Perylene derivative sensitized multi-walled carbon nanotube thin film

Perylene-sensitized multi-walled carbon nanotubes (PV-MWNT) have been prepared by a π-stacking between nanotubes and perylene derivatives, N,N′-diphenyl glyoxaline-3,4,9,10-perylene tetracarboxylic acid diacidamide (PV). The resultant nanocomposites have been characterized by transmission electron microscope (TEM), UV-vis absorption, photoluminescence (PL) and photocurrent spectra. Long range ordering can be observed in the form of PV-MWNT via π-stacking by TEM. Red-shift in the optical spectra consisting of the UV-vis absorption and PL spectra with the attraction of PV on the surface of the MWNTs were observed. The evident quenching in PL spectra of PV-MWNT was ascribed to the absorption and transfer of recombination energy by MWNT. Photosensitivity spectra demonstrated an increasing photocurrent in the ultraviolet region and a broadening photosensitivity in the red spectral region for solar cells based on PV-MWNT.     

A PRACTICAL METHOD FOR RECTIFYING INTERFACIAL TENSION DATA TO PREDICT THE SHAPE OF INTERFACES IN AN IMMISCIBLE LIQUID/LIQUID/GAS SYSTEM

The shape of interfaces formed by the contact of two liquid phases, immiscible with each other, and a gaseous phase can be predicted on the condition that the tension to work at each interface is known with a sufficient accuracy. In general, interfacial tension data available are not so accurate, however, as to be useful as they are in predicting the shape of interfaces, particularly when the spreading coefficient of either liquid (liquid 1) on the other (liquid 2) has a negative value of a small magnitude. Presented in this note is a simple method to rectify the interfacial tension data, with the aid of a measurement of the radius of a lens of liquid 1 of a known volume placed on the horizontal surface of liquid 2, and thereby make them usable for predicting interfacial geometries. The method is tested by applying it to benzene/water and n-pentane/water systems.     

Fibrous support for immobilization of enzymes

A poly(vinyl alcohol) (PVA) fiber support incorporating various aminoacetal functional groups has been developed for immobilizing enzymes. The aminated PVA fiber seems to adsorb enzymes with electrostatic force of attraction; thus the immobilization procedure is simple. By the use of this fiber having immobilized enzymes, the reaction between enzymes and substrates is nearly independent of the size of subtstrates. This newly developed type of fiber, which is formed by a mass superfine fibers (SFF), each measuring 1 μm or less in diameter, permits much more increased surface area than the conventional enzyme immobilization supports. Our studies of the properties of the fiber for immobilization of enzymes show the following results: (1) SFF has a greater ability for the immobilization of invertase than ordinary fibers; (2) dimethyl-aminated SFF has the best performance for the immobilization of invertase. From these results, it is concluded that the dimethyl-aminated SFF is an excellent support for the immobilization of invertase.     

Decomposition of chlorofluorocarbons on TiO2ZrO2

The decomposition of chlorofluorocarbons (CFCs) in the presence of water was examined over a variety of solid acid catalysts. The TiO₂ZrO₂ catalyst was found to have the highest activity and longest life among the catalysts examined. The activity of the TiO₂ZrO₂ catalysts depended upon the content of TiO₂. At the contents of TiO₂ from 58 to 90 mole%, the TiO₂ZrO₂ catalysts exhibited high activity, and these catalysts were proven to contain TiZrO₄ crystal. From the study of the XRD peak intensity of the TiZrO₄ crystal, it was highest on the TZ-58 which contained 58 mole% of TiO₂, and decreased with increasing the content of TiO₂. Furthermore, the conversion of CFC113 measured at 673 K was highest at TZ-58, and decreased gradually with increasing TiO₂ content. Therefore, the TiZrO₄ crystal influences the activity of decomposition of CFC113. However, the TiO₂ZrO₂ catalyst was gradually deactivated during the reaction due to the elimination of titanium atoms. A good relationship was found between the activity on TiO₂ZrO₂ catalyst and bond energy of CCl in the compounds of chlorofluorocarbons and hydrochlorocarbons, suggesting that the rate controlling step was the cleavage of CCl bond.     

Synthesis of Cubic Boron Nitride from Boron Nitride Synthesized by Pressure Pyrolysis of Borazine

Cubic BN was synthesized under high-temperature and -pressure conditions from BN powder formed by pressure pyrolysis of borazine below 700°C and 100 MPa. The conversion of BN powder to cubic BN was strongly influenced by the residual hydrogen identified by the BH/BN ratio of IR absorption band. The activation energy for cubic BN synthesis from BN powder-20 mol% AIN was 46 kJ/mol, when the starting BN was synthesized at 250°C. A mixture of BN powder and cubic BN particles was converted to cubic BN in a 100% yield by heat treatment at 1800°C and 6.5 GPa without any catalyst. The presence of cubic BN particles does enhance the conversion to cubic BN from BN powder. The energy required for the transformation of starting BN to cubic BN in the presence of cubic BN seed was 355 kJ/mol.     

