电刷镀纳米Ni-P-SiC复合镀层性能的研究

纳米微粒加入镀液可提高镀层的性能,用电刷镀方法制备了纳米SiC/ Ni-P复合镀层,测试了纳米SiC微粒添加量对复合镀层的硬度、耐磨性的影响,探讨了纳米SiC微粒复合镀层的强化机制及Ni-P晶化过程中的强化作用.结果表明,采用电刷镀制备工艺,能在一定程度上改善纳米微粒在镀液中的分散均匀性并能提高复合镀层性能.在Ni-P合金镀液中适量添加纳米SiC微粒(7～10 g/L),纳米SiC微粒在形成复合镀层时能起到硬质点的强化作用,同时在Ni-P晶化过程中还能在细化晶粒中起到再强化作用.不仅能使镀层硬度提高1.5～1.8倍,还能提高其耐磨性.     

电刷镀Ni-P／纳米WC复合镀层工艺及性能研究

为了改善电刷镀Ni-P镀层的硬度和耐磨性,通过在电刷镀Ni-P镀液中加入纳米WC微粒制备Ni-P/纳米WC复合镀层,研究了镀液中纳米WC含量与镀层中纳米WC含量的关系;测定了不同WC含量对镀层硬度和镀层结构的影响.考察了试样在1 mol/L H2SO4,1 moL/L HCl及3%NaCl介质中的耐蚀性.采用扫描电子显微镜(SEM)及X射线衍射(XRD)研究了Ni-P/纳米WC镀层的性能.结果表明,Ni-P/纳米WC电刷镀复合镀层耐蚀性能与原电刷镀Ni-P镀层相当,耐磨性优于电刷镀Ni-P镀层.镀液含25 g/L纳米WC时,电刷镀复合镀层的显微硬度为918 HV.     

Ni-P-SiC(纳米)化学复合镀层的组织与性能

利用化学镀方法制备了Ni-P-SiC(纳米)复合镀层,研究了镀液中纳米SiC微粒的含量对复合镀层组织与性能的影响,结果表:由于纳米SiC的加入,使复合镀时的镀速加快,原因是液固界面增加,从而增加了有效催化面积.由于镀层中纳米SiC的存在,使复合镀层的硬度得到显著提高,镀态下硬度可达1000～1100HV,退火处理后则可达到1650HV.与微米SiC复合镀层相比,纳米复合镀层的耐磨性也有明显改善.用DSC分析了镀层的晶化规律,发现纳米复合镀层的晶化温度大幅度提高.     

纳米Al_2O_3-Ni-P化学复合镀层的制备及其摩擦学性能

为了获得摩擦学性能优良的镀层,在20#钢基材上实施了纳米Al_2O_3-Ni-P化学复合镀,采用正交试验法优选了镀液配方,研究了镀液中纳米Al_2O_3含量、镀液温度对复合镀层显微硬度、摩擦和磨损性能的影响,用扫描电子显微镜对复合镀层表面形貌进行观察。结果表明,镀液中纳米Al_2O_3含量是影响复合镀层硬度和耐磨性能最主要因素。纳米Al_2O_3能有效改善Ni-P合金镀层结构,在镀层中分布较均匀,使复合镀层硬度和耐磨性能明显提高。当纳米Al_2O_3含量为6 g/L时,纳米粒子在复合镀层中分布致密、均匀,复合镀层硬度和耐磨性最佳,与基材20#钢结合性较好。镀液温度对复合镀层硬度和耐磨性能有一定影响,最佳镀液温度为85℃,此时复合镀层硬度和耐磨性较好。     

Ni-Fe-W-SiC纳米复合镀层耐磨性能的研究

采用电沉积法制备了Ni-Fe-W-SiC纳米复合镀层,研究了镀液中SiC含量对镀层中SiC含量的影响,采用显微硬度计测试了镀层的硬度,对镀层进行了磨损试验比较.结果表明,镀层中SiC含量随着镀液中SiC含量增加先增加、后减少;镀层硬度随着镀层中SiC含量增加而增强;耐磨性能随着镀层中SiC含量增加而加强,镀层磨损机制相应由剥落磨损向颗粒磨损转化.     

