Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

A novel method has been developed to fabricate carbon fiber reinforced SiC (C_f/SiC) composites by combining 3D printing and liquid silicon infiltration process. Green parts are firstly fabricated through 3D printing from a starting phenolic resin coated carbon fiber composite powder; then the green parts are subjected to vacuum resin infiltration and pyrolysis successively to generate carbon fiber/carbon (C_f/C) preforms; finally, the C_f/C preforms are infiltrated with liquid silicon to obtain C_f/SiC composites. The 3D printing processing parameters show significant effects on the physical properties of the green parts and also the resultant C_f/C preforms, consequently greatly affecting the microstructures and mechanical performances of the final C_f/SiC composites. The overall linear shrinkage of the C_f/SiC composites is less than 3%, and the maximum density, flexural strength and fracture toughness are 2.83?±?0.03?g/cm³, 249?±?17.0?MPa and 3.48?±?0.24?MPa m^1/2, respectively. It demonstrates the capability of making near net-shape C_f/SiC composite parts with complex structures.     

Microstructure and mechanical properties of quasi-isotropic chopped fiber-reinforced PyC–SiC matrix composite prepared by novel nondamaging method

In this work, quasi-isotropic chopped carbon fiber-reinforced pyrolytic carbon and silicon carbide matrix (C_f/C–SiC) composites and chopped silicon carbide fiber-reinforced silicon carbide matrix (SiC_f/SiC) composites were prepared via novel nondamaging method, namely airlaid process combined with chemical vapor infiltration. Both composites exhibit random fiber distribution and homogeneous pore size. Young's modulus of highly textured pyrolytic carbon (PyC) matrix is 23.01 ± 1.43 GPa, and that of SiC matrix composed of columnar crystals is 305.8 ± 9.49 GPa in C_f/C–SiC composites. Tensile strength and interlaminar shear strength of C_f/C–SiC composites are 52.56 ± 4.81 and 98.16 ± 24.62 MPa, respectively, which are both higher than those of SiC_f/SiC composites because of appropriate interfacial shear strength and introduction of low-modulus and highly textured PyC matrix. Excellent mechanical properties of C_f/C–SiC composites, particularly regarding interlaminar shear strength, are due to their quasi-isotropic structure, interfacial debonding, interfacial sliding, and crack deflection. In addition to the occurrence of crack deflection at the fiber/matrix interface, crack deflection in C_f/C–SiC composites takes also place at the interface between PyC–SiC composite matrix and the interlamination of multilayered PyC matrix. Outstanding mechanical properties of as-prepared C_f/C–SiC composites render them potential candidates for application as thermal structure materials under complex stress conditions.     

Processing of Cf/SiC composites by hot pressing using polymer binders followed by polymer impregnation and pyrolysis

Continuous carbon fiber (C_f) reinforced silicon carbide (SiC) matrix composite (C_f/SiC) was processed through hot pressing (HP) using polycarbosilane (PCS) in matrix and polysilazane in interphase regions as polymer binders. HP experiments were conducted at 4 MPa, 1200 °C and 1 h; followed by PCS polymer impregnation and pyrolysis (PIP) at 1200 °C under vacuum. The BN/SiC-Si₃N₄ interphase formed on the C_f cloth during BN dispersed polysilazane polymer coating and pyrolysis. The influence of PCS quantity during HP experiments on C_f/SiC composites was studied. Results suggest that sintering of SiC matrix in C_f/SiC composite improves by increasing PCS content during HP; however, high PCS content increases the liquidity of SiC-PCS mixture to flow out of the composite structure. The C_f/SiC composites with relative density ranging from 79 to 83% and flexural strength from 67 to 138 MPa was achieved.     

