On the optical, structural, and morphological properties of ZrO2 and TiO2 dip-coated thin films supported on glass substrates

This article reports the optical and morphological properties of dip-coated TiO₂ and ZrO₂ thin films on soda-lime glass substrates by metal-organic decomposition (MOD) of titanium^IV and zirconium^IV acetylacetonates respectively. Thermogravimetric and differential thermal analysis (DTA–TG) were performed on the precursor powders, indicating pure TiO₂ anatase and tetragonal ZrO₂ phase formation. Phase crystallization processes took place in the range of 300–500 °C for anatase and of 410–500 °C for ZrO₂. Fourier Transform Infrared Spectroscopy (FT-IR) was used to confirm precursor bidentate ligand formation with keno-enolic equilibrium character. Deposited films were heated at different temperatures, and their structural, optical and morphological properties were studied by grazing-incidence X-ray Diffraction (GIXRD) and X-Ray Photoelectron Spectroscopy (XPS), Ultraviolet Visible Spectroscopy (UV-Vis), and Atomic Force Microscopy (AFM) respectively. Film thinning and crystalline phase formation were enhanced with increasing temperature upon chelate decomposition. The optimum annealing temperature for both pure anatase TiO₂ and tetragonal ZrO₂ thin films was found to be 500 °C since solid volume fraction increased with temperature and film refractive index values approached those of pure anatase and tetragonal zirconia. Conditions for clean stoichiometric film formation with an average roughness value of 2 nm are discussed in terms of material binding energies indicated by XPS analyses, refractive index and solid volume fraction obtained indirectly by UV-Vis spectra, and crystalline peak identification provided by GIXRD.     

Thermal evolution of TiO2---ZrO2 composites prepared by chemical coating processing

A xZrO₂ (100−x)TiO₂ composite gel powder (x = 50 mol%) has been prepared by chemical processing of anatase as inner core coated with in situ precipitated amorphous zirconia as outer core, which was obtained from controlled hydrolysis of zirconyl chloride using ammonia at pH=9–10. The thermal evolution of this composite is reported, showing the crystallization of metastable cubic/tetragonal zirconia at 437°C, as detected by DTA at 10°C min⁻¹ and XRD, with activation energy of 407 ± 10 kJ mol⁻¹, and the feasibility of preparing zirconium titanate powders by reaction of TiO₂ and ZrO₂ by heating at higher temperatures is discussed.     

Investigation on the cross sensitivity of NO2 sensors based on In2O3 thin films prepared by sol-gel and vacuum thermal evaporation

In₂O₃ thin films have been prepared from commercially available pure In₂O₃ powders by high vacuum thermal evaporation (HVTE) and from indium iso-propoxide solutions by sol-gel techniques (SG). The films have been deposited on sapphire substrates provided with platinum interdigital sputtered electrodes. The as-deposited HVTE and SG films have been annealed at 500°C for 24 and 1 h, respectively. The film morphology, crystalline phase and chemical composition have been characterised by SEM, glancing angle XRD and XPS techniques. After annealing at 500°C the films’ microstructure turns from amorphous to crystalline with the development of highly crystalline cubic In₂O_3−x (JCPDS card 6-0416). XPS characterisation has revealed the formation of stoichiometric In₂O₃ (HVTE) and nearly stoichiometric In₂O_3−x (SG) after annealing. SEM characterisation has highlighted substantial morphological differences between the SG (highly porous microstructure) and HVTE (denser) films. All the films show the highest sensitivity to NO₂ gas (0.7–7 ppm concentration range), at 250°C working temperature. At this temperature and 0.7 ppm NO₂ the calculated sensitivities (S=R_g/R_a) yield S=10 and S=7 for SG and HVTE, respectively. No cross sensitivity have been found by exposing the In₂O₃ films to CO and CH₄. Negligible H₂O cross has resulted in the 40–80% relative humidity range, as well as to 1 ppm Cl₂ and 10 ppm NO. Only 1000 ppm C₂H₅OH has resulted to have a significant cross to the NO₂ response.     

