Mg（OH）2为碱源的H2O2漂白纸浆性能和废液特性的研究

用Mg（OH）2或者NaOH作为碱源,在不同条件下对针叶木TMP浆进行过氧化氢漂白,主要考察漂后纸浆的光学性能和物理强度性能。比较传统的以NaOH作为碱源的H2O2漂白和Mg（OH）2作为碱源的H2O2漂白,二者所得纸浆白度和物理强度值相近,但后者有较高的光散射系数。Mg（OH）2作为碱源的H2O2漂白所得纸浆羧基总量较少,但表面电荷密度接近于以NaOH作为碱源的H2O2漂白纸浆。用Mg（OH）2作为碱源的H2O2漂白所产生的废液中COD负荷较低．主要原因是乙酸和甲醇生成量的减少以及木素溶出量的下降。 应用Mg（OH）2取代NaOH作为碱源的H2O2漂白可以改善机械浆漂后废液的性质。     

高得率浆和DIP以Mg（OH）_2为碱源的H_2O_2漂白

研究了以Mg（OH）2替代NaOH为碱源对机械浆（TMP和CTMP）和脱墨浆（DIP）进行H2O2漂白的影响。结果表明,与以NaOH为碱源的H2O2漂白相比,以Mg（OH）2为碱源对TMP、CTMP、DIP进行H2O2漂白可使活性碱用量分别减少75%、50%、90%,同时残余H2O2增加;与以NaOH为碱源相比,以Mg（OH）2为碱源的H2O2漂白浆白度稍有降低：TMP、CTMP和DIP的白度分别降低1.4、0.9和1.7个百分点,但漂白浆得率提高1%～2%。以Mg（OH）2为碱源的H2O2漂白废水的阳离子需求量（CD）、生物需氧量（BOD）、化学需氧量（COD）、溶解物质（DS）、总有机碳（TOC）等参数降低。     

氢氧化镁与氢氧化钠用于麦草NaOH-AQ浆DP漂白的研究

本文以麦草NaOH-AQ浆为原料,进行了DP漂白的研究,研究过程中探讨了NaOH和Mg(OH)2分别用作D段漂白终点pH控制剂和P段漂白碱源对最终漂白效果的影响。实验中进行了氢氧化钠和氢氧化镁的四组组合研究,分别为DNaOHPNaOH,DNaOHPMg(OH)2,DMg(OH)2PNaOH和DMg(OH)2PMg(OH)2。结果表明,麦草NaOH-AQ浆经DMg(OH)2PMg(OH)2漂白后纸浆白度和强度性能与传统的DNaOHPNaOH漂白纸浆相比,其白度和强度性能略低,但DMg(OH)2PMg(OH)2漂白废液中含有较高的残余ClO2和残余H2O2,因此与DNaOHPNaOH漂白相比较,DMg(OH)2PMg(OH)2漂白具有更高的漂白效率。Mg(OH)2用作D段漂白pH控制剂时,能明显降低后续P段漂白的碱用量。Mg(OH)2替代P段漂白NaOH对最终浆料的影响大于替代D段NaOH对最终浆料性能的影响。     

机械浆过氧化氢漂白工艺的优化

阐述了各种因素对机械浆H2O2漂白的影响：已知参数如浆浓、温度、反应时间及NaOH和H2O2用量对漂白的影响;添加Na2SiO3对纸浆获得高白度的影响。高温漂白若使用NaOH,Na2SiO3的存在就特别关键。目前,短的水循环造成温度升高,影响了漂白反应的活化与漂白剂H2O2热分解之间的平衡;温度超过75℃时,H2O2热分解速度迅速提高,导致漂白效果下降。文中对在机械浆漂白车间不能使用Na2SiO3的情况下,如何最好地控制漂白工艺提出了建议,同时对Na2SiO3的替代物（如有机聚合物）对漂白效果的影响进行了讨论。同时,介绍了替代NaOH的碱源如Mg（OH）2、Ca（OH）2、Na2CO3的利弊。实验结果表明,与使用Ca（OH）2和Mg（OH）2相比,使用NaOH可以获得更高的白度,但漂白时使用Ca（OH）2和Mg（OH）2会明显降低COD负荷,这也意味着可获得更高的纸浆得率。使用Mg（OH）2有助于保持阔叶木漂白机械浆的纤维体积（fibr evolume）,但对针叶木（云杉或松树）机械浆的机械性质几乎没有影响。     

