激光填丝焊接超薄不锈钢工艺研究

对0.2 mm厚的1Cr18Ni9Ti奥氏体不锈钢薄板脉冲激光填丝焊相关的工艺参数对焊缝成形质量的影响进行了研究,分析了焊接接头的组织和力学性能,比较了填丝与非填丝两种情况下获得的焊缝成形质量。结果表明:激光填丝焊相对于非填丝焊有更好的焊缝成形质量;抗拉强度较非填丝焊接接头强度提高了3%,可达到母材抗拉强度的99%;在最佳焊接工艺参数下激光填丝焊接接头的显微组织是由焊缝中心区的等轴晶区和焊缝边缘细小的柱状晶区组成;采用激光填丝焊接超薄不锈钢可为解决非填丝焊焊接接头的凹陷问题提供参考。     

轿车电控喷油器脉冲激光焊研究

研究了轿车电控喷油器喷孔零件的脉冲激光焊工艺参数特征,详细分析了脉冲激光焊焊缝的组织特征,主要为奥氏体枝晶和等轴晶,焊缝边界处枝晶结晶方向垂直于熔合线指向焊缝中心,到焊缝中部枝晶的结晶方向变得杂乱,开始出现等轴晶。部分焊缝组织晶粒特征有明显的分层现象,通过分析脉冲激光焊重叠度和熔池液态金属的流动特性,解释了晶粒特征的分层现象。随着脉冲峰值功率密度的加大,焊缝容易出现根部气孔、塌陷、裂纹等缺陷。     

哈氏合金薄板激光填丝焊与TIG填丝焊焊缝微观组织及显微硬度分析

针对屏蔽电机核主泵屏蔽套高质量焊接要求,对厚度0.7 mm的Hastelloy C-276薄板分别进行了激光填丝焊和TIG填丝焊试验,对比了2组焊缝在成形形貌、显微组织、显微硬度等方面的异同。结果表明:激光焊焊缝较TIG焊焊缝均匀稳定、熔宽小,两者焊缝成形均无咬边、裂纹、气孔等缺陷;激光焊和TIG焊焊缝组织均以枝晶为主,由焊缝熔合线到焊缝中心依次为平面晶、柱状枝晶及等轴枝晶,但激光焊焊缝显微组织尺寸仅为TIG焊焊缝组织的50%左右;激光焊焊缝纵向显微硬度约HV282,横向显微硬度约HV290;而TIG焊焊缝纵向显微硬度约HV267,横向显微硬度约HV292。     

填充焊丝对6A02铝合金光纤激光焊接接头组织性能的影响

采用ER4043焊丝开展了1.0 mm厚6A02铝合金的光纤激光填丝焊接,对比分析了是否填丝对焊缝横截面形貌、接头组织、显微硬度分布和拉伸性能的影响.结果表明,激光填丝焊缝成形饱满,能够显著提高焊前装配的最大间隙容忍裕度.与自熔激光焊接接头相比,激光填丝焊接接头熔合区附近的柱状晶组织和焊缝中心的混合组织（柱状晶+等轴晶）均相对粗化,接头软化现象更加明显,焊态时接头抗拉强度基本相当,仅达到母材水平的83.2%,但经历固溶时效热处理后,接头强度得以恢复,并高于母材水平,断后伸长率获得显著改善,可以达到21.29%,远高于前者的8.13%.     

PLC控制激光焊接2524铝合金接头的组织研究

采用PLC控制激光焊接工艺参数对2524铝合金进行了焊接处理,研究了激光功率、焊接速度和送丝速度对2524铝合金焊接接头热裂纹倾向和显微组织的影响。结果表明,随着激光功率的增加,焊接接头的裂纹总数量呈现不断增加的趋势;焊缝中心为等轴树枝晶组织,而靠近熔合线附近为柱状晶组织,焊缝中心的平均晶粒尺寸和靠近熔合线附近的焊缝柱状晶间距均增大;随着焊接速度的增加,焊接接头的裂纹总数量不断增加,热裂纹倾向加大,且焊缝区域的熔宽和焊缝面积减小;随着送丝速度的增加,焊接接头的裂纹总数量降低。采用填充焊丝的焊接工艺后,焊缝的成形性相对自熔焊接更好,且焊缝面积明显增大。     

