模铸用高铝质流钢砖的显微结构分析

选取市场上模铸用高铝质流钢砖与用后残砖作为研究对象,通过检测不同高铝质流钢砖的理化性能,对比其使用前后的显微结构变化,进一步探讨模铸过程中高铝质流钢砖的显微结构对钢铁产品质量的影响。结果表明:由于显气孔率较大、结构比较疏松、烧结不致密等特性,高铝质流钢砖在经受钢水冲刷时,钢水容易渗透至高铝质流钢砖内部,加速其损毁;其次,高铝质流钢砖与钢水发生物理化学反应后在其表面生成低熔点物,使钢水中产生夹杂物,影响钢铁产品的质量。     

Tailoring the electron-blocking layer by addition of YSZ to Ba-containing anode for improvement of ceria-based solid oxide fuel cell

The in-situ fabrication of an electron-blocking layer between the Ba-containing anode and the ceria-based electrolyte is an effective approach in suppressing the internal electronic leakage in ceria-based solid oxide fuel cell (SOFC). To improve the thickness of the electron-blocking layer and to research the effect of the layer thickness on the improvement of SOFC, a Ba-containing compound (0.6NiO-0.4BaZr_0.1Ce_0.7Y_0.2O_3-δ) modified by Y stabilized zirconia (YSZ) was employed as a composite anode in this research. SEM analyses demonstrated that the thickness of the interlayer can be simply controlled by regulating the proportion of YSZ at anode. The in-situ formed interlayer in the cell with the anode modified by 20?mol% YSZ possesses a thickness of 0.9?µm which is more suitable for the cell achieving an enhanced performance.     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Cross-Layer Optimization of Dynamic Packet Assignment for Video Transmission Over IEEE 802.11e Networks

Video transmission over IEEE 802.11e wireless networks still shows poor performance for large bandwidth demand and frequently changed environments. Thus, several enhancements of IEEE 802.11e were proposed. On the other hand, big frames and simultaneous sending of adjacent frames always cause packet dropping for buffer overflow. In the past, we proposed an IEEE 802.11e enhancement named DFAA and a content aware mechanism to solve the above problems. The motivation of this paper is to find a proper way to integrate these two mechanisms. A DFAA enhancement (DFAA-E) is proposed to make up the insufficiency of content aware mechanism. Experiments results show that the combination of DFAA-E and content aware mechanism improves the video decoded quality greatly. And its performance can be further enhanced by selecting the suitable settings of certain parameters.     

Influences of gap pressure on machining performance in radial ultrasonic rolling electrochemical micromachining

Microdimples as a typical surface texture has been widely used for improving the properties in tribology and heat transfer fields. Ultrasonically assisted     

The origin of the modulated structure in Sr2CuO3+δ (δ = 0.4): [CuO2] in-plane oxygen vacancy or apical oxygen vacancy?

We propose the question of the modulated structures of copper oxide is caused by the [CuO₂] in-plane oxygen vacancy or apical oxygen vacancy. Sr₂CuO_3+δ single-crystal samples were prepared using high-temperature and high-pressure methods. The major phase of Sr₂CuO_3+δ (δ = 0.4) single-crystal system is found to be constituted by the 5 a modulated structure with the Fmmm space group, which originates from the [CuO₂] in-plane oxygen vacancy appearing in octahedral Cu-O. Besides, the presence of the [CuO₂] in-plane oxygen vacancy may obliterate the superconductivity of the system. Experimental results deduce that the oxygen vacancy may appear in the apical oxygen sites in high-temperature copper oxide superconductors.