5A06铝合金厚板双丝PMIG焊接头组织与性能

采用双丝PMIG协同式高效焊接方法对板厚为60 mm的5A06铝合金进行了焊接试验,获得了优良的焊接接头,并对焊接接头进行了金相组织和力学性能分析. 结果表明,母材保持轧制态纤维状组织,焊缝组织细密均匀,主要为α(Al),β(Mg₂Al₃)及部分Mg₂Si杂质相. 接头平均抗拉强度和断后伸长率分别为306.17 MPa和11.93%,达到母材的90.5%和61.5%. 对比接头各层显微组织和力学性能发现,热输入影响焊接接头热影响区宽度和力学性能. 在焊接热输入最小的正面盖面层,焊缝组织更细,热影响区宽度更窄,试样力学性能更好.     

焊接热输入对铝/镀锌钢CMT熔-钎焊接头组织与性能的影响

采用ER4043焊丝对5052铝/Q235镀锌钢进行CMT熔-钎焊,研究焊接热输入对接头组织及性能的影响.结果表明,焊缝熔宽、热影响区粗化程度、界面层硬度及厚度均随热输入的增加而增大,过热组织粗化导致拉伸试样在铝母材热影响区断裂.熔焊区组织主要为垂直于基底向焊缝中心生长的α-Al树枝晶及Al-Si共晶组织,钎焊区界面层厚度在2.55~6.86μm之间,铝侧界面主要为FeAl₃金属间化合物,呈凹凸不平锯齿状;钢侧界面平滑,主要为Fe₂Al₅(热输入较低时)或FeAl₂,FeAl(热输入较高时).     

大线能量焊接用FH500高强船板钢的研制与焊接试验

采用复合微合金化的成分设计,通过TMCP(热机械处理)工艺开发了适应大线能量焊接的FH500高强船板钢。运用埋弧焊和垂直气电立焊对FH500船板钢进行了焊接试验,对两种焊接方式的焊接接头分别进行了拉伸、弯曲、冲击等力学试验,研究了不同热输入值对接头力学性能的影响;运用透射电镜对焊接热影响区组织析出物进行了分析。结果表明:FH500高强船板钢组织以针状铁素体为主,具有良好的强韧性匹配;两种焊接方式接头力学性均能满足船级社标准。焊接热影响区(HAZ)组织为针状铁素体和贝氏体组织,晶内含有大量纳米级析出物,能谱显示,其成分为钛铌的复合析出物。     

Ti-23Al-17Nb激光焊接接头的组织性能研究

通过室温和高温拉伸性能测试研究焊后热处理和同步预热对Ti-23Al-17Nb(原子分数,下同)合金CO_2激光焊接接头性能的影响.结果表明,接头室温和高温拉伸性能低,焊后真空热处理提高接头室温和高温拉伸性能,仍低于母材;同步预热接头室温强度和塑性与母材相当,高温强度与焊后热处理效果相当.组织分析显示,焊缝存在两个腐蚀衬度区,组织为B2相,热影响区晶粒由熔合线到母材逐渐细化,焊后热处理和同步预热改变β相基体上α2相的析出.     

舰船用6082铝合金TIG焊组织与力学性能分析

采用ER4043和ER4047焊丝,对厚度为12 mm的舰船用6082铝合金进行了TIG焊接试验研究,测试了焊缝强度并对其显微组织进行了观察分析.结果表明,在采用文中推荐的焊接参数条件下,使用Al-Si系焊丝的焊接接头力学性能优良,焊缝区组织为树枝状晶的铸态组织,熔合区出现异于焊缝中心的胞状晶;热影响区受焊接热循环作用组织有所粗化.使用ER4043焊接的接头抗拉强度略低于使用ER4047的接头,但塑性相对较好并且生成大气孔的倾向相对较低.     

大热输入焊接EH36船板钢接头力学性能

以EH36高强度船板钢为研究对象,通过拉伸和冲击分析试验手段,对EH36船板钢不同热输入埋弧焊接头进行了力学性能测试,同时采用扫描电镜对冲击试样断口形貌进行分析.结果表明,所有断裂均发生在拉伸试样的母材区,EH36船板钢在大焊接热输入条件下,焊缝和焊接热影响区的强度好于母材,并没有出现热影响区软化现象;随着焊接热输入增加焊缝的冲击韧性降低,从焊缝和熔合区断口形貌来看,断裂类型为韧性断裂和准解理断裂的混合断裂.随着远离熔合线距离的增加,冲击吸收功有增加的趋势,在距离熔合线4 mm处的冲击吸收功跟母材接近,说明该位置处韧性基本不受焊接热循环的影响.     