AZ31镁合金CO2激光填丝焊工艺

采用CO2激光焊接试验系统,对AZ31镁合金的激光填丝焊工艺进行了研究.试验中采用AZ31焊丝作为填充金属,对各种焊接工艺参数的影响进行了较系统地研究,并获得了较好的工艺参数选择范围.焊后对典型的焊接接头的性能进行了研究,结果表明,在适当的填丝速率下,填丝焊工艺形成的焊缝成形更加美观,克服了不填丝焊接情况下焊缝的严重下塌问题.微观组织分析表明,焊接接头区域主要由细小的枝状晶组成,晶粒明显细化.焊接接头的显微硬度和抗拉强度都接近母材,说明获得的焊缝具有较好的力学性能.表明了CO2激光填丝焊工艺是实现AZ31镁合金焊接的有效方法.     

铝锂合金激光填丝焊接接头组织性能研究

利用激光填丝焊接方法对5A90铝锂合金薄板焊接头的组织性能进行了研究。结果表明:激光填丝焊接头的主要组织特征为细晶层和焊缝区大范围等轴晶,与激光焊接头类似,而不同之处表现为激光填丝焊接头的显微组织相对细化,柱状晶区范围相对减小。激光填丝焊缝区硬度HV0.2(925.7MPa)略低于激光焊缝区硬度(956.5MPa),但前者硬度分布更加均匀。激光填丝焊接头的抗拉强度稍低于激光焊接头,分别达母材的79.22%和73.03%,但其断后延伸率却显著高于后者,分别达母材的38.65%和20.38%。综上所述,5A90铝锂合金激光填丝焊接头的组织性能略优于激光焊接头,若使激光填丝焊接头的综合力学性能达到使用要求,不仅需要焊后热处理强化,还需要与母材匹配性更好的焊丝。     

焊丝熔化方式对激光焊接过程的影响

研究了两种焊丝熔化方法(电弧预熔丝激光焊、激光填丝焊)激光焊接过程对匙孔稳定性以及焊缝成形的影响，进一步研究了焊丝熔化方法对焊接接头质量的影响，并对比分析了两种焊丝熔化方式对焊接速度的适应性. 结果表明，电弧预熔丝激光焊过程中，熔池表面匙孔开口尺寸变化不大，匙孔较为稳定；激光填丝焊方法由于熔化的液态金属距离匙孔边缘很近，焊接过程中熔池表面匙孔开口尺寸变化较大,而且容易出现熔池表面匙孔的闭合. 与激光填丝焊相比，电弧预熔丝激光焊熔化的焊丝端部可以沿熔池边缘流入，与匙孔边缘的距离较远，匙孔稳定性较好，焊缝气孔数量较少. 当焊接速度为8 m/min时，电弧预熔丝激光焊的焊缝成形良好；而激光填丝焊焊缝背面成形不连续，并且出现了未焊透的缺陷.     

铝合金厚板电子束焊接头组织与特征

研究了2519铝合金厚板电子束焊接头组织分布特征,并进一步研究电子束焊过程中熔池金属的流动及凝固。结果表明:焊缝由枝晶和等轴晶组成,但其沿熔深方向焊缝中心和焊缝靠近熔合线区域存在明显组织不均匀性;沿焊缝中心的上部和中部为等轴枝晶,根部则以等轴枝晶和等轴晶混合存在;靠近熔合线边缘的焊缝自上而下分别为树枝晶、柱状晶、等轴晶,晶粒生长的方向性逐渐减弱;越接近焊缝根部,其晶粒尺寸和分布越不均匀,焊缝根部晶粒沿熔池金属凝固分层轮廓线分布,且存在微裂纹等缺陷。这些现象反映出焊接过程中熔池各区域内的焊接能量和金属流动性差异显著。     

