Formation of vertical cracks in air plasma sprayed YSZ coatings using unpyrolyzed powder

Thick thermal barrier coatings (TTBCs) with vertical cracks deposited by air plasma spray (APS) and solution precursor plasma spray (SPPS) techniques have been widely investigated to achieve good thermal insulation along with reasonable service life. In this study, synthesized unpyrolyzed YSZ powder was air plasma sprayed in order to produce segmentation crack TTBCs. The microstructure and hardness of the deposits were then compared with those of the conventional TTBCs and dense vertically cracked (DVC)TTBCs. In this regard, spraying parameters were optimized to achieve deposits with the appropriate amount of unpyrolyzed particles in them to assist inducing vertical cracks in the deposited layers. The effect of the unpyrolyzed particles on microstructure, porosity, and microhardness of plasma sprayed coatings were also evaluated and compared. The new fabricated coating showed a bimodal structure combining non-molten sub-micron size particles and conventional splats along with segmentation cracks with higher amount of porosity and lower hardness compared to those of the DVC coatings. The results implied that, depositing unpyrolyzed powder by APS, as a new approach for achieving segmentation crack TTBCs, is very promising.     

Thick thermal barrier coatings with different segmentation crack densities: Microstructure analysis and thermal oxidation behavior

Thick thermal barrier coatings (TTBCs) have been developed to increase the lifetime of hot section parts in gas turbines by increasing the thermal insulating function. The premeditated forming of segmentation cracks was found to be a valuable way for such an aim without adding a new layer. The TTBC introduced in the current study are coatings with nominal thickness ranging from 1 to 1.1 consisting of MCrAlY bond coat and 8YSZ top coat deposited by air plasma spray technique (APS). TTBCs with segmented crack densities of 0.65 mm^?1 (type-A) and 1 mm^?1 (type-B) were deposited on a superalloy substrate by adjusting the coating conditions. It was found that the substrate temperature has an influential role in creating the segmentation crack density. The crack density was found to increase with substrate temperature and liquid splat temperature. The two types of coatings (type-A and B) with different densities of segmentation crack were heat-treated at 1000 °C (up to 100 h) and 1100 °C (up to 500 h). The variation of hardness measured by indentation testing indicates a similar trend in both types of coatings after heat treatments at 1000 °C and 1100 °C. Weibull analysis of results demonstrates that higher preheating coating during the deposition results in a denser YSZ coating. The growth rate of TGO for TTBCs was evaluated for cyclic and isothermal oxidation routes at 1000 °C and 1100 °C. The TGO shows the parabolic trend for both two types of coatings. The Kps value for two oxidation types is between 5.84 × 10^?17 m²/s and 6.81 × 10^?17 m²/s. Besides, the type B coating endures a lifetime of more than 40 cycles at thermal cycling at 1000 °C.     

Atmospheric plasma sprayed 7%-YSZ thick thermal barrier coatings with controlled segmentation crack densities and its thermal cycling behavior

Yttria-stabilized zirconia (YSZ)-coatings are deposited on Ni-based superalloy IN738 by atmospheric plasma spraying (APS). For the first time, controlled segmentation crack densities are manually developed in the coatings, even after the APS deposition. This method allows to user to control segmentation densities as well as cracks depth, which could be designed as per coating thickness and required application. Thermal cycling test shows promising strain tolerance behavior for the segmented coatings, whereas coating without segmentation could not sustain even for its first thermal cycle period. Further, microstructural studies reveal that a very thin layer of TGO was formed and obvious no coating failure or spallation was observed after thermal cycling test at 1150 °C for 500 cycles.     

Characterization of Thermal Barrier Coatings Produced by Various Thermal Spray Techniques Using Solid Powder,Suspension, and Solution Precursor Feedstock Material

Use of a liquid feedstock in thermal spraying (an alternative to the conventional solid powder feedstock) is receiving an increasing level of interest due to its capability to produce the advanced submicrometer/nanostructured coatings. Suspension plasma spraying (SPS) and solution precursor plasma spraying (SPPS) are those advanced thermal spraying techniques which help to feed this liquid feedstock. These techniques have shown to produce better performance thermal barrier coatings (TBCs) than conventional thermal spraying. In this work, a comparative study was performed between SPS‐ and SPPS‐sprayed TBCs which then were also compared with the conventional atmospheric plasma‐sprayed (APS) TBCs. Experimental characterization included SEM, porosity analysis using weight difference by water infiltration, thermal conductivity measurements using laser flash analysis, and lifetime assessment using thermo‐cyclic fatigue test. It was concluded that SPS coatings can produce a microstructure with columnar type features (intermediary between the columnar and vertically cracked microstructure), whereas SPPS can produce vertically cracked microstructure. It was also shown that SPS coatings with particle size in suspension (D₅₀) <3 μm were highly porous with lower thermal conductivity than SPPS and APS coatings. Furthermore, SPS coatings have also shown a relatively better thermal cyclic fatigue lifetime than SPPS.     

