Preparation and enhanced electrochemical properties of nano-sulfur/poly(pyrrole-co-aniline) cathode material for lithium/sulfur batteries

Poly(pyrrole-co-aniline) (PPyA) copolymer nanofibers were prepared by chemical oxidation method with cetyltrimethyl ammonium chloride (CTAC) as template, and the nano-sulfur/poly(pyrrole-co-aniline) (S/PPyA) composite material in lithium batteries was achieved via co-heating the mixture of PPyA and sublimed sulfur at 160 °C for 24 h. The component and structure of the materials were characterized by FTIR, Raman, XRD, and SEM. PPyA with nanofiber network structure was employed as a conductive matrix, adsorbing agent and firm reaction chamber for the sulfur cathode materials. The nano-dispersed composite exhibited a specific capacity up to 1285 mAh g⁻¹ in the initial cycle and remained 866 mAh g⁻¹ after 40 cycles.     

Preparation and performance of a core-shell carbon/sulfur material for lithium/sulfur battery

The core-shell carbon/sulfur material with high performance is prepared by a facile and fast deposit method in an aqueous solution. As sulfur ratio is 85% (w/w) in the composite, scanning electron microscope (SEM) and transmission electron microscope (TEM) observation show that the moniliform particles with 10 nm sulfur shells preserve the morphology of carbon cores. Tested as the cathode material in a lithium cell with binary organic electrolyte at room temperature, the composite shows excellent electrochemical performance. It exhibits a specific capacity up to 1232.5 mAh g⁻¹ at the initial discharge and its specific capacity remained above 800 mAh g⁻¹ after 50 cycles. Meanwhile, the composite also exhibits the high-rate behavior at 800 mA g⁻¹ of current density. Assuming a complete reaction to the final product, Li₂S, the utilization of the electrochemically active sulfur is about 85% at the initial cycle. Electrochemical impedance spectroscopy (EIS) is introduced to understand the impact of the microstructure of composite on electrochemistry. According to our study, a novel core-shell structural carbon/sulfur material is proposed and the key factors of the preparation are discussed.     

Synthesis and characterization of high-density LiFePO4/C composites as cathode materials for lithium-ion batteries

To achieve a high-energy-density lithium electrode, high-density LiFePO₄/C composite cathode material for a lithium-ion battery was synthesized using self-produced high-density FePO₄ as a precursor, glucose as a C source, and Li₂CO₃ as a Li source, in a pipe furnace under an atmosphere of 5% H₂-95% N₂. The structure of the synthesized material was analyzed and characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The electrochemical properties of the synthesized LiFePO₄/carbon composite were investigated by cyclic voltammetry (CV) and the charge/discharge process. The tap-density of the synthesized LiFePO₄/carbon composite powder with a carbon content of 7% reached 1.80 g m⁻³. The charge/discharge tests show that the cathode material has initial charge/discharge capacities of 190.5 and 167.0 mAh g⁻¹, respectively, with a volume capacity of 300.6 mAh cm⁻³, at a 0.1C rate. At a rate of 5C, the LiFePO₄/carbon composite shows a high discharge capacity of 98.3 mAh g⁻¹ and a volume capacity of 176.94 mAh cm⁻³.     

A novel micro-spherical CoSn2/Sn alloy composite as high capacity anode materials for Li-ion rechargeable batteries

Micro-scaled spherical CoSn₂/Sn alloy powders synthesized from oxides of Sn and Co via carbothermal reduction at 800 °C were examined for use as anode materials in Li-ion battery. The phase composition and particle morphology of the CoSn₂/Sn alloy composite powders were investigated by XRD, SEM and TEM. The prepared CoSn₂/Sn alloy composite electrode exhibits a low initial irreversible capacity of ca. 140 mAh g⁻¹, a high specific capacity of ca. 600 mAh g⁻¹ at constant current density of 50 mA g⁻¹, and a good rate capability. The stable discharge capacities of 500-515 mAh g⁻¹ and the columbic efficiencies of 95.8-98.1% were obtained at current density of 500 mA g⁻¹. The relatively large particle size of CoSn₂/Sn alloy composite powder is apparently favorable for the lowering of initial capacity loss of electrode, while the loose particle structural characteristic and the Co addition in Sn matrix should be responsible for the improvement of cycling stability of CoSn₂/Sn electrode.     

