Low temperature solid-state synthesis routine and mechanism for Li3V2(PO4)3 using LiF as lithium precursor

Monoclinic lithium vanadium phosphate, Li₃V₂(PO₄)₃, has been successfully synthesized using LiF as lithium source. The one-step reaction with stoichiometric composition and relative lower sintering temperature (700 °C) has been used in our experimental processes. The solid-state reaction mechanism using LiF as lithium precursor has been studied by X-ray diffraction and Fourier transform infrared spectra. The Rietveld refinement results show that in our product sintered at 700 °C no impurity phases of VPO₄, Li₅V(PO₄)₂F₂, or LiVPO₄F can be detected. The solid-state reaction using Li₂CO₃ as Li-precursor has also been carried out for comparison. X-ray diffraction patterns indicate that impurities as Li₃PO₄ can be found in the product using Li₂CO₃ as Li-precursor unless the sintering temperatures are higher than 850 °C. An abrupt particle growth (about 2 μm) has also been observed by scanning electron microscope for the samples sintered at higher temperatures, which can result in a poor cycle performance. The product obtained using LiF as Li-precursor with the uniform flake-like particles and smaller particle size (about 300 nm) exhibits the better performance. At the 50th cycle, the reversible specific capacities for Li₃V₂(PO₄)₃ measured between 3 and 4.8 V at 1C rate are found to approach 147.1 mAh/g (93.8% of initial capacity). The specific capacity of 123.6 mAh/g can even be hold between 3 and 4.8 V at 5C rate.     

Preparation of narrowly distributed nanoparticles of poly(n‐butyl methacrylate‐co‐vinyl pyrrolidone) through microemulsion polymerization

Narrowly distributed nanoparticles of poly (n‐butyl methacrylate‐co‐vinyl pyrrolidone) were prepared through microemulsion polymerization with a nonionic surfactant of Tween‐80 as emulsifier (6 wt % of the latex) and n‐butanol as coemulsifier. The polymerizations were initiated with benzoylperoxide (BPO), potassium persulfate (KPS), KPS/ferric sulfate (FeSO₄), and BPO/FeSO₄, respectively, where the initiation in the case of BPO/FeSO₄ took place mainly at the interphase between the oil phase and the reaction media. Namely, this interfacial‐initiated microemulsion polymerization resulted in larger particles with relatively narrower particle size distribution as well as higher limiting monomer conversion but lower polymerization rate compared with the polymerization initiated with KPS/FeSO₄. In this article, the influences of initiation method, monomer ratio, and addition of water‐soluble components on microemulsion polymerization and latex particle size were studied to discuss the mechanism of interfacial‐initiated microemulsion polymerization. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2334–2340, 2004     

注塑产品色差控制技术研究

色差是注塑中最常见缺陷，因其牵涉因素众多，十分难以掌握。本文从实用角度出发，讨论了影响色差主要因素和控制色差的实用技术．为减少色差问题的产生提供了一些好的经验和方法。     

Influence of polymerization conditions on the structure and properties of polyethylene/polypropylene in‐reactor alloy synthesized in the gas phase with a spherical Ziegler–Natta catalyst

A spherical TiCl₄/MgCl₂‐based catalyst was used in the synthesis of in‐reactor polyethylene/polypropylene alloys by polyethylene homopolymerization and subsequent homopolymerization of propylene in the gas phase. Different conditions in the ethylene homopolymerization stage, such as monomer pressure and polymerization temperature, were investigated, and their influences on the structure and properties of in‐reactor alloys were studied. Raising the polymerization temperature is the most effective way of speeding up polymerization and regulating the ethylene content of polyethylene (PE)/polypropylene (PP) alloys, but it will cause a greater increase in the PE‐b‐PP block copolymer fraction (named fraction D) than in the fraction of PP‐block‐PE in which the PP segments have low or medium isotacticity (named fraction A). Although changing ethylene monomer pressure could influence the ethylene content of PE/PP alloys slightly, it is an effective way of regulating the structural distribution. Reducing the monomer pressure will evidently increase fractions A and D. The mechanical properties of the alloys, including impact strength and flexural modulus, can be regulated in a broad range with changes in polymerization conditions. These properties are highly dependent on the amount, distribution, and chain structure of fractions A and D. The impact strength is affected by both fraction A and fraction D in a complicated way, whereas the flexural modulus is mainly determined by the amount of fraction A. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 2136–2143, 2006     

Synthesis and properties of polystyrene‐b‐poly(ethylene oxide)‐b‐polystyrene triblock copolymers

A series of well‐defined and property‐controlled polystyrene (PS)‐b‐poly(ethylene oxide) (PEO)‐b‐polystyrene (PS) triblock copolymers were synthesized by atom‐transfer radical polymerization, using 2‐bromo‐propionate‐end‐group PEO 2000 as macroinitiatators. The structure of triblock copolymers was confirmed by ¹H‐NMR and GPC. The relationship between some properties and molecular weight of copolymers was studied. It was found that glass‐transition temperature (T_g) of copolymers gradually rose and crystallinity of copolymers regularly dropped when molecular weight of copolymers increased. The copolymers showed to be amphiphilic. Stable emulsions could form in water layer of copolymer–toluene–water system and the emulsifying abilities of copolymers slightly decreased when molecular weight of copolymers increased. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 727–730, 2006     

