酸性土壤中破损防腐层下X80管线钢的应力腐蚀行为

设计加载阵列电极应力腐蚀实验装置,针对我国典型的华南酸性红壤环境,研究高强度低合金(HSLA)X80管线钢在破损防腐层(涂层)模拟缝隙下的应力腐蚀开裂(SCC)行为及影响因素,采用电化学阻抗谱(EIS)监测加载电极的腐蚀电化学过程,利用微电极监测防腐层剥离区局部电位和p H值变化,探讨破损涂层下HSLA管线钢SCC行为和规律.结果表明,防腐层开放破损(漏点)处管线钢发生严重腐蚀:不受力试样表面以阳极溶解占主导的均匀腐蚀为主,而拉伸试样表面出现大量微裂纹和点蚀坑,且沿试样划痕优先生长;封闭的剥离区内部管线钢的腐蚀程度显著减缓.同时,对涂层破损点及剥离区深处管线钢的腐蚀现象和过程进行了讨论.     

外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响

采用电化学动电位极化技术、慢应变速率拉伸(SSRT)实验和SEM对X80管线钢在鹰潭土壤模拟溶液中的应力腐蚀行为进行了研究.结果表明:X80管线钢在酸性土壤环境中具有较高的SCC敏感性,其断口模式为穿晶SCC;SCC机制随外加电位的不同而改变,在外加电位高于-930 mV时,其SCC机制由阳极溶解和氢致腐蚀两种电极过程控制,呈现阳极溶解和氢脆复合机制;当电位低于该电位时,其SCC为氢脆机制.随着外加阴极电位的降低,X80管线钢的SCC敏感性不断增大;与X70钢相比,氢脆作用在X80管线钢SCC过程中发挥了更重要的作用.     

剥离涂层下的X80钢在鹰潭土壤模拟溶液中的腐蚀行为

构建了埋地管线钢在鹰潭土壤模拟溶液中的矩形缝隙剥离涂层模型,采用原位电化学测量方法对剥离区的X80钢进行电化学交流阻抗谱(EIS)表征,并对其腐蚀行为进行了研究.结果表明.腐蚀初期剥离区各位置的电化学反应特征相同、EIS由高频容抗弧和低频感抗弧组成.随着腐蚀反应进行,高频容抗弧半径增大.低频感抗弧消失.距漏点不同距离的X80钢试样的腐蚀程度有所区别:漏点处和剥离区底部的腐蚀最严重.为吸氧腐蚀和阳极溶解所致;剥离区中部腐蚀较弱,去除腐蚀产物的X80钢表面出现明显的点蚀坑,点蚀倾向加重,腐蚀类型由全面腐蚀向局部腐蚀转变.根据EIS规律和实验结果.剥离区的腐蚀进程可分为氧耗尽、阴离子迁移和腐蚀扩展3个阶段.     

温度和外加电位对X70管线钢在土壤模拟溶液中应力腐蚀行为的影响

采用动电位扫描、慢应变拉伸（SSRT）和扫描电镜观察研究了温度和外加电位对X70管线钢在成都土壤模拟溶液中的应力腐蚀行为的影响。结果表明,在不同温度和不同电位下,X70管线钢在土壤模拟溶液中表现出不同的应力腐蚀敏感性。在温度和外加电位的交互试验中,电位的变化对X70管线钢在成都土壤模拟溶液中的应力腐蚀敏感性的影响占主导地位,应力腐蚀敏感性在不同温度下的变化趋势保持一致。在－450 mV(vs SCE,下同)的阳极电位下,SCC的机理为阳极溶解;在－850 mV电位下,阴极保护作用抑制了阳极溶解;当电位负移至－1200 mV时,表现出较强的应力腐蚀敏感性,SCC机理以氢脆为主。温度对应力腐蚀敏感性的影响主要体现在对阴极极化电位的影响,但是各种因素综合在一起导致应力腐蚀敏感性随温度变化的复杂性。     

