmh2‐coated glass slides are proven to immobilize not only proteins but also nanomaterials such as graphene oxide (GO) and quantum dots (QDs). As models, bovine serum albumin labeled with Alexa 555 fluorophore, anti‐immunoglobulin G antibodies, and cadmium telluride QDs are patterned in a microarray fashion in order to demonstrate functionality, reproducibility, and versatility of the proposed substrate. Additionally, a GO layer is effectively and homogeneously self‐assembled onto the studied functionalized surface. This approach offers a quick and simple alternative to immobilize nanomaterials and proteins, which is appealing for new bioanalytical and nanobioenabled applications.     

Thermal treatment of waste photovoltaic module for recovery and recycling: Experimental assessment of the presence of metals in the gas emissions and in the ashes

The rapid expansion of the photovoltaic (PV) module market in the last years will determine in the near future a remarkable growth of corresponding waste. Then, the hazardous materials contained in the modules, such as Cd, Pb and Cr, could be released in the environment if the waste panels will not be handled adequately. Recycling processes of silicon crystalline panels, finalized to separate PV cells from the glass, involve the removal of the EVA (Ethylene Vinyl Acetate) layer through different methods, as the thermal treatment. During this treatment, some hazardous components can be released due to thermal degradation process. In this paper the metals released in the gas emissions and in the ashes due to the thermal treatment of modules were evaluated. For this purpose, three samples of crystalline panels were heated in furnace up to 600 °C and the complete degradation of the EVA was obtained. A mass balance between the sample and its components, before and after treatment, was performed in order to assess the weight loss percentage. Finally, after thermal treatment a qualitative analysis on the separated PV cell surface was performed by SEM-EDS (Scanning Electron Microscope equipped with Energy Dispersive Spectrometer).     

轻质滤料滤池的试验与研究

轻质滤料滤池是以比水密度略小的滤料为滤床的滤池，通过以净水厂的原水和污水处理厂的二级处理出水为过滤试验对象，所取得的结果表明：下向流轻质滤料滤池对浊度和悬浮固体（SS）的去除率分别可以达到80％和45％，而滤床的水头损失不超过15cm。因此轻质滤料滤池可以以预过滤的形式配置在过滤处理的净水和污水的处理工艺中。     

Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

一种微透镜阵列的研制

介绍一种利用表面张力的作用、以光纤作材料、用分离的自聚焦透镜制作微透镜阵型的方法，这种方法具有制作工艺简单、无须昂贵设备等优点，用此方法实际制作了具有良好连续面型的微透镜阵列，并对制作的微透镜阵列进行了测试，效果较好。     

The Soft-Contact Method and Instruments for Measuring the Surface Temperature of Solids

A method and instruments based on it are proposed for the contact measurement of surface temperature when carrying out industrial experiments and when monitoring technological parameters.     

Anthocyanin composition of the red wine Babić affected by maceration treatment

Identification of anthocyanins in the wine made of the Croatian autochthonous grape variety of Babić (Vitis vinifera L.) was carried out and their profile was determined by means of high-performance liquid chromatography with diode array and mass spectrometric detection. Dependence of anthocyanins content and profile on maceration treatment conditions was investigated. Statistically significant differences of anthocyanins concentration in wines Babić produced by various maceration treatments were confirmed by the use of multivariate analysis of variances. The investigation results indicated that the maceration temperature exerts higher influence on anthocyanins concentration than the duration of maceration. In addition, on the basis of anthocyanin composition and using different multivariate statistical analyses, differentiation of wines Babić according to maceration treatments was procured.