热输入对双光束激光焊接Ti-6Al-4V合金T型接头焊接过程、焊缝成形、组织及力学性能的影响

采用双光束同步激光填丝焊接的方法制备了Ti-6Al-4V合金T型接头,使用高速摄像机拍摄了焊接过程图像并研究了热输入对焊接过程稳定性、焊缝成形、组织及力学性能的影响。试验结果表明,热输入显著影响熔池行为和填丝焊接熔滴过渡,进而影响T型接头焊缝形貌及质量。随着热输入的增加,T型接头组织发生变化,晶粒尺寸变大。热影响区及焊缝处的马氏体使得这2个区域的显微硬度高于母材。另外,沿蒙皮方向及筋条方向的抗拉伸强度随着热输入的增加而增大。由于接头处马氏体增强作用,拉伸断裂均发生于母材处。     

激光焊接热输入对Ti2AlNb合金组织性能的影响

研究激光焊接热输入对Ti-22Al-27Nb(at%)合金焊缝成形和力学性能的影响,利用OM、SEM、XRD和TEM等手段对焊接接头的显微组织特征进行了分析,并探讨了焊后热处理对焊接接头组织性能的影响。结果表明,连续激光焊接可以获得无缺陷、成形良好的焊接接头。焊缝区域组织主要为柱状的B2相,柱状晶的生长方向垂直于熔合线。焊缝和热影响区的显微硬度要高于母材,焊缝的平均显微硬度最高。随着热输入的增加,焊接接头的室温抗拉强度增加,但是焊接接头的延伸率较低。焊接接头650℃高温强度为母材的71%~75%,塑性则仅为母材塑性的40%左右。经过焊后热处理,焊缝由B2+O相组成。O相增多使得焊缝的室温强度略有提高,且提高了650℃高温拉伸性能,高温抗拉强度最高可达母材的87.5%。     

双丝埋弧焊接头性能研究

在16Mn钢板上进行双丝自动埋弧焊工艺试验,得到了不同焊接速度下的焊件.对不同工艺参数下得到的焊接接头试样进行了拉伸试验、硬度测试以及金属显微组织观察,并计算了双丝自动埋弧焊时的熔敷率.结果表明:采用双丝埋弧焊得到的焊缝外形美观;金属熔敷率与焊接速度成反比;随着焊接速度的降低焊接线能量相应的增大,较长的高温停留时间会促...     

焊后热处理对输送H_2S介质压力管道维修焊接接头组织性能的影响

采用手工钨极氩弧焊(TIG焊)打底,焊条电弧焊(SMAW)填充、盖面的焊接工艺对输送H_2S介质压力管道(20钢)进行维修焊接,并对其焊接接头进行720～750℃下保温1h的焊后热处理.对热处理前、后焊接接头组织和性能进行分析研究,结果表明:720～750℃×1h热处理使焊缝区与热影响区成针状分布的魏氏组织铁索体晶粒得到细化,并使其呈退化形态;焊缝区、热影响区与母材的显微硬度整体呈下降趋势;焊接接头抗拉强度大幅度提高,断裂均处在远离焊缝的母材上.焊后热处理有效地降低了焊接接头的残余应力,改变了残余应力的分布特征,使其分布趋于"均匀",拉应力大幅度降低.     

焊后热处理对6063铝合金激光填丝焊接头组织与性能的影响

采用激光填丝焊对6063铝合金进行焊接,并对焊接接头进行人工时效和固溶+人工时效的热处理。通过光学显微镜、扫描电镜观察及拉伸试验,对焊后经不同热处理的焊接接头组织和性能进行研究。结果表明:未热处理的焊接接头抗拉强度为196 MPa,焊缝内部为铸态组织,弥散分布着Mg₂Si强化相,熔合线附近存在向焊缝内部生长的粗大柱状晶,焊缝内部为细小的树枝晶,焊缝中心为等轴晶;经时效处理后,焊接接头组织不均匀性和强化相的分布得到改善,焊接接头抗拉强度提高27 MPa;经固溶+时效处理的焊接接头抗拉强度提高64 MPa,焊缝组织、熔合区及热影响区组织得到显著细化。焊接接头均为韧脆混合断裂;时效处理的断口韧窝大小差异较大,韧窝较深;固溶+时效处理后的断口韧窝大小均匀,韧窝尺寸较大较深,韧窝数量更多。     