破损涂层下管线钢的交流电干扰腐蚀行为

构建了带破损点的剥离涂层管道腐蚀模拟实验装置,采用微电极技术研究交流干扰X80管线钢破损/剥离涂层下局部腐蚀行为及规律。结果表明:交流电干扰使涂层破损管线钢电位负向偏移;随交流电密度增大,X80钢的阳极溶解速率增大,腐蚀形态由均匀腐蚀逐渐向局部腐蚀转变;破损点处管线钢发生严重腐蚀,剥离区腐蚀程度稍有减缓;但施加100 A/m~2交流电时,剥离区深处X80钢表面仍出现了较严重的点蚀坑。从交流干扰的整流效应、阳极反应不可逆性及交流电对钢/环境界面双电层结构影响等角度讨论了交流电干扰对涂层破损下管线钢腐蚀行为的影响。     

外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响

采用慢应变速率拉伸(SSRT)实验、SEM观察和动电位极化曲线测量等方法,研究了外加电位对X80管线钢母材及焊缝在轮南土壤模拟溶液中的应力腐蚀开裂(SCC)行为。结果表明,X80钢母材及焊缝在轮南土壤模拟溶液中均具有一定的应力腐蚀敏感性。在同一外加电位下,X80钢焊缝的SCC敏感性高于母材的;X80钢SCC敏感性及开裂机理受外加电位影响显著,在-500 mV外加阳极电位下,X80钢的SCC机理为裂尖阳极溶解-膜破裂机制,在-800 mV阴极电位以下(-850,-1000和-1500 mV),氢脆作用在SCC过程中的影响明显增强,阴极析氢反应促进了钢的氢致开裂,导致X80钢SCC敏感性显著增加。     

外加电位对X70管线钢在库尔勒土壤模拟溶液中应力腐蚀开裂敏感性的影响

采用慢应变速率拉仲试验(SSRT)研究了不同外加电位下X70管线钢在库尔勒土壤模拟溶液中的应力腐蚀开裂(SCC)行为,并用扫描电镜分析了不同电位下的断面形貌.结果表明,X70管线钢在库尔勒土壤模拟溶液中具有SCC敏感性;在Ecorr附近施加弱极化时,应力腐蚀开裂敏感性增加;施加强阳极电位时,发生强烈阳极溶解,导致阳极溶解断裂;施加强阴极电位时,析氢过程加强,导致氢致应力腐蚀断裂.     

X80钢在鹰潭土壤模拟溶液中应力腐蚀裂纹扩展行为机理

采用电化学极化曲线测试、EIS测试、裂纹扩展实验和SEM分析研究了X80管线钢在鹰潭土壤溶液环境下的应力腐蚀开裂(SCC)裂纹扩展行为及机理.结果表明,X80管线钢在酸性土壤环境中的裂纹扩展速率随着外加电位的降低呈现增加趋势,相较于开路电位下的裂纹扩展,在裂纹扩展初期,-850 m V下裂纹扩展速率较大,而在裂纹快速扩展阶段,过保护电位-1200 m V下裂纹扩展速率更大;同时X80管线钢在酸性土壤环境中的SCC裂纹扩展机制也随着施加外加电位的不同而改变,在外加电位高于-930 m V时为阳极溶解与氢脆的混合机制,负于-930 m V时则为氢脆机制.     

X70钢焊接接头在近中性溶液中应力腐蚀行为研究

采用慢应变速率试验(SSRT)、扫描电镜以及电化学测量技术研究了X70管线钢焊接接头在近中性模拟土壤溶液中的应力腐蚀开裂(SCC)行为。结果表明,断口和柱面SCC裂纹均发生在热影响区(HAZ)。在试验溶液中,随着外加极化电位降低管线钢SCC敏感性增强,电位负移到一定电位值后,SCC敏感性减弱;随着溶液pH值降低,腐蚀速率增大,敏感电位区间负移。施加阴极电位时,在试样断口观察到明显的准解理脆断特征,断口和柱面有穿晶SCC裂纹。分析了焊接接头试样HAZ的SCC机理,在试验介质中,管线钢应力腐蚀开裂主要受阳极溶解和氢致开裂两种机理的联合作用,适当的电位可以使阳极溶解和氢致开裂的联合作用达到最大,从而造成较严重的应力腐蚀开裂。     

