铜材表面激光合金化和激光熔覆制备Ni/Cu-Cr3C2/Co梯度涂层

目的提高铜合金的表面硬度,改善其耐磨性能。方法利用激光表面合金化和激光熔覆工艺在铜合金表面制备出Ni/Cu-Cr_3C_2/Co梯度涂层。采用X射线衍射仪、扫描电镜及能谱仪,系统分析了合金化过渡层与熔覆层的物相构成及显微组织,通过硬度测试、摩擦磨损实验,对梯度涂层的显微硬度和耐磨性进行评估。结果合金化过渡层组织致密且具有单一柱状晶结构,主要由α-(Cu,Ni)固溶体、Ni_3Al和Ni Al构成。Cr_3C_2/Co复合熔覆层中分布着未熔Cr_3C_2颗粒,且以未熔Cr_3C_2颗粒为中心,四周有大量呈杆状(或针状)的M_(23)C_6和M_7C_3型碳化物,这种碳化物可以有效提高熔覆层的硬度。梯度涂层的显微硬度从基体的80HV逐渐增加到熔覆层的640HV,梯度涂层的摩擦磨损失重仅为铜合金基体的1/8。铜基体的磨损表面发生大规模破坏并形成大量磨屑,其磨损机制主要是粘着磨损;Cr_3C_2/Co喷涂层由于内部结合力较弱,出现了大量的疲劳磨损面,其磨损机制为表面疲劳磨损;而Ni/Cu-Cr_3C_2/Co梯度涂层的磨损表面比较平整,只存在轻微的"犁沟",其磨损机制为典型的磨粒磨损。结论梯度涂层由于Cr_3C_2、M_(23)C_6及M_7C_3相的存在,显微硬度和耐磨性能显著提高。同时,涂层的成分与性能均呈一定的梯度变化,改善了铜基体与涂层的相容性。     

激光熔覆Cr_3C_2-Ni复合涂层的减摩性能

以粉末化学镀法制备的Cr_3C_(2-)Ni复合粉末作为预置层,在Q235钢板表面用激光熔覆技术制备了减摩复合涂层.研究了Cr_3C_(2-)-Ni涂层在干摩擦条件下的减摩性能,并对磨损形貌进行了SEM观察,对涂层的硬度进行了测 试.结果表明,该涂层组织均匀致密、硬度较高;涂层的摩擦性能稳定,摩擦系数为0.44;硬质Cr_3C_(2-)粒子与金属粘结相的配合能有效提高熔覆层的承载能力,减小摩擦损失.     

TiN含量对Ni基感应熔覆涂层组织与性能的影响

采用高频感应熔覆技术在45钢表面制备了TiN增强Ni基合金涂层,利用OM、EDS、SEM和XRD分析了涂层的微观结构和化学组成;利用显微硬度计和摩擦磨损机研究了TiN添加量对涂层硬度和耐磨性的影响。结果表明:感应熔覆Ni基涂层无裂纹、气孔等缺陷出现,与基体达到了冶金结合;涂层主要为胞状树枝晶,由γ-Ni、Ni_2B、Cr_(23)C_6、CrB等构成;Ni基涂层的硬度较高,耐磨性能良好,随着涂层中TiN含量的增加,涂层的硬度增大,耐磨性增强;与不添加TiN的Ni基涂层相比,40%TiN+Ni基涂层的最大硬度值提高了37.3%,摩擦因数降低了48.3%,摩擦磨损质量损失减小了28.0%。     

热处理对超音速火焰喷涂NiCr-Cr_3C_2涂层组织及性能的影响

利用超音速火焰(HVOF)喷涂工艺在316L不锈钢表面制备NiCr-Cr_3C_2涂层。采用XRD、SEM、EDS、维氏硬度计、洛氏硬度计、摩擦磨损试验机等系统考察了不同热处理温度对NiCr-Cr_3C_2涂层组织结构、显微硬度及其分布、断裂韧性、结合强度以及耐磨性能的影响。结果表明:热处理可提高涂层结合强度。200～400℃,随温度升高,涂层显微硬度及耐磨损性能提高,并在400℃出现峰值,这源于固溶在NiCr合金相中的Cr_3C_2析出,形成大量细小二次碳化物硬质相,产生沉淀强化作用;高于400℃,涂层硬度下降,断裂韧性提高;1000℃热处理后,涂层结合强度降低。磨损试验表明:随热处理温度升高,磨损机制逐渐由磨粒磨损、疲劳磨损向磨粒磨损、黏着磨损转变。     

