光催化降解渗滤液DOM不同组分的相对分子质量变化特征

采用凝胶色谱技术研究了光催化氧化处理过程中垃圾渗滤液DOM 6种组分的分子质量变化规律.结果表明,垃圾渗滤液DOM的相对分子质量大多在104以下,平均在104以上的大分子物质主要是HIB和HIN,仅占渗滤液DOM总量的20%左右.其余组分大多位于(1～10)×103之间,低于500的组分含量很少.说明垃圾渗滤液DOM是以中等相对分子质量的黄腐酸类物质为主,难以生物降解.光催化处理过程中渗滤液DOM的相对分子质量分布范围逐渐变宽,多分散系数D逐渐增大.HOB、HIB、HIA以及HON组分在光催化处理后,相对分子质量显著减小;其中HOB减小最为明显,由初始的(4～25)×103,减小为72 h的(0.4～1)×103之间.而HOA和HIN组分的相对分子质量呈增加趋势,其中HOA增加最为明显,在垃圾原液中分布于(2～20)×103,在72 h光催化处理液中位于(20～50)×103之间.随着处理时间延长,DOM各组分的RID信号均降低,说明其浓度下降.整体上看,渗滤液DOM各组分均发生了明显光催化转化.     

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

Photocatalytic activity of TiO2 containing anatase nanoparticles and rutile nanoflower structure consisting of nanorods

A series of TiO2 with different crystal phases and morphologies was synthesized via a facile hydrothermal process using titanium nbutoxide and concentrated hydrochloric acid as raw materials. The photocatalytic activity of the samples was evaluated by degradation of Methyl Orange in aqueous solution under UV-Visible light irradiation. On the basis of detailed analysis of the characterizing results of high-resolution transmission electron microscopy, X-ray powder diffraction measurements, X-ray photoelectron spectroscopy and Brunauer-Emmett-Teller measurement, it was concluded that the photo-activity of the catalyst is related directly to the 3D morphology and the crystal phase composition. An excellent catalyst should have both a futile 3D flower-like structure and anatase granulous particles. The 3D flower-like structure could enhance light harvesting, as well as the transfer of reactant molecules from bulk solution to the reactive sites on TiO2. In addition, the optimum anatase/rutile phase ratio was found to be 80：20, which is beneficial to the effective separation of the photogenerated electron-hole pairs.     

Enhanced photocatalytic activity of quantum-dot-sensitized one-dimensionally-ordered ZnO nanorod photocatalyst

An efficient photocatalyst was fabricated by assembling quantum dots （QDs） onto one-dimensionally-ordered ZnO nanorods, and the photocatalytic properties for Methyl Orange degradation were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-Vis-NIR absorption spectroscopy and photoluminescence. The results indicate that the catalyst with assembled QDs is more favorable for the degradation than the pristine ZnO nanorods. The QDs with core-shell structure lower the photocatalytic ability due to the higher carder transport barrier of the ZnS shell layer. Besides its degradation efficiency, the photocatalyst has several advantages given that the one-dimensionally-ordered ZnO nanorods have been grown directly on indium tin oxide substrates. The article provides a new method to design an effective and easily recyclable photocatalyst.     

多壁碳纳米管的制备与可见光催化性能

采用溶胶-凝胶法,制备了多壁碳纳米管(MWCNTs)/CdS/TiO2复合半导体光催化剂。通过扫描电镜(SEM)、X射线衍射(XRD)和紫外-可见吸收光谱(UV-vis)等分析方法对光催化剂进行了结构表征,并考察了在可见光照射条件下MWCNTs/CdS/TiO2对甲基橙(MO)降解的光催化性能。结果表明,MWCNTs/CdS/TiO2能有效降解甲基橙。低浓度MO降解效果比高浓度好,光催化剂投加量为1.2 g/L即可达到较好的催化效果,酸性条件有利于光催化,投加适宜浓度的H2O(2低于10 mmol/L)时会和催化剂产生协同效果,浓度过大,催化效果下降。阴离子对催化效果有抑制作用,其中PO43-的抑制作用最强。所制备的复合催化剂具有较好的实际应用价值。     

