一种Al-Cu-Mg-Ag合金欠时效态的耐热性能

研究了欠时效态(165℃,2 h)Al-Cu-Mg-Ag合金在热暴露、高温持久过程中组织与性能的变化.结果表明,试样在200℃,200 MPa高温持久下,随时间延长,其剩余强度先上升后下降,强度峰值出现在持久20 h.延伸率变化与强度变化基本相似.持久100 h后,合金力学性能相对欠时效态无明显下降,显示出优良的热稳定性;合金欠时效状态的组织为细小分布的Ω相,随着高温持久时间的延长,θ'相与Ω相竞争析出.无析出带(PFZ)逐渐增宽,同时发现晶界上有颗粒状析出物.在200℃热暴露下,其剩余强度的变化趋势与高温持久相同,但延伸率随时间延长而下降,其组织为过时效组织.     

Al-Cu-Mg-Ag合金的高温力学性能

利用高温短时拉伸试验、扫描电镜和透射电镜等分析手段,研究了经165℃×2 h时效处理的Al-Cu-Mg-Ag合金在不同温度下的显微组织和力学性能.结果表明:随着温度的升高,强度逐渐下降,而伸长率先降后升.在200℃时合金具有最低的伸长率(12%),在温度高于200℃时,合金强度下降较快.当温度升至350℃时,抗拉强度、屈服强度分别降至105 MPa、98 MPa,伸长率增至23%.在高温条件下,该合金力学性能的下降主要是由于析出相的粗化与转变引起的.     

热暴露对欠时效态Al-Cu-Mg-Ag合金拉伸性能的影响

采用拉伸力学性能测试、透射电镜微观组织分析和扫描电镜断口分析等方法,研究热暴露对一种欠时效态Al-Cu-Mg-Ag合金力学性能及微观组织的影响.结果表明:在150 ℃热暴露下,欠时效态Al-Cu-Mg-Ag合金的剩余强度先上升后下降,强度峰值出现在100 h;热暴露1 000 h后,合金的力学性能相对欠时效态合金的无明显下降;在200～300 ℃热暴露时,合金强度随时间的延长而下降,伸长率随着时间的延长而增大;在300 ℃热暴露时,强度明显下降,热暴露10 h后,其抗拉强度只有272.5 MPa,暴露100 h后, 其抗拉强度降至114.5 MPa;欠时效态合金细小分布的Ω相随着热暴露温度的升高,Ω相长大并粗化,θ′相析出,无沉淀析出带(PFZ)变宽;在250 ℃下热暴露时,Ω相明显粗化且数量稀少;合金中的Ω相和θ′相在300 ℃热暴露100 h后,均转变成平衡θ相.     

Sc对Al-Zn-Mg-Cu系铸造铝合金组织与性能的影响

研究了添加x％Sc (x=0.15,0.30,0.45)对Al-6.0Zn-2.8Mg-1.9Cu试验铝合金金属型铸造组织和室温及200～300℃高温力学性能的影响.研究表明,Sc可以有效改变合金基体α(Al)相的尺寸和形态,并对合金共晶组织有明显的变质作用,同时可以有效去除合金组织中的Al7Cu2Fe含铁相,从而提高试验合金的室温抗拉强度.当Sc添加量为0.45％时,合金的室温抗拉强度最高可达510MPa.但Sc对合金的室温塑性影响不大.当Sc添加量为0.30％时,合金的高温瞬时抗拉强度明显提高.     

