和成矿业洗矿系统改造实践

针对和成矿业井下原矿含泥量和含水量较大，且矿泥中存在绿泥石、高岭土等黏土类矿物，造成供矿系统粘堵严重，系统台时量仅为设计水平一半的问题，对原矿进行了洗矿工艺研究。通过洗矿工艺，将原矿中的矿块和矿泥分离，实现矿块和矿泥按粒度分选，彻底解决了供矿系统粘堵严重的问题，稳定了磨选系统给矿量。     

Experimental investigation of different morphology textured ceramic tools by in-situ formed for the dry cutting

Surface texture is considered an important measure to improve the cutting performance of a tool. In this study, we have prepared three types of textured and conventional tools on the rake face by an in-situ formed method. During the experiment, the best parameters of three types of textured tools were selected for dry cutting AISI 1045 steel at different cutting speeds. Cutting forces, cutting temperatures, workpiece surface roughness, and tool wear were measured during the cutting process. The results showed that textured tools have significantly reduced cutting force, cutting temperature, and tool wear, and the roughness of the workpiece was improved compared with the conventional tool. The micro-pit texture tool has less stress contact region than the micro-groove width texture tool, but the micro-groove width texture tool exhibiting the best cutting performance. This investigation clearly showed that the textured tool prepared by the in-situ formed method has improved cutting performance.     

黔北桑木场背斜铅锌矿深部找矿实例分析*#br#

黔北桑木场背斜位于上扬子地块黔北隆起区毕节弧形褶皱带与赤水克拉通盆地的交汇部位，属于有利的铅锌成矿区带。区内铅锌矿的赋矿层位主要有震旦系灯影组、寒武系清虚洞组、高台组及石冷水组，矿体多产于背斜核部并受断层或裂隙控制。通过对地层岩性特征、地表矿化特征、控容矿构造特征、化探异常特征、物探异常特征等进行综合研究，选择在成矿有利地段进行了工程验证，为进一步开展桑木场背斜铅锌矿深部找矿工作提供了思路。     

华为事件对践行习近平“坚定不移把自己的事情办好”深邃思想的启示

在中美全面较量中,科技领域是双方博弈的一个重要焦点。面对美国极限施压,华为发起的成功反击提供了一个可借鉴的蓝本。在以任正非为代表的华为人身上,可以感受到中国企业的强大实力、中国人民的强大自信、中华民族的强大定力。通过解析华为事件、借鉴华为经验、放大华为效应,能够为践行习近平总书记“坚定不移把自己的事情办好”深邃思想提供思考和启鉴。     

基于材料力学性能的最低设计金属温度曲线分析

铁素体钢在低温条件下存在明显的韧脆转变现象。为防止脆断事故的发生,需要确定铁素体钢制压力容器的最低使用温度。针对ASME中的A^D四条冲击豁免曲线,对应地选取了4种材料,基于材料实际的屈服强度和参考温度,按照ASME中豁免曲线的计算方法,计算得到4种材料的最低设计金属温度曲线,并与对应的A^D曲线对比,定量地分析ASME中豁免曲线的保守性。结果表明,ASME中的豁免曲线相对于材料自身的最低设计金属温度曲线保守性较大;韧性相近的材料被划分到不同的豁免曲线,使得韧性富裕量差异较大,对于某些材料,其断裂韧性被低估。     

干熄焦锅炉炉管失效机理分析

通过对干熄焦锅炉炉管及腐蚀产物开展系统研究，提出炉管失效原因为氧化/硫腐蚀＋高温粉尘冲刷。长寿命炉管仅耐磨层发生了较为严重的氧化及硫腐蚀，而近基体层发生了轻微氧化及硫腐蚀，基体只发生了轻微氧化；短寿命炉管耐磨层、近基体层以及基体裂纹内均发生了较为严重的氧化及硫腐蚀，且存在珠光体球化、内表面产生全脱碳层等缺陷。推测短寿命炉管存在超温现象，而超温可加剧氧化及硫腐蚀反应。此外，短寿命炉管遭受了较为严重的高温粉尘冲刷，不仅可造成炉管减薄，还会导致炉管表面温度升高。因此，减少循环气体中粉尘量尤其是大颗粒，可有效减弱冲刷以及控制炉管表面温度，是提高炉管使用寿命的关键。     

Preparation and flocculation properties of biodegradable konjac glucomannan-grafted poly(trimethyl allyl ammonium chloride)

Polymer Bulletin - Preparation of konjac glucomannan-grafted poly(trimethyl allyl ammonium chloride) (KGM-g-PTMAAC) was carried out using KGM as polysaccharide matrix and TMAAC as cationic...     

Hydrogen Production from Catalytic Steam Reforming of Bio-Oils: A Critical Review

In the future, hydrogen will be an important energy carrier and industrial raw material. Catalytic steam reforming of bio-oils is a promising and economically viable technology for hydrogen production. However, during the reforming process, the catalysts are rapidly deactivated due to coke formation and sintering. Thus, maintaining the activity and stability of catalysts is the key issue in this process. Optimized operation conditions could extend the catalyst lifetime by affecting the coke morphology or promoting coke gasification. This article summarizes the recent developments in the field of catalytic steam reforming of bio-oils, focusing on the operation conditions, the properties of the catalysts, and the effects of the catalyst supports. The expected insights into the catalytic steam reforming of bio-oils will provide further guidance for hydrogen production from bio-oils.