Effect of preform and carbon matrix on bending strength of Cf/Cu/C composites

Aiming to obtain composites with appropriate mechanical properties for pantograph sliders, copper mesh modified carbon/carbon (C_f/Cu/C) composites were prepared by chemical vapor infiltration (CVI) in C₃H₆ +?N₂ atmosphere and impregnation-carbonization (I-C) with furan resin. In this paper, C_f/Cu/C composites with two kinds of preforms and carbon matrixes were obtained. The effect of preforms and carbon matrixes on bending strength was investigated. The results indicated that the bending strength of carbon fiber/copper mesh reinforced pyrolytic carbon matrix composites was about 181.39–195.43?MPa, while that reinforced resin carbon matrix composites had the worst bending strength around 54.45–57.04?MPa, in terms of the same preform. The bending strength of C_f/Cu/C composites in the parallel orientation and vertical orientation were also similar. As for C_f/Cu/C composites with the same carbon matrix, the bending strength of C_f/Cu/C composites with non-woven fiber/fiber web/copper mesh type preform was higher than that with fiber web/copper mesh type preform. However, the bending strength of carbon fiber/copper mesh reinforced resin carbon matrix composites showed the opposite trend, and its reasons were analyzed and discussed taking advantage of the fracture mechanisms.     

Fabrication of a 3D4d braided SiCf/SiC composite via PIP process assisted with an EPD method

In order to improve the thermal conductivity and full-fill the gaps between the fiber bundles for three-dimensional four-directional (3D4d) braided SiC_f/SiC composites, 500?nm submicron-sized β-SiC particles were introduced into the 3D4d preform by an electrophoretic deposition (EPD) method. ζ-potential of the KD-Ⅱ SiC fibers and the aqueous suspension of the β-SiC particles were analyzed, as well as the efficiency of the deposition. After densified via PIP process, microstructure, three-point bending strength and thermal conductivity of the composite were investigated. The results showed that, SiC particles filled the gaps between the SiC fiber bundles efficiently, and thermal conductivity of the composites fabricated through PIP process assisted by EPD was 2.3 times that of the composites fabricated via PIP only. The bending strength of the EPD-composites was 647.08?±?69.53?MPa, which decreased to 2/3 of that of the composites manufactured only by PIP, owing to the reduction of fiber volume fraction and the damages to the interface coatings and fibers under the action of the electric field.     

High-temperature flexural strength of I-CVI processed Cf/SiC composites with variable interphases

The effect of single-layer pyrocarbon (PyC) and multilayered (PyC/SiC)_n=4 interphases on the flexural strength of un-coated and SiC seal-coated stitched 2D carbon fiber reinforced silicon carbide (C_f/SiC) composites was investigated. The composites were prepared by I-CVI process. Flexural strength of the composites was measured at 1200 °C in air atmosphere. It was observed that irrespective of the type of interphase, the seal coated samples showed a higher value of flexural strength as compared to the uncoated samples. The flexural strength of 470 ± 12 MPa was observed for the seal coated C_f/SiC composite samples with multilayered interphase. The seal coated samples with single layer PyC interphase showed flexural strength of 370 ± 20 MPa. The fractured surfaces of tested samples were analyzed in detail to study the fracture phenomena. Based on microstructure-property relations, a mechanism has been proposed for the increase of flexural properties of C_f/SiC composites having multilayered interphase.     

Additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites via paper laminating,direct slurry writing,and precursor infiltration and pyrolysis

