Effects of carbon content and solidification rate on thermal conductivity of grey cast iron

The thermal conductivity or diffusivity of pearlitic grey irons with various carbon contents is investigated by the laser flash method. The materials are cast in controlled thermal environments and produced in three dissimilar cooling rates. The cooling rate together with the carbon content largely influence the thermal conductivity of grey iron. Linear relationships exist between the thermal conductivity and the carbon content, the carbon equivalent and the fraction of former primary solidified austenite transformed into pearlite. The work shows that optimal thermal transport properties are obtained at medium cooling rates. Equations describing the thermal conductivity of pearlite,solidified as pre-eutectic austenite, and the eutectic of grey iron are derived. The thermal conductivity of pearlitic grey iron is modeled at both room temperature and elevated temperature with good accuracy.     

双主流道注射模设计

注射模中的长型芯若受到塑料熔体侧压力则易发生弹性弯曲变形,这种情况成为塑件成型的一种障碍。介绍双主流道模具及注射机双喷嘴机构能在模具结构简单的前提下,提供成对浇口,使长型芯受到的塑料熔体压力保持平衡,明显地减少弹性弯曲变形。     

Effect of strontium on columnar growth of dendritic α phase in near-eutectic Al-11.6%Si alloys

For Al-11.6 % Si alloy, the influence of the addition of Sr on the morphology of the dendrite α phase was investigated, and the characteristic parameters of the dendrite α phase, the primary dendrite spacing and the secondary dendrite arm spacing, were also measured. The addition of strontium promotes the columnar dendrite growth and leads to a decrease of both the primary dendrite spacing and secondary dendrite arm spacing with the increase of the content of strontium in the modified near-eutectic Al-Si alloys. It is thought that the addition of Sr leads to a reduction of the solid-liquid interfacial energy of the dendrite α phase, consequently resulting in a decrease of the growth undercooling of dendrite tips. And hence, the nucleation of the equiaxed grains in the liquid in front of the columnar dendrite tips is restrained, thus the addition of strontium in Al-Si alloys promotes the growth of the columnar dendrites. The reduction of the solid-liquid interfacial energy also leads to the decreases in the primary dendrite spacing and the secondary dendrite arm spacing.     

Mn和Mg对Al-5Fe合金初生Al3Fe相形貌的影响

Mn和Mg添加到Al-5Fe(质量分数，％，下同)合金中，初生Al3Fe相的形貌发生明显变化．未加入合金元素时，该合金中的初生Al3Fe相长成粗大的针片状；加入2．5％Mn和0．1％Mg(质量分数，下同)后，粗大的初生富铁相消失，取而代之的是细小针状、粒状和花朵状；加入2．5％Mn和1．5％Mg，合金中的富铁相大部分转变为粒状和穗状(分叉状)两种．探讨了粒状和穗状的形成机理．对合金力学性能的测试表明，加入Mn和Mg后，合金的抗拉强度得到了不同程度的提高：Al～5Fe合金为107MPa，Al-5Fe-2．5Mn-0．1Mg合金为139MPa，Al-5Fle-2．5Mn-1．5Mg合金为122MPa，增长幅度分别为29．9％和14％．     

一段炉分气管泄漏原因分析及解决措施

本文介绍了中原大化集团一段炉分气管的泄漏状况，分析了泄漏原因，介绍了解决措施。     

过共晶铝硅自生梯度复合材料的组织与性能

用电磁分离工艺成功制备了初生Si相体积分数、材料显微硬度和耐磨性沿径向呈梯度分布的棒状复合材料 ,讨论了梯度层的形成过程。微观组织观察和力学性能测试结果表明 :在近外壁区域形成了体积分数高达16 %的细小初生Si相偏聚区 ,此区硬度高 ,耐磨性好 ,中心区为细小和均匀的共晶组织 ,两部分之间为颗粒体积分数渐变的过渡区 ,可使耐磨层与基体的结合强度得到保证     

Al-Cu-Fe系初生准晶相凝固过程的热力学分析

采用XRD,SEM和TEM等方法,研究了铸态 Al58.8Cu36.6Fe3.5Si1.1合金(973K保温2.5h后水淬)的显微组织及相组成.观察到铸态样品中存在4种不同的相,即初生准晶I相、Φ相、θ-Al2Cu相和η-AlCu相.对准晶I相及其晶体近似相R相,提出相应的自由能计算模型及算法,从理论上说明准晶(Al61.89Cu25.61Fe11.10)I相是高温稳定相,当温度低于938K时,将形成其晶体近似相R相.     

旋转交变磁场和静磁场对Al-18%Si合金变质处理的影响

分别研究了旋转磁场和静磁场对过共晶Al-18％Si合金变质处理的影响。结果表明：变质处理后．不施加磁场的条件下，块状初晶Si偏聚在试样边缘处，试样中心处为共晶Si；施加旋转交变磁场的条件下，粗大的板条状初晶Si偏聚在试样边缘处，试样中心处为共晶Si；施加静磁场的条件下，在试样整个横断面上初晶Si都是细小的块状，且大小和分布均匀。     

伊朗铝工业

本文对伊朗铝工业的现状和未来发展规划进行了阐述。伊朗是一个资源非常丰富的国家，有许多发展原铝生产的有利条件。目前伊朗有两座电解铝厂和一座产能为30万t的氧化铝厂，原铝的产量达到了16．75万t。2004年伊朗的原铝产量将达到23万t，2005年将达到50万t。伊朗计划在2009年，使本国的原铝产量达到100万t，氧化铝产量达到220万t，生石油焦产量达到40万t。     

初生M6C的形成及其对高钨铸造模具高温合金的影响

高钨铸造合金已用于铸造大型模具，由于大量初生M6C碳化物的形成使模具变脆，需探明初生M6C的形成条件．实验表明当含碳量超过0．15％时，合金中易析出初生M6C，而10％Co起有效的抑制作用．初生M6C是在1375℃时形成的，它对通过固-液范围的冷却速度十分敏感，快冷抑制它的形成．铸件中M6C的形成存在明显的尺寸效应，枝晶间距大于150μm时的较厚截面极易形成毫米量级的M6C，严重的损伤合金的高温强度．因此对大截面的模具合金，为防止初生M6C的析出，合金中最好保持0．04％—0．07％C和10％—15％Co．