Fabrication of a new substrate for atomic force microscopic observation of DNA molecules from an ultrasmooth sapphire plate

A new stable substrate applicable to the observation of DNA molecules by atomic force microscopy (AFM) was fabricated from a ultrasmooth sapphire (alpha-Al2O3 single crystal) plate. The atomically ultrasmooth sapphire as obtained by high-temperature annealing has hydrophobic surfaces and could not be used for the AFM observation of DNA. However, sapphire treated with Na3PO4 aqueous solution exhibited a hydrophilic character while maintaining a smooth surface structure. The surface of the wet-treated sapphire was found by x-ray photoelectron spectroscopy and AFM to be approximately 0.3 nm. The hydrophilic surface character of the ultrasmooth sapphire plate made it easy for DNA molecules to adhere to the plate. Circular molecules of the plasmid DNA could be imaged by AFM on the hydrophilic ultrasmooth sapphire plate.     

Wheel/rail contact dynamics in turnout negotiations with combined nodal and non-conformal contact approach

In railroad turnouts, geometries of tongue and crossing rails are very complex and their shapes are changing along the track. Therefore, wheels are subjected to not only tread and flange contacts, but also the back-of-flange and top-of-flange contacts in the case of spring switches of tram vehicles. For this reason, one needs to deal with significant jumps in contact points for solving wheel/rail contact problems in turnout, and an accurate prediction of jumps in contact points is one of the most important issues that need to be carefully handled in the dynamic simulation of vehicle/turnout interactions. In this investigation, a numerical procedure that can be used for solving such a complex wheel/rail contact problem in turnout is proposed. In particular, a combined nodal and non-conformal contact approach is developed such that significant jumps in contact points are detected using the nodal search, while the exact location of contact point is then determined with continuous surface parameterizations using non-conformal contact equations. With this combined nodal and non-conformal contact approach for the contact geometry analysis of vehicle/turnout interactions, multiple look-up contact tables can be generated in an efficient way without losing accuracy. Since detailed contact search is performed off-line to obtain look-up contact tables, significant changes in contact points in turnout can be efficiently predicted on-line with tabular data to be interpolated in a standard way. Several numerical examples are presented in order to demonstrate the use of the numerical procedure developed in this investigation.     

Robust digital control of a DC–DC buck converter with low frequency samplings

A robust DC?CDC converter which can covers extensive load change and also input voltage changes with one controller is needed. Then the demand to suppress output voltage change becomes still severer. We propose an approximate 2-degree-of-freedom (2DOF) digital controller which realized start-up response and dynamic load response independently. The controller makes a control bandwidth wider, and at the same time makes variations of the output voltage small at sudden changes of a load and an input voltage. In this paper, a new approximate 2DOF digital control system with additional zeros is proposed. Using the additional zeros, the second-order differential transfer characteristics between equivalent disturbances and a output voltage are realized. Therefore, the new controller makes variations of the output voltage smaller and the sudden changes of the load and the input voltage. This controller is actually implement on a DSP and is connected to the DC?CDC converter. Experimental results demonstrate that this type of digital controller can satisfy given severe specifications with low frequency sampling.     

Preparation of rod-shaped BaTiO3 powder

Rod-shaped BaTiO₃ powder particles have been prepared from rod-shaped TiO₂ ·nH₂O and BaCO₃ in molten chloride. The morphology of BaTiO₃ particles was studied referring to the effects of the chemical species of the starting titanium compound, amount of chloride, particle size of the titanium compound and reaction conditions, and the preparation condition of rod-shaped BaTiO₃ has been determined: i.e., large TiO₂ ·nH₂O particles were heated at 700°C in molten salt with an equal amount of BaTiO₃. This condition was effective in suppressing the formation of BaTiO₃ by a solution-precipitation process as well as the deformation of either TiO₂ ·nH₂O or BaTiO₃, which are responsible for the formation of equiaxed BaTiO₃ particles. The obtained rod-shaped BaTiO₃ particles had a cubic symmetry. Electron diffraction analysis showed that the following topotactic relation is retained; 0 1 0_{potassium tetratitanate} 0 1 0_{hydrated titania} 1 0 0_anatase 1 0 0_{barium titanate}     

Vapor phase hydroformylation of ethene over Co/SiO2 promoted by noble metals: dynamic in situ diffuse reflectance FT-IR study of surface species

An in situ diffuse reflectance FT-IR technique was employed to investigate the active surface species and the reaction mechanism of the oxygenate formation in the vapor phase hydroformylation of ethene on Co/SiO₂ promoted with various noble metals such as Ir, Rh, Pt, Re, Ru, and Pd. Co(A)/SiO₂ and Ir(CO)/SiO₂ which were derived from cobalt(II) acetate and Ir₄(CO)₁₂, respectively, were quite inactive in the reaction, and showed only quite small peaks of adsorbed CO under the conditions of 1.1 MPa of C₂H₄/CO/H₂ at 298 K. In contrast, Co(A)-Ir(CO)/SiO₂, which were very active in the reaction, exhibited strong absorption bands of linear and bridged CO species. At 423–463 K, propanal adsorbed on the catalyst and acyl species which is suggested as the intermediate for the formation of propanal were also observed on this catalyst. By exposing CO preadsorbed on this catalyst to C₂H₄/H₂ at 289 K and 0.1 MPa, the intensity of the linear CO band decreased, and the bands of propanal and acyl species emerged simultaneously, whereas that of the bridged CO band remained constant after the initial drop. These results suggested that the oxygenates are formed via the CO insertion into adsorbed ethyl species, and linear CO species plays a major role in the CO insertion on these noble metal-promoted cobalt catalysts.     