碱法蔗渣浆全无氯漂白技术研究

研究了碱法蔗渣浆的(OP)Q(PO)全无氯漂白(TCF)工艺.结果表明,与常规氧脱木素相比.加入0.5%用量的H2O2强化氧脱木素,可使漂白浆的脱木素率和黏度基本不变,而白度大幅提高;螯合处理段EDTA用量(最佳EDTA用量为0.05%)对后续漂白效果产生较大影响;与氮气加压H2O2漂白相比,在同等条件下氧气加堆H2O2漂白具有更高的白度,对于白度超过83.5%的纸浆,采用氧气加压H2O2漂白比采用氮气具有更商的黏度.(OP)Q(P0)全无氯漂白工艺漂白蔗渣浆,具有纸浆白度高、强度性能优良和污染负荷低的特点,用于生产高品质碱法蔗渣漂白浆足可行的.     

Mg（OH）2在CMP H2O2漂白中的应用

与以NaOH为碱源相比,以Mg（OH）2为碱源对阔叶木化学机械浆（CMP）进行H2O2漂白有显著的优越性。在H2O2用量相同的情况下,以Mg（OH）2为碱源的H2O2漂白能够得到得率较高、光学性能较好的浆料,且废水中COD负荷较低,但这2种H2O2漂白工艺得到的浆料物理性能相差不大。以Mg（OH）2为碱源的H2O2漂白浆的初始游离度较高,故使其游离度达到350mL时（CSF）所需的磨浆转数更高,且漂白废水的残余H2O2量也高于以NaOH为碱源。     

用氢氧化镁基过氧化物漂白机械浆

加拿大New Brunswick大学制浆和造纸研究与教育中心科技人员的最新研究结果表明，在过氧化物漂白机械浆过程中，以Mg（OH）：代替NaOH，可明显降低废水中COD和阴离子垃圾含量。据文献报道，在云杉热磨机械浆（TMP）过氧化物漂白过程中以Mg（OH）2代替NaOH，浆料白度为68％-70％，槭木化学热磨机械浆（CTMP）过氧化物漂白过程中以Mg（OH）2代替NaOH，浆料白度为80％，而漂白机械浆强度没有降低。试验采用槭木CTMP、槭木PGW（加压磨木浆）和云杉TMP等3种纸浆在不同游离度下经过氧化物漂白，在各种不同漂白条件下。采用Mg（OH）2或NaOH作为碱来源，对漂白浆强度的影响进行了研究。     

高浓化机浆以氢氧化镁为碱源的过氧化氢漂白

研究目的是探究Mg(OH)2为碱源的H2O2高浓漂白性能。在浆浓分别为10%和25%时,对比Mg(OH)2或NaOH为碱源的H2O2漂白化机浆(CMP)。结果表明:浆浓为25%时,1.5%Mg(OH)2和3%H2O2条件下漂白浆的白度与2.1%NaOH、3%Na2SiO3和3%H2O2条件下漂白浆白度基本相同,而前者的返黄指数小于后者;2种条件下的漂白温度和时间均相同,分别为70℃和150 min;在前述条件下,Mg(OH)2为碱源的H2O2漂白得率高于NaOH为碱源的H2O2漂白得率;与NaOH为碱源的H2O2漂白相比,Mg(OH)2为碱源的H2O2漂白废水中残余H2O2较高,而化学需氧量(COD)和浊度较低;然而,与后一种漂白方式相比,前一种漂白方式漂后的纸浆强度性能和保水值(WRV)较低、松厚度较大。     

桑枝硫酸盐浆的氧脱木素及其后续漂白研究

对桑枝硫酸盐浆的氧脱木素工艺进行了详细探讨,并对氧脱木素后续漂白流程进行了初步探讨。结果表明,氧脱木素段NaOH的最佳用量为4.0%,H_2O_2强化氧脱木素可以提高氧脱木素的效果,最佳H_2O_2用量为0.5%。优化后的OQPo漂白,可使桑枝硫酸盐浆白度达到71.4%。采用O_pDE_(OP)三段漂白,纸浆白度可以达到81.7%,ODED漂白流程可以使纸浆获得90%以上的白度。     