纳米WC增强Ni基合金喷熔层组织结构与抗磨粒磨损特性

目的研究纳米WC对Ni基合金喷熔层抗磨粒磨损性能的影响。方法采用扫描电镜、X射线衍射分析了氧乙炔火焰喷熔Ni基合金层和两种不同结构WC增强Ni基合金喷熔层的微观组织和相结构,并通过磨粒磨损试验平台对三种涂层进行磨损性能测试。结果纳米WC粉末的加入,能有效提高喷熔层的宏观硬度。通过组织分析得出纳米WC增强Ni基喷熔层中除含有γ-(Ni,Cr)固溶体、Cr的碳化物、硼化物以及微米级WC颗粒之外,还含有一定量的纳米WC团聚体和少量高硬度的W_2C相。磨粒磨损实验结果显示,纳米WC增强Ni基喷熔层的磨损失重分别为Ni60和NiWC35涂层失重的56%和73%。对比磨损后涂层的表面微观形貌可知,纳米WC颗粒在涂层中能有效降低磨粒压入喷熔层的深度,从而控制磨粒对喷熔层的犁削量。结论纳米WC增强Ni基合金喷熔层中含有的γ-(Cr,Ni)固溶体、Cr_(23)C_6、Cr_7C_3、Cr_3Ni_2及未熔化的WC颗粒和WC脱碳形成的W_2C等硬质相,使镍基自熔合金涂层的硬度有较大提高,同时也大大提高了涂层的抗磨粒磨损性能。     

基于激光熔覆的自润滑复合涂层制备及其性能研究

为了防止H13热作模具钢在使用过程中出现的磨损失效现象,使其在工作环境下(200℃)具有自润滑能力,在H13热作模具钢表面进行激光熔覆,成功制备了具有自润滑能力的Stellite 6-Cr_3C_2-WS_2复合涂层。研究了Stellite 6-Cr_3C_2-WS_2复合涂层对熔覆涂层表面性能的影响。对熔覆涂层分别进行了X射线衍射(XRD)分析、扫描电子显微镜(SEM)组织观察、能谱(EDS)分析、显微硬度测试和摩擦磨损试验测试,系统地研究了物相组成、微观组织、显微硬度和磨损性能等。试验结果表明:熔覆涂层在激光束照射下反应生成的主要物相有γ-(Fe, Co)、Cr_7C_3硬质相、(Cr, W)C碳化物和CrS自润滑相;熔覆涂层显微组织主要由平面晶和树枝晶构成;熔覆涂层硬度是基材硬度的2～3倍,表面摩擦因数为基材表面摩擦因数的65%。因此,热作模具钢H13表面的熔覆涂层的硬度和耐磨性均得到了很大的提高。     

感应熔覆铁基合金涂层的显微组织与性能

采用感应熔覆技术在奥氏体不锈钢1Cr18Ni9Ti基体上制备了Fe基合金涂层。利用带有能谱仪的场发射扫描电镜(FESEM)分析了熔覆层的显微组织形貌和元素组成,使用X射线衍射仪分析了涂层的物相组成,采用差热分析仪对合金粉末进行了热分析,用显微硬度计和摩擦磨损试验机测试了涂层的显微硬度及干摩擦条件下的滑动磨损性能。结果表明,感应熔覆铁基合金涂层组织致密,内部和界面无孔隙,涂层与基体形成了良好的冶金结合;涂层主要由α-Fe、(Cr,Fe)_7C_3、Cr_7C_3、Ni_3Fe和Fe_3C等组成,且α-Fe中均匀分布颗粒细小的(Cr,Fe)_7C_3、Cr_7C_3析出相;涂层显微硬度约为250HV_(0.1);在不同载荷下,感应熔覆Fe基合金涂层的耐磨损性能均优于1Cr18Ni9Ti基体,涂层磨损机理为典型的层状剥落和粘着磨损。     

