喷丝板规格及纺丝速度对Lyocell纤维力学性能和结构的影响

为提高Lyocell纤维的力学性能,采用不同孔径和长径比的喷丝板制备Lyocell纤维,研究喷丝板规格和纺丝速度与Lyocell纤维的力学性能和结构之间的关系。结果表明,随着喷丝板的孔径增大,Lyocell纤维的结晶度和取向度增大,初始模量和断裂强度相应提高,但喷丝板的孔径过大会导致Lyocell纤维的结晶度和取向度减小,初始模量和断裂强度相应下降;随着喷丝板的长径比和纺丝速度的提高,Lyocell纤维的结晶度和取向度提高增大,初始模量和断裂强度相应提高。     

喷头拉伸比对热致液晶聚芳酯纤维结构与性能的影响

为探究喷头拉伸比对热致液晶聚芳酯(TLCPAR)纤维结晶结构以及力学性能的影响,通过熔融纺丝法制备了不同喷头拉伸比的TLCPAR纤维,采用WAXD分析纤维结晶度、晶粒尺寸以及晶区取向的变化,并分析其力学性能。结果表明,随喷头拉伸比的增大,纤维的结晶度增大,而晶粒尺寸没有明显的变化。经喷头拉伸后,初生纤维晶区取向度较高,且随喷头拉伸比的增大先增大后不变。由于纤维结晶度随喷头拉伸比的增加而增大,晶区取向度先增大后不变,使得TLCPAR初生纤维的强度和模量随着喷头拉伸比的增加而增大。     

静电纺工艺对PA6/MWNTs纳米纤维纱结构与性能的影响

 以PA6、多壁碳纳米管（MWNTs）为原料,利用自制的静电纺丝装置,探索了碳纳米管增强PA6纳米纤维纱的连续静电纺丝。研究了纺丝电压、纺丝高度、电场强度等参数对PA6/MWNTs纳米纤维纱的结构与性能的影响。结果表明：随着电压的增大,纤维和纱线的直径、纤维结晶度、断裂强力增加,纤维间黏连减少;随着纺丝高度的增加,纤维的定向排列程度、纤维结晶度提高,纱线断裂强度和初始模量增加;电场强度一定时,随着电压和纺丝高度的增加,纤维的平行排列程度提高,纱线的断裂强力、断裂伸长率、初始模量和断裂强度都增大。     

制备工艺对海岛型超细纤维物性的影响探究

以不定岛LDPE/PA6超细纤维为研究对象,通过选择不同制备工艺,包括原材料配比、纺丝速度、环吹风风量和温度、牵伸温度和倍数,探究制备工艺对海岛型超细纤维物性的影响。结果表明,纤维中PA6的比例越高,纤维的断裂强度、断裂伸长率、初始模量和断裂比功就越高。提高环吹风的风量或者降低环吹风的温度,会导致纤维的断裂强度和初始模量提高,断裂伸长率和断裂比功降低。纺丝速度越高,纤维的断裂强度和初始模量就越高,纤维的断裂伸长率和断裂比功则越低。在玻璃化温度之上,牵伸温度越高或者牵伸比例越高,纤维的断裂强度和初始模量就越高,纤维的断裂伸长率和断裂比功则越低。     

蒲葵再生纤维素纤维纺丝工艺及形态探讨

为了获得较好力学性能的蒲葵再生纤维素纤维,以蒲葵为原料制备纤维素浆粕,采用N-甲基吗啉氧化物体系溶解蒲葵纤维素制备纺丝原液,然后通过干湿法纺丝工艺制备蒲葵再生纤维素纤维。探讨了干湿法纺丝工艺条件,如喷丝头拉伸比、空气层高度、凝固浴温度、纺丝液浓度等对获得的有关纤维力学性能的影响。结果表明:当喷丝头拉伸比3.4,空气层高度2.2cm、凝固浴温度16℃,纺丝液质量分数9%时,所制得纤维的各项力学性能较好。其纤维线密度17.83 dtex,断裂强度2.21cN/dtex,断裂伸长率8.71%,初始模量74.55cN/dtex。认为:通过优化纺丝工艺所制得蒲葵再生纤维素纤维能够满足织造要求。     

竹纤维纯纺纱和混纺纱拉伸性能探讨

对不同混纺比例的竹浆/棉混纺纱线的拉伸性能进行了测试和分析.结果表明,当混纺纱线的竹浆/棉混纺比为70/30时,混纺纱线的断裂强度、断裂伸长率和断裂功出现一个极低值,在实际应用中,该混纺比在设计中应尽量避免选用.同时将竹浆纤维纯纺纱与竹浆/棉70/30、竹浆/棉55/45、竹浆/棉30/70混纺纱、棉纤维纯纺纱拉伸图比较.结果表明:竹纤维纯纺纱的初始模量比棉纤维纯纺纱的初始模量高,随着棉纤维含量的增加,混纺纱的初始模量减少.     