A novel germanium/carbon nanotubes nanocomposite for lithium storage material

A new nanocomposite of Ge/carbon nanotubes (n-Ge/CNTs) was reported by a facile precursor method through a pyrolysis technique. Among it, germanium nanoparticles are encapsulated with a thin layer of amorphous carbon, which benefits to keep a good electronic contact with carbon nanotubes. Germanium nanoparticles are mainly supported inside the carbon nanotubes, which can effectively buffer the volume changes of Germanium. The composite was an effectively mixed (Li⁺ and e⁻) conducting network, which is vital to a quick Li insertion. The composite was shown to exhibit a reversible capacity of about 750 mAh g⁻¹ (74.4 mA g⁻¹) and an improved rate performance, compared with that of CNTs processed as the same condition. Our results demonstrated the composite to be a good active Li-storage material for Li batteries.     

Synthesis and electrochemical performance of novel loose structured submicro/micro-sized NiSnx alloy composites for lithium batteries

An effective method of carbothermal reduction was employed to prepare spherical microcrystal NiSn_x alloy powders from oxides of Sn and Ni used as anode materials for Li-ion battery. According to XRD, SEM and TEM analysis, the synthesized spherical NiSn_x powders show a loose submicro/micro-sized structure and a multi-phase composition. The prepared NiSn_x alloy composite electrode exhibits a stable discharge capacity of electrode is ca. 380 mAh g⁻¹ at constant current density of 50 mA g⁻¹, and can be retained at 350 mAh g⁻¹ after 25 cycles. Moreover, NiSn_x alloys exhibit excellent high rate performance, i.e. stable discharge capacities of 300-310 mAh g⁻¹ and the coulombic efficiencies of 97.5-99.5% have been obtained at the current density of 500 mA g⁻¹. The loose submicro-sized particle structural characteristic and the Ni addition in Sn matrix should be responsible for the improvement of cycling stability of NiSn_x electrode. The carbothermal reduction method is simple, low-cost and mass-productive, which should be viable to other alloy composite materials system of rechargeable lithium ion batteries.     

1-Alkyl-2,3-dimethylimidazolium bis(trifluoromethanesulfonyl)imide ionic liquids as highly safe electrolyte for Li/LiFePO4 battery

Several 1-alkyl-2,3-dimethylimidazolium bis(trifluoromethanesulfonyl)imide ionic liquids (alkyl-DMimTFSI) were prepared by changing carbon chain lengths and configuration of the alkyl group, and their electrochemical properties and compatibility with Li/LiFePO₄ battery electrodes were investigated in detail. Experiments indicated the type of ionic liquid has a wide electrochemical window (−0.16 to 5.2 V vs. Li⁺/Li) and are theoretically feasible as an electrolyte for batteries with metallic lithium as anode. Addition of vinylene carbonate (VC) improves the compatibility of alkyl-DMimTFSI-based electrolytes towards lithium anode and LiFePO₄ cathode, and enhanced the formation of solid electrolyte interface to protect lithium anodes from corrosion. The electrochemical properties of the ionic liquids obviously depend on carbon chain length and configuration of the alkyl, including ionic conductivity, viscosity, and charge/discharge capacity etc. Among five alkyl-DMimTFSI-LiTFSI-VC electrolytes, Li/LiFePO₄ battery with the electrolyte-based on amyl-DMimTFSI shows best charge/discharge capacity and reversibility due to relatively high conductivity and low viscosity, its initial discharge capacity is about 152.6 mAh g⁻¹, which the value is near to theoretical specific capacity (170 mAh g⁻¹). Although the battery with electrolyte-based isooctyl-DMimTFSI has lowest initial discharge capacity (8.1 mAh g⁻¹) due to relatively poor conductivity and high viscosity, the value will be dramatically added to 129.6 mAh g⁻¹ when 10% propylene carbonate was introduced into the ternary electrolyte as diluent. These results clearly indicates this type of ionic liquids have fine application prospect for lithium batteries as highly safety electrolytes in the future.     

Synthesis and electrochemical performance of Li2FeSiO4/carbon/carbon nano-tubes for lithium ion battery

Li₂FeSiO₄/carbon/carbon nano-tubes (Li₂FeSiO₄/C/CNTs) and Li₂FeSiO₄/carbon (Li₂FeSiO₄/C) composites were synthesized by a traditional solid-state reaction method and characterized comparatively by X-ray diffraction, scanning electron microscopy, BET surface area measurement, galvanostatic charge-discharge and AC impedance spectroscopy, respectively. The results revealed that the Li₂FeSiO₄/C/CNT composite exhibited much better rate performance in comparison with the Li₂FeSiO₄/C composite. At 0.2 C, 5 C and 10 C, the former composite electrode delivered a discharge capacity of 142 mAh g⁻¹, 95 mAh g⁻¹, 80 mAh g⁻¹, respectively, and after 100 cycles at 1 C, the discharge capacity remained 95.1% of its initial value.     