Study on gradient structure and interface mechanical properties of n–8YSZ/AlCoCrFeNi high–entropy coatings

In this study, gradient and double-layer coatings were prepared by atmospheric plasma spraying (APS) with nano ZrO₂–8%Y₂O₃(n–8YSZ)/AlCoCrFeNi high–entropy powder. The microhardness of the gradient coating changed in a manner consistent with the microstructure, and the average bond strength of the gradient coating was 2.50 times higher than that of the double-layer coating, indicating that the gradient structure of the coating can improve the sharp interface of the coating, and play a significant role in dispersion toughening to improve the bond strength of the coating. After 450 thermal cycles, the double-layer coating exhibited transverse propagation cracks accompanying coating spalling. In contrast, vertical cracks occurred inside the gradient coating, effectively increasing the coating strain tolerance and improving the coating life. Simultaneously, internal oxidation and cracks appeared in the substrate during cycles, the cracks were more obvious, and bridging occurred in the substrate of the double-layer coating, the substrate under the protection of the gradient coating produced microcracks that were discontinuous, indicating that the design of the gradient structure of the coating can effectively release the internal stress and improve the thermal shock resistance of the coating.     

Evolution of cracks within an Al2O3–40 wt%TiO2/NiCoCrAl gradient coating

In this paper, an Al₂O₃–40?wt%TiO₂/NiCoCrAl gradient coating is deposited by atmospheric plasma spraying (APS). The microstructure and element distribution of the coating are studied by scanning electron microscopy (SEM) and electron probe X-ray microanalysis (EPMA). The crack propagation behaviour in the coating under applied and thermal stress is analysed through a three-point bending test and a thermal shock test, respectively. Two rapid propagation processes of the cracks can be found during the three-point bending test, which lead to two peaks in the load-displacement curves of the gradient coating. The gradual change in the composition also has an effect on the crack propagation process within the coating. Non-directional propagation paths of cracks and the formation of oxides can be observed in the gradient region under the effect of thermal stress, which lead to the spallation failure of the coating.     

Sintering resistance of suspension plasma sprayed 7YSZ TBC under isothermal and cyclic oxidation

This study examines sintering resistance of a thermal barrier coating (TBC), composed of a 7YSZ suspension plasma sprayed (SPS) top coat (TC), an air plasma sprayed (APS) NiCoCrAl bond coat (BC), and an INCONEL 625 substrate, under isothermal and cyclic conditions with a peak temperature of 1080 °C for 400, 800, and 1300 h/cycles. Microstructure, phase composition and microstrain were examined using SEM and XRD. Mechanical properties of fracture toughness, hardness and elastic modulus were obtained using nano-indentation. Samples under cyclic conditions presented faster sintering rate than under isothermal condition due to larger compressive strain and frequent heating and cooling cycles. Faster degradation of mechanical properties due to sintering leads to shorter lifetime of SPS coating under cyclic conditions. Moreover, vertical cracks within SPS coatings reduces compressive stress leading to a greater lifetime as compared to APS coatings exposed to similar conditions.     

Review of suspension and solution precursor plasma sprayed thermal barrier coatings

As one of the promising methods that can be employed to fabricate high-performance thermal barrier coatings (TBCs), suspension plasma spraying (SPS) or solution precursor plasma spraying (SPPS) has received significant attention in academic research. Enhanced performances have been shown in the SPS-/SPPS-coatings due to their special microstructures, such as uniformly distributed micro-pores, vertical cracks or columnar structures. Since there are more complexities than conventional plasma spraying methods, many works have been devoted to study the mechanism and properties of SPS-/SPPS-coatings during the past decades. In this work, the latest development of SPS or SPPS is reviewed in order to discuss some key issues in terms of preparation of suspension or solution precursor, injection mode of liquid phase, interaction between liquid and plasma jet, microstructure of as-sprayed coatings and corresponding deposition mechanism. Meanwhile, the potential application of SPS or SPPS in some new-type TBCs is introduced at the end of this paper.     

