热处理对多孔铝合金压缩吸能性能的影响

采用渗流铸造工艺 ,制备了Al Si系多孔铝合金 ,讨论了其压缩变形特征及能量吸收性能 ,分别对ZL10 1、ZL111两种多孔铝合金进行T6热处理 ,研究了热处理对这两种多孔铝合金压缩吸能性能的影响。研究结果表明 ,热处理能够提高多孔铝合金的能量吸收能力 ,对屈服强度及能量吸收效率也有显著的影响 ,为提高多孔铝合金的压缩性能 ,应尽可能施行热处理     

铝合金铸轧组织的物理模拟

设计了铝合金铸轧工艺模拟的实验装置，研究了在该试验条件下，铝合金变形组织与工艺参数的关系。结果表明：按照本试验的设计，在夹头通水冷却的Gleeble-1500热模拟机上能够得到铝的“人”字形特征的柱状晶组织，实现铸轧组织的物理模拟过程。铝合金模拟铸轧的显微组织对外力施加的应变速率很敏感：Ё=0．125s^-1时，变形开始与凝固过程发生耦合，铸轧组织发生转变；应变速率增大至Ё=0．300s^-1时，铸轧柱状晶发生等轴化。铸轧组织的形成主要是变形作用于未凝固的液相，引起质量和热量的分布状态发生改变所致。提高铸轧速度，有利于铸轧组织的形成和铸轧柱状晶的等轴化，并且使所需的轧制力减小，有利于铸轧工艺的优化。     

Indium tin oxide nanosized composite powder prepared using waste ITO target

Indium tin oxide （ITO） nano-particles were prepared directly using waste ITO target, which had been coated by magnetron controlled sputtering. The waste ITO target was cleaned with de-ionized water, and then dissolved in acid, filtrated, neutralized, manipulated through azeotropic distillation and finally dried, and in this way the precursor of indium tin hydroxide was obtained. The nanosized rio composite powder was prepared after the precursor heat-treated at 500℃ for 2 h. TEM images show a narrow distribution of particle size is 5-20 nm and the particle size can be controlled. Its granule has a spherical shape and the dispersion of the particle is well. X-ray diffraction （XRD） patterns indicate the only cubic In2O3 phase in the ITO powder hot-treated at 500℃. The purity of ITO composite powder is 99.9907%. The content of radium within filtrate was detected by using the EDTA titration of determination of indium in the ITO powder and ITO target. Appropriate amount of SnCl4.5H2O was dissolved in the filtrate, and then ITO powder containing 10 wt.% SnO2 was successfully prepared by heat-treating.     

ON THE COMPOSITION UNIFORMITY AND SHAPE COEFFICIENT OF MOLTEN POOL BY LASER ALLOYING

The effect of the laser processing parameters on the composition uniformity and shapecoefficient of fusion zone with laser surface alloyed Cr plated on medium carbon low alloysteel has been studied.It was found that the composition uniformity depends on the shapecoefficient of fusion zone,and the later is a function of both power density and interactiontime.If the power density is fixed to a certain value,the shape coefficient is directly,propor-tional to the interaction time.A completely,uniform molten pool can be obtained,when theshape coefficient is between 1.6 and 3.0.     

AN EXPERIMENTAL-NUMERICAL METHOD FOR MEASURING CRACK PROPAGATING VELOCITIES UNDER STRESS WAVE LOADING

An experimental-numerical method for measuring dynamic crack propagating velocities under stress wave loading is established in this paper. The experiments of the three-point bend specimen are done on the improved Hopkinson bar. Deflection of loading point, dynamic load and instantaneous crack length are measured, then crack propagating velocities are calculated. Experiments on 40Cr steel show that the results given by this method have a good agreement with that obtained by the resistance fracture gage method. Therefore this method is feasible for measuring crack propagating velocities under high loading rate and will have wide application.     

船舶腐蚀与防腐涂装的特点

本文论述了船舶腐蚀与防腐涂装的特点，工艺及配套。     

近终型金属铸造模具制造工艺设计分析与应用

近终型制模技术，可以缩短制模周期、降低生产成本。本文介绍近终型技术在制模工艺实际中的应用概况。并举出实例，指出近终型制模技术可以提高生产效率，快捷地制造出各种复杂的零件/金属模具，该技术有着广阔的应用前景。     

钢丝绳张紧装置在大行程拖链上的应用

介绍了给DY3000×20m数控机床大行程拖链增设的张紧装置,该装置解决了拖链无法自动复位的问题,使用方便、经济可行。     

基于Web的模具制造工艺的协同规划

针对模具制造特点，从面向生产管理的角度，提出了基于Web的模具制造工艺协同规划方法，探讨了实现这一方法的相关技术，并用Java语言开发了基于Web的模具CAPP原型系统。     

冶金企业面临的严峻局面及今后工作重点

阐述了冶金企业在当前的严峻形势下，要求得生存必须转变传统观念。并提出“九五”期间的工作重点是：节能降耗、调整品种结构、提高生产率及加强决策管理。重点论述了实现节能降耗应抓好的四项工作：连铸坯一火成材与热装直轧，轧钢炉窑节能技术，轧机主传动交流调速技术及控制冷却技术。