Electrochemical analysis of the microbiologically influenced corrosion of steels by sulfate-reducing bacteria

The differences between the general corrosion and microbiologically influenced corrosion (MIC) of steels were investigated in terms of its electrochemical behavior and surface phenomena. The corrosion potential of steels in the absence of SRB (sulfate-reducing bacteria) shifted to a negative value with the immersion time. However, the potential of the presence of SRB shifted to a positive value after 30 days' incubation, indicating the growth of SRB biofilms on the test metal specimens and the formation of corrosion products. In addition, the color of a medium inoculated with SRB changed from gray to black. The change in color appeared to be caused by the formation of pyrites (FeS) as a corrosion product, while no significant change in color was observed in a medium without SRB inoculation. Moreover, corrosion rates of various steels tested for MIC were higher compared to those of steels in the absence of SRB. In particular, the corrosion current density of TMCP steels in the presence of SRB was larger than that of other steels. Pitting corrosion was also observed at the surface of all steels in the SRB-inoculated medium. The pitting corrosion likely occurred due to SRB that was associated with the increasing corrosion rates through increasing cathodic reactions, which caused a reduction of sulfate to sulfide as well as the formation of an oxygen concentration cell.     

Discharge characteristics of lead dioxide electrode prepared with cementation lead oxide

Lead acid batteries have had restricted applications because of relatively low energy density below 50Wh/kg. Many efforts have achieved lighter battery components such as separators, connections and containers etc. Thus, the most important problem of the lead acid battery is to improve the low capacity of the active material in the positive electrode. The purpose of this study is to improve the utilization of the active material in the lead dioxide electrode for the lead acid battery through the production of lead oxide with better physicochemical characteristics through cementation. A cementation reaction was performed in 1.0wt.%HCl solution using pure magnesium plate as the reductant. We investigated the utilization of the active material and discharge characteristics of the positive electrode with a current density ranging from 3.4 to 108.8mAcm⁻². As a result, the active material utilization was about 72% at 3.48 mAcm⁻² and increased with decreasing current density. The discharge characteristics according to current density are especially very good at high current density     

Durability of Titanium/Dicalcium Silicate Composite Coatings in Simulated Body Fluid

Titanium/dicalcium silicate composite coatings with different ratios (weight ratios as Ca₂SiO₄: Ti = 3:7, 5:5, 7:3) were prepared by plasma spraying. Effects of titanium addition on coating properties, such as bonding strength, flexural modulus, and dissolution in simulated physiological environment, were studied. Results showed that the bonding strength between coating and Ti-6Al-4V substrate increased with increase of titanium content in the composite coatings. It was explained by the narrowed dissimilarity of thermal expansion coefficients between the coatings and substrates. Degradation of mechanical properties after immersion in simulated body fluid was also studied. The dissolution of dicalcium silicate in the composite coatings resulted in the decrease of flexural strength and flexural modulus of the coatings in the simulated physiological environment. The higher titanium content in the composite coatings, the stabler are the composite coatings in the physiological environment.     

Investigation of micro-EDM material removal characteristics using single RC-pulse discharges

Similar to EDM, in micro-EDM, intense heat is generated between the workpiece and tool electrode by the discharge through a dielectric medium to result in the formation of a microcrater that is much smaller in size. In this study, a single-spark generator has been developed to study the erosion characteristics from the microcrater size. Using a simple heat transfer model, the efficiency at different discharge condition is also deduced. It is found that at lower-energy (<50 μJ) discharges, the energy required to remove the unit volume of material, defined as the specific energy, is found to be much less than that at higher-energy discharges. Additionally, the ratio of the standard deviation to the measured microcrater size is found to be lower at lower discharge energy, indicating greater consistency in shape and size when the discharge occurs at lower energy. The fundamental erosion mechanism of material is discussed by considering melting and evaporation phenomena using theoretical modeling. The average efficiency of erosion, when estimated to be due primarily to melting or evaporation alone, is found to be up to an order of magnitude higher at lower-energy discharges than that at higher-energy discharges.     