外加电位对X90钢及其焊缝在近中性土壤模拟溶液中应力腐蚀行为的影响

采用慢应变速率拉伸(SSRT)实验、动电位极化技术和SEM观察等方法,研究了X90钢基体和焊缝在近中性土壤模拟溶液中不同阴极保护电位下的应力腐蚀行为。结果表明,X90管线钢及其焊缝组织在近中性土壤模拟溶液中均具有一定的应力腐蚀敏感性,裂纹扩展为穿晶腐蚀裂纹;应力腐蚀开裂(SCC)的裂纹萌生与扩展与外加保护电位有关。在开路电位(OCP)~-1000 m V的电位范围内,X90钢的SCC机制均为阳极溶解(AD)+氢脆(HE)的混合机制;在OCP下,由于AD作用较强,SCC敏感性较明显;在-800 m V下,由于AD和HE作用均较弱,导致SCC敏感性最低;而在-900 m V时,由于HE作用明显增强,具有最高的SCC敏感性;在相同电位条件下,焊缝的SCC敏感性高于母材。     

Effect of Strength and Microstructure on Stress Corrosion Cracking Behavior and Mechanism of X80 Pipeline Steel in High pH Carbonate/Bicarbonate Solution

The stress corrosion cracking (SCC) behaviors and mechanisms of X80 pipeline steels with different strength and microstructure in high pH carbonate/bicarbonate solution were investigated by slow strain rate testing and electrochemical test. The results showed that the cracking mode of low strength X80 steel composed of bulky polygonal ferrite and granular bainite in high pH solution was intergranular (IGSCC), and the SCC mechanism was anodic dissolution (AD). While the mixed cracking mode of high strength X80 steel consisted of fine acicular ferrite and granular bainite was intergranular (IGSCC) in the early stage, and transgranular (TGSCC) in the later stage. The decrease of pH value of crack tip was probably the key reason for the occurrence of TGSCC. The SCC mechanism may be a mixed mode of AD and hydrogen embrittlement (HE), and the HE mechanism may play a significant role in the deep crack propagation at the later stage. The cracking modes and SCC mechanisms of the two X80 steels were associated with its microstructure and strength.     

Electrochemical Behavior and Stress Corrosion Sensitivity of X70 Steel Under Disbonded Coatings in Korla Soil Solution

The corrosion of X70 pipeline steel under a model disbonded coating was studied in a simulated solution of Korla soil by combining in situ electrochemical measurements at different locations in the crevice and stress corrosion cracking (SCC) sensitivity analyses in the corresponding simulated environments. The results from electrochemical impedance spectroscopy showed that the corrosion product resistance R _t and charge transfer resistance R _ct of X70 steel first increased and then decreased with increasing distance from the opening of the crevice in the disbonded coating. Scanning electron micrographs showed that pitting in the crevice became more severe at deeper locations in the crevice. Slow strain rate tests showed that the lowest SCC sensitivity of X70 steel was found at 15 cm away from the opening, and the highest SCC sensitivity was at the end of the crevice.     

阴极极化下X80钢在鹰潭土壤模拟溶液中应力腐蚀行为研究

采用电化学阻抗和慢应变速率方法,结合扫描电子显微镜,研究了不同阴极极化电位下X80钢在鹰潭土壤模拟溶液中的应力腐蚀行为。结果表明：鹰潭土壤模拟溶液中,X80钢/溶液界面处电荷转移电阻随阴极极化程度增加先升后降。在自腐蚀电位条件下开裂机理为阳极溶解,当外加电位为-1000 mV (vs SCE),应力腐蚀敏感性最低,此电位为最佳保护电位;继续增大阴极极化程度,应力腐蚀敏感性增加,此时开裂机制为氢和应力协同作用下的氢致开裂。     

Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution

The influence of various AC current densities on stress corrosion cracking behavior and mechanism of X80 pipeline steel was investigated in carbonate/bicarbonate solution by polarization curves and slow strain rate tensile tests. With the increasing AC current density, the SCC susceptibility of the steel increases, especially at high AC current density. A significant difference in the SCC behavior and mechanism is found for the steels with or without AC application. In the absence of AC, the fracture mode is intergranular and the mechanism is attributed to anodic dissolution. Under AC application, the cracks propagation is transgranular, and the mechanism is mixed controlled by both anodic dissolution and hydrogen embrittlement.     