薄板2524铝合金激光填丝焊接工艺及组织性能

2524铝合金是具有优异损伤容限的新型航空高强Al-Cu-Mg合金.采用高功率光纤激光器焊接1.6 mm厚2524铝合金,研究了填充5087焊丝情况下,激光功率、焊接速度和填丝速度对焊缝成形、热裂纹倾向和焊缝显微组织的影响,优化焊接工艺参数,考察接头静态拉伸性能.结果表明,采用填充材料后,焊缝柱状枝晶生长方向性明显减小、晶粒细化、晶界共晶增多、热裂纹倾向降低.当激光功率为2.5 kW,焊接速度为2 m/min,填丝速度为2 m/min时,可获得成形良好、无缺陷的焊缝,接头抗拉强度达到313~324 MPa,拉伸断裂于接头熔合线附近,断口处有大量韧窝,呈韧性断裂特征.     

铝合金液态填充焊的工艺特性分析

采用高速摄像和工艺试验相结合的方法分析了液态填充焊的影响因素,进行了焊接接头质量分析.结果表明,激光液态填充焊有两种填充模式:焊丝半熔态、焊丝全熔态.焊接电流较小时,焊丝为半熔态,液态填材顺焊丝流向熔池;焊接电流较大时,焊丝为全熔态,依靠间隙的毛细作用,能稳定的流入熔池中.随着焊接速度的提高匙孔距熔池边缘的距离变小.为了使液态填材稳定的过渡到熔池中,光丝间距应控制在-0.5~2.0 mm范围内.经过接头质量分析发现:与激光填丝焊相比,液态填充焊接焊缝中的气孔率明显降低.     

镁合金低脉冲激光-气体混合焊的熔池形貌演变和多级调控

利用基于COMSOL Multiphysics的脉冲激光-气体钨极电弧（GTA）混合焊接新型双热源模型,分析了焊缝沿线选定点的温度分布,研究了激光脉冲参数和电弧电流对熔池形貌的影响。工艺参数对熔池深度的影响由大到小为：激光激励电流>电弧电流>激光脉冲宽度>激光脉冲频率;工艺参数对熔池宽度的影响由大到小为：电弧电流>激光脉冲宽度或激光激励电流>激光脉冲频率。在此基础上,构建了激光诱导电弧焊接镁合金熔池形貌数据库体系,通过复合热源参数的分级调控,以实现对熔池形貌的精准控制。利用T形焊接熔池来验证熔池形貌的调控效果,结果表明控形的准确度高至95.1%。     

Microstructural and mechanical characteristics of laser welding of Ti6Al4V and lead metal

Titanium alloy Ti6Al4V and lead metal were welded using a continuous wave Nd:YAG laser. The influences of laser power, scanning velocity, and laser beam offset on weld morphology were investigated. Microstructure, chemical composition and mechanical properties of the joints were evaluated. Experimental results showed that fusion weld formed at the upper part of the weld and brazing weld with solder of Pb formed at the lower part of the weld under appropriate process condition. Interfaces were formed between mixed fusion zone and liquid lead zone in molten pool during laser welding of Ti6Al4V and lead. Reasons for interface formation may be different driving force of various regions in molten pool, and the miscibility gap of Ti and Pb binary system. Ti-Pb intermetallic compound Ti₄Pb was detected at the fusion weld zone, which made the microhardness of the weld seam was higher than that of the base materials. The strength of the joint was at least equal to or larger than that of lead base material.     

脉冲激光-电弧复合焊接镁合金过程中熔池行为与气孔产生的关系研究

激光-电弧复合焊接镁合金过程中气孔是一种重要缺陷。本文针对复合热源焊接过程中熔池行为和激光匙孔引起的气孔之间的关系进行了实验研究。研究中重点考查了激光脉冲对熔池的冲击作用，匙孔的动态行为以及气孔的形成规律。研究结果表明激光脉冲的参数决定其对液态熔池的冲击作用，较强的激光脉冲作用可以有效抑制气孔的形成；液态金属的行为主要有匙孔行为主导；匙孔的尺寸和开-闭状态直接影响焊后气孔的形成；过高的激光脉冲功率会导致焊后气孔的形成；匙孔开口维持时间越长，焊后气孔数量越少。     