Ti-6Al-4V表面电子束熔覆(Ti,W)C1-x复合涂层的形成及摩擦性能

通过高能电子束熔覆技术,利用WC-10Co粉末在Ti-6Al-4V (TC4)合金表面制备了(Ti, W)C_(1-x)复合涂层。采用SEM、EPMA和XRD等手段对不同熔覆电流下复合涂层的显微组织和相组成进行了分析,讨论了各相的形成机理;采用显微硬度计和球盘摩擦实验设备对复合涂层的显微硬度和摩擦性能进行分析,讨论了不同熔覆电流下复合涂层的摩擦机理。结果表明,3种复合涂层中WC粉末均全部分解,涂层由α-Ti、β-Ti、树枝状和块状(Ti, W)C_(1-x)及少量W组成。复合涂层厚度为400～600μm,涂层与基体结合性良好。与基体相比,(Ti, W)C_(1-x)复合涂层的平均硬度和耐磨性提高2～3倍且随熔覆电流增加而降低,在熔覆电流为12 mA时,表面显微硬度最高为860 HV;熔覆电流为12和15 m A时摩擦机理分别为轻微磨粒磨损和严重的磨粒磨损,而18 mA时还伴随着少量疲劳磨损。     

添加CeO_2对MoS_2基复合涂层摩擦学性能的影响

针对MoS_2基复合涂层耐磨性差和承载能力低的问题,以不同含量(质量分数)的CeO_2作为添加剂,采用喷涂法在GCr15钢表面制备MoS_2基复合涂层。利用摩擦磨损试验机和划痕仪分别研究涂层摩擦磨损性能和结合强度,并借助金相显微镜对涂层磨损形貌进行表征。结果表明:添加适量CeO_2可以改善涂层的摩擦磨损性能,其最佳含量为2%,此时摩擦因数和磨损量均最小,分别为0.232和0.011 3 mm~3;同时结合强度从22 N提高到28.29 N。涂层磨损量随载荷的增大而增大;而载荷小于8 N时,涂层的摩擦因数随载荷的增大而减小,当载荷大于8 N时,摩擦因数又有回升趋势。添加稀土后涂层的承载能力有明显提高。未添加稀土时,涂层产生严重剥离,并发生磨粒磨损;添加2%CeO_2后,涂层发生轻微磨粒磨损,耐磨性得到显著提高。     

纳米Al2O3对Ni基合金激光熔覆层干滑动磨损性能的影响

在18-8不锈钢上激光熔覆制备了纳米a-Al2O3+Ni基合金复合涂层;考察了纳米Al2O3含量对Ni基合金熔覆层的组织、硬度及干滑动摩擦磨损性能的影响.结果表明,Ni基合金中添加适量的纳米颗粒可使激光涂层的硬度增加,耐干滑动摩擦磨损的抗力提高,其中以较少纳米Al2O3添加量(1wt%)的涂层硬度和耐磨性的改善较为明显.     

等离子喷涂与超音速火焰喷涂NiCr-Cr3C2涂层组织与摩擦磨损性能研究

目的 研究等离子喷涂与超音速火焰喷涂NiCr-Cr3C2涂层的组织、力学性能和摩擦磨损性能。方法 采用等离子喷涂与超音速火焰喷涂工艺制备NiCr-Cr3C2涂层,并采用X射线衍射仪（XRD）、扫描电镜（SEM）、万能试验机、显微硬度计和高速往复摩擦磨损试验机,系统地分析了两种工艺所得涂层的物相、组织、结合强度、硬度及摩擦磨损性能。结果 两种工艺制备的NiCr-Cr3C2涂层与基体界面结合效果良好。等离子喷涂NiCr-Cr3C2涂层为层片状组织,层间可见微裂纹,孔隙率较高;超音速火焰喷涂NiCr-Cr3C2涂层组织均匀,无明显微裂纹,可见少量微小孔隙。物相分析表明,等离子喷涂涂层由NiCr、Cr3C2和Cr7C3相组成,而超音速火焰喷涂涂层由NiCr和Cr3C2相组成。超音速火焰喷涂NiCr-Cr3C2涂层的耐磨性优于等离子喷涂涂层,等离子喷涂涂层和超音速火焰喷涂涂层的稳态摩擦系数分别为0.4和0.6。随载荷升高,两种工艺制备的NiCr-Cr3C2涂层摩擦系数均显著下降。磨损后,等离子喷涂NiCr-Cr3C2涂层表面具有明显的凹痕和剥落,而超音速火焰喷涂NiCr-Cr3C2涂层磨痕表面较光滑,未见明显剥落。两种工艺制备的涂层磨损机制均为磨粒磨损和疲劳磨损。结论 超音速火焰喷涂NiCr-Cr3C2涂层较等离子喷涂涂层组织更为致密,具有更为优良的综合力学性能和耐磨性,等离子喷涂制备的NiCr-Cr3C2涂层的减摩性较好。     