Effect of SnO2 on the photocatalytical properties of TiO2 films

TiO₂/SnO₂ thin films with different tin atomic percentages were successfully prepared on glass substrates by the spray pyrolysis method from an alcoholic solution of TiO[C₅H₇O₂]₂ with different concentrations of SnCl₄. The TiO₂/SnO₂ thin films prepared at 450 °C presented the anatase phase in polycrystalline configuration from %Sn = 0 in the starting solution up to %Sn = 20, at higher tin content the films present an amorphous configuration. The resulting thin films have a homogeneous surface structure with some porosity. The photocatalytical properties of the films were evaluated with the degradation of methylene blue. The products of the degradation reaction were identified by ¹H nuclear magnetic resonance and the film properties were studied by atomic force microscopy, scanning electron microscopy, UV–Vis spectroscopy, and X-ray diffraction.     

Structural characterization of TiNxOy/TiO2 single crystalline and nanometric multilayers grown by LP-MOCVD on (110)TiO2

TiO₂/TiN_xO_y superlattices were grown by Low Pressure-Metal-Organic Vapor Phase Epitaxy (LP-MOVPE) technique at deposition temperatures ranking from 650 to 750°C. The growth was performed on top of TiO₂(110) rutile substrates. Intense peaks observed in the X-rays rocking curves and θ-2θ diffraction patterns show the presence of crystalline epilayers. The TiN_xO_y layers were grown in a (200) cubic structure on the (110) quadratic TiO₂ epilayer structure. Transmission electron microscopy confirmed the XRD results and showed the formation of periodic and well structured epilayers.     

Photocatalyzed degradation of flumequine by doped TiO2 and simulated solar light

Titanium dioxide was obtained in its pure form (TiO₂) and in the presence of urea (u-TiO₂) and thiourea (t-TiO₂) using the sol–gel technique. The obtained powders were characterized by BET surface area analysis, Infrared Spectroscopy, Diffuse Reflectance Spectroscopy and the Rietveld refinement of XRD measurements. All the prepared catalysts show high anatase content (>99%). The a and b-cell parameters of anatase increase in the order TiO₂ < u-TiO₂ < t-TiO₂, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO₂ > u-TiO₂ > TiO₂. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO₂ and t-TiO₂, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO₂ catalyst. Changing simultaneously the catalyst amount (t-TiO₂) and pH, multivariate analysis using the response surface methodology was used to determine the roughly optimal conditions for flumequine degradation. The optimized conditions found were pH below 7 and a catalyst amount of 1.6 g L⁻¹.     

Structural and electrochemical characterization of LiMn2−δVδOy spinels

The spinel phase compounds with the composition of LiMn_2−δV_δO_y were prepared by solid reaction of the mixture of LiNO₃·H₂O, MnCO₃ and NH₄VO₃ powders. Evolution of the crystalline phases of the samples versus the vanadium content was analyzed using X-ray diffraction (XRD) technique, EPR and FT-IR spectroscopes. Cubic spinel is the predominant phase in the powders under heat treatment at 550 °C for 5 h. The valence state of manganese ion changed from +4 to +3 with vanadium substitution for charge compensation. The vanadium substitution of manganese leads the decline in capacity and cyclic behavior of the powders. The electrochemical behaviors relating to the variation of structure corresponding to the vanadium substitution were discussed.     

RuO2-TiO2/Ti阳极的研究进展

钌系涂层钛阳极具有稳定性好、电催化活性高、环境友好等特点,在电解水、阴极保护以及电化学除垢等领域具有广泛的应用前景。其中,涂层中二氧化钌(RuO₂)的比例与存在形态是决定其电催化活性和稳定性的关键。在涂层钛阳极的制备中,热分解法因其操作简单、成本低、易工业化生产等优势而被广泛使用。介绍了目前在电解行业广泛应用的钌系涂层钛阳极——RuO₂-TiO₂/Ti阳极的应用领域,简述了RuO₂-TiO₂/Ti阳极中钌钛氧化物的特点和作用,并对RuO₂-TiO₂/Ti阳极的失效原因和制备工艺进行了阐述。主要综述了前处理、涂液组分比例、涂液浓度和烧结温度等工艺参数对通过热分解法制备的钛电极稳定性和电催化活性的影响,以及针对RuO₂-TiO₂/Ti阳极的失效原因提出钛阳极未来的改进方向,旨在促进本领域研究者更深入地了解钌钛阳极的特点、失效原因以及如何制备性能优良的涂层钛电极。     

Hydrophilicity on carbon-doped TiO2 thin films under visible light

Carbon-doped TiO₂ thin films in the anatase phase with dopant concentrations of 1.1, 0.9, and 0.7 mol% were fabricated by a radio-frequency magnetron sputtering method. Dopant carbons were located at the oxygen sites. Carbon substitution caused the absorbance edge and/or the shoulder of TiO₂ to shift to a higher wavelength region. Carbon-doped TiO₂ thin films underwent a hydrophilic conversion when irradiating with visible light (400–530 nm). The hydrophilic property under visible light was inferior to that under ultraviolet light, which is explained by considering that the visible light sensitivity originates from the localized C 2p formed in the band-gap.     