Factors influencing MnO2/multi-walled carbon nanotubes composite's electrochemical performance as supercapacitor electrode

Poor crystallined α-MnO₂ grown on multi-walled carbon nanotubes (MWCNTs) by reducing KMnO₄ in ethanol are characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and Brunauer-Emmett-Telle (BET) surface area measurement, which indicate that MWCNTs are wrapped up by poor crystalline MnO₂ and BET areas of the composites maintain the same level of 200 m² g⁻¹ as the content of MWCNTs in the range of 0-30%. The electrochemical performances of the MnO₂/MWCNTs composites as electrode materials for supercapacitor are evaluated by cyclic voltammetry (CV) and galvanostatic charge-discharge measurement in 1 M Na₂SO₄ solution. At a scan rate of 5 mV s⁻¹, rectangular shapes could only be observed for the composites with higher MWCNTs contents. The effect of additional conductive agent KS6 on the electrochemical behavior of the composites is also studied. With a fixed carbon content of 25% (MWCNTs included), MnO₂ with 20% MWCNTs and 5% KS6 has the highest specific capacitance, excellent cyclability and best rate capability, which gives the specific capacitance of 179 F g⁻¹ at a scan rate of 5 mV s⁻¹, and remains 114.6 F g⁻¹ at 100 mV s⁻¹.     

Mesoporous polyaniline or polypyrrole/anatase TiO2 nanocomposite as anode materials for lithium-ion batteries

A functional composite as anode materials for lithium-ion batteries, which contains highly dispersed TiO₂ nanocrystals in polyaniline matrix and well-defined mesopores, is fabricated by employing a novel one-step approach. The as-prepared mesoporous polyaniline/anatase TiO₂ nanocomposite has a high specific surface area of 224 m² g⁻¹ and a predominant pore size of 3.6 nm. The electrochemical performance of the as-prepared composite as anode material is investigated by cyclic voltammograms and galvanostatic method. The results demonstrate that the polyaniline/anatase nanocomposite provides larger initial discharge capacity of 233 mAh g⁻¹ and good cycle stability at the high current density of 2000 mA g⁻¹. After 70th cycles, the discharge capacity is maintained at 140 mAh g⁻¹. The excellent electrochemical performance of the polyaniline/TiO₂ nanocomposite is mainly attributed to its special structure. Furthermore, it is accessible to extend the novel strategy to other polymer/TiO₂ composites, and the mesoporous polypyrrole/anatase TiO₂ is also successfully fabricated.     

One-step microwave synthesis and characterization of carbon-modified nanocrystalline LiFePO4

The precursors of LiFePO₄ were prepared by a sol-gel method using lithium acetate dihydrate, ferrous sulfate, phosphoric acid, citric acid and polyethylene glycol as raw materials, and then the carbon-modified nanocrystalline LiFePO₄ (LiFePO₄/C) cathode material was synthesized by a one-step microwave method with the domestic microwave oven. The effect of microwave time and carbon content on the performance of the resulting LiFePO₄/C material was investigated. Structural characterization by X-ray diffraction and scanning electron microscopy proved that the olivine phase LiFePO₄ was synthesized and the grain size of the samples was several hundred nanometers. Under the optimal conditions of microwave time and carbon content, the charge-discharge performance indicated that the nanosized LiFePO₄/C had a high electrochemical capacity at 0.2 C (152 mAh g⁻¹) and improved capacity retention; the exchange current density was 1.6977 mA cm⁻². Furthermore, the rate capability was improved effectively after LiFePO₄ was modified with carbon, with 59 mAh g⁻¹ being obtained at 20 C.     