离心高速电沉积Ni-SiC复合镀层的研究

利用自制的离心高速电沉积实验装置,研究了镀液温度、镀液pH值、电流密度、镀液中SiC浓度和阴极旋转速度对Ni-SiC复合镀层中SiC含量的影响;同时还对镀层中SiC微粒的分布情况及镀层的性能进行了研究。结果表明:温度、电流密度、镀液中的SiC含量及阴极旋转速度对镀层中复合粒子的含量有显著的影响,而pH值对镀层中SiC含量影响不大。利用离心高速电沉积方法能够制备出高体积分数的、微粒分布均匀的Ni-SiC复合镀层。所制备的高体积分数的Ni-SiC复合镀层硬度和耐磨性能优于普通槽镀镀层。     

Ni-P/Ag纳米复合化学镀层的耐磨损性能

Ni-P/非金属纳米化学镀溶液中纳米粒子容易团聚,镀液难以保持稳定性.在化学镀Ni-P溶液中添加纳米银粒子,在钢铁基体上制备了Ni-P/Ag纳米复合镀层.用显微硬度计、金相显微镜等技术分析了镀层的厚度、硬度和表面形貌,用磨损试验机研究了镀层的耐磨损性能.结果表明:银纳米粒子在镀液中的含量为1.0×10-7mol/,L,银纳米粒子加快了镀层的沉积速度,使纳米复合镀层厚度增加;在相同的施镀条件下,Ni-P/Ag纳米复合镀层比Ni-P镀层具有更高的硬度和更好的耐磨损性能.     

n-SiC/Ni复合电刷镀参数优化的均匀设计试验研究

采用在快速镍镀液中添加纳米SiC粉末的方法制备了纳米复合镀液,对影响镀层性能的镀液中纳米SiC粉末含量、表面活性剂浓度、刷镀电压、镀液初始温度四个因素进行了正交试验,结果表明:镀液中纳米粉末含量和刷镀电压对复合镀层的性能有显著影响.通过均匀设计试验法,对影响镀层显微硬度的主要因素进行回归分析,得到了相应的数学模型.     

Au/纳米SiC颗粒复合镀层的制备工艺及性能

研究了纯铜表面Au/纳米SiC颗粒复合镀层的制备工艺,特别是镀液中SiC悬浮量及阴极电流密度对复合共沉积的影响.通过扫描电镜(SEM)、能谱(EDS)、X射线衍射(XRD)等对镀层的形貌、成分、结构组成进行了分析,结果表明镀层中复合了一定量的纳米SiC.显微硬度结果显示,复合镀层的显微硬度较纯金镀层有很大的提高.     

45钢Ni-P/SiC化学复合镀层结合力初探

采用化学复合镀技术在45钢表面制备了Ni-P/SiC复合镀层,通过金相显微镜、扫描电镜以及EDS能谱分析考察了镀层的微观组织以及镀层中获得的SiC的沉积量随镀液中SiC浓度的变化,利用划痕仪分析了镀层与基体的结合力.结果表明:镀层与基体界面处无夹杂孔洞存在、结合致密,SiC颗粒在复合镀层中分布均匀,复合镀层中SiC的沉积量随镀液中SiC浓度的增加而增加,镀液中SiC的浓度为6 g/L时镀层中SiC的沉积量达到最大值10.6%,Ni-P/SiC复合镀层与基体的结合力和镀液中SiC的浓度呈抛物线关系,镀液中的SiC浓度为6 g/L时,其结合力最小,为63 N.     

激光熔覆涂层的研究进展

激光熔覆层具有许多优点,未来具有良好的应用前景.为此,从普通涂层、复合涂层以及非晶化涂层等方面,综述了激光熔覆涂层的研究进展.结合目前熔覆涂层存在的质量问题,指出了未来激光熔覆涂层研究的主要方向.     