Microstructural, photocatalysis and electrochemical investigations on CeTi2O6 thin films

The properties of sol–gel derived CeTi₂O₆ thin films deposited using a solution of cerium chloride heptahydrate and titanium propoxide in ethanol are discussed. The effect of annealing temperature on structural, optical, photoluminescence, photocatalysis and electrochemical characteristics has been examined. Lowest annealing temperature for the formation of crystalline CeTi₂O₆ phase in these samples is identified as 580 °C. The optical transmittance of the films is observed to be independent of the annealing temperature. The optical energy bandgap of the 600 °C annealed film for indirect transition is influenced by the presence of anatase phase of TiO₂ in its structure. Fourier transform infrared spectroscopy investigations have evidenced increased bond strength of the Ti–O–Ti network in the films as a function of annealing temperature. The photoluminescence intensity of the films has shown dependence on the annealing temperature with the films fired at 450 °C exhibiting the maximum photoluminescence activity. The decomposition of methyl orange and eosin (yellow) under UV–visible light irradiation in the presence of crystalline CeTi₂O₆ films shows the presence of photoactivity in these films. The photocatalytic response of CeTi₂O₆ films is found to be superior to the TiO₂ films. In comparison to crystalline films, the amorphous films have shown superior electrochemical characteristics. The 500 °C annealed amorphous films have exhibited the most appropriate properties for incorporation in electrochromic devices comprising tungsten oxide as the primary electrochromic electrode.     

Structural, optical and electrical characterization of spray-deposited TiO2 thin films

Titanium oxide (TiO₂) thin films were deposited onto glass substrates by means of spray pyrolysis method using methanolic titanyl acetyl acetonate as precursor solution. The thin films were deposited at three different temperatures namely 350, 400 and 450 °C. As-deposited thin films were amorphous having 100–300 nm thickness. The thin films were subsequently annealed at 500 °C in air for 2 h. Structural, optical and electrical properties of TiO₂ thin films have been studied. Polycrystalline thin films with rutile crystal structure, as evidenced from X-ray diffraction pattern, were obtained with major reflexion along (1 1 0). Surface morphology and growth stages based on atomic force microscopy measurements are discussed. Electrical properties have been studied by means of electrical resistivity and thermoelectric power measurements. Optical study shows that TiO₂ possesses direct optical transition with band gap of 3.4 eV.     

Synthesis and the luminescent properties of europium-activated Ca2SnO4 phosphors

The synthesis and photoluminescent (PL) properties of calcium stannate crystals doped with europium grown by mechanically activated in a high energy vibro-mill have been investigated. The characteristics of Ca₂SnO₄:Eu³⁺ phosphors were found to depend on the amounts of europium ions. The XRD profiles revealed that the system, (Ca_1−xEu_x)₂SnO₄, could form stable solid solutions in the composition range of x = 0–7% after being calcined at 1200 °C. The calcined powders emit bright red luminescence centered at 618 nm due to ⁵D₀ → ⁷F₂ electric dipole transition. Both XRD data and the emission ratio of (⁵D₀ → ⁷F₂)/(⁵D₀ → ⁷F₁) reveal that the site symmetry of Eu³⁺ ions decreases with increasing doping concentration. The maximum PL intensity has been obtained for 7 mol% concentration of Eu³⁺ in Ca₂SnO₄.     

Influence of rare-earth oxides on structure and crystallization properties of Bi2O3–B2O3 glass