高速列车用耐候钢活性MAG焊接技术

提出了活性熔化极气体保护焊焊接新方法,获得了高质量的活性熔化极气体保护焊焊接接头.结果表明,活性熔化极气体保护焊焊缝表面成形好、活性焊接接头内部质量高、活性焊接操作性好、活性熔化极气体保护焊相对传统熔化极气体保护焊同等焊接热输入下熔深增加,焊接接头拉伸及弯曲力学性能不降低,同时焊接接头的冲击韧性得到提高,特别是活性焊接接头热影响区的冲击吸收功得到提升,焊接接头的断口韧窝尺寸更细小.活性熔化极气体保护焊可以提高耐候钢焊接质量,改善难熔结构焊接熔深,具有工程应用价值.     

铝合金/镀锌钢板脉冲MIG电弧熔-钎焊接头组织与性能

采用数字化脉冲MIG焊机,以ER4043焊丝为填充材料.实现了6013-T4铝合金薄板与镀锌钢板的熔-钎焊接,研究了焊接热输入对接头组织和性能的影响,结果表明,在熔-钎焊接头熔化焊缝焊趾处存在主要由Zn-Al共晶体、富A1的α固溶体和Fe3Al组成的富Zn区:钎焊界面上的Fe-Al金属间化合物层厚度在1.05-4.50μm之间.且随焊接热输入的增加而增大.Fe-Al金属间化合物呈"锯齿"或"舌"状向焊缝内生长,主要为FeAl₂,Fe₂Al₅和Fe₄Al₁₃.随着焊接热输入的增大,熔-钎焊接头的抗拉强度先增大而后减小.在850 J/cm的热输入下达到229 MPa,拉伸后在铝合金焊接热影响区发生断裂,为塑韧性断裂;当焊接热输入较小时接头在钎焊界面断裂,属于脆性断裂.     

Mechanical properties and microstructure of pure nickel PAW and PAW-TIG welded joints

A plasma arc welding( PAW)-tungsten inert gas( TIG) hybrid welding process is proposed. And this paper investigated the microstructure and properties of pure nickel N6 joints by PAW-TIG hybrid welding. Compared with the conventional PAW method,the characteristic of PAW-TIG welding process is that there is no interaction between the two arcs.The addition of TIG can enhance the intrinsic high-efficiency peculiarity and the stability of the keyhole status of PAW. The joints made using PAW and PAW-TIG,respectively,were subjected to microstructural evaluations and tensile testing so as to analyze the effect of TIG arc energy on the microstructure and mechanical properties of these joints. The results of this investigation indicate that significant grain coarsening was observed in the weld metal( WM) and heat affected zone( HAZ)and it is found that the extent of grain coarsening increased with the addition of TIG arc. And the microstructure in hybrid joint,with wider weld width and the smooth surface,is coarser than in PAW joint. Furthermore,the microhardness and ultimate tensile strength( UTS) of hybrid joint is slightly lower than that of PAW joint. The fractograph observation shows that the fracturing mechanism of PAW joints ductile,while the hybrid welding joints exists as brittle-ductile fracture mode. The outcome of this work shows that in the condition of same deposited rate,TIG arc post-weld heat treatment can improve the welding efficiency and welding speed. The proposed PAW-TIG hybrid welding process is demonstrated to be suitable for welding nickel and its alloys in industry application.     

PM-TZM钼合金电子束焊接特性

为研究PM-TZM钼合金电子束焊接特性,对其进行了电子束焊接试验,分别对接头显微组织及力学性能进行了分析. 结果表明,PM-TZM钼合金电子束焊缝呈“钉状”几何特征,熔合线附近有链状气孔出现. 焊缝区由粗大的等轴晶及柱状晶组成,热影响区晶粒相比于母材明显长大. 接头各区域硬度值不同,焊缝区硬度与母材相当,硬度最低值出现在两侧热影响区.PM-TZM合金电子束焊接接头有较大的性能损失. 接头室温最高抗拉强度378 MPa,为母材抗拉强度的47%,1 000℃抗拉强度168 MPa. 接头拉伸断裂均发生于焊缝区,呈典型的脆性解理断裂特征.     