Mg(OH)2对松木CTMP H2O2漂白的影响

探讨了Mg(OH)2部分取代NaOH对马尾松CTMP H2O2漂白的影响.实验结果表明,随着Mg(OH)2用量的增加,漂后浆料白度逐步降低,但漂后残余H2O2明显增加,返黄值下降.减小Mg(OH)2颗粒的尺寸,可提高漂后浆料的白度和残余H2O2.Mg(OH)2取代25%的NaOH时,漂后浆料白度变化不大,但漂白浆得率、不透明度、松厚度和抗张指数均有所提高.     

Sulfite-Formaldehyde Pulping and Oxygen Delignification of Wheat Straw

In this study,wheat straw pulp was prepared by sulfiteformaldehyde(SF) pulping combined with oxygen delignification to develop a sustainable methodology for chemical pulping of straw materials.The bleachability of oxygen-delignified SF pulp was also evaluated by hypochlorite bleaching.The results indicated that the Na_2SO_3 charge played an important role in lignin removal during SF pulping as well as oxygen delignification.The efficiency of oxygen delignification of wheat straw SF pulp was markedly high.After the oxygenation stage,the Kappa number decreased by over 50%(the original Kappa number of SF pulp was lower than 30) when the Na OH charge was in the range of 3%~5%.The optimal conditions for preparing bleached pulp via combined SF pulping and oxygen delignification involved the use of 12% of Na_2SO_3 and 3% of Na OH,respectively.Pulp with relatively high brightness,a low Kappa number,as well as an acceptable viscosity could be obtained when oxygen-delignified SF pulp was bleached with hypochlorite under a low active chlorine dosage.     

桉木常规KP浆和RDH浆的氧脱木素研究(Ⅰ)--常规KP浆和RDH浆的氧脱木素效果

对桉木常规KP浆和RDH硫酸盐浆的氧脱木素进行了研究和对比，确定了氧脱木素的最佳条件。结果表明，常规KP浆和RDH硫酸盐浆在适宜的条件下经氧脱木素后，纸浆卡伯值分别降低58．2％和42．25％，纸浆白度分别增加了29．5％ISO和22．4％ISO，达到56．8％ISO和63．O％ISO，而纸浆的粘度变化不大。综合而言，氧脱木素对常规KP浆和RDH浆的卡伯值、白度和脱木素选择性的影响规律类似，但由于RDH浆的初始卡伯值和粘度较低，因而氧脱木素时可以采用相对温和的反应条件，且RDH氧漂浆的粘度也相对较低。     

乙酸浆TCF漂白的初步探讨

对三倍体毛白杨乙酸浆进行了TCF漂白的初步研究，发现与其他浆种比较，乙酸原浆具有较低的白度；乙酸浆进行氧脱木素时需要高的碱用量才能得到低的卡伯值，进行碱预处理可以降低氧脱木素段的碱用量，避免纸浆粘度较大程度的降低；并研究了漂白前后纸浆物理强度的变化。乙酸浆氧脱木素较佳的碱用量为4％～5％，经EOPP漂序漂白后白度达到70％ISO左右。     

P-RC APMP高浓停留段Mg（OH）2取代NaOH比例对三倍体毛白杨浆料性能的影响

以三倍体毛白杨为原料进行P-RC APMP制浆,优选并固定其他工艺条件,控制高浓停留段用碱量为3.0%(以NaOH计),探讨高浓停留段Mg(OH)2取代NaOH比例对纸浆的成纸物理性能(白度、松厚度、强度)以及保水值、纤维形态的影响。结果表明,随着Mg(OH)2取代比例的增加,纸浆的白度均高于75%ISO,在取代比例低于50%时,对纸浆白度会产生积极的影响;当Mg(OH)2取代比例由0增加至75%时,成纸的松厚度由2.12 cm3.g-1提高到2.67 cm3.g-1;当Mg(OH)2取代比例由0增加至50%时,抗张指数由26 N·m·g-1下降到18 N·m·g-1,撕裂指数由3.9mN·m2·g-1下降到2.7 mN·m2·g-1;浆料的保水值、纤维长度、纤维扭结指数和扭结角均随着Mg(OH)2取代量的增加而下降。     