超音速等离子喷涂NiCr-Cr3C2涂层的结构及冲蚀磨损机理

目的改善流体机械部件的耐冲蚀磨损性能。方法采用超音速等离子喷涂(Supersonic Plasma Spraying)系统制备NiCr-Cr_3C_2涂层,通过X射线衍射仪(XRD)分析了喷涂粉末和涂层的物相结构。采用扫描电子显微镜(SEM)及配套的能谱分析仪(EDS)观察和分析了涂层的微观形貌及化学成分。采用透射电子显微镜(TEM)从超微观角度分析了涂层的晶粒结构。采用Image J2x孔隙率计算软件测定了涂层的孔隙率。采用显微硬度仪、纳米压痕仪及万能拉伸试验机分别测定了涂层的显微硬度、弹性模量和结合强度。采用动载磨料试验机进行了冲蚀试验,冲蚀角度为90°,砂浆比为5:8,冲蚀时间为3 h。结果获得的超音速等离子喷涂Ni Cr-Cr_3C_2涂层主要含有NiCr、Cr_3C_2、Cr_7C_3等物相,至少含有单晶、纳米晶、过渡区三个区域。涂层的显微硬度值为911HV0.3,约为基体的3倍,孔隙率为1.4%,结合强度为66 MPa,弹性模量为215.3 GPa。在90°攻角下,涂层的冲蚀磨损失效以疲劳剥落磨损为主。结论用超音速等离子喷涂系统在基体表面制备的Ni Cr-Cr_3C_2涂层具有较好的耐冲蚀磨损性能。     

Improvement of the oxidation and wear resistance of pure Ti by laser cladding at elevated temperature

NiCrBSi and NiCrBSi/WC-Ni composite coatings were produced on pure Ti substrates by the laser cladding technology. Thermal gravimetric (TG) analysis was used to evaluate the high temperature oxidation resistance of the laser cladding coatings. The friction and wear behavior was tested through sliding against the Si₃N₄ ball at elevated temperatures of 300 °C and 500 °C. Besides, the morphologies of the worn surfaces and wear debris were analyzed by scanning electron microscopy (SEM) and three dimensional non-contact surface mapping. The results show that the microhardness, high temperature oxidation resistance and high temperature wear resistance of the pure Ti substrates are greatly increased. For the pure Ti substrate, the wear behavior is dominated by adhesive wear, abrasive wear and severe plastic deformation, while both laser cladding coatings, involving only mild abrasive and fatigue wear, are able to prevent the substrates from severe adhesion and abrasive wear. In particular, the laser cladding NiCrBSi/WC-Ni composite coating shows better high temperature wear resistance than the NiCrBSi coating, which is due to the formation of a hard WC phase in the composite coating.     

激光熔覆TiC增强FeAl金属间化合物基复合材料涂层磨损性研究

利用激光熔覆技术在1Cr18Ni9Ti奥氏体不锈钢表面制得了以TiC为增强相、以FeAl 金属间化合物为基体的耐磨复合材料涂层，研究了激光熔覆。FiC／FeAl复合材料涂层在干滑动磨损条件下的耐磨性能及磨损机制。结果表明：随着载荷和滑动速率的增加，TiC／FeAl金属间化合物基复合材料涂层的磨损速率增加，其磨损机制随着载荷的增加逐渐由磨料磨损向粘着磨损转变；激光熔覆层中TiC体积分数的增加，一方面提高了涂层的磨料磨损抗力，另一方面降低了熔覆层表面与对磨材料之间的粘着倾向，提高了TiC／FeAl涂层的滑动磨损性能。激光熔覆TiC/FeAl金属间化合物基复合材料涂层具有优异的耐磨性能并随TiC体积分数的增加而提高。     

