The Ni3Al-Ni3Cr-Ni3Mo section of the Ni-Cr-Al-Mo system

An investigation is reported of the constitution of the 75 at % nickel section of the Ni-Cr-Al-Mo system in the temperature range 1523 to 1073 K. Alloys in the region 10 to 20 at % Al were annealed at 1523, 1273, and 1073 K, respectively, and subjected to electron microprobe analysis, X-ray diffraction, and microscopical and hardness examination. Constitutional data are presented as partial isothermal sections and as vertical sections. At 1523 K the section consists only of fields containing ,+ and , the last mentioned phase being predominant. With decreasing temperature the and + fields increase in extent. Also, the NiMo and Ni₃Mo phases were encountered in the ternary Ni-Al-Mo alloy studied. The quaternary + alloys showed small lattice mismatch values, i.e. up to 0.25%. Raft like morphologies of were found in the quaternary alloys, resulting from directional coarsening. Observations of as-cast structures are also reported.     

Phase decomposition in extruded Zn-Al based alloy

Ageing characteristics of an extruded eutectoid Zn-Al based alloy were investigated using X-ray diffraction and scanning electron microscopy techniques. The extruded alloy consisted of Al rich phase and Zn rich _E and phases. The original cast eutectoid Zn-Al alloy was extruded at 250 °C. Both supersaturated _s and _s phase decomposed during extrusion and appeared as fine and coarse lamellar structures. The _E and phases particles formed in the original interdendritic region. It was found that two Zn rich phases _E and decomposed sequentially during ageing at 170, 140 °C. The decomposition of the _E phase occurred as a discontinuous precipitation in the early stage of ageing and the decomposition of the phase took place in a four phase transformation: + T + in the prolonged ageing. Two typical morphologies of the decomposition of the Zn rich phases _E and were distinctive in back-scattered scanning electron microscopy.     

Microstructure and mechanical properties of rapidly quenched L20 and L20+L12 alloys in Ni-Al-Fe and Ni-Al-Co systems

Ductile L2₀-type wires and+L1₂-type duplex wires with high strengths and large elongation in the Ni-Al-Fe and Ni-Al-Co ternary systems have been manufactured directly from the liquid state by an in-rotating-water spinning method. The wire diameter was in the range 80 to 180m and the average grain size was 2 to 4m for the wires and 0.2 to 1.0m for the+ wires. _y, _f and _p of the wires were found to be about 360 to 760 MPa, 560 to 960 MPa, and 0.2 to 5.5%, respectively, for the Ni-Al-Fe system, those of the+ wires were about 395 to 660 MPa, 670 to 1285 MPa, and 3.5 to 17%, respectively, for the Ni-Al-Fe system, and about 260 to 365 MPa, 600 to 870 MPa, and 4.0 to 7.0%, respectively, for the Ni-Al-Co system. Cold-drawing caused a significant increase in _y and _f and the values attained were about 1850 and 2500 MPa, respectively, for Ni-20Al-30Fe and Ni-25Al-30Co wires drawn to about 90% reduction in area. The high strengths, large elongation and good cold-workability of the melt-quenched and+ compound wires have been inferred to be due to the structural change into a low-degree ordered state containing a high density of phase boundaries, suppression of grain-boundary segregation and refinement of grain size.     

IN-713C characteristic properties optimized through different heat treatments

The strength of a nickel-based superalloy hardened through precipitation is related to the volume fraction, particle size and distribution of the precipitated phase, . These parameters may vary as a result of heat treatment, or high-temperatures service. The information obtained, describing the influence of time and temperature on the precipitated phase, , is of special importance owing to its technological application at high temperatures. Dissolution or precipitation kinetics are such that the volume-fraction balance of the phase is quickly established at an ageing temperature given by successive changes due only to the particle growth. The results of the present study describe heat-treatment effects on size and distribution of the phase, and precipitated carbides ageing of a nickel-based superalloy (IN-713C). These on ageing studies at a certain temperature show that the kinetic growth of particles by controlled diffusion follows that r t ^1/3 law.     

Dielectric properties of thin solid films formed on silicon

We report on the measurement of the frequency-dependent complex permittivity, ()=()-i(), over the frequency range, 30 MHz to 6 GHz, of silicon wafers and of thin dielectric films formed on silicon. Measurements, as a function of temperature and time treatments, were obtained by means of an HP Network Analyzer and dielectric probe and the resulting ()and()plots for the silicon wafers are shown to have a Debye-type [1] profile, thereby indicating that the associated polarization mechanism is of the orientational variety.     