高速激光热丝钎焊表面成形质量的控制

高速激光钎焊会引起熔池流动紊乱导致焊缝成形质量恶化,从而限制了其在汽车制造领域的应用。通过正交试验研究了高速下激光功率、送丝角度等工艺参数对焊缝成形质量的影响,发现焊缝成形质量随激光功率增加和送丝角度减小而提升。激光功率是通过影响熔池获得的热输入,从而影响熔池表面扰动的铺展来影响焊缝成形质量的。送丝角度是通过影响焊丝送入熔池的位置,从而影响焊丝对熔池的扰动强度和扰动的铺展速度来影响焊缝成形质量的。采用正交试验获得的最优工艺参数组合进行试验,获得了表面光滑平整无缺陷的高质量焊缝,为激光钎焊在高速下的应用发展奠定了基础。     

Homogenisation of chemical composition and microstructure in laser filler wire welding of AA 6009 aluminium alloy by in situ electric current stirring

Owing to the rapid cooling rates, the deposited and base metals could be mixed incompletely during laser welding of Al alloys in most cases. The objective of this research is to explore a possible method to promote the mixing of materials inside the molten pool by making use of the magnetofluid dynamic effect of electric current. Full penetration CO₂ laser welding of 3?mm thick alloy 6009 sheets was performed with an external electric current simultaneously into the weld pool via a filler wire. It is found that the deposited metal is mainly concentrated on the upper part of the weld fusion zone, and the weld zone microstructure is non-uniform without the electric current addition. With the application of an electric current, the weld fusion zone geometry is reshaped, and the chemical composition and microstructure of the weld metal are homogenised. The mechanism is found to be electromagnetic force stirring of the molten pool.     

Effect of pulse parameters on microstructure of joint in laser beam welding for SiC_p/6063 composite

1　INTRODUCTIONSiC particlesreinforcedcomposites ,thankstotheirlowcostsandhighlevelofstructuralproperties ,areshowingtheirpotentialincivilandmilitaryappli cation .SiC particlesreinforcedaluminummatrixcomposites wideapplicationinaerospaceandautomo tiveareattributedtotheirperformanceofhighspecif icstrength ,highspecificstiffness ,highelasticmodu lusandexcellentwearresistance .Thecoefficientofthermalexpansionandthermalconductivitycanberegulatedbychangingthecontentandsizeofrein forcingparticl…     

激光液态填充焊的填材熔化与过渡稳定性

针对激光填丝焊过程中焊丝对入射激光能量的反射、匙孔不稳定等问题,提出了激光液态填充焊方法,采用电弧提前预熔焊丝,让填材以液态方式流入熔池中.分析了激光液态填充焊的熔化、过渡模式,以及工艺参数对过渡模式的影响规律.结果表明,在电弧热作用下焊丝有液桥过渡和滴状过渡两种模式,焊接电流较小时,焊丝的上部熔化,下部依然保持固态,形成稳定的液桥过渡;焊接电流较大时,焊丝端部全部熔化易回缩成球为滴状过渡,过渡稳定性变差.为改善滴状过渡的稳定性,可依靠间隙的毛细作用稳定流入熔池中.激光液态填充焊可降低对匙孔的冲击,提高匙孔的稳定性.     

超塑成形对GH4169合金激光焊接组织的影响

采用激光连接/超塑成形组合技术制造了GH4169合金三层板结构件,研究了超塑成形(温度965℃,成形时间130min)对GH4169高温合金激光焊接组织的影响.试验结果表明:GH4169高温合金激光焊接组织主要由树枝晶构成,枝晶间中有Nb元素偏聚现象,即形成了一种金属间化合物Laves相;焊接组织在超塑成形后,焊缝中心出现了粗大的等轴晶粒,熔合线附近的柱状晶粒变得粗大,成形后大部分Laves相转变为δ相,但仍有少部分Laves相保留了下来;成形后焊缝的维氏硬度明显提高,由成形前的331.63HV0.1提高到391.74HV0.1,接近成形后母材的硬度415.63.超塑成形对GH4169高温合金激光焊接组织有明显的改善作用.