Bi₂O₃·B₂O₃ glasses doped with rare-earth oxides (RE₂O₃) (RE³⁺ = La³⁺, Pr³⁺, Sm³⁺, Gd³⁺, Er³⁺ and Yb³⁺) were prepared by the melting–quenching method. The relationships between composition and properties were demonstrated by IR, DSC, XRD and SEM analysis. The results show that the network structure resembles that of undoped Bi₂O₃·B₂O₃ glass, composing of [BO₃], [BO₄] and [BiO₆] units. RE₂O₃ stabilizes the glass structure as a modifier. Transition temperature (T_g) increases linearly with cationic field strength (CFS) of RE³⁺. La₂O₃, Pr₂O₃, Sm₂O₃ and Gd₂O₃ are benefit to promote the formation of BiBO₃ crystal. When Er₂O₃ and Yb₂O₃ are introduced, respectively, the main crystal phase changes to Bi₆B₁₀O₂₄. Transparent surface crystallized samples are obtained by reheating at 460–540 °C for 5 h. In this case, needle like BiBO₃ crystal or rare-earth-doped BiBO₃ crystal (Pr_xBi_1−xBO₃ and Gd_xBi_1−xBO₃) are observed, which is promising for non-linear optical application.     

Sol–gel preparation of boron-containing cordierite Mg2(Al4−xBx)Si5O18 and its crystallization

Five cordierite-based powders were investigated regarding their thermal and crystallization behaviors. The powders were obtained from amorphous gels having nominal compositions of 2Mg : xAl : (4 − x)B : 5Si where x = 4 down to 0. Thermal gravimetry analysis of the dry gels showed some absorbed water and decomposition of organic ligands in addition to network condensation. Gradual substitution of B for Al in the dried gel powders showed a new band in their infrared spectra corresponding to triangular BO₃, whereas the bands corresponding to Al vanished. This also showed a noticeable effect on the crystallization trends, type and stability of cordierite. Cordierite crystallized in samples of B/Al ratio up to 1 while protoenstatite predominated in samples of higher B/Al ratios. In addition, some silica minerals, with little amorphous phase, were formed. Incorporation of boron and increase in temperature enhanced the transformation of γ cordierite to its form.     

Enhanced ferroelectric properties of multilayer SrBi2Ta2O9/SrBi2Nb2O9 thin films for NVRAM applications

Ferroelectric SrBi₂Ta₂O₉/SrBi₂Nb₂O₉ (SBT/SBN) multilayer thin films with various stacking periodicity were deposited on Pt/TiO₂/SiO₂/Si substrate by pulsed laser deposition technique. The X-ray diffraction patterns indicated that the perovskite phase was fully formed with polycrystalline structure in all the films. The Raman spectra showed the frequency of the O–Ta–O stretching mode for multilayer and single layer SrBi₂(Ta_0.5Nb_0.5)₂O₉ (SBNT) samples was 827–829 cm⁻¹, which was in between the stretching mode frequency in SBT (813 cm⁻¹) and SBN (834 cm⁻¹) thin films. The dielectric constant was increased from 300 (SBT) to 373 at 100 kHz in the double layer SBT/SBN sample with thickness of each layer being 200 nm. The remanent polarization (2P_r) for this film was obtained 41.7 μC/cm², which is much higher, compared to pure SBT film (19.2 μC/cm²). The coercive field of this double layer film (67 kV/cm) was found to be lower than SBN film (98 kV/cm).     

Microstructures, densification and mechanical properties of TiC–Al2O3–Al composite by field-activated combustion synthesis

Dense TiC–Al₂O₃–Al composite was prepared with Al, C and TiO₂ powders by means of electric field-activated combustion synthesis and infiltration of the molten metal (here Al) into the synthesized TiC–Al₂O₃ ceramic. An external electric field can effectively improve the adiabatic combustion temperature of the reactive system and overcome the thermodynamic limitation of reaction with x < 10 mol. Thereby, it can induce a self-sustaining combustion synthesis process. During the formation of Al₂O₃–TiC–Al composite, Al is molten first, and reacted with TiO₂ to form Al₂O₃, followed by the formation of TiC through the reaction between the displaced Ti and C. Highly dense TiC–Al₂O₃–Al with relative density of up to 92.5% was directly fabricated with the application of a 14 mol excess Al content and a 25 V cm⁻¹ field strength, in which TiC and Al₂O₃ particles possess fine-structured sizes of 0.2–1.0 μm, with uniform distribution in metal Al. The hardness, bending strength and fracture toughness of the synthesized TiC–Al₂O₃–Al composite are 56.5 GPa, 531 MPa and 10.96 MPa m^1/2, respectively.     

