甘油锌用作PVC热稳定剂的研究

运用刚果红试纸法、热烘箱老化实验法和流变仪试验,以硬脂酸锌作对比,对甘油锌配合物(简称甘油锌)用作聚氯乙烯(PVC)热稳定剂的热稳定作用进行了研究,并对甘油锌的复配进行了研究;还研究了稳定剂对 PVC 耐候性的影响。结果表明,甘油锌与硬脂酸钙在质量比为1.0/1.5时具有较好的协同作用,甘油锌/硬脂酸钙与环氧大豆油和亚磷酸三苯酯质量比为1.0/1.5/0.2/0.2时有较好的协同效应;所研究的甘油锌/硬脂酸钙复合热稳定剂对PVC 具有较好的热稳定作用,PVC 与复合热稳定剂质量比为100.0/2.9时,PVC 的刚果红试验热稳定时间达25 min、热烘老化试验热稳定时间达130 min。另外,研究发现环氧大豆油和亚磷酸三苯酯对硬脂酸锌/硬脂酸钙复合热稳定剂也有较好的协同效应。     

硬质PVC用钙锌复合热稳定剂的研究

运用刚果红试纸法和热烘箱老化实验法，对硬质PVC（聚氯乙烯）用钙锌复合稳定剂的主要组分如硬脂酸钙、硬脂酸锌、多元醇、环氧大豆油、亚磷酸酯以及稳定性助剂等进行了考察，得到了各组分及各组分用量之间协同作用的关系，同时还得到了硬质PVC用钙锌复合热稳定剂的实用配方。     

钙/锌盐复合热稳定剂对CPE高温脱氯化氢的影响

采用刚果红试验法研究钙/锌盐复合热稳定剂对氯化聚乙烯(CPE)脱氯化氢热降解性的影响.结果表明.硬脂酸钙/硬脂酸锌复合热稳定剂与辅助稳定剂环氧大豆油和亚磷酸酯配合使用后具有比普通钙/锌盐更好的稳定效果;当硬脂酸钙/硬脂酸锌并用比为5 : 1,用量为5份,环氧大豆油和亚磷酸酯用量分别为5和1份时,CPE的热稳定性最好.     

PVC新型无毒热稳定剂季戊四醇锌的合成及应用研究

采用固相反应法合成了季戊四醇锌,通过红外光谱及X射线衍射证实形成了新配合物。采用刚果红试纸法与烘箱老化试验测试了季戊四醇锌及与辅助热稳定剂硬脂酸钙、环氧大豆油、水滑石、β-二酮复配下的热稳定效果。结果表明,季戊四醇锌与环氧大豆油协同效果最好,热稳定时间最高可达54 min;季戊四醇锌与β-二酮复配在抑制初期变色时效果最佳;季戊四醇锌作为热稳定剂,使聚氯乙烯（PVC）的热稳定性能得到较大的提升,无锌烧现象,其效果接近于铅盐。     

硬脂酸钙及其复合热稳定剂对PVDC热稳定性能的影响

用刚果红法测定了硬脂酸钙、硬脂酸钙/环氧大豆油和硬脂酸钙/甲基锡热稳定剂对PVDC降解时脱氯化氢的影响.结果表明:硬脂酸钙/环氧大豆油、硬脂酸钙/甲基锡复合热稳定剂的组成分别为2:1和3:1时,具有最佳的协同效应.三种热稳定剂对PVDC降解时释放氯化氢的抑制能力为硬脂酸钙<硬脂酸钙/环氧大豆油<硬脂酸钙/甲基锡,PVD...     

氰尿酸钙/锌的制备及其在PVC制品中的应用

以氰尿酸、氢氧化钙和氧化锌为原料,去离子水为溶剂,分别合成了聚氯乙烯(PVC)用热稳定剂氰尿酸钙、氰尿酸锌。采用元素分析仪(EA)、傅里叶变换红外光谱仪(FTIR)、热失重分析仪(TG)以及扫描电镜(FESEM)对氰尿酸钙/锌进行了表征分析。通过烘箱热老化和刚果红测试考察了氰尿酸钙/锌对PVC制品热稳定性能的影响,并对热稳定机理进行了探究。结果表明,单独加入PVC质量1%的氰尿酸钙或氰尿酸锌,PVC制品的热稳定性要优于加入等量的硬脂酸钙或硬脂酸锌;氰尿酸钙/锌复配后表现出良好的协调作用,氰尿酸钙/锌最佳质量比为3∶1,热稳定时间达28 min,PVC试片在70 min完全锌烧;并且,环氧大豆油(ESBO)是一种非常适合氰尿酸钙/锌体系的辅助稳定剂,能够进一步提高PVC体系的热稳定性能。     

