芴酮在合成功能高分子方面的应用

介绍了由芴酮合成的双酚芴在高分子材料方面的应用，尤其是在环氧树脂、聚碳酸酯、有机玻璃方面，与双酚A相比，用双酚芴改性的高分子材料具更高的耐热性及透明性。     

草酸钙在硫酸软骨素自组装膜上周期沉淀的研究

利用硫酸软骨素(chondroitin sulfate，CS)在云母基底上通过浇铸法制备的自组装膜为基底，诱导草酸钙在其上的凝集生长。发现当硫酸软骨素的浓度为1．Omg／ml时在该膜体系中可形成规整的周期性草酸钙环状沉淀。这种有序的环状结构可能是耗散结构的一种具体表现形式。利用原子力显微镜(atomic forcemicroscope，AFM)和傅立叶红外光谱仪对这种结构进行了表征，实验结果显示合适浓度下形成的CS膜在一定程度上可以抑制草酸钙的凝集结晶，表明高分子基质与无机离子间强烈的相互作用对无机盐的成核结晶有显著影响，为探讨结石的形成与抑制提供了一定的实验依据。     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

哈得4联合站技术改造

位于塔克拉玛干大沙漠腹地的哈得4油田,2004年成为全国最大的沙漠油田,2005年产量达到200×104t。在对联合站存在问题逐一分析的基础上,提出了技术改造的措施。现场采集的运行数据表明技术改造效果明显,增强了流程可靠性,提高了自动化水平,降低了能耗。     

LD抽运免调试谐振腔被动调Q的固体激光器

将免调试谐振腔应用于二极管抽运固体激光器 ,采用Cr4 + ∶YAG晶体被动调Q ,准连续二极管侧向非均匀抽运Nd∶YAG激光棒 ,传导冷却 ,KTP腔外倍频 ,具有结构紧凑、抗失调能力强的特点。获得了远场近似平顶高斯分布的激光输出 ,输出波长 0 5 3μm ,能量 5 2 2mJ pulse ,稳定性 0 5 % ,电 光转换效率 3 4 % ,脉宽～ 6ns,重复频率 10～ 4 0Hz,发散角 2 8mrad。     

IS-2000规范在Walsh Code定义上的局限性

本文针对IS-2000规范关于W alsh Code的定义,发现IS-2000规范有关W alshCode的定义不合理,在前向RC 3下限制了最大数据用户数和最高数据速率;如按本文修改规范关于W alsh Code的定义,不但可以在前向RC 3下提高最大数据用户数,同时在理论上可以将最高数据速率提高一倍。     

Synthesis and luminescence of Sr2CeO4 fine particles

Fine particles of a blue emission phosphor Sr₂CeO₄ have been synthesized using a chemical co-precipitation technique, and the textual and luminescent properties were compared with the one synthesized by the conventional solid-state reaction method. Particle size and distribution of the Sr₂CeO₄ fine powder prepared by the co-precipitation process were smaller and narrower than those obtained by the samples prepared from the conventional one. The emission intensity of the fine particles was equal to that of the larger particles prepared from the solid-state reaction, on the contrary to the general tendency that emission intensity decrease with particle size reduction. Although no Ce³⁺ peaks were observed in EPR measurements, X-ray photoelectron spectra of the samples clearly elucidated the existence of Ce³⁺ only on the surface of Sr₂CeO₄.     

Fe3O4/PSt/TiO2多层包覆电磁响应微球的制备

首先采用分散聚合法将自制的Fe3O4磁流体和苯乙烯反应合成有磁核的Fe3O4/PSt磁性聚合物微球，然后，用非均匀成核水解反应在Fe3O4/PSt微球外包覆无定形二氧化钛，获得Fe3O4/PSt/TiO2复合微粒。用红外光谱、扫描电镜和热分析对粒子的形貌和结构进行了表征。并测试了微粒的介电性能和磁性，结果表明，所制得复合微粒有良好的电、磁响应性。     

Processing and microstructure of non-oxide ceramic fibres

Research and development efforts on high-temperature, oxidation-resistant fibres have increased over the past decade due to the demand for light-weight, stiff and strong composite materials in aerospace applications. Varieties of ‘high-performance’, continuous, non-oxide fibres with low-density, high tensile strength and tensile modulus have been developed either from organic precursors or via chemical vapour deposition for fabrication of ceramic matrix composites. Fibres derived from polymer precursors (e.g. Nicalon, Tyranno, HPZ) are small in diameter (compared to CVD monofilaments) and are ideally suited for ceramic composites. Processing, microstructural stability and mechanical properties of these newly developed SiC and Si₃N₄ base fibres are briefly reviewed in this paper.     

Microstructure-Property Correlation in AI_4C_3 Dispersion Strengthened Al Composite

The microstructure and tensile properties of Al_4C_3 dispersion strengthened Al composite fabricatedby reaction milling technique were investigated.It is indicated that the rod-like Al_4C_3 dispersoidshaving a diameter of 0.02-0.03 μm and a length of 0.1-0.3μm are formed by reaction of C with Al,and uniformly distributed in the Al matrix.The interface between Al_4C_3 and Al is clean and theinterfacial bonding is good.The matrix consists of the subgrains which have the size of 0.3-0.4μm,and most of the Al_4C_3 dispersoids are distributed on the subgrain boundaries.The 11 vol.-%Al_4C_3/Al composite exhibits an UTS (ultimate tensile strength) of 400 MPa and anelongation-to-failure of 8.0%.