In this study, continuous carbon reinforced C_f/(Ti_0.2Zr_0.2Hf_0.2Nb_0.2Ta_0.2)C–SiC high entropy ceramic matrix composites were additively manufactured through paper laminating (PL), direct slurry writing (DSW), and precursor infiltration and pyrolysis (PIP). (Ti_0.2Zr_0.2Hf_0.2Nb_0.2Ta_0.2)C high entropy ceramic (HEC) powders were synthesized by pressureless sintering and ball milling. A certain proportion of HEC powder, SiC powder, water, binder, and dispersant were mixed to prepare the HEC-SiC slurry. Meanwhile, BN coating was prepared on the 2D fiber cloth surface by the boric acid-urea method and then the cloth was cut into required shape. Additive manufacturing were conducted subsequently. Firstly, one piece of the as-treated carbon fiber cloth was auto-placed on the workbench by paper laminating (PL). Then, the HEC-SiC slurry was extruded onto the surface of the cloth by direct slurry writing (DSW). PL and DSW process were repeated, and a C_f/HEC-SiC preform was obtained after 3 cycles. At last, the preform was densified by precursor infiltration and pyrolysis (PIP) and the final C_f/HEC-SiC composite was prepared. The open porosity of the C_f/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 7.7, 10.6, and 11.3%, respectively. And the density of the C_f/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 2.9, 2.7 and 2.3 g/cm³, respectively. The mechanical properties of the C_f/HEC-SiC composites increased firstly and then decreased with the HEC content increase, reaching the maximum value when the HEC volume fraction was 30%. The mechanical properties of the C_f/HEC-SiC composites containing 45, 30 and 15% HEC were as follows: flexural strength (180.4 ± 14 MPa, 183.7 ± 4 MPa, and 173.9 ± 4 MPa), fracture toughness (11.9 ± 0.17 MPa m^1/2, 14.6 ± 2.89 MPa m^1/2, and 11.3 ± 1.88 MPa m^1/2), and tensile strength (71.5 ± 4.9 MPa, 98.4 ± 12.2 MPa, and 73.4 ± 8.5 MPa). From this study, the additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites was achieved, opening a new insight into the manufacturing of ceramic matrix composites.     

Influence of the SiC matrix introduction time on the microstructure and mechanical properties of Cf/Hf0.5Zr0.5C-SiC ultra-high temperature composites

C_f/Hf_0.5Zr_0.5C-SiC composites were prepared by introducing Hf_0.5Zr_0.5C matrix (11 cycles) and SiC matrix (9 cycles) into the carbon cloth preform through precursor impregnation and pyrolysis (PIP) process. The influence of the introduction time of SiC matrix on the microstructure and mechanical properties of C_f/Hf_0.5Zr_0.5C-SiC composites was studied, and the results show that with the increase of the PIP cycles of the SiC matrix introduced before Hf_0.5Zr_0.5C matrix, the composite open porosity decreased, and the flexural strength and modulus presented an obvious upward trend. CS45 sample, which has 4 cycles of PIP SiC introduced in advance, has the highest flexural strength, flexural modulus and interfacial shear strength of 402.73 ± 35.73 MPa, 56.92 ± 3.97 GPa and 100.88 ± 7.79 MPa, respectively. Hf_0.5Zr_0.5C matrix has a loose and porous structure, so when more SiC matrix was introduced in advance, its covering effect on the surface of fibers led to less intra-bundle pores and thusly denser composite structure, and due to the compactness of SiC matrix, better overall bonding of fiber, interface and matrix was achieved, as well as better load transfer effect, which led to obvious interfacial debonding and cracking based on the in-situ SEM observation during flexural tests. While in the sample without pre-introduced SiC, the cracking occurred mainly between the interface and porous matrix and the overall performance of the material was poor.     

Additive manufacturing of continuous carbon fiber–reinforced silicon carbide ceramic composites

A material extrusion (MEX) technology has been developed for the additive manufacturing of continuous carbon fiber–reinforced silicon carbide ceramic (C_f/SiC) composites. By comparing and analyzing the rheological properties of the slurries with different compositions, a slurry with a high solid loading of 48.1 vol% and high viscosity was proposed. Furthermore, several complex structures of C_f/SiC ceramic composites were printed by this MEX additive manufacturing technique. Phenolic resin impregnation–carbonization process reduces the apparent porosity of the green body and protects the C_f. Finally, the reactive melting infiltration (RMI) process was used to prepare samples with different C_f contents from 0 to 2 K (a bundle of carbon fibers consisting of 1000 fibers). Samples with C_f content of 1 K show the highest bending strength (161.6 ± 10.5 MPa) and fracture toughness (3.72 ± 0.11 MPa·m^1/2) while the thermal conductivity of the samples with the C_f content of 1 K reached 11.0 W/(m·K). This study provides a strategy to prepare C_f/SiC composites via MEX additive manufacturing and RMI.     