In situ co-precipitation synthesis and photoluminescence of YxGd1−xVO4:Tm microcrystalline phosphors by hybrid precursors

Y_xGd_1−xVO₄:Tm³⁺ (5 mol%) phosphors were prepared by in situ co-precipitation technology with the different content ratio of Y/Gd (x = 0.2, 0.3, 0.4, 0.5, 0.6, 0.8, respectively). During the process, rare earth coordination polymers with o-hydroxylbenzoate were used as precursors, composing with polyethylene glycol (PEG) as dispersing media. After heat-treatment of the resulting multicomponent hybrid precursors at 900 °C, the samples were obtained. SEM indicated the particles present good crystalline state, whose crystalline grain sizes were about 0.2–2 μm. Under the excitation of 257 nm, all the materials show the characteristic emission of Tm³⁺ which is the strong blue emission centered at 475 nm originating from ¹G₄ → ³H₆ of Tm³⁺. Besides this, concentration quenching appears in the system of YVO₄:Tm³⁺ and GdVO₄:Tm³⁺. And when x reaches 0.5, the system of Y_xGd_1−xVO₄:Tm³⁺ shows the strongest blue emission.     

Low-temperature growth and orientational control in RuO2 thin films by metal-organic chemical vapor deposition

For growth temperatures in the range of 275°C to 425°C, highly conductive RuO₂ thin films with either (110)- or (101)-textured orientations have been grown by metal-organic chemical vapor deposition (MOCVD) on both SiO₂/Si(001) and Pt/Ti/SiO₂/Si(001) substrates. Both the growth temperature and growth rate were used to control the type and degree of orientational texture of the RuO₂ films. In the upper part of this growth temperature range ( 350°C) and at a low growth rate (< 3.0 nm/min.), the RuO₂ films favored a (110)-textured orientation. In contrast, at the lower part of this growth temperature range ( 300°C) and at a high growth rate (> 3.0 nm/min.), the RuO₂ films favored a (101)-textured orientation. In contrast, higher growth temperatures (> 425°C) always produced randomly-oriented polycrystalline films. For either of these low-temperature growth processes, the films produced were crack-free, well-adhered to the substrates, and had smooth, specular surfaces. Atomic force microscopy showed that the films had a dense microstructure with an average grain size of 50–80 nm and a rms. surface roughness of 3–10 nm. Four-probe electrical transport measurements showed that the films were highly conductive with resistivities of 34–40 μΩ-cm (at 25°C).     

Cathodoluminescence study of SnO2 powders aimed for gas sensor applications

In this paper we report on cathodoluminescence (CL) spectra of SnO₂ powders, synthesized using the wet chemical route. The analysis of influence of the modes of calcination (T_an-450–800 °C), and doping by both Pd and Pt (0.01–10.0 wt.%) on CL spectra was made. It was found that the measurement of CL spectra could be an effective research method of nanostructured metal oxides, aimed for gas sensor applications. It was established that in nanocrystalline SnO₂ the same system of energy levels, associated with radiative recombination, as in single crystalline and polycrystalline SnO₂, is retained. It was found that doping by both Pd and Pt modifies the structural properties of SnO₂ grains. Also, there is an optimum doping; near 0.1–0.2 wt.%, at which a maximum intensity of cathodoluminescence is reached. It was concluded that for low concentrations of both Pd and Pt additives in SnO₂ an improvement of the material's crystal structure is promoted, and is associated with a decrease in the non-radiating recombination rate.     

均匀沉淀法制备核-壳型TiO2@SbxSn1-xO2及其导电性能

以尿素为沉淀剂,采用均匀沉淀法包覆改性TiO₂,制备了核壳型TiO₂@Sb_xSn_1-xO₂（ATO）复合导电粉体,利用SEM、EDS、HRTEM、XRD、XPS、顺磁波谱仪（EPR）、FTIR及激光粒度仪（LPSA）等对其进行表征,并对其导电性的主要影响条件进行了研究及分析,提出了均匀沉淀包覆及反应机制。研究表明,反应温度为92℃时,尿素与金属阳离子摩尔比为10∶1的情况下,OH-释放量及释放速率适中,引入SO₄2-作为催化剂,降低金属阳离子成核能垒,且SO₄2-与Cl-最佳摩尔比为1∶25时,所得产品的纳米Sb_xSn_1-xO₂（ATO）壳层在TiO₂表面包覆均匀连续完整,其厚度约为15 nm。当包覆完全时,随着Sb掺杂量增加,复合粉体电阻率降低,Sn与Sb摩尔比达到12∶1时,再增加Sb含量,其电阻率不变。最优制备条件下,复合粉体电阻率值为7.5 Ωcm,导电性能良好。