20Cr2Ni4A钢表面WC增强铁基涂层耐磨性能的研究

目的 制备优异的耐磨性涂层用于机械零部件表面,可有效地提高其使用寿命,减少机械设备因磨损失效而带来的各类故障.方法 以20Cr2Ni4A合金钢为基体材料,利用激光熔覆技术,制备了铁基涂层和铁基/WC复合涂层.采用X射线衍射仪(XRD)、金相显微镜、扫描电子显微镜(SEM)、HV-1000显微维氏硬度计,分别对铁基涂层和铁基/WC复合涂层的相组成、组织形貌、显微硬度进行表征.利用HRS-2M型高速往复摩擦磨损试验机对铁基涂层和铁基/WC复合涂层的磨损性能进行研究,并分析其磨损机理.结果 两种涂层的显微硬度与基体相比改善较大,其中铁基/WC复合涂层改善最为明显,表面平均硬度值为610HV.以直径为6 mm的GCr15对磨球为摩擦副,铁基涂层的平均摩擦因数为0.53左右,磨损量为0.1432 mm3,而铁基/WC复合涂层的平均摩擦因数为0.36左右,磨损量为0.05935 mm3,与铁基涂层相比,20Cr2Ni4A合金钢表面结合铁基/WC复合涂层的硬度提高了17％左右,磨损量减小了58.6％,具有良好的耐磨损性能.结论 铁基/WC复合涂层因其表面存在W2C、WC、Fe3C等物相,能够均匀分布在铁基涂层上作为耐磨骨架,显著提高了涂层的硬度和耐磨性能.     

碳化铬基金属陶瓷电火花沉积涂层的微观组织与性能

采用电火花沉积分别制备了碳化铬基金属陶瓷单涂层和碳化铬基金属陶瓷/Ni复合涂层。采用X射线衍射仪(XRD)、扫描电镜(SEM)、显微硬度计和摩擦磨损试验机对比研究了单涂层和复合涂层的物相、微观组织结构、显微硬度和摩擦磨损性能。结果表明,两种涂层组织结构致密,与基体呈良好的冶金结合,并在涂层内形成了纳米晶的微观组织。复合涂层中FeCr_0.29Ni_0.16C_0.06韧性相含量增加,在涂层界面处存在过渡层Ni,并以塑性变形的方式释放了更多沉积时产生的热应力,因而涂层裂纹明显减少。复合涂层的峰值硬度(1186HV_0.05)虽略低于单涂层,但该涂层具有最小的摩擦系数(0.2462),1h磨损量仅为单涂层的1/3,因此表现出更好的耐磨性能,其主要磨损机制为磨粒磨损和疲劳磨损。     

Properties and tribological performance of ceramic-base chromium and vanadium carbide composite coatings

In the current study, the surface of AISI D2 steel was coated with the powder blends of ferro-vanadium (Fe-V) and ferro-chromium (Fe-Cr). The coatings were performed using a thermo-reactive diffusion (TRD) treatment by the pack cementation method at three different temperatures (900 °C, 1000 °C, and 1100 °C) and three different durations (1 h, 2 h, and 3 h). The structural and mechanical characteristics of the coatings were compared between the treatment groups. For this aim, the types of the formed phases, the microstructure, the microhardness, the surface roughness, and the wear and friction performance of the coated samples were examined. XRD analysis found composite carbide coatings including chromium carbide (Cr-C), vanadium carbide (V-C), and chromium vanadium carbide (Cr-V-C). The coatings' thickness was 11.3–23.2 μm, hardness was 2100–2500 HV, and average surface roughness (R_a) was 0.286–0.550 μm, depending on the treatment condition. The vanadium containing phase contents of the coatings increased with the elevating coating temperatures. The formed composite coating layers caused a change in the appearance of wear track and wear mechanism on the material surface. After the coating process, there found to be a decrease in the friction coefficient as well as an improvement in the wear resistance up to 7 times. In the composite coating layers, the increase in V-C content in comparison to Cr-C led to an enhancement in wear resistance on the material surface.     