PSA performances and viscoelastic properties of SIS‐based PSA blends with H‐DCPD tackifiers

Hotmelt pressure sensitive adhesives (PSAs) usually contain styrenic block copolymers like styrene–isoprene–styrene (SIS), SBS, SEBS, tackifier, oil, and additives. These block copolymers individually reveal no tack. Therefore, a tackifier is a low molecular weight material with high glass transition temperature (T_g), and imparts the tacky property to PSA. The SIS block copolymer with different diblocks was blended with hydrogenated dicyclopentadiene (H‐DCPD tackifier), which has three kinds of T_g. PSA performance was evaluated by probe tack, peel strength, and shear adhesion failure temperature. PSA is a viscoelastic material, so that its performance is significantly related to the viscoelastic properties of PSAs. We tested the viscoelastic properties by dynamic mechanical analysis and the thermal properties by differential scanning calorimeter to investigate the relation between viscoelastic properties and PSA performance. © 2006 Wiley Periodicals, Inc. J Appl PolymSci 102: 2839–2846, 2006     

Synthesis of polystyrene/poly(butyl acrylate) core–shell latex and its surface morphology

A polystyrene (PS)/poly(butyl acrylate) (PBA) composite emulsion was produced by seeded emulsion polymerization of butyl acrylate (BA) with PS seed particles which were prepared by emulsifier‐free polymerization of styrene with potassium persulfate (KPS) under a nitrogen atmosphere at 70°C for 24 h with stirring at 60 rpm and swelled with the BA monomer in an ethanol/water medium. The structure of the PS/PBA composite particles was confirmed by the presence of the characteristic absorption band attributed to PS and PBA from FTIR spectra. The particles for pure PS and PS/PBA with a low content of the BA monomer were almost spherical and regular. As the BA monomer content was increased, the particle size of the PS/PBA composite particles became larger, and more golf ball‐like particles were produced. The surface morphology of the PS/PBA composite particles was investigated by AFM and SEM. The T_g's attributed to PS and PBA in the PS/PBA composite particles were found at 110 and ?49°C, respectively. The thermal degradation of the pure PS and PS/PBA composite particles occurred in one and two steps, respectively. With an increasing amount of PBA, the initial thermal decomposition temperature increased. On the contrary the residual weight at 450°C decreased with an increasing amount of PBA. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 595–601, 2003     

Synthesis and thermotropic liquid‐crystalline behavior of novel main‐chain poly(aryl ether ketones)

Novel aromatic poly(ether ketones) containing bulky lateral groups were synthesized via nucleophilic substitution reactions of 4,4′‐biphenol and (4‐chloro‐3‐trifluoromethyl)phenylhydroquinone (CF‐PH) with 1,4‐bis(p‐fluorobenzoyl)benzene. The copolymers were characterized by differential scanning calorimetry (DSC), wide‐angle X‐ray diffraction, and polarized light microscopy observation. Thermotropic liquid‐crystalline behavior was observed in the copolymers containing 40, 50, 60, and 70 mol % CF‐PH. The crystalline–liquid‐crystalline transition [melting temperature (T_m)] and the liquid‐crystalline–isotropic phase transition appeared in the DSC thermograms, whereas the biphenol‐based homopolymer had only a melting transition. The novel poly(aryl ether ketones) had glass‐transition temperatures that ranged from 143 to 151°C and lower T_m's that ranged from 279 to 291°C, due to the copolymerization. The polymers showed high thermal stability, and some exhibited a large range in mesophase stability. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 1347–1350, 2003     

Preparation and swelling behavior of biodegradable hydrogels based on α,β‐poly(N‐2‐hydroxyethyl‐DL‐aspartamide)

Biodegradable polymers and the hydrogels have been increasingly applied in a variety of biomedical fields and pharmaceutics. α,β‐Poly(N‐2‐hydroxyethyl‐DL ‐aspartamide), PHEA, one of poly(amino acid)s with hydroxyethyl pendants, are known to be biodegradable and biocompatible, and has been studied as an useful biomaterial, especially for drug delivery, via appropriate structural modification. In this work, hydrogels based on PHEA were prepared by two‐step reaction, that is, the crosslinking of polysuccinimide, the precursor polymer, with oligomeric PEG or PEI‐diamines and the following nucleophilic ring‐opening reaction by ethanolamine. Soft hydrogels possessing varying degrees of gel strength could be prepared easily, depending on the amount of different crosslinking reagents. The swelling degrees, which were in the range of 10–40 g–water/dry gel, increased somewhat at higher temperature, and also at alkaline pH of aqueous solution. A typical hydrogel remained almost unchanged for 1 week, at 37°C in phosphate buffer of pH 7.4, and then seemed to degrade slowly as time. A porous scaffold could be fabricated by the freeze drying of water‐swollen gel. The PHEA‐based hydrogels have potential for useful biomaterial applications including current drug delivery system. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3741–3746, 2003     

全钢载重子午线轮胎钢丝圈受力分析

以10．00R20全钢载重子午线轮胎为例进行钢丝圈钢丝受力分析。利用有限元模型计算得到各种充气压力下钢丝圈钢丝的应力分布特征，并进一步得到钢丝圈钢丝的最大应力和平均应力，它们基本上与充气压力成正比；以最大应力和平均应力分别计算得到的钢丝圈安全系数相差2．3倍。有限元计算结果还表明，超载情况下钢丝圈的安全性能明显下降。