Changes in thermal conductivity and thermal shock resistance of YSZ-SiO2 suspension plasma spray coatings according to various raw material particle sizes

Recently, a technique for improving the thermal efficiency of automotive engines has received considerable attention, namely the application of thermal insulation coatings to automotive engine components to reduce heat loss. This study presents thermal shock resistance and related microstructural changes and thermal properties of 8 wt% yttria-stabilized zirconia (8YSZ)/SiO₂ multi-compositional thermal insulation coatings with suspensions of various particle sizes, when subjected to suspension plasma spray. After 10,000 cycles of thermal shock testing of the coatings, it was found that different degradation behavior related to the different microstructure of the coatings was influenced by the particle sizes of the suspension. The thermal conductivity of the coatings was significantly reduced by increasing the distribution of the unmelted particles within the coating.     

Investigation of the thermomechanical properties of a plasma-sprayed nanostructured zirconia coating

Yttria partially stabilized nanostructured zirconia coatings were deposited by atmospherical plasma spraying (APS). The microstructure of the as-sprayed nanostructured coating was characterized with Scanning electronic microscopy (SEM), Transmission electron microscopy (TEM), X-ray diffraction (XRD) and Raman spectrum (RS). The laser-flash diffusivity method and push-rod method were used to examine the thermomechanical properties of the nanostructured zirconia coatings. The results obtained indicated that the plasma-sprayed zirconia coating possessed nano-structure and its average grain size was about 73 nm. The average thermal expansion coefficients of the nanostructured coating at the first thermal cycle and second thermal cycle from room temperature to 1200 °C are 11.0 and 11.6×10⁻⁶ °C⁻¹, respectively. The thermal diffusivity of the nanostructured zirconia coating was 1.80–2.54×10⁻³ cm²/s between 200 and 1200 °C. The microhardness of the nanostructured zirconia coating was 8.6 GPa, which was 1.6 times as large as that of traditional zirconia coating.     

Assessment of the performance of Y2SiO5-YSZ/YSZ double-layered thermal barrier coatings

Y₂SiO₅ is a promising material for the thermal barrier coatings due to its low thermal conductivity, high temperature stability and exceptional resistance for molten silicate attack. However, it suffers low fracture toughness and low coefficient of thermal expansion compared with yttria-stabilized zirconia (YSZ). In this study, a composite coating approach, i.e., incorporating YSZ into Y₂SiO₅ coating, was employed to overcome those limitations. The double-layered Y₂SiO₅-YSZ/YSZ coatings were fabricated using atomospheric plasma spraying and tested under thermal cycling at 1150 °C. The phase compositions, microstructure, mechanical properties and the failure behavior were evaluated. It was found that the amorphous phase during spraying would crystallize at high temperature accompanied by volume shrinkage, leading to cracks and spallation in the coating. With YSZ addition, the composite coatings exhibited a much longer lifetime than the single phase Y₂SiO₅ coating due to a lower volume shrinkage and enhanced toughness.     

Sintering resistance of advanced plasma-sprayed thermal barrier coatings with strain-tolerant microstructures

Sintering is one of the key issues in the high temperature service of thermal barrier coatings (TBCs), considering the continuously increasing operation temperature of gas-turbine for higher energy efficiency. Based on the conventional processing method of air plasma spraying (APS), suspension plasma spraying (SPS) technique has been developed recently, in order to improve the strain tolerance of TBCs. This strain tolerance of plasma-sprayed TBCs is largely effected by the sintering behavior, which is presently not fully understood. In this work, evolution of mechanical properties, in terms of Young’s modulus and viscosity, is systematically investigated by in-situ three-point bending test at 1200?°C on free-standing coatings, including micro-cracked APS, segmented APS, vertically cracked SPS and columnar structured SPS TBCs and correlated to the microstructural evolution. Based on experimental results, power law relations are proposed for the sintering induced mechanical evolution, which deepen the understanding of the sintering behavior of plasma-sprayed TBCs.     