电流密度对喷射电沉积Co-Ni-Cr3C2复合镀层组织及性能的影响

目的研究不同电流密度下,Co-Ni-Cr3C2纳米复合镀层中纳米Cr3C2的含量变化及其对组织性能的影响,确定最佳电流密度。方法采用喷射电沉积的方法,选择不同电流密度(30、40、50、60 A/dm^2)制备Co-Ni-Cr3C2纳米复合镀层。利用SEM、XRD、显微硬度计、摩擦磨损试验机、3D测量激光显微镜对Co-Ni-Cr3C2纳米复合镀层的形貌、成分、结构、硬度和耐磨性能进行研究,并对Co-Ni-Cr3C2纳米复合镀层和Co-Ni合金镀层在不同退火温度下的硬度变化进行比较。结果纳米Cr3C2颗粒的加入未明显改变Co-Ni的异常共沉积,在电流密度为40A/dm^2时,Co-Ni-Cr3C2纳米复合镀层中Cr3C2纳米颗粒的质量分数最高,为12.05%。复合镀层表面凹凸不平,呈瘤状结构。电流密度的增加对复合镀层的成分及相结构影响不大,出现了Co和Cr3C2的衍射峰。Co-Ni-Cr3C2纳米复合镀层的硬度随电流密度的升高,先增大后减小,在电流密度为40 A/dm^2时,硬度最高,为585HV0.05。复合镀层的摩擦系数在电流密度为30、60 A/dm^2时波动较大,在40、50 A/dm^2时波动较小。其磨损体积随电流密度的升高,先减少后增加,在40 A/dm^2时,磨损体积最小。Co-Ni-Cr3C2纳米复合镀层硬度随退火温度的升高,先升高后降低,在退火温度为400℃时,显微硬度最高,为602HV0.05。结论Co-Ni-Cr3C2纳米复合镀层在电流密度发生变化时,其Cr3C2纳米颗粒的沉积量、硬度及耐磨性均发生了变化,在电流密度为40A/dm^2时,沉积量最高,硬度和耐磨性能最佳。此外,Co-Ni-Cr3C2纳米复合镀层在高温退火条件下仍能保持较高的硬度。     

1Cr18Ni9Ti 不锈钢表面电火花熔覆 WC 涂层特性研究

目的研究1Cr18Ni9Ti不锈钢经电火花强化后,WC涂层的显微组织和性能。方法采用电火花熔覆技术在不锈钢1Cr18Ni9Ti基体表面制备WC熔覆层,并分析熔覆层的表面形貌、显微组织、显微硬度、耐磨性,采用线性极化法研究熔覆层在3.5%(质量分数)Na Cl腐蚀溶液中的耐腐蚀性能。结果熔覆层组织均匀、连续、致密,与基体呈冶金结合。显微硬度最大值达到1680HV0.3,平均值为1336HV0.3,比不锈钢基材提高了4倍,耐磨性是不锈钢基材的4倍。在3.5%Na Cl腐蚀溶液中,熔覆层的自腐蚀电位较不锈钢减小了约165 m V,击破电位低于不锈钢基材,维钝电流密度高于不锈钢基材。结论熔覆层具有高硬度和高耐磨性能,磨损机理主要是粘着磨损和磨粒磨损,但在3.5%Na Cl腐蚀体系中,耐腐蚀性能低于1Cr18Ni9Ti不锈钢。     

热处理对TA2合金表面激光熔覆Ti2SC/TiS涂层组织和力学性能的影响

目的对激光熔覆自润滑耐磨涂层进行热处理,获得具有较好摩擦学性能的复合涂层。方法采用激光熔覆技术在TA2合金表面熔覆40%Ti-25.2%TiC-34.8%WS_2复合粉末制备自润滑耐磨复合涂层。将涂层置于500℃真空中分别保温1、2 h,采用扫描电镜(SEM)、X射线衍射仪(XRD)、能谱仪(EDS)、显微硬度计、摩擦磨损试验机以及原子力显微镜(AFM)系统地分析了热处理前后涂层的物相、组织、显微硬度及摩擦学性能。结果未经过热处理和经过热处理涂层的主要物相均为α-Ti、(Ti,W)C_(1-x)、TiC、Ti_2SC和TiS。相比未经热处理涂层的显微硬度(1049.8 HV_(0.5)),经过热处理1 h和2 h涂层的显微硬度(1143.3 HV_(0.5)和1162.7 HV_(0.5))有所上升。热处理1 h和2 h涂层的摩擦系数和磨损率分别为0.29和6.66×10~(-5) mm~3/(N·m)以及0.29和5.65×10~(-5) mm~3/(N·m),比未热处理涂层(0.32和18.92×10~(-5) mm~3/(N·m))的耐磨减摩性能有所提升。经过热处理1 h和2 h涂层的磨损机理均主要表现为磨粒磨损,未经热处理涂层的磨损机理主要为塑性变形和粘着磨损。结论相比未经热处理的涂层,经过热处理1 h和2 h的涂层显微硬度有所升高,摩擦学性能得到提升,但在两种热处理时间条件下,涂层显微硬度和摩擦学性能变化较小。