Band-theoretical calculation for the anomalous resistivity of Ni near the Curie temperature

The anomalous resistivity of nickel near the Curie temperature T _c is investigated using the itinerant model of the magnetic electron. The 3d-band wave functions are used to calculate the form factor. The temperature derivative of resistivity diverges positively when T approaches T _c from below and negatively when it approaches from above. The calculation of the correlation function shows that both short-range and long-range orders exist. The critical exponents = 1/2 and = 0 are equal to the Ornstein—Zernike values in the paramagnetic region, but in the ferromagnetic region in addition to these values ₁ = 1/2 and ₁ = 0 there is simultaneously a second set of values ₂ = and ₂ = –1.     

Complex microstructural changes in as-cast eutectoid Zn-Al alloy

Phase transformations and microstructural changes of an as-cast eutectoid Zn-Al alloy (ZnAl₂₂Cu₂) were investigated during isothermal holding. The typical dendritic structures consisted of _s phase as a core with the edge of decomposed _s phase and decomposed _s in the interdendritic regions. A series of complex phase transformations was observed. Both decompositions of _s and _s were determined at an early stage of ageing and a four-phase transformation, _f+T+, was observed at the boundaries of _f phase and the phase, instead of clearly observed at the boundaries of phase, in a solution-treated Zn-Al alloy during prolonged ageing.     

Carbothermal production of β′-sialon from alumina,silica and carbon mixture

Mixtures of pure nanometer-sized amorphous silica and -alumina with the atomic ratio SiAl=1 were reduced by a stoichiometric amount of carbon between 1100 and 1450 °C in flowing nitrogen in order to produce -sialon powder. Using aqueous suspensions of starting materials, compacts with different microstructures were prepared for reaction. Silica reduction to SiO occurred at a temperature as low as 1300 °C and part of it was removed with flowing nitrogen. Carbothermal reaction involving nitrogen stated at 1350 °C and Si₂N₂O was found as an intermediate together with SiC, resulting in -sialon formation. Loss of silica from the system led to AlN formation. Decomposition of -sialon into sialon polytypoids (15R, 12H) was observed as a result of sialon and AlN reaction at 1450 °C. The reaction rate of sialon formation was slowed down compared to the carbothermal reduction of kaolin because of the lack of impurities. The microstructure of the reacted pellets influenced the reaction products, and the narrow pore size distribution as well as good homogeneity enhanced -sialon formation.On leave, from Silesian Technical University, Krasiskiego 8, 40-019 Katowice, Poland.     

The dielectric behaviour of single-crystal MgO,Fe/MgO and Cr/MgO

The dielectric constants and loss factors,, for pure single-crystal MgO and for Fe-and Cr-doped crystals have been measured at frequencies, , from 500 Hz to 500 kHz at room temperature. For pure MgO at 1 kHz the values of and the loss tangent, tan , (9.62 and 2.16×10^–3, respectively) agree well with the data of Von Hippel; the conductivity, , varies as ⁿ withn=0.98±0.02. In Fe-doped crystals increases with Fe-concentration (at any given frequency); for a crystal doped with 12800 ppm Fe, was about four times the value for pure MgO. At all concentrations the variation of log with log was linear andn=0.98±0.02. A decrease in with increasing Fe-concentration was also observed. A similar, although less pronounced, behaviour was found in Cr-doped crystals. The effects are discussed in terms of hopping mechanisms.     

Ageing characteristics of rapidly solidified Al-Li-Ti alloys at 473 K

The influence of titanium on the precipitate free zones (PFZs) and on the stable phase is investigated in four melt-spun Al-Li-Ti alloys with 2 mass% lithium and 0.10–0.35 mass% titanium. Rapid solidification gives rise to a homogeneous distribution of titanium on the wheel side of the ribbons, and to a cellular distribution of solute atoms in intermediate regions and on the gas side. Heat treatments of up to 1000 h at 473 K do not modify titanium distribution, which remains in solid solution. During ageing, preferential coarsening of particles occurs on cell walls. The growth rate of the PFZs is lower than in other Al-Li alloys and is mainly controlled by the titanium concentration of the alloys. The nucleation and growth of the stable phase is also delayed by the presence of titanium. These results indicate that the effect of titanium in solid solution is to retain vacancies thus reducing lithium diffusion rate.