甲基锡及其复合热稳定剂在PVDC中的应用

用变色法测定了甲基锡、甲基锡/环氧大豆油和甲基锡/硬脂酸钙3种热稳定剂对PVDC的热稳定作用.结果表明:3种热稳定剂对PVDC的热稳定作用是甲基锡/硬脂酸钙＞甲基锡/环氧大豆油＞甲基锡,甲基锡/环氧大豆油复合热稳定剂的最佳组成为(1:1)～(2:1),甲基锡/硬脂酸钙复合热稳定剂的最佳组成为1:3.     

金属皂类热稳定剂对软质PVC脱氯化氢反应的影响

本实验通过刚果红法研究金属皂类热稳定剂硬脂酸钙、硬脂脂锌、硬脂酸钡在软质PVC体系中单独使用、两两混合、三者混合使用时的热管理性能以及协同稳定性能.重点研究热稳定剂的用量对软质PVC刚果红试纸初始变色时间和初始变色温度的影响.结果表明：在软质PVC体系中单独使用金属皂类热稳定剂时软质PVC的热稳定性能不好;两两混合时硬脂酸锌/硬脂酸钡按1：2混合和硬脂酸锌/硬脂酸钙按1：2混合时软质PVC体系热稳定性能比硬脂酸锌/硬脂酸钡按1：1和2：1以及硬脂酸锌/硬脂酸钙按1：1、2：1、1：3、3：1混合时要好;三者混合时硬脂酸钙/硬脂酸锌/硬脂酸钡按1：1：1混合时软质PVC体系热稳定性能较好,比两两混合使用时好,同时能有效的抑制软质PVC体系初期着色现象,是软质PVC体系的较佳热稳定剂.     

改性PVC基树脂铅芯的制备与性能

聚氯乙烯(PVC)基树脂铅芯主要以PVC树脂为黏结剂,以石墨、其他有机或无机颜料为着色剂制作而成的铅芯,PVC基树脂铅芯的配方决定着其加工的工艺性与铅芯质量。通过对现有PVC基树脂铅芯的配方产量低、易分解的问题基础上进行分析,提出添加钙锌稳定剂或硬脂酸钙作PVC热稳定剂、环氧大豆油作助稳定剂的改进方案,并进行挤出实验分析和性能测试。结果表明,当加入10份硬脂酸钙、5份环氧大豆油时能获得较稳定的挤出机扭矩、熔体压力和挤出量,可作为生产测试新配方,采用新工艺、新材料成功实现了使用单螺杆挤出机连续挤出改性PVC基树脂铅芯的目标。     

复合钙/锌热稳定剂中的辅助热稳定剂

正辅助热稳定剂是一种特殊的热稳定剂,其特点是单独使用时热稳定作用甚微,但与金属皂类或有机锡类稳定剂并用时会产生协同作用,有效提高金属皂类或有机锡类稳定剂的使用效率,常见的钙/锌复合热稳定剂用的辅助热稳定剂有多元醇类、亚磷酸酯类、环氧类化合物、β-二酮化合物以及水滑石、沸石等。本文总结并论述了常见辅助稳定剂在聚氯乙烯(PVC)加工体系中对钙/锌稳定剂作用与影响。1钙/锌复合热稳定剂     

Stabilization of poly(vinyl chloride). X. Synergisms between epoxidized polybutadienes and metal soaps on the stabilization of poly(vinyl chloride)