铋-镧复合氧化物的制备与光催化活性

以同时含La(Ⅲ)和B(iⅢ)的双金属配合物BiLa(dtpa)(NO3).3.5H2O为前驱体,通过500℃的热分解制得铋-镧复合氧化物Bi0.775La0.225O1.5,并利用XRD、SEM和UV-Vis漫反射等分析手段研究灼烧时间对样品的结构及光吸收特性的影响。以甲基橙模拟废水的光催化降解为模型,研究不同灼烧时间对铋-镧复合氧化物光催化活性的影响。结果表明,热分解所得铋-镧复合氧化物样品呈疏松多孔结构,对光具有较宽的吸收范围,在紫外光区具有较好的光催化活性,灼烧时间影响样品的粒径和形貌以及光催化效果,在20 mg/L甲基橙溶液中添加灼烧1 h和4 h所得的催化剂样品1 g/L,光照4 h后甲基橙褪色率分别达95%和91%。     

纳米Fe_3O_4/膨润土的制备、表征及光催化降解焦化废水

以铝柱撑膨润土负载纳米Fe_3O_4制备出性能良好的复合型催化剂。结合X射线粉末衍射(XRD)、扫描电镜(SEM)和比表面孔隙分析(BET)对催化剂的晶相、比表面积和粒度进行表征。负载的纳米Fe_3O_4粒径约为20～30nm,均匀分散到膨润土表面,未发生明显的团聚。在紫外光作用下用该催化剂对焦化厂二沉池出水进行深度处理。结果表明,在催化剂投加量为0.7 g/L,pH为2.5,温度40℃,H_2O_2初始浓度为17.6mmol/L的反应条件下,二沉池出水(化学需氧量COD=140mg/L,色度=400度)经催化氧化降解后,COD和色度可分别降低到54.44 mg/L和10度,达到国家工业再生用水水质标准GB/T 19923-2005(COD≤60 mg/L,色度≤30度)。催化剂重复使用4次时,废水COD和色度去除率保持稳定。     

磁性纳米Fe_3O_4对毒死蜱的增效和催化降解研究

应用溶剂热法制备了磁性纳米Fe3O4(NMFO),并用聚乙二醇-6000对其进行改性,使纳米Fe3O4表面由亲水性转变为亲脂性,从而实现与亲脂性毒死蜱的复合。纳米Fe3O4的加入使毒死蜱的生物活性明显提高。室内毒力试验结果表明:含0.2%纳米Fe3O4的Fe3O4/毒死蜱制剂的毒力在室内和紫外光照下分别是同浓度纯毒死蜱的3.84倍和4.17倍;其降解率也显著提高,纳米Fe3O4/毒死蜱制剂在太阳光照下放置10 d,其降解率可达93.2%,相同条件下纯毒死蜱的降解率是10.14%,而将添加或未添加纳米Fe3O4的毒死蜱于暗处放置相同的时间,其降解率分别为1.21%和0.23%。     

酞菁-二氧化钛光催化剂的制备及其光催化降解效果

采用溶胶-凝胶法制备酞菁-TiO2光催化剂,并分别掺杂铁、铜、钴、镍元素。酞菁作为光敏化剂,提高TiO2在可见光下对有机染料的降解效果。采用SEM对催化剂进行表征,研究在可见光下酞菁-TiO2光催化剂对5种有机染料(甲基橙、甲基红、甲酚紫、亚甲基蓝和孔雀石绿)的降解效果,结果表明,酞菁铁-TiO2,酞菁钴-TiO2,酞菁铜-TiO2,酞菁镍-TiO2均能有效降解这几种有机染料,光催化反应300 min后降解率达92%。比较4种催化剂对甲基橙的降解率,酞菁钴-TiO2催化剂降解效果最明显,以下是酞菁铁、酞菁镍和酞菁铜-TiO2催化剂。     

光氧化反应脱汞技术发展综述

燃煤电厂烟气中汞污染的控制技术研究是目前重要的环保课题之一。气相元素汞成为大气中汞污染的主要来源。文章分析了光氧化反应脱汞技术(包括光化学氧化反应和光催化氧化反应)的反应机理,认为光化学氧化反应技术脱汞均是在紫外光作用下,产生具有强氧化性的基态原子或自由基,将难以脱除的Hg0氧化为高价汞,再通过配套的电除尘器等设备将高价汞捕集,进而达到汞污染控制的目的。不同的是,在光化学氧化反应中,汞的氧化需要借助于电厂烟气中的O2、H2O等成分,而在光催化氧化反应中,反应需要在光催化剂(TiO2或TiO2负载复合物等)的催化作用下进行。阐述了光氧化反应汞脱除技术研究进展。光氧化反应脱汞技术的汞脱除率均可达到60%~70%,具备设备简单、无二次污染等优点。