高纯Al-Cu-Mg-Ag合金的时效析出行为

利用拉伸力学性能测试和透射电镜等研究了高纯Al-Cu-Mg-Ag合金在长时间时效过程中的时效析出行为。结果表明：实验用高纯Al-Cu-Mg-Ag合金板材具有较好的热稳定性和塑性,经185℃时效50h后合金的强度较峰值状态仅下降6%～7%,同时伸长率δ10保持在8%以上;Ω相是高纯Al-Cu-Mg-Ag合金的主要强化相,当合金处于峰值状态时,Ω相与基体之间会产生较大的错配应变,并在Ω相的细小片层处产生位错,为随后二次析出相θ′的析出提供有利的形核位置;延长时效时间将促进尺寸较大的Ω相和大部分θ′相（包括先析出相和二次析出相）向平衡相θ转变,但Ω→θ的转变远比θ′→θ的转变缓慢。     

添加Mn、Sc元素对Mg-9Gd-4Y合金组织和力学性能的影响

对MgGdYMn和MgGdYMnSc合金挤压成形,并对挤压合金热处理后的试样进行室温和高温拉伸实验.用金相显微镜（OM）、扫描（SEM）和透射电镜（TEM）等方法,研究添加Mn、Sc元素对该合金组织与力学性能的影响.结果表明：添加Mn元素能有效地提高Mg-9Gd-4Y合金形变细化晶粒的能力以及T6处理提高室温综合性能.添加Sc元素能提高合金的室温伸长率,但强度有所降低.添加Mn的合金在300℃拉伸时强度为200MPa,在400℃拉伸时显示出超塑性行为,而再添加Sc的合金在300℃拉伸时有超塑性表现.同时添加Mn和Sc的合金室温和高温强度下降.     

一种Al-Cu-Mg-Ag合金时效析出行为

用原位加热X射线衍射方法测量了固溶态的Al-Cu-Mg-Ag合金在不同温度下的X射线衍射谱,确定不同温度下该合金中存在物相。结果表明:实验合金在145℃以下基本不形成Ag-Mg原子团簇;合金在165～350℃存在Ag-Mg原子团簇,Ag-Mg原子团簇在250～350℃最为明显;合金在400℃时Ag-Mg原子团簇消失。TEM结果表明,165℃时效,合金组织由大量的Ω相和少量的θ′相组成,而在250℃时效,合金组织为Ω相,没有发现θ′相存在。分析表明:高温有助于Ag-Mg原子团簇存在,即高温时效有助于Ω相形核。     

Al-Cu-Mg-Ag-Zr铝合金热稳定性能研究

研究了Al-Cu-Mg-Ag-Zr合金高温短时拉伸和热暴露行为及其微观组织.高温拉伸试验结果表明,在150～250 ℃范围内,高温强度下降比较平缓,且250℃下的拉伸强度达到270MPa;在250～300 ℃范围内,高温强度迅速下降.热暴露试验结果表明,在相同时间的条件下,暴露温度从室温至150℃合金的强度和伸长率几乎没有变化,从200～300 ℃合金强度下降,但在200℃热暴露后的拉伸强度仍保持386MPa.透射电镜分析表明,合金欠时效状态由大量细小分布的Ω相及极少量的θ'相组成,随着暴露温度的提高,Ω相长大并粗化,至250℃热暴露后Ω相大幅度减少,无析出带(PFZ)宽化.研究表明,短时高温拉伸条件下,Ω相在250℃下仍能保持稳定,而长时间(100h)热暴露时,Ω相只能在200℃下维持稳定.     

Al—Cu—Mg—Ag合金热变形本构方程模型

在Gleeble-1500热模拟机上进行高温等温压缩试验,研究了Al-Cu-Mg-Ag合金在变形温度为300～500 ℃、应变速率为0.01～10.00 s-1条件下的流变变形行为,建立了Al-Cu-Mg-Ag合金热变形本构方程.结果表明,流变应力随温度的降低、应变速率的提高而增大,在应变速率小于10.00 s-1的条件下,流变应力随应变增加而迅速增大,达到峰值后趋于平稳,表现出动态回复的特征;在应变速率为10.00 s-1,温度大于300 ℃的条件下,应力达到峰值后逐渐下降,并出现锯齿波动现象,表明合金发生了局部动态再结晶;Al-Cu-Mg-Ag合金高温变形时的流变行为可用Zener-Hollomon参数来描述,其变形激活能为160.08 kJ/mol.     