Effects of random chopped short carbon fibers on microstructure and mechanical properties of joints for Cf/SiC composites by reaction bonding process

Random chopped short carbon fibers (C_sf)/phenol-formaldehyde resin (PF)/SiC powder mixtures are used as filler for the joining of C_f/SiC composites to obtain SiC interlayer at the joining region. The influences of C_sf on the microstructure and mechanical properties have been investigated. Research shows that the introduction of C_sf can improve the microstructure uniformity of the joint and reduce residual silicon content in the interlayer. The joint achieve a high flexural strength of 232?±?33?MPa as the carbon fiber content is 30?wt.%, which is similar to that of the C_f/SiC composites (220?±?21?MPa). The decrease in residual silicon content and the formation of nano-sized SiC particles are the main reasons for high joining strength.     

Fabrication of carbon fiber reinforced ceramic matrix composites with improved oxidation resistance using boron as active filler

Boron was introduced into C_f/SiC composites as active filler to shorten the processing time of PIP process and improve the oxidation resistance of composites. When heat-treated at 1800 °C in N₂ for 1 h, the density of composites with boron (C_f/SiC-BN) increased from 1.71 to 1.78 g/cm³, while that of composites without boron (C_f/SiC) decreased from 1.92 to 1.77 g/cm³. So when boron was used, two cycles of polymer impregnation and pyrolysis (PIP) could be reduced. Meanwhile, the oxidation resistance of composites was greatly improved with the incorporation of boron-bearing species. Most carbon fiber reinforcements in C_f/SiC composite were burnt off when they were oxidized at 800 °C for 10 h. By contrast, only a small amount of carbon fibers in C_f/SiC-BN composite were burnt off. Weight losses for C_f/SiC composite and C_f/SiC-BN composite were about 36 and 16 wt%, respectively.     

Mechanical properties and microstructures of 2D Cf/ZrC–SiC composites using ZrC precursor and polycarbosilane

Two-dimensional C_f/ZrC–SiC composites were fabricated through mold-pressing and polymer infiltration and pyrolysis (PIP) using T700SC plain weave fiber fabrics as reinforcements with ZrC precursor and polycarbosilane. The mechanical properties and microstructures of the composites with 34, 45, and 56% fiber fraction were investigated. All composites showed a typical non-brittle fracture behavior and a large amount of pulled-out fibers were observed on the fracture surface. The bending strength and elastic modulus of the composite with 56 vol% fiber fraction increased up to 582 ± 80 MPa and 167 ± 25 GPa, with increasing fiber fraction. The mass loss and linear recession rate of the composites during the oxy-propane torch test were 0.008 g/s and ?0.003 mm/s, respectively. The formation of a ZrSiO₄ melt on the surface of the composite significantly contributed to the excellent ablative property of the 2D C_f/ZrC–SiC composites.     

Effect of short carbon fiber content on the mechanical properties of TiB2-based composites prepared by spark plasma sintering

In this study, TiB₂-30 vol% SiC composites containing 0, 5, 10, and 15 vol% short carbon fibers (C_f) were produced by spark plasma sintering (SPS). The effect of carbon fiber content on microstructure, density, and mechanical properties (micro-hardness and flexural strength) of the fabricated composites was studied. Scanning electron microscopy (SEM) results indicated that the fibers were uniformly dispersed in the TiB₂–SiC matrix using wet ball milling before SPS process. Fully dense TiB₂–SiC–C_f composites were achieved by SPS process at 1900°C for 10 min under 30 MPa. With the addition of fibers, the relative density of the composites did not change considerably. Mechanical tests revealed that microhardness was reduced about 19% by the incorporation of carbon fibers, whereas the flexural strength improved significantly. However, the flexural strength diminished by adding carbon fibers above to critical value (5 vol%) due to residual thermal stresses, nonhomogeneous structure and graphitization of carbon fibers. It was found that the composite with 5 vol% C_f had the highest flexural strength (482 MPa), which was enhanced by 20% compared with the TiB₂–SiC composite.     