超支化聚合物及其在环保涂料中的应用

介绍了超支化聚合物的分子结构及其独特的性能和制备方法,论述了超支化聚合物在各种环保涂料中作为粘合剂的研究应用情况及优势,包括高固体分涂料、辐射固化涂料以及粉末涂料,探讨了涂料用超支化聚合物的设计原则,归纳了今后的研究方向,指出其在涂料工业中将会有广阔的应用前景。     

Dry coating of solid dosage forms: an overview of processes and applications

Dry coating techniques enable manufacturing of coated solid dosage forms with no, or very limited, use of solvents. As a result, major drawbacks associated with both organic solvents and aqueous coating systems can be overcome, such as toxicological, environmental, and safety-related issues on the one hand as well as costly drying phases and impaired product stability on the other. The considerable advantages related to solventless coating has been prompting a strong research interest in this field of pharmaceutics. In the article, processes and applications relevant to techniques intended for dry coating are analyzed and reviewed. Based on the physical state of the coat-forming agents, liquid- and solid-based techniques are distinguished. The former include hot-melt coating and coating by photocuring, while the latter encompass press coating and powder coating. Moreover, solventless techniques, such as injection molding and three-dimensional printing by fused deposition modeling, which are not purposely conceived for coating, are also discussed in that they would open new perspectives in the manufacturing of coated-like dosage forms.     

系列环保型重防腐蚀涂料的开发

介绍了以改性环氧树脂为基料的无溶剂环保型功能涂料研制技术路线、主要技术性能、特性和施工工艺 ,并举例说明了它们在实际工程中的应用。     

Controllable coating of microneedles for transdermal drug delivery

Coated microneedles have been paid much attention recently, and several coating strategies have been developed to address the problems during coating process. However, there are still some unresolved issues, such as, precise control requirements, microneedle substrate contamination and high processing temperature. The purpose of this study was to develop a simple and controllable method to make uniform coatings on microneedles at room temperature. This novel method avoids the contamination of microneedle substrate by providing both the adsorption force of thickener and micro-scale coating film produced by a newly design device. Thickeners were screened to enhance the mass of coatings. The parameters that influence the coatings were tested systematically, which made coating process controllable. Finally, three model drugs were coated onto microneedles to prove the method is applicable more broadly. In addition, insertion experiments were carried out to test the drug delivery feasibility of the coated microneedles. In conclusion, this study presents a simple and controllable method to coat microneedles with small molecular chemical drugs or large proteins for rapid skin drug delivery.     

防腐涂料和涂装技术(Ⅴ)

第五部分主要介绍船舶近海工程各领域中应用的防腐蚀涂料 ,包括车间底漆、防锈漆、船底防污漆、压载水舱漆、油舱漆、海上采油平台涂料、滨海桥梁保护涂料、海洋化工及相关工业设备保护涂料     

平板玻璃表面涂料的研究及应用

透明装饰性涂料在玻璃上的应用使其表面功能多样化,应用范围更加广泛.本文阐述了平板玻璃涂料制备技术中基料树脂的选取、涂膜耐久性以及涂装工艺,并综述了几类玻璃涂料,如普通装饰性涂料、低辐射涂料、防反射涂料以及新型玻璃建材的应用研究进展.     

五辊无溶剂涂布涂层厚度数学模型与影响因子分析

目的研究如何实现高效的无溶剂涂布,获得稳定的预定厚度涂层。方法在建立两辊间隙间涂布液流动数学模型的基础上,从涂布液辊间间隙分流分配关系和总结构内涂布液流量平衡两方面,分析无溶剂五辊顺转涂布系统涂布厚度的影响因素。结果转移钢辊和涂布钢辊的速比,计量辊和转移钢辊之间的间隙以及橡胶转移辊的压力等是对涂层厚度有直接影响的因子,毛细准数是涂层竖条道缺陷的主要影响因子,而涂布液的非牛顿特性会加重竖条道缺陷。结论设计无溶剂五辊顺转涂布系统时,需要综合考虑辊的直径、施加给橡胶辊载荷大小的范围、橡胶辊的硬度、适用涂布液的粘度范围和速度极限等因素。     

热障陶瓷涂层的最新发展

综述了现代航空发动机用热障陶瓷涂层的最新发展，着重介绍了双陶瓷层，电子束物理气相沉积（EB－PVD）和溶液等离子喷涂（SPS）纳米热障陶瓷涂层的性能和特点。     

水性聚苯胺微乳液及其防腐涂料研究

利用改进的新型微乳液聚合法合成了聚苯胺水性微乳液,该微乳液不经破乳可直接应用于金属防腐涂料。将其与环氧树脂的共混乳液作为底漆、与环氧树脂面漆复合后,可制备出性能优良的水性金属防腐涂料。该复合涂层能将裸露钢板的平衡开路电位提高235mV左右,在自来水中至少可浸泡3个月不起泡、不生锈,是一种环境友好型绿色涂料。