Cu和Mg含量对Al-Cu-Mg-Ag合金组织与性能的影响

通过力学试验及透射电镜研究了不同Cu和Mg含量对Al-Cu-Mg-Ag合金室温、高温力学性能以及显微组织的影响.结果表明,提高Cu和Mg的含量可以提高合金在室温及高温条件下的屈服强度和抗拉强度,但伸长率下降.透射电子显微分析表明,增加Cu和Mg的含量将提高时效过程中强化相的形核密度与体积分数,从而提高合金的强度.     

胫骨生物陶瓷复合材料的微结构增韧机理

扫描电镜观察显示胫骨是一种由羟基磷灰石和胶原蛋白组成的自然生物陶瓷复合材料.羟基磷灰石具有层状的微结构并且平行于骨的表面排列.观察也显示这些羟基磷灰石层又是由许多羟基磷灰石片所组成,这些羟基磷灰石片具有长而薄的形状,也以平行的方式整齐排列.基于在胫骨中观察到的羟基磷灰石片的微结构特征,通过微结构模型分析及实验,研究了羟基磷灰石片平行排列微结构的最大拔出能.结果表明,羟基磷灰石片长而薄的形状以及平行排列方式增加了其最大拔出能,进而提高了骨的断裂韧性.     

Prospects of the Use of Synergetic Approach to Solution of Problems of the Science of Nanomaterials

A synergetic approach to solution of problems of self-controlled synthesis of nanostructures and creation of self-organizing nanotechnologies is considered in connection with the superproblem of creation of materials with functional properties resembling those of biosystems. __________ Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 7, pp. 55 – 61, July, 2005.     

Kinetics of the oxidation of metals — Influence of self-diffusion of metal

The importance of the self-diffusion of a metal during its oxidation by a gas is treated for the cases of nonstoichiometric oxides having either interstitial cation or cation vacancies. We have established a general relationship for the reaction rate when a mixed diffusion process occurs. From this relationship, we have shown that the pressure dependence can be different, according to whether the rate-determining process is the self-diffusion through the metal or through the product.     

Features of formation of the structure in production of blanks of disks of heat-resistant nickel alloys

Conclusions To provide a high level of mechanical properties in wrought blanks of cast ÉP741NP and ÉP962 alloys it is necessary to form controlled structures. A necklace-type structure formed in homogenizing isostatic treatment, subsequent thermomechanical working including alternation of the operations of deformation in the (+)-area and recrystallization anneals, and final heat treatment is preferable. The temperature conditions of all stages of thermomechanical working are strictly controlled, especially the final operation of deformation and heating for hardening. To eliminate hardening cracks and distortions it is necessary to use molten salts at t=600°C as quenchants. The use of multiple production operations makes it possible to significantly reduce the structural inhomogeneity related to inhertance of the original dendritic structure. However, the structure of the final semifinished product is nevertheless characterized by a difference in occurrence of the processes of polygonization and recrystallization between the former dendritic cells and the interdendritic spaces in deformation and heat treatment.To obtain structurally homogeneous blanks for gas turbine engine parts it is necessary to use basically new methods of remelting such as vacuum double electrode remelting and electron beam remelting with an intermediate vessel.Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 12, pp. 25–29, December, 1991.     

Ab-initio calculation of enthalpies of formation of intermetallic compounds and enthalpies of mixing of solid solutions

A large number of ab-initio calculations of energies of formation of intermetallic compounds have been performed in the last 15 years. The currently used methods are listed. The paper presents a review of the aluminium based compounds which have been studied. Comparisons of calculated and experimental enthalpies of formation are provided for aluminim-3d and-4d transition metal alloys at equiatomic composition. The modelling of the enthalpies of mixing of solid solutions based on a given lattice is described.     

试论洋务派教师聘任的思想

洋务派在洋务学堂的办学活动中,为了解决西学专业学科的教学困难,采用了聘请外籍教师的应急措施.他们以真才实学,合同制管理作为主导思想,并认为这种解决师资的途径只是权宜之计,并非久远.从客观上看,洋务派的教师聘任思想有深刻的历史影响.