Processing and mechanical performance of 3D Cf/SiCN composites prepared by polymer impregnation and pyrolysis

The processing of 3D carbon fiber reinforced SiCN ceramic matrix composites prepared by polymer impregnation and pyrolysis (PIP) route was improved, and factors that determined the mechanical performance of the resulting composites were discussed. 3D C_f/SiCN composites with a relative density of ∼81% and uniform microstructure were obtained after 6 PIP cycles. The optimum bending strength, Young's modulus and fracture toughness of the composites were 75.2 MPa, 66.3 GPa and 1.65 MPa m^1/2, respectively. The residual strength retention rate of the as-pyrolyzed composites was 93.3% after thermal shock test at ΔT = 780 °C. It further degraded to 14.6% when the thermal shock temperature difference reached to 1180 °C. The bending strength of the composites was 35.6 MPa after annealing at 1000 °C in static air. The deterioration of the bending strength should be attributed to the strength degradation of carbon fibers and decomposition of interfacial structure.     

Effects of in-situ carbon layer and volume fraction of SiC fiber on the mechanical properties and fracture behaviors of SiCf/SiC composites fabricated by a modified PIP method

Unidirectional SiC_f/SiC composites (UD SiC_f/SiC composites) with excellent mechanical properties were successfully fabricated by a modified PIP method which involved the preparation of film-like matrix containing carbon layer with a low concentration PCS solution followed by the rapid densification of composites with a high concentration PCS solution. Carbon layers were in-situ formed and alternating with SiC layers in the as-received matrix. The unique microstructure endows the composites with appropriate interfacial bonding state, good load transfer ability of interphase and matrix and load bearing ability of fiber, and great crack deflection capacity, which ensures the synergy of high strength and toughness of composites. It is also found that the fiber volume fraction in the preform makes a non-negligible effect on the distribution of interphase and matrix, of which the reasonable adjustment can be utilized to optimize the mechanical properties of composites. Compared with the composites only using high concentration PCS solution, the UD SiC_f/SiC composites prepared by the modified PIP method exhibit superior mechanical properties. Ultrahigh flexural strength of 1318.5 ± 158.3 MPa and fracture toughness of 47.6 ± 5.6 MPa·m^1/2 were achieved at the fiber volume fraction of 30%.     

Combustion synthesis of SiC-based ceramics reinforced by discrete carbon fibers with in situ grown SiC nanowires

This study proposes a combustion-based ceramic matrix composite processing technique intended on single-step in situ deposition of single-crystal SiC nanowires (SiC_nw) on the surface of carbon fibers (C_f) and formation of SiC_nw–reinforced SiC matrix. This was accomplished by Ta-catalyzed combustion of poly-(C₂F₄)-containing reactive mixtures with pre-mixed chopped C_f. Depending on the combustion conditions, carbon fiber surface is subjected either to formation of diffusion layers, ceramic particle incrustation or growth of continuous arrays of carbon-coated single-crystal SiC_nw with a nearly defect-free lattice, 10–50 nm diameter and 15–20 μm length. Thermodynamics, phase and structure formation mechanisms are explored, and the optimal conditions are outlined for reproducible C_f/in situ SiC_nw dual reinforcement of SiC-based ceramics. Hot pressing at 1500 °C produced C_f/in situ SiC_nw-reinforced ceramic SiC–TaSi₂ specimens with a relative density of 97%, 19 GPa Vickers hardness, 3-point flexural strength σ = 420 ± 70 MPa and fracture toughness K_1C = 12.5 MPa m^1/2.     