Evaluation of microstructure evolution of thermal barrier YSZ coating after thermal exposure

Understanding the microstructural transformation of plasma sprayed (APS) yttria-stabilized zirconia (YSZ) after experiencing the thermal shocking cycles is practically important for the coating optimization in terms of structure and performance. In this study, thermal shocking tests were conducted on the YSZ coated piston crown. The microscopic morphology and structure alteration across the YSZ coating interface over the piston crown was characterized by the ex-situ techniques. The results revealed that the YSZ coating primarily consisted of a stable tetragonal phase, without the monoclinic phase even after 800 cycles of thermal shocking. As the thermal shocking test continued, the pore number within the YSZ coating gradually decreased due to their spontaneous closure and the grain size correspondingly increased. Some visible cracks parallel to the interface consisting of YSZ and bonding layer happened at the localized regions of the YSZ coating. The stress state of YSZ coating was from originally tensile to compressive after thermal exposure, which helped prolonging the service lifetime of YSZ coating. In particular, the thermal shock resistance of plasma sprayed YSZ coated piston crown in association with the varying microstructure was also discussed.     

Hot corrosion and thermal shock resistance of Dense-CYSZ/YSZ bilayer thermal barrier coatings systems applied onto Ni-base superalloy

Bilayer thermal barriers coatings of Dense Ceria-Yttria-Stabilized Zirconia (D-CYSZ)/Yttria-Stabilized Zirconia (YSZ) were deposited onto Inconel 625 using atmospheric plasma spray (APS). The thickness of the d-CYSZ layer varied (0, 50, 100, and 150 μm), but the total thickness of the system was kept at 300 μm. The thermo-mechanical resistance of the multilayer system was evaluated through thermal shock tests, in which the bilayer systems evaluated exceeded 500 cycles with percentages of delamination of the coating below 20 % of the exposed area and showed higher thermomechanical resistance than a conventional YSZ system. Hot corrosion (HC) resistance of the bilayer system was evaluated using a salt mixture of 32 wt.% Na₂SO₄ and 68 wt.% V₂O₅ at 900 °C. The systems with a d-CYSZ layer showed higher resistance to HC, exhibiting fewer changes into the microstructure and presence of the monoclinic phase despite the presence of vertical cracks in the microstructure.     

Thermal shock behavior of a 8YSZ/CoCrAlYTaSi thermal sprayed barrier coating on GH202 superalloy

The thermal shock behavior of a thermal barrier coating (TBC) prepared by plasma spraying at 1100 °C was investigated. The TBC consisted of a double layer structure of 8YSZ/CoCrAlYTaSi. The morphology, microstructure, phases and the elemental distribution of the TBCs were characterized using scanning electron microscopy (SEM), transmission electron microscope (TEM), scanning transmission electron microscope (STEM), X-ray diffraction (XRD) and electron probe micro-analysis (EPMA). The characterization results showed that the film consisted primarily of metastable tetragonal phases (t′), and a large number of micro-cracks were present in the 8YSZ crystals. Following eighty-six thermal shock cycles of the specimens a large areal spallation was observed on the 8YSZ coating. The decreased concentration of yttrium at the coating interfaces weakened the inhibition of crystal growth and the phase transition of the Al₂O₃. The growth of TGO (Thermal growth oxide) and the diffusion into the 8YSZ coating produced deformation and stress in the ceramic coating. Tantalum appeared to absorb the oxygen that diffused into the coatings and delayed the growth of TGO in the interface between the CoCrAlYTaSi and substrate, which was beneficial to prolonging the life of the TBC.     

Effect of functionally graded structure design on durability and thermal insulation capacity of plasma-sprayed thick thermal barrier coating

This paper aimed to design and optimize the structure of a thick thermal barrier coating by adding graded layers to achieve a balance between high thermal insulation capacity and durability. To this end, conventional TBC, conventional TTBC, and functionally graded TTBCs were deposited on the superalloy substrate by air plasma spraying. To determine the quality of the bond strength of the coatings, the bonding strength was measured. The durability of coatings was evaluated by isothermal oxidation and thermal shock tests. Then, at a temperature of 1000 °C, the thermal insulation capacity of the coatings was carried out. The microstructure of the coatings was characterized by a scanning electron microscope. The results showed that the thickness of the TGO layer formed on the bond coat in the conventional TBC and TTBC under the oxidation test at 1000 °C after 150 h was 2.79 and 2.11 μm, respectively, whereas, in the functionally graded TTBC samples, no continuous TGO layer was observed as a result of internal oxidation. The functionally graded TTBC presented higher durability than conventional TTBC due to improved bonding strength, thermal shock resistance, and the lack of a TGO layer at the bond/top coat interface. Also, the thermal insulation capacity of the functionally graded TTBC (with 1000 μm thickness of YSZ coating) was better than TTBC.     