凝固浴温度对Lyocell纤维结构及性能的影响

探讨凝固浴温度对Lyocell纤维纺丝工艺中纤维结构及性能的影响。实验表明：随着凝固浴温度提高,最大纺丝速度和纤维延伸度提高;而无定区取向度、结晶度、相对强度和初始模量下降。     

高强高模聚甲醛纤维的制备及其性能

为提升高强高模聚甲醛纤维的可纺性,通过研究聚甲醛树脂的流变行为和热稳定性确定了聚甲醛的熔融纺丝温度,研究聚甲醛树脂的等温结晶能力以确定聚甲醛初生纤维的超高倍热拉伸温度,并分析了卷绕速度、热拉伸倍数和热定型条件对聚甲醛纤维结晶度、取向度和力学性能的影响。结果表明：聚甲醛纤维的最佳熔融纺丝温度为215 ℃,其取向度、结晶度和力学性能随着卷绕速度的增加而增加;聚甲醛初生纤维的最佳热拉伸温度为155 ℃,极限拉伸倍数可达17 倍,此时聚甲醛纤维的断裂强度为8.87 cN/etex,初始模量为108.07 cN/dte;初生纤维经过拉伸后结晶度和取向度提高,随着拉伸倍数增大,聚甲醛纤维的力学性能提高;聚甲醛初生纤维的最佳定型温度为145 ℃,定型时间为40~50 s。     

再生纤维素纤维的结构与力学性能的研究

采用扫描电镜、红外光谱、X-射线衍射等测试方法对粘胶、Tencel、Viloft等再生纤维素纤维的结构进行了研究,并对其拉伸性能进行了比较分析。结果表明：粘胶、Tencel、Viloft纤维由于纺丝方法不同,其形态结构存在一定的差异;3种纤维的红外光谱图都具有纤维素的特征;X射线特征衍射峰的位置与纤维素Ⅱ接近,都属于纤维素Ⅱ晶型,Tencel的结晶度最大,粘胶和Viloft相接近。由于Tencel纤维的结晶度较高,故纤维的断裂强度、初始模量高,伸长率较低;粘胶的断裂强度与Viloft相接近,断裂伸长率最高,初始模量最小。     

竹浆纤维含量及纬密对棉/竹浆纤维交织物力学性能的影响

对15种不同规格的棉与棉/竹浆纤维交织物面料的拉伸断裂强度、断裂伸长率、撕破强度、磨损牢度等力学性能进行测试比较,研究竹浆纤维含量及纬密对其力学性能的影响。结果表明：随着竹浆纤维含量增加,织物的经纬向拉伸断裂强力之和下降,纬向断裂伸长率上升,经向断裂伸长率先上升而后下降再上升;纬向撕破强力先下降而后上升,经向撕破强力变化不大;织物的质量减少率快速增加,织物磨损牢度变差,竹浆纤维含量为30%时,织物的磨损牢度最好;竹浆纤维含量达到70%时,交织物的断裂伸长率、撕破强力、摩损牢度均为最低,在实际生产应用中应尽量避免选用。当经密保持不变,纬密增加时,织物的断裂强力增加,断裂伸长率逐渐增大,撕破强力减小,耐磨性能提高。     

竹炭涤纶纤维的性能检测与分析

为了进一步了解竹炭涤纶纤维的力学性能,解决在纺织生产中存在的问题,测试了竹炭涤纶纤维的力学性能,包括直接拉伸性能、非直接(结节、钩接)拉伸性能和松弛性能等;比较了竹炭涤纶纤维与普通涤纶纤维之间的不同;选择了适当的力学模型,应用Origin8.0数据分析软件对竹炭涤纶纤维的非直接(结节、钩接)拉伸性能和松弛性能分别进行拟合,综合分析了实验结果和拟合参数。结果表明:在常温干态条件下,竹炭涤纶纤维的断裂强度、初始模量均低于普通涤纶纤维,断裂伸长和断裂功有所增加;经湿处理后,各项性能较干态时普遍下降。非直接拉伸状态下,竹炭涤纶纤维的断裂强度、断裂伸长、初始模量和断裂功等全部减小;对于竹炭涤纶纤维,多项式模型可以很好地拟合其直接拉伸、结节拉伸和钩接拉伸性能。标准线性固体模型可以很好地拟合竹炭涤纶纤维的松弛性能。     

Mechanical properties,moisture absorption,and dyeability of polyamide 5,6 fibers

Polyamide 5,6 (PA56) and polyamide 6 (PA6) fibers were spun by melt spinning process and drawn by a thermal drawing in order to improve their mechanical properties. The effects of drawing conditions on mechanical properties, moisture absorption, and dyeing behavior were investigated by means of tensile testing measurements, moisture absorption test, as well as color strength measurements. It was found that the tenacity and Young’s modulus were significantly increased, while the elongation at break decreased as the draw ratio (DR) and temperature increased due to the increase in molecular orientation along the fiber axis and the crystallinity. PA56 fibers showed a little lower mechanical properties and much higher moisture regain than PA6 fibers at different DRs. This can be attributed to the amide group content in the polymer backbone, which yields higher moisture regain in PA56 fibers than PA6 fibers. The dyeing behaviors of PA56 fiber, in terms of dyebath exhaustion, color strength, and wash fastness are similar as those of PA6. Those results indicated that PA56 is a competitive novel fiber for textile material.     