Tailoring Carbon Fiber/Carbon Nanotubes Interface to Optimize Mechanical Properties of Cf‐CNTs/SiC Composites

C_f/SiC composites were fabricated using fiber coatings including CNTs and matrix infiltration using the polymer impregnation and pyrolysis process. Interface between fiber and CNTs (CF/CNTs) was tailored to optimize mechanical properties of hybrid composites. The tailored interphases, such as Pyrocarbon (PyC) and PyC/SiC, protect fibers from degradation during the growth of CNTs successfully. Hybrid composites with well‐tailored CF/CNTs interface displayed significantly increased mechanical strength (352 ± 21 MPa) compared with that (34 ± 3 MPa) of composites reinforced with CNTs, which grown on carbon fibers directly. The interfacial bonding strength of hybrid composites was improved and optimized by tailoring the CF/CNTs interface. Interfacial failure modes were studied, and a firm interface bonding at the joint where CNTs grown was observed.     

Preparation and characterization of ZrB2 and TaC containing Cf/SiC composites via Polymer-Infiltration-Pyrolysis process

To improve the thermo-chemical resistance of PIP–C_f/SiC composites, the SiC matrix is modified by adding ZrB₂ and Ta powder to the pre-ceramic slurry to form C_f/SiC–ZrB₂–TaC composites. Within this study the modified composites are investigated regarding their microstructure, chemical composition and physical properties (density = 2,39–2,72 g/cm³; porosity = 20,3–24,8 vol.-%; fiber volume content = 52–57 vol.-%). Mechanical properties are investigated in order to ensure that there is no negative influence by ZrB₂ and TaC matrix modification. The matrix modification is followed by an improvement in bending strength (up to 27% increase), Young’s modulus (up to 28% increase) and for interlaminar shear strength (up to 22% increase). Finally the thermo-chemical behavior of the C_f/SiC–ZrB₂–TaC composites is evaluated in a combustion chamber-like environment using the Airbus Group long-term material test facility (Environmental Relevant Burner Rig-Kerosene, ERBURIG^K). The results show that the thermo-chemical resistance of C_f/SiC–ZrB₂–TaC composites is improved and the oxygen permeability through the composite is decreased (from 5 to 1 layer).     

Co-reinforcing of ZrB2–SiC ceramics with optimized ZrC to Cf ratio

Characteristics of ZrB₂–SiC ultrahigh temperature ceramic matrix composites (UHTCMCs) reinforced with ZrC and carbon fiber (C_f) were investigated in this article. Spark plasma sintering (SPS) process was utilized to fabricate the samples at 1800 °C for 5 min under 30 MPa punch pressure and vacuumed atmosphere. In all samples, the volume ratio of ZrB₂: SiC was equal to 4:1, and the summation of ZrC and C_f reinforcements was 7.5 vol% with different ZrC: C_f ratios. Field emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), densitometry, flexural strength, and hardness measurements were employed for characterization of the prepared samples. Microstructural inspection revealed the formation of SiC sheath around the carbon fibers due to several reactions in the surface SiO₂ layers existed on the SiC particles. Optimal flexural strength (628.4 MPa) and hardness (20.8 GPa) values were achieved for the sample co-reinforced with 6.5 vol% ZrC and 1 vol% C_f, with a relative density of 97.7%.     

Mechanical properties and microstructure evolution of 3D Cf/SiBCN composites at elevated temperatures

3D C_f/SiBCN composites were fabricated by an efficient polymer impregnation and pyrolysis (PIP) method using liquid poly(methylvinyl)borosilazanes as precursor. Mechanical properties and microstructure evolution of the prepared 3D C_f/SiBCN composites at elevated temperatures in the range of 1500‐1700°C were investigated. As temperature increased from room temperature (371 ± 31 MPa, 31 ± 2 GPa) to 1500°C (316 ± 29 MPa, 27 ± 3 GPa), strength and elastic modulus of the composite decreased slightly, which degraded seriously as temperature further increased to 1600°C (92 ± 15 MPa, 12 ± 2 GPa) and 1700°C (84 ± 12 MPa, 11 ± 2GPa). To clarify the conversion of failure mechanisms, interfacial shear strength (IFSS) and microstructure evolution of the 3D C_f/SiBCN composites at different temperatures were investigated in detail. It reveals that the declines of the strength and changes of the IFSS of the composites are strongly related to the defects and SiC nano‐crystals formed in the composites at elevated temperatures.