Optimizing the structure and properties of Y2O3 stabilized zirconia: An atmospheric plasma spray (APS) and solution precursor plasma spray (SPPS) based comparative study

The yttria stabilized zirconia (8%YSZ) is widely used to insulate the metallic components of the engine from high temperature and improve the operating temperature of gas turbine engines. With different processing parameters, 8YSZ coatings are prepared by atmospheric plasma spray (APS) and solution precursor plasma spray (SPPS) techniques and the microstructural features and thermodynamics properties are compared. The electron back scattered diffraction (EBSD) analysis indicate that the substitutional point defects (Zr_0.86Y_0.14O_1.93) in the 8YSZ APS coatings are considerably higher than the corresponding SPPS coatings. The replacement of Zr⁴⁺ by Y³⁺ disturbs the charge neutrality of the system which might be compensated by the creation of oxygen vacancy. Both the substitutional point defects and the oxygen vacancies are the sources of phonon scattering, modifying the thermal conductivity of the coating. Pores and cracks are qualitatively and quantitatively analyzed in the microstructure of 8YSZ coatings. Strain tolerant and high thermal cycling life coatings are prepared by SPPS due to the existence of vertical cracks in the microstructure. Comparing the thermal insulation properties of the coatings, the APS coating provided lower thermal conductivities relative to the SPPS coatings which might be due to the high concentration of point defects and low concentration of the mixed oxide phase.     

Thermophysical properties and cyclic lifetime of plasma sprayed SrAl12O19 for thermal barrier coating applications

About 6-8 wt% yttria-stabilized zirconia (YSZ) is the industry standard material for thermal barrier coatings (TBC). However, it cannot meet the long-term requirements for advanced engines due to the phase transformation and sintering issues above 1200°C. In this study, we have developed a magnetoplumbite-type SrAl₁₂O₁₉ coating fabricated by atmospheric plasma spray, which shows potential capability to be operated above 1200°C. SrAl₁₂O₁₉ coating exhibits large concentrations of cracks and pores (~26% porosity) after 1000 hours heat treatment at 1300°C, while the total porosity of YSZ coatings progressively decreases from the initial value of ~18% to ~5%. Due to the contribution of porous microstructure, an ultralow thermal conductivity (~1.36 W m⁻¹ K⁻¹) can be maintained for SrAl₁₂O₁₉ coating even after 1000 hours aging at 1300°C, which is far lower than that of the YSZ coating (~1.98 W m⁻¹ K⁻¹). In thermal cyclic fatigue test, the SrAl₁₂O₁₉/YSZ double-ceramic-layer coating undertakes a thermal cycling lifetime of ~512 cycles, which is not only much longer than its single-layer counterpart (~163 cycles), but also superior to that of YSZ coating (~392 cycles). These preliminary results suggest that SrAl₁₂O₁₉ might be a promising alternative TBC material to YSZ for applications above 1200°C.     

Experimental visualization of microstructure evolution during suspension plasma spraying of thermal barrier coatings

This paper investigates the evolution of microstructure of thermal barrier coatings (TBCs) produced by suspension plasma spraying (SPS) through a careful experimental study. Understanding the influence of different suspension characteristics such as type of solvent, solid load content and median particle size on the ensuing TBC microstructure, as well as visualizing the early stages of coating build-up leading to formation of a columnar microstructure or otherwise, was of specific interest. Several SPS TBCs with different suspensions were deposited under identical conditions (same substrate, bond coat and plasma spray parameters). The experimental study clearly revealed the important role of suspension characteristics, namely surface tension, density and viscosity, on the final microstructure, with study of its progressive evolution providing invaluable insights. Variations in suspension properties manifest in the form of differences in droplet momentum and trajectory, which are found to be key determinants governing the resulting microstructure (e.g., lamellar/vertically cracked or columnar).     

Effect of environmental pressure on the microstructure of YSZ thermal barrier coating via suspension plasma spraying

Suspension plasma spraying (SPS) as a potential technique to prepare thermal barrier coatings (TBCs) has been attracting more and more attention. However, most reports on SPS were carried out in the atmosphere. Given the unique features of in-flight particles and plasma jets under low pressure, the resulting coatings are expected to be different from those under atmospheric pressure. In this article, yttria-stabilized zirconia (YSZ) thermal barrier coatings were prepared using suspension plasma spraying under different environmental pressures. The results show that as the environmental pressure decreased, the column-like structural coating turned into a vertical crack segmented structure, as well as a dramatic decrease in surface roughness. More nanoparticle agglomerates were formed in the coating under lower environmental pressures. The real porosity of the coating increased with a decrease in environmental pressure.