Effects of epoxidized 1,2- or 1,4-polybutadienes on the zinc stearate/calcium stearate synergetic soap-induced thermal stabilization of poly(vinyl chloride) (PVC) were investigated by colorimetry. The remarkable stabilization effects of epoxidized polybutadienes could not be observed on the PVC films without synergetic soaps, while the stabilization of PVC was markedly enhanced by combined use of epoxidized polybutadienes with synergetic soaps. Excessive coloration of cool color-producing zinc chloride-polyene complexes that were the source of abrupt discoloration of stabilized PVC was retarded by using epoxidized polybutadienes together with synergetic soap. The synergism of epoxidized polybutadienes was enhanced with increasing epoxy contents. Moreover, the effect is also clearly dependent on degree of dispersion of epoxidized polybutadienes in PVC. Further colorimetries, infrared (IR), and X-ray photoelectron spectroscopies on the various PVC-containing epoxidized polybutadienes and zinc chloride indicated that the epoxy groups capture the zinc chloride. The synergistic effect between epoxidized polybutadienes and metal soap was ascribed to epoxidized polybutadienes serving as acceptors for the excessive cool color-producing zinc chloride produced by zinc stearate to retard the abrupt discoloration of stabilized PVC. The plate-out phenomenon appeared during the molding process of PVC-containing epoxy compounds was considerably retarded by epoxidized polybutadienes which modified polyols. The polyol-modifying epoxidized polybutadienes also exhibited a marked effect on PVC stabilization with metal soap.     

硬脂酸稀土和硬脂酸钙对PVC热稳定特性的比较研究

为有助于加深对稀土热稳定剂的认识,尝试以CaSt2为参照,并以LaSt3为代表,比较研究了硬脂酸稀土对PVC的热稳定特性,并探讨了有关的原理。结果表明:(1)硬脂酸稀土的热稳定特性与CaSt2相似;(2)LaSt3/ZnSt2和环氧大豆油(ESO)的并用效果与CaSt2/ZnSt2相当,但与季戊四醇(PET)和二苯甲酰甲烷(DBM)的并用效果与CaSt2/ZnSt2相比略有逊色;(3)LaSt3/ZnSt2和PET、DBM的并用效果不如CaSt2/ZnSt2的原因可能在于,与Ca2 相比,La3 能更强烈地与Zn2 竞争和PET和DBM形成配合物,从而使后两者的作用更不能得到充分发挥。     

Effect of lanthanide (La(III))‐containing ionomer on thermal stabilization of poly(vinyl chloride)

A type of lanthanide (La(III))‐containing ionomer based on acrylate processing aid (ACR) for poly (vinyl chloride) (PVC) was synthesized, and influence of the ionomer on thermal stabilization of PVC was investigated with visual color comparison and Congo red methods. Results revealed that the ionomer with a suitable La(III) content behaved as a good costabilizer to PVC. It was able to extend static stabilization time of PVC and postpone “zinc burning.” The stabilizing efficiency of the ionomer to PVC depended on ion content, which was discussed in terms of Eisenberg–Hird–Moore model. Moreover, Fourier transform infrared test verified that this ionomer can react with zinc stearate (ZnSt₂) to form some new structures, which is responsible for postponing “zinc burning.” The ionomer and epoxidized soybean oil exhibited a synergistic effect on the stabilizing efficiency of calcium stearate (CaSt₂)/ZnSt₂ stabilizer to PVC compounds. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

取代二苯基脲对PVC的热稳定作用——性能递变规律与机理

用烘箱变色法研究了几种取代二苯基脲对聚氯乙烯(PVC)的热稳定性能。结果表明,取代二苯基脲均具有类似于硬脂酸锌的热稳定特性,属于初效型主热稳定剂,与硬脂酸钙(CaStz)和环氧大豆油并用存在着明显的协同效应;取代二苯基脲的热稳定性能随其分子中与尿母核相连基团的吸电子性的增强而提高;根据其热稳定性能递变规律可以推测出取代二苯基脲是通过其拨基C原子作为亲电原子与PVC发生亲电反应而发挥热稳定作用的,传统的Frye和Horst理论不适用于取代二苯基脲。     

有机锡及其复合热稳定剂对PVDC降解性能的影响

用刚果红法测定了甲基锡、甲基锡/环氧大豆油和甲基锡/硬脂酸钙热稳定剂对聚偏二氯乙烯(PVDC)降解性能的影响。结果表明:对PVDC降解时释放氯化氢的抑制能力为甲基锡甲基锡/环氧大豆油甲基锡/硬脂酸钙,PVDC的刚果红试纸变色时间分别达到23、25和30min。甲基锡/环氧大豆油、甲基锡/硬脂酸钙复合热稳定剂的组成分别为2/1和1/3时具,有最佳的协同效应。