生物可降解聚己二酸-对苯二甲酸丁二醇酯纤维的制备及其环境降解性能

为研究生物可降解聚己二酸-对苯二甲酸丁二醇酯(PBAT)的可纺性及纤维降解性能,采用熔融纺丝-牵伸二步法制得生物可降解PBAT纤维,研究了纺丝温度、牵伸倍数对PBAT纤维结晶度、回潮率、力学性能的影响,对比分析了PBAT纤维在不同环境下的降解性能.结果 表明:PBAT的最佳纺丝温度为260℃,且随着牵伸倍数的增加,PB...     

PDMS共混改性超柔PBT纤维的制备及其性能

文章以聚对苯二甲酸丁二醇酯-聚二甲基硅氧烷(PBT-PDMS)为母粒,与聚对苯二甲酸丁二醇酯(PBT)进行共混纺丝,通过控制PBT-PDMS添加量制备不同PDMS含量的PBT/PDMS共混纤维,探讨了PDMS含量对纤维柔软性及其他性能的影响。结果表明:PDMS作为改性组分与PBT相容性良好,PDMS质量分数为6%时可纺性好,继续增加至8%时可纺性变差;随着PDMS含量的增加,PBT/PDMS共混纤维的初始模量显著降低,断裂强度略有降低,断裂伸长率、断裂比功均逐渐提高,染色性能也得到改善。当PDMS质量分数为6%、拉伸倍数为2.8时,PBT/PDMS共混纤维的断裂比功达0.92 cN/dtex,初始模量较低,为22.9 cN/dtex;制成的1/2斜纹织物的硬挺度为2.595 cm,抗弯刚度B为0.1098 cN·cm^2/cm(经向)、0.1542 cN·cm^2/cm(纬向),弯曲滞后量2HB为0.2283 gf·cm/cm(经向),0.2976 gf·cm/cm(纬向),纤维及织物的柔软性得到了明显提升,综合性能最好。     

一步法PET/CDP混纤牵伸丝的制备与性能

以聚对苯二甲酸乙二醇酯（PET）、阳离子染料可染改性聚酯（CDP）为原料,利用复合纺牵联合设备,一步法制备了PET/CDP混纤FDY（牵伸丝）;采用声速法、差示扫描量热法（DSC）等测试手段,对纤维的性能进行了研究。结果表明：在其它主要工艺条件不变的条件下,随着第一热盘（GR1）速度的提高,纤维的声速取向因子和声速模量下降,纤维的结晶度也下降;随着GR1速度的提高,纤维的断裂强度下降、断裂伸长上升,而沸水收缩率则略有上升;针对PET、CDP二种聚合物性能的不同,纺丝牵伸工艺条件的优化选择,应以满足CDP的条件为主,兼顾PET的特性。     

Effects of drawing process on crimp formation-ability of side-by-side bicomponent filament yarns produced from recycled,fiber-grade and bottle-grade PET

In this study, side-by-side bicomponent filaments from recycled poly(ethylene) terephthalate (R-PET) from post-consumer bottles, fiber-grade PET (FG-PET) and bottle-grade PET (BG-PET) successfully were extruded. The bicomponent fibers in the forms of FG/R, BG/R and FG/BG were produced in a spinning machine and drawn by a thermal drawing process to improve their mechanical properties using draw ratios between ‘2.5 and 2.8’. The effects of conditions on the fiber structure, physical properties and crimp formation of resultant fibers were evaluated. The birefringence, shrinkage and mechanical properties, such as tensile strength and tensile modulus, increased and elongation at break decreased for the drawn fibers, and this was attributed to the fiber orientation. Distinct crimp formation was observed from drawn bicomponent fibers after thermal treatment. There were significant birefringence and shrinkage difference between two components in drawn bicomponent fibers caused to severe crimp formation.     

板蓝根粘胶共混膜的物理性能研究

文章将板蓝根提取物溶液和粘胶纺丝液进行共混制得共混膜,对共混膜的物理性能进行了测试。结果表明:与纯粘胶膜相比,共混膜的断裂强力、断裂伸长率和初始模量都有所减小;共混膜的断裂强力和断裂伸长率都随共混纺丝液中板蓝根提取物含量的增加而减小;初始模量值随着板蓝根含量的增加先降低后升高。     

浅析纺丝温度和牵伸倍数对聚乳酸纤维性能的影响

文章通过对纺丝条件——牵伸倍数和纺丝温度做单因子试验,并对聚乳酸纤维的断裂强度、断裂伸长率、沸水收缩率、取向度、粘均分子量进行测试,研究了纺丝条件对聚乳酸性能的影响关系,并得出了最佳的纺丝条件。