Investigation of the grain coarsening behavior of some Aluminum alloys

Grain coarsening tests were carried out on Al-4.5 pct Cu and Al-4.5 pct Si alloys. The effects of three variables, melt composition, pour temperature, and mold temperature, were determined. It was found that the macrostructure generally coarsened with increased pour and mold temperatures. Coarsening was extreme in the unrefined alloys but was retarded by the active grain refiners like titanium and columbium. The effect of boron was spectacular in suppressing coarsening tendencies. The results of the investigation support the carbide theory of nucleation as opposed to the peritectic theory.     

Microstructure evolution during batch annealing

Design of industrial annealing cycles requires recrystallization and grain growth studies, which are typically carried out under isothermal laboratory condition. The kinetics coefficients of these phase transformations are obtained from such studies, which are subsequently used in designing the industrial nonisothermal cycles using the additivity principles. However, the strong heating rate effects on the grain growth kinetics necessitate such kinetics studies using industrial thermal profiles. In the present work, the hot and cold spot cycles of an industrial batch annealing cycle for AIK grade steel have been simulated in a programmable laboratory furnace. Subsequently, the effect of annealing temperature, soaking time, and heating rate on the microstructural features, such as grain size distribution, grain shape anisotropy, and grain orientation, have been investigated through extensive quantitative microscopy. The implications of these results on the design of industrial batch annealing cycles have been discussed.     

Determination of Active Slip/Twinning Modes in AZ31 Mg Alloy Near Room Temperature

In order to determine the deformation modes in AZ31 magnesium alloy at room temperature, computer simulations of deformation texture development and calculation of formability have been carried out. The simulation results were compared with the measured texture results. Based on agreement between the experiments and simulations the active deformation modes were determined. A Visco Plastic Self Consistent model was employed for the simulation of plastic deformation. Simulations and experiments were performed for different initial textures. The goal of the study was to develop the understanding of deformation texture evolution and its effects on mechanical properties of magnesium, with an ultimate goal of improving room temperature formability of magnesium alloys. This article was presented at Materials Science & Technology 2006, Innovations in Metal Forming symposium held in Cincinnati, OH, October 15-19, 2006.     

Effects of solid solution alloying on creep deformation of aluminum

The effects of solid solution alloying on the creep-rupture properties, deformation characteristics, ductility, and fracture of pure aluminum were studied by means of creep-rupture tests on polished specimens of three alloys each of Al-Cu (0.24, 0.79, and 2.05 pct Cu), Al-Zn (4.93, 9.89, and 19.78 pct Zn), and Al-Mg (0.94, 1.92, and 5.10 pct Mg) at 500°, 700°, and 900°F.     

Microstructure and creep behavior in AE42 magnesium die-casting alloy

The micro structural analysis of die-cast AE42 reveals a correlation between micro structure and creep strength. A lamellar-phase Al₁₁RE₃, which dominates the interdendritic microstructure of the alloy, partly decomposes above 150‡C into Al₂RE and Al (forming Mg₁₇Al₁₂). The increased solubility of aluminum in magnesium at higher temperatures may also promote the decomposition of Al₁₁RE₃. The creep strength decreases sharply with these phase changes. A mechanism for the decrease in creep strength of AE42 is proposed whereby the reduced presence of lamellar Al1₁₁RE₃ and/or the presence of Mg₁₇Al₁₂ contribute to the observed poor creep strength at higher temperatures.     

Chromium distribution between liquid iron and molten basic slags

An equilibrium study was made of the distribution of chromium and oxygen between liquid iron, containing less than 1 pct Cr, and simple slags of the CaO(MgO)-SiO₂-FeO-Cr₂O₃ type in the temperature range 1526° to 1734°C The effects of slag oxidation, temperature, and basicity were observed.