水热法一步合成磷酸铁锂及其性能研究

为优化液相法一步制备磷酸铁锂（LiFePO₄）技术,以七水合硫酸亚铁、磷酸二氢铵、一水合氢氧化锂为原料,通过添加十二烷基苯磺酸钠（SDBS）作为表面活性剂,采用液相水热法合成技术,一步合成了LiFePO₄正极材料。研究了水热法一步合成技术对LiFePO₄材料的组成、结构、形貌、粒度等的影响,通过电感耦合等离子体发射光谱仪（ICP-OES）、X射线衍射仪（XRD）、扫描电镜（SEM）、粒度分析仪等对材料进行了表征分析,并测试了材料的电化学性能。研究结果表明,合成得到的LiFePO₄材料为微米级球形颗粒形貌的正交晶系非化学计量比的Li_1.02Fe_0.994PO₄材料。电化学性能测试结果表明,在0.1C倍率下首次充、放电比容量分别为162.0、159.9 mA·h/g,库伦效率达到98.7%、倍率性能（以1C/0.1C保持率计）为92.3%,0.1C倍率循环100次容量保持率为96.4%,展现出良好的电化学性能。     

A Student's t-based density peaks clustering with superpixel segmentation (tDPCSS) method for image color clustering

Image color clustering is a basic technique in image processing and computer vision, which is often applied in image segmentation, color transfer, contrast enhancement, object detection, skin color capture, and so forth. Various clustering algorithms have been employed for image color clustering in recent years. However, most of the algorithms require a large amount of memory or a predetermined number of clusters. In addition, some of the existing algorithms are sensitive to the parameter configurations. In order to tackle the above problems, we propose an image color clustering method named Student's t-based density peaks clustering with superpixel segmentation (tDPCSS), which can automatically obtain clustering results, without requiring a large amount of memory, and is not dependent on the parameters of the algorithm or the number of clusters. In tDPCSS, superpixels are obtained based on automatic and constrained simple non-iterative clustering, to automatically decrease the image data volume. A Student's t kernel function and a cluster center selection method are adopted to eliminate the dependence of the density peak clustering on parameters and the number of clusters, respectively. The experiments undertaken in this study confirmed that the proposed approach outperforms k-means, fuzzy c-means, mean-shift clustering, and density peak clustering with superpixel segmentation in the accuracy of the cluster centers and the validity of the clustering results.     

陕南山地烟田不同植烟年限土壤养分的变化

为给陕南山地烟草生产布局及有针对性的施肥措施提供依据,分析了陕南山地烟田不同植烟年限(0~15年)与土壤养分含量的关系。结果表明:随着植烟年限延长,有机质线性下降,全氮和速效钾显著上升,有效磷先上升后下降;氯、有效铁、有效锰、有效硼和有效铜无显著变化或变化很小,有效锌则在第1年急剧下降,之后保持稳定,10年后再次显著下降。认为陕南山地烟区烟叶生产中应适当增加有机肥的施用而合理控制氮肥、磷肥和钾肥的施用,并要注意锌肥的补充。     

The formation of fibrous structure of polyamide 6 induced by the three-step forming process and its prominent reinforcement in nitrile rubber

Nitrile rubber (NBR) blends with excellent performance have always been a hot research topic in petroleum field. Due to the excellent performance and compatibility of polyamide 6 (PA6), it provides an opportunity for the preparation of high-performance NBR/PA6 blends. In this article, NBR/PA6 blends were prepared by the three-step molding process. Experimentally, it was found that PA6 has a prominent reinforcement effect in NBR matrix. The variation of this mechanical property was investigated from different aspects of the crystal structure, crystallinities, phase morphology, and so on. It can be cleared that the formation of fibrous structure of PA6 phase is the main factor for reinforcement of the polymer blends. Meanwhile, the formation mechanism of the special phase structure induced by the three-step process is deeply expounded and its structural evolution schematic is established. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47472.     

澳门融入粤港澳大湾区世界机场群路向研究

粤港澳大湾区世界城市群与世界机场群相伴而生、联动发展.建设世界级机场群，需要5大机场错位发展和良性互动.澳门国际机场是澳门融入粤港澳大湾区重要一极，但机场发展存在与澳门定位、香港珠海空域空运矛盾、澳门土地和环境现状等相关的问题.因此，澳门国际机场今后发展需在葡语国家航线、珠澳密切合作、公务机产业方面努力实现跨越式发展.然而，澳门国际机场改扩建问题争议不断，本文就原址扩建、填海区新建、飞地黄茅岛新建3种模式进行比较分析，探索符合澳门长远利益之方案.     

In situ characterization of LiY(WO4)2 nanotubes for electrochemical energy storage

Here, LiY(WO₄)₂ nanotubes are prepared via a feasible electrospinning technique. This new anode material shows excellent electrochemical properties. The capacity loss of LiY(WO₄)₂ nanotubes is as low as 6.9% after 156 cycles, while bulk LiY(WO₄)₂ presents the capacity loss higher than 55.0%. Even after 600 long-life cycles, the capacity loss of the nanotubes is only 9%. It can be seen that the hollow structure with a rough surface and a porous morphology contributes to the improvement of electrochemical performance. Furthermore, online X-ray diffraction (XRD) method is firstly applied to understand the lithium ions insertion/extraction mechanism of LiY(WO₄)₂ nanotubes. It can be concluded that it is an asymmetrical two-phase reaction. A phase transformation from LiY(WO₄)₂ to Li₃Y(WO₄)₂ can be obviously seen from the in situ XRD during discharge process. While Li₂Y(WO₄)₂ appears as an intermediate phase with a reverse charge reaction. In addition, in situ XRD also demonstrates that LiY(WO₄)₂ nanotubes have surprised electrochemical reversibility. All the above results indicate that LiY(WO₄)₂ nanotubes can be expected to be anode candidate for rechargeable lithium ion batteries (LIBs).