焊后热处理对AA7075铝合金DP-MIG焊接接头组织及力学性能的影响

采用双脉冲熔化极精性气体保护焊（DP-MIG）工艺方法焊接AA7075-T651铝合金,焊接试板采用固溶处理（480℃×50 min）后水淬,再进行（80℃×24 h）+（120℃×24 h）两级人工时效热处理,通过金相观察、扫描电镜观察、X射线衍射分析、拉伸试验以及硬度测试,研究焊后热处理（PWHT）工艺对焊接接头显微组织及力学性能的影响.结果表明,焊缝区经热处理后,晶粒由枝晶向等轴晶转变,晶界处非平衡第二相溶解,晶界变细,焊缝显微组织特性改善明显;焊接接头经热处理后,抗拉强度由342.5 MPa提高到490 MPa,接头强度系数为0.872,焊缝软化区硬度得到较大改善,焊接接头力学性能有显著提升.     

高铌X80管道不同强度匹配环焊接头性能及应变演化

为探究管道环焊缝断裂失效机理,测试了两种不同强度匹配的高铌X80环焊缝接头的组织和性能,并借助数字图像相关法(digital image correlation,DIC)观测了焊接接头在拉伸载荷下的应变行为.结果表明,低强匹配和高强匹配的高铌X80管道环焊接头均具有较好的冲击韧性,二者的夏比冲击吸收能量平均值相当,热影...     

Effect of Heat Input on the Microstructure and Properties of Dissimilar Weld Joint Between Incoloy 28 and Superaustenitic Stainless Steel

Abstract This work focuses on studying the effect of welding heat input within the range from 1 to 5 kJ/mm on the microstructure and the corresponding mechanical and corrosion properties of dissimilar joint between superaustenitic stainless steel （UNS S31254） and Incoloy 28 （UNS N08028）. The two materials were butt-welded with ER NiCrMo3. The metallurgical changes associated with welding of SASS and Incoloy 28 were studied using optical microscope, SEM, and EDX. The mechanical and corrosion properties were investigated using tensile test, Vickers hardness test, and pitting and crevice corrosion tests. The weld metal microstructure showed precipitates with needle-like shape at 3 and 5 kJ/mm. Also, the microstructure showed unmixed zone （UMZ） at the fusion line of both SASS and Incoloy 28 sides at all the investigated heat inputs. The Mo microsegregation within UMZ at Incoloy 28 side increased as the heat input increased from 1 to 5 k J/ram but that in SASS increased with increasing heat input from 1 to 3 kJ/mm and then decreased with increasing from 3 to 5 kJ/mm. The ultimate tensile strengths for all specimens at all the investigated heat inputs are acceptable. The average hardness noticeably changed in weld metal as the heat input increased from 1 to 5 kJ/mm. Other zones such as HAZ or UMZ did not demonstrate marked changes in the average hardness. The pitting and crevice corrosion rates of the weld joint were found significant at l and 3 kJ/mm but insignificant at 5 kJ/mm according to ASTM G48.     

热输入对超薄443铁素体不锈钢组织性能的影响

针对443铁索体不锈钢焊接接头存在粗晶组织与性能脆化等问题进行研究,采用光学显微镜(OM)、扫描电子显微镜(SEM)分析了不同焊接方法焊后接头组织和性能的变化.采用钨极氩弧焊(TIG)、脉冲钨极氩弧焊(P-TIG)和脉冲激光焊(P-LBW)三种焊接方法进行焊接,分析了不同热输入对超薄443铁素体不锈钢焊接接头微观组织、拉伸性能和杯突性能的影响规律.结果表明,焊接热输入是影响该铁素体不锈钢焊接接头组织和性能的重要因素,采用脉冲焊接方法来细化组织可以有效提高焊接接头综合性能.     

Properties and structure of friction stir welded joints in 1424 and V-1461 (Al–Li) alloys*

The effect of the friction stir welding (FSW) conditions on the structure of welded joint and mechanical properties of 1424 and V-1461 alloys is investigated. FSW is accompanied by the formation of a recrystallized fine-grain microstructure in the welded joint. It is shown that the increase of the heat input to the welded sheets does not increase the average grain size in the weld zone (the average grain size is 1.5–2.2 μm). The tensile strength of the welded joints depends on the welding conditions for both alloys. Special features of the microstructure formed in the zone of the welded joint are discussed and the effect of the microstructure on the mechanical properties of the welded joints and evolution under the effect of heat treatment after FSW are determined.