Isotactic polypropylene hollow microfibers prepared by CO2 laser‐thinning

An isotactic polypropylene hollow microfiber was continuously produced by using a carbon dioxide (CO₂) laser‐thinning method. To prepare the hollow microfiber continuously, the apparatus used for the thinning of the solid fiber was improved so that the laser can circularly irradiate to the hollow fiber. Original hollow fiber with an outside diameter (OD) of 450 μm and an internal diameter (ID) of 250 μm was spun by using a melt spinning machine with a specially designed spinneret to produce the hollow fiber. An as‐spun hollow fiber was laser‐heated under various conditions, and the OD and the ID decreased with increasing the winding speed. For example, when the hollow microfiber obtained by irradiating the CO₂ laser to the original hollow fiber supplied at 0.30 m min^?1 was wound up at 800 m min^?1, the obtained hollow microfiber had an OD of 6.3 μm and an ID of 2.2 μm. The draw ratio calculated from the supplying and the winding speeds was 2667‐fold. The hollow microfibers obtained under various conditions had the hollowness in the range of 20–30%. The wide‐angle X‐ray diffraction patterns of the hollow microfibers showed the existence of the highly oriented crystallites. Further, the OD and ID decreased, and the hollowness increased by drawing hollow microfiber obtained with the laser‐thinning. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 2600–2607, 2006     

Formation of Small-Sized CdSxSe1-x Crystals in Sol-Gel-Derived SiO2 Glasses

Silica glasses doped with small-sized CdS_x-Se_1-x crystals were prepared by the sol-gel method. Gels synthesized by the hydrolysis of Si(OC₂H₅)₄, in the presence of CdSeO₄ with NH₄SCN dissolved in HNO₃ or NH₄OH, were heated in H₂-N₂ atmosphere. The pH value of solutions for CdSeO⁴ and NH⁴SCN primarily determined the fraction of anions in CdS^xSe^1-x crystals. The anion content in crystals was dependent on the pH value of the solvent and/or heat-treatment temperature, and the sulfur fraction changed from 0.1 to 0.6. The optical absorption spectra were red-shifted as the selenium content and the crystal size increased, and the emission spectra showed a sharp band near the absorption edge position and a broad tail extending into the long wavelength. The optical band gap energies increased reciprocally proportional to the square of the crystal size.     

Organic–silicate hybrid catalysts based on various defined structures for Knoevenagel condensation

Two types of organic–inorganic hybrid base catalysts are prepared. Organic-functionalized molecular sieves (OFMSs), particularly “amine-immobilized porous silicates”, are designed based on common idea to immobilize catalytic active sites on silicate surface. Silicate–organic composite materials (SOCMs), such as “ordered porous silicate–quaternary ammonium composite materials”, are the precursors of ordered porous silicates obtained during the synthesis. Both the OFMS and the SOCM are used as the catalysts for Knoevenagel condensation. Among the OFMSs, there is clear tendency that the use of molecular sieve with larger pore volume and/or surface area gives the product in higher yield. Aminopropylsilyl (AP)-functionalized mesoporous silicates such as AP-MCM-41 gives the product in high yield under mild conditions. No loss of activity is observed after repeated use for three times. The SOCMs are also active for the same reaction. The precursors of the mesoporous silicates are more active than those of microporous silicates. This material can be repeatedly used without significant loss of activity. High activity is not due to the leached species. The active sites of the SOCM catalysts are considered to be SiO⁻ moieties located on the pore-mouth. Activity of the SOCM increases when the reaction is carried out without solvent, whereas decrease in activity of the OFMS is observed in the solvent-free system.     

Synthesis of AlPO4 Molecular Sieves with AFI and AEL Structures by Dry-Gel Conversion Method and Catalytic Application of Their SAPO Counterparts on Isopropylation of Biphenyl

AlPO₄-5 and AlPO₄-11 were synthesized by dry-gel conversion (DGC) method. Steam-assisted conversion (SAC) and vapor-phase transport (VPT) techniques were applied for this purpose. The synthesis was successful in presence of a certain minimum amount of external bulk water, without which the crystallization failed. Crystallization by VPT method was slower than corresponding SAC and HTS method. SAPO analogs of the samples, SAPO-5 and SAPO-11 were also synthesized by DGC method. Samples made by DGC methods had higher yield than the conventional hydrothermal synthesis (HTS); otherwise the samples showed similar characteristics as that made by HTS. XRD, SEM and N₂-adsorption results showed high crystallinity and purity of the samples made by DGC, and ²⁷Al MAS NMR spectra indicated the tetrahedral framework nature of Al. SAPO-5 and SAPO-11 were tested for their catalytic activity in isopropylation of biphenyl, and in terms of conversion and selectivity, SAPO-5 was found to be suitable for this application.     

Preparation of Porous Ceramics with Calcium Metaphosphate Fiber Skeleton for Biomedical Use

High-strength calcium metaphosphate fibers for biomedical applications are extracted from crystallized products of calcium ultraphosphate glasses by aqueous leaching. In the present work, new types of porous ceramics with a skeleton composed of the crystalline fibers are prepared by heating the fibrous products extracted. The fibers in the ceramic are interlinked to each other by glassy phases formed during the heating. This porous material has a large porosity of >60%. The surface of the skeleton can be successfully converted into new calcium phosphate phases such as apatite by heating the porous material treated with a molten salt mixture of CaCl₂-Ca(NO₃)₂.