湿地松KP浆氧和过氧化氢脱木素的研究

湿地松KP浆(卡伯值28.2,粘度1024ml/g)经氧和过氧化氢脱木素,卡伯值分别降低45％和32.3％。H_2O_2脱木素时通O_2可大幅度提高脱木素作用,但选择性差。经0.8％H_2O_2强化的脱木素纸浆其卡伯值降低51.8％。在酸性介质中,对纸浆进行活化预处理可显著改善其脱木素的选择性,效果以KMnO_4和HNO_3/NaNO_3为佳,可使纸浆卡伯值降至10以下,其粘度高于800ml/g。     

三倍体毛白杨低硬度NaOH-AQ浆的氧脱木素研究

对三倍体毛白杨低硬度NaOH-AQ浆氧脱木素进行了研究,通过实验分析了各影响因素(用碱量、温度、时间、氧压及助剂用量)对三倍体毛白杨低硬度NaOH-AQ浆氧脱木素后的卡伯值、黏度、白度以及木素的脱除情况等的影响,确定了该浆种氧脱木素较适宜的工艺条件.     

AS-AQ麦草浆氧脱木素后的过氧化氢漂白

研究了氧脱木素后的AS-AQ麦草浆H2O2漂白工艺,并对漂前预处理进行了探讨。结果表明：采用预处理剂X对浆料进行H2O2漂前预处理能够显著提高漂浆白度;在提高H2O2漂白效率方面,预处理剂X预处理优于EDTA、DTPA等传统预处理方式;柠檬酸钠可以替代Na2SiO3用作H2O2漂白稳定剂。H2O2漂白最适宜的工艺条件为：浆浓12%,H2O23%,NaOH1.2%,柠檬酸钠1%,温度95℃,时间120min。在优化条件下,漂终白度达83.9%ISO。     

桉木常规KP浆和RDH浆的氧脱木素研究(Ⅲ)--HNO3/NaNO3预处理对常规KP浆氧脱木素的影响

研究了HNO3/NaNO3预处理对桉木常规KP浆氧脱木素的改善效果.研究表明,在氧脱木素前,用HNO3/NaNO3对浆料进行预处理,可以有效改善后续氧脱木素段的脱木素效率,提高氧脱木素的选择性.但HNO3/NaNO3用量有一最佳值,且宜采用短时间高温预处理的方式进行.若将HNO3/NaNO3预处理与H2O2强化氧脱木素相结合,可取得进一步降低氧脱木素浆卡伯值、提高纸浆白度和保持较高纸浆粘度的良好效果.     

改善亚硫酸盐浆氧脱木素选择性的研究

研究了亚硫酸盐蔗渣浆氧脱木素过程中的选择性,并对其改善方法进行了探讨。结果表明：氧脱木素过程中采用硝酸和木聚糖酶预处理及分别添加H2O2甲醇或硫化钠强化方法,均可改善脱木素选择性,其中硝酸用量2％最明显,添加0．6％的H2O3次之,但改善漂白效果最好;一定量的木聚糖酶、甲醇和硫化钠处理,也可以提高脱木素选择性,但幅度不大。     

粗皮桉AS-AQ浆氧脱木素后的过氧化氢漂白

研究粗皮桉AS-AQ浆氧脱木素后的过氧化氢漂白工艺,并对漂前预处理进行了探讨。结果表明:粗皮桉AS-AQ氧漂浆在进行过氧化氢漂白前采用高锰酸钾进行预处理,预处理条件为高锰酸钾用量0.6%,温度25℃,时间20 min,硫酸3%,浆浓5%,可以有效地提高纸浆的白度,降低卡伯值,同时纸浆黏度下降比例不大。使用柠檬酸钠取代硅酸钠和硫酸镁作为过氧化氢漂白的稳定剂是可行的,添加2%的柠檬酸钠作稳定剂可以达到添加3%的硅酸钠作稳定剂的效果。过氧化氢漂白的最佳工艺条件为:过氧化氢用量3%,温度90℃,时间120 min,氢氧化钠用量1.5%,柠檬酸钠2%,浆浓10%。在最优条件下,纸浆白度可以达到80.8%ISO。