Mechanistic aspect of near-neutral pH stress corrosion cracking of pipelines under cathodic polarization

This paper investigates mechanistically stress corrosion cracking (SCC) of an X70 pipeline steel that is under cathodic protection (CP) in a near-neutral pH solution. It was found that there is a critical potential range, i.e., ?730 and ?920 mV_SCE, where the steel is in a non-equilibrium electrochemical state, and anodic dissolution (AD) reaction may occur when the steel is polarized cathodically. When the applied potential is more positive than this range, SCC is AD-based; while the applied potential is more negative, SCC of pipelines is under hydrogen embrittlement (HE) mechanism. When the polarization potential is within the range, SCC of the steel is under the combined effect of AD and HE. Therefore, AD may still occur on pipeline steel that is under CP with the potential within this critical range, contributing to the cracking process.     

X100管线钢在酸性土壤模拟溶液中的应力腐蚀行为

采用慢拉伸(SSRT)、动电位极化和SEM观察等方法,研究了在不同的阴极保护电位条件下X100钢在酸性土壤模拟溶液中的应力腐蚀行为.结果表明,X100钢发生穿晶裂纹的应力腐蚀,裂纹的萌生和发展与阴极保护电位有关.完全阳极过程控制时,X100钢无裂纹出现,但出现晶间腐蚀;在混合过程控制时,应力腐蚀敏感性较低,裂纹发展缓慢;在完全阴极过程控制时,氢脆机制起主要作用,裂纹扩展迅速.     

X80管线钢在近中性pH溶液中腐蚀行为研究

目的研究X80管线钢在近中性p H溶液中的腐蚀与应力腐蚀裂纹萌生行为。方法采用电化学实验和浸泡实验研究X80管线钢在近中性p H溶液中的腐蚀行为,采用慢应变速率拉伸实验研究X80管线钢在近中性p H溶液中,在自腐蚀电位和外加电位下的应力腐蚀裂纹萌生行为。结果 X80管线钢在近中性p H溶液中的极化曲线只有活化区,没有钝化区,其自腐蚀电位约为-750 m V,浸泡195天后,试样表面没有氧化膜出现,但是观察到点蚀坑。在自腐蚀电位下,X80管线钢试验表面有大量的应力腐蚀裂纹;在-500 m V阳极外加电位下,X80管线钢试验表面几乎没有观察到应力腐蚀裂纹;在-850 m V阴极外加电位下,X80管线钢试验表面的应力腐蚀裂纹很少,但是随着外加阴极电位负移到-1300 m V时,X80管线钢试验表面的应力腐蚀裂纹增多。结论 X80管线钢在近中性p H溶液中发生均匀腐蚀,但是夹杂物剥落能在X80管线钢表面形成点蚀坑。在近中性p H溶液中,在自腐蚀电位下,X80管线钢应力腐蚀裂纹萌生敏感性最强;外加阴极电位抑制应力腐蚀裂纹萌生,但是随着外加阴极电位的负移,应力腐蚀裂纹萌生敏感性增强;外加阳极电位下,由于均匀腐蚀的作用,应力腐蚀裂纹萌生敏感性较弱。     

X70管线钢在近中性及高pH值溶液中的电化学行为和SCC敏感性

采用动电位极化曲线测试法研究了温度、通气条件和pH值对X70管线钢在NS4溶液和0.5 mol/LNa2CO3 1 mol/L NaHCO3溶液中的电化学极化行为的影响,并用慢应变速率试验(SSRT)研究了X70管线钢在这些溶液中的应力腐蚀破裂(SCC)敏感性。结果表明,X70管线钢在NS4溶液中不出现活化—钝化转变区,随外加电位负移,SCC敏感性增加,表现出氢致破裂(HIC)的特征;在0.5 mol/L Na2CO3 1 mol/L NaHCO3高pH值溶液中出现活化—钝化转变区,在阴极极化区,也表现出氢致破裂(HIC)的特征,但在阳极极化区,发生的是阳极溶解型应力腐蚀破裂(ADSCC)。