Rapid preparation and electrochemical behavior of carbon-coated Li3V2(PO4)3 from wet coordination

An improved solid-state coordination method namely wet coordination has been developed to synthesize carbon-coated monoclinic Li₃V₂(PO₄)₃ rapidly at a low temperature of 600 °C in 1 h. The structure of the sample was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM) and energy dispersive analysis of X-rays (EDAX). The diffusion coefficient of the lithium ions was measured by cyclic voltammetry (CV). The electrochemical behavior of the sample exhibits a high initial discharge capacity of 130 mAh g⁻¹, which is very close to its theoretical capacity of 132 mAh g⁻¹ under 95 mA g⁻¹ (0.67 C) in the range of 3.3-4.3 V (vs. Li/Li⁺). These results suggest that wet coordination is a promising method for large-scale production of carbon-coated Li₃V₂(PO₄)₃.     

Enhanced electrochemical properties of LiFePO4/C synthesized with two kinds of carbon sources,PEG-4000 (organic) and Super p (inorganic)

Olivine structured LiFePO₄/C cathode was synthesized via a freeze-drying route and followed by microwave heating with two kinds of carbon sources: PEG-4000 (organic) and Super p (inorganic). XRD patterns indicate that the as-prepared sample has an olivine structure and carbon modification does not affect the structure of the sample. Image of SEM shows a uniform and optimized particles size, which greatly improves the electrochemical properties. TEM result reveals the amorphous carbon around the surface of the particles. At a low rate of 0.1 C, the LiFePO₄/C sample presents a high discharge capacity of 157.8 mAh g⁻¹ which is near the theoretical capacity (170 mAh g⁻¹), and it still attains to 149.1 mAh g⁻¹ after 200 cycles. It also exhibits an excellent rate capacity with high discharge capacities of 143.2 mAh g⁻¹, 137.5 mAh g⁻¹, 123.7 mAh g⁻¹ and 101.6 mAh g⁻¹ at 0.5 C, 1.0 C, 2.0 C and 5.0 C, respectively. EIS results indicate that the charge transfer resistance of LiFePO₄ decreases greatly after carbon coating.     

Nanostructured Si/TiC composite anode for Li-ion batteries

Si/TiC nanocomposite anode was synthesized by a surface sol-gel method in combination with a following heat-treatment process. Through this process, nanosized Si was homogeneously distributed in a titanium carbide matrix. The electrochemically less active TiC working as a buffer matrix successfully prevented Si from cracking/crumbling during the charging/discharging process. The interspaces in the Si/TiC nanocomposite could offer convenient channels for Li ions to react with active Si. The Si/TiC composite exhibited a reversible charge/discharge capacity of about 1000 mAh g⁻¹ with average discharge capacity fading of 1.8 mAh g⁻¹ (0.18%) from 2nd to 100th cycle, indicating its excellent cyclability when used as anode materials for lithium-ion batteries.     

Carbon nanobeads as an anode material on high rate capability lithium ion batteries

Carbon nanobeads (CNBs) were prepared by reacting cyclohexachlorobenzene with dispersed sodium metal at 200 °C for 4 h. The CNBs prepared in this manner formed uniform nanobeads, with sizes ranging from 100 to 300 nm. Heating resulted in a reduction in the size of the CNBs, and improvements in their degree of crystallinity. The nanosized carbon materials considerably increased the surface area of the powder, reducing the distance of the intercalation/deintercalation pathway, substantially improving the charge capacity of the lithium ion battery at a high charging rate. The charge capacity of CNBs was found to be 238 mAh g⁻¹, while that of commercial MCMB reached only 36 mAh g⁻¹, when the charging rate was 1C (372 mAh g⁻¹). As the charging rate was further increased to 2C (744 mAh g⁻¹) and 3C (1116 mAh g⁻¹), the charge capacities of CNBs dropped to 173 and 111 mAh g⁻¹, respectively. The cyclic performance of the CNBs was measured and found to be significantly improved in comparison to other carbonaceous materials, for up to 100 cycles. Although cyclic performance did result in a gradual reduction in capacity, the CNBs still greatly exceeded the capacity of MCMB. These results clearly demonstrate the potential role of CNBs as anodes for high capacity Li ion batteries for use in the automobile industry.     

The effect of the interlayer anions on the electrochemical performance of layered double hydroxide electrode materials

Both high energy density and high power density are vitally required for new applications such as electric vehicles. Here we present a comparison of two well-crystallised layered double hydroxides, [Ni₄Al(OH)₁₀]OH and [Ni₄Al(OH)₁₀]NO₃, which shows that the former can maintain a better discharge capacity, 294-299 mAh g⁻¹, than the latter, 233-287 mAh g⁻¹ at a current density of 2000 mA g⁻¹ within about 300 cycles, although both electrodes deliver a similar capacity of 326 mAh g⁻¹ at 200 mA g⁻¹ initially. It is believed that both the more watery interlayer space in [Ni₄Al(OH)₁₀]OH than in [Ni₄Al(OH)₁₀]NO₃ and the morphologic changes induced by anion exchange of NO₃⁻ by OH⁻ during electrochemical cycles play key roles in their behaviour.     