Charged ultrafiltration membrane for permeation of proteins

Polyacrylonitrile-g-poly(N,N-dimethylaminoethyl methacrylate) was synthesized photochemically and quaternized. The positively charged membranes made from the quaternized graftcopolymer showed high ultrafiltration rate for water by adding poly(vinyl alcohol) to casting solution and washing it out after the casting. In buffered saline solution, the permeability of the membranes was very small at pH below isoelectric point of albumin but increased markedly at higher pH. On the other hand, the permeability for γ-globulin was very small and did not show any pH dependence.     

Organic–silicate hybrid catalysts based on various defined structures for Knoevenagel condensation

Two types of organic–inorganic hybrid base catalysts are prepared. Organic-functionalized molecular sieves (OFMSs), particularly “amine-immobilized porous silicates”, are designed based on common idea to immobilize catalytic active sites on silicate surface. Silicate–organic composite materials (SOCMs), such as “ordered porous silicate–quaternary ammonium composite materials”, are the precursors of ordered porous silicates obtained during the synthesis. Both the OFMS and the SOCM are used as the catalysts for Knoevenagel condensation. Among the OFMSs, there is clear tendency that the use of molecular sieve with larger pore volume and/or surface area gives the product in higher yield. Aminopropylsilyl (AP)-functionalized mesoporous silicates such as AP-MCM-41 gives the product in high yield under mild conditions. No loss of activity is observed after repeated use for three times. The SOCMs are also active for the same reaction. The precursors of the mesoporous silicates are more active than those of microporous silicates. This material can be repeatedly used without significant loss of activity. High activity is not due to the leached species. The active sites of the SOCM catalysts are considered to be SiO⁻ moieties located on the pore-mouth. Activity of the SOCM increases when the reaction is carried out without solvent, whereas decrease in activity of the OFMS is observed in the solvent-free system.     

Synthesis and Magneto-mechanical Properties of Ce-TZP/La M-Type Hexaferrite Composite

An in situ composite composed of ceria-stabilized tetragonal zirconia polycrystals (Ce-TZP) and La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ was synthesized from a powder mixture of Ce-TZP, La(Fe_0.9Al_0.1)O₃, Fe₂O₃, Al₂O₃, and CoO. The dense Ce-TZP dispersed with platelike La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ crystals as a second phase were formed after sintering from 1250° to 1350°C. The saturation magnetization of the in situ composite Ce-TZP/La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ was proportional to the mass fraction of the hexaferrite second phase in Ce-TZP. The coercivity of the composite with a 20 mass% of second phase decreased from 9.14 to 2.52 kOe (from 728 to 201 kA/m) after the pulverization of the composite. The susceptibility (χ) increased by 15%–25% under uniaxial stress on the composite. The change of the susceptibility (Δχ/χ) value increased with decreasing the mass fraction of the second phase in the composite. The Δχ was found to increase linearly with applied stress and abruptly change on cracking, which is expected for the application in fracture sensing of the composite.     

Electrochemical formation of Sm-Co alloys by codeposition of Sm and Co in a molten LiCl-KCl-SmCl3-CoCl2 system

Electrocodeposition of Sm and Co on a Cu substrate was investigated in a molten LiCl-KCl-SmCl₃ (0.5 mol.%)-CoCl₂ (0.1 mol.%) system at 723 K. Phase of the deposited Sm-Co alloys could be controlled by electrolysis potential. SmCo₃ was formed on a Cu substrate by potentiostatic electrolysis in the potential range of 0.20-0.90 V (vs. Li⁺/Li). Sm₂Co₁₇ was obtained in the potential range of 0.90-1.50 V.     

Surface Orientation and Wetting Phenomena in Si/α-Alumina System at 1723 K

Wetting phenomena and the effect of alumina surface orientation on the wettability in Si/α-Al₂O₃ system were studied by an improved sessile drop method using     ,     , C(0001) faces of single crystals and polycrystals at 1723 K in a reducing Ar–3% H₂ atmosphere. The contact angles show a vibration behavior for all the single crystals but to a less extent for the polycrystals. The extent of the vibration correlates not only with the reaction intensity but also with the stability of the Si droplet on the alumina surfaces. The interfacial reaction leads to the formation of a series of reaction rings, which is more serious at the single crystal surfaces. More importantly, the wettability is dependent on the alumina surface orientation, with the intrinsic contact angles being about 98±2°, 101±1°, 69±1°, and 98±2°, respectively, for the     ,     , C(0001) and polycrystal α-Al₂O₃ substrates. The much smaller contact angle for molten Si on the C(0001) surface is explained by the favorable reduction in the Si/α-Al₂O₃ interfacial free energy by the terminated and enriched aluminum atoms at the reconstructed     surface. The importance of the aluminum presence at the Si/α-Al₂O₃ interface to the wettability of this system was further demonstrated by a substantial improvement in the wettability of the     α-Al₂O₃ substrates by Si–Al alloys.