TiO2 nanotube arrays annealed in CO exhibiting high performance for lithium ion intercalation

Anatase titania nanotube arrays were fabricated by means of anodization of Ti foil and annealed at 400 °C in respective CO and N₂ gases for 3 h. Electrochemical impendence spectroscopy study showed that CO annealed arrays possessed a noticeably lower charge-transfer resistance as compared with arrays annealed in N₂ gas under otherwise the same conditions. TiO₂ nanotube arrays annealed in CO possessed much improved lithium ion intercalation capacity and rate capability than N₂ annealed samples. At a high charge/discharge current density of 320 mA g⁻¹, the initial discharge capacity in CO annealed arrays was found to be as high as 223 mAh g⁻¹, 30% higher than N₂ annealed arrays, ∼164 mAh g⁻¹. After 50 charge/discharge cycles, the discharge capacity in CO annealed arrays remained at ∼179 mAh g⁻¹. The improved intercalation capacity and rate capability could be attributed to the presence of surface defects like Ti-C species and Ti³⁺ groups with oxygen vacancies, which not only improved the charge-transfer conductivity of the arrays but also possibly promoted phase transition.     

Facile preparation and good electrochemical hydrogen storage properties of chain-like and rod-like Co-B nanomaterials

Chain-like and rod-like Co-B nanomaterials are prepared by chemical reduction method in cetyltrimethylammonium bromide (CTAB) and polyvinylpyrrolidone (PVP) aqueous solution, respectively. XRD patterns demonstrate that the two materials both have amorphous structures. SEM and TEM images show that the chain-like Co-B constructs of one-by-one tactic ball-like particles with nanoflakes on the surface, whereas the rod-like Co-B alloy possesses a porous nanostructure. The results of electrochemical measurements indicate that, as negative electrode materials of Ni-MH batteries, their electrochemical properties are both better than those of regular Co-B alloy. At the discharge current density 25 mA g⁻¹, the discharge capacities of the chain-like and the rod-like Co-B alloys are 314 mAh g⁻¹ and 292 mAh g⁻¹ after 50 cycles, respectively, which are both higher than that of regular Co-B alloy. XRD patterns of the electrodes on different charge-discharge states illustrate that the discharge capacity is attributed to hydrogenation of Co-B alloy.     

Porous polythiophene as a cathode material for lithium batteries with high capacity and good cycling stability

Polythiophene (PTh) has been synthesized by chemical oxidative polymerization and used as an active cathode material in lithium batteries. The lithium batteries are characterized by cyclic voltammetry (CV), galvanostatic charge/discharge cycling and electrochemical impedance spectroscopic studies (EIS). The lithium battery with the PTh cathode exhibits a discharge voltage of 3.7 V compared to Li⁺/Li and excellent electrochemical performance. PTh can provide large discharge capacities above 50 mA h g⁻¹ and good cycle stability at a high current density 900 mA g⁻¹. After 500 cycles, the discharge capacity is maintained at 50.6 mA h g⁻¹. PTh is a promising candidate for high-voltage power sources with excellent electrochemical performance.     

Electrostatic heterocoagulation of carbon nanotubes and LiCoO2 particles for a high-performance Li-ion cell

Nanotubes were coated on the surface of active LiCoO₂ particles using electrostatic heterocoagulation to enhance the electrochemical properties of a Li-ion battery. Only 0.5 wt% of multiwalled carbon nanotubes (MWCNTs) was added as a conducting agent into the LiCoO₂ cathode, which had a density of 4.0 g cm⁻³. We found that our electrode that was prepared using heterocoagulation with 0.5 wt% of thin MWCNTs maintained a volumetric capacitance of 403 mAh cm⁻¹ after 40 cycles from the initial 624 mAh cm⁻¹, compared with previous result of 310 mAh cm⁻¹ obtained from simple mixing with 3 wt% MWCNTs. The high volumetric capacity with smaller swelling using less amount of MWCNTs was attributed to the self-assembled nanotube network formed between active particles during coagulation, which was maintained with volume expansion during cycle testing.