Eu~(3+)和Gd~(3+)共掺杂TiO_2粉体的制备及催化活性

采用溶胶-凝胶法制备纯TiO2和Gd3+/Eu3+共掺杂TiO2复合粉体,采用X射线衍射、漫反射光谱和扫描电镜等技术对样品进行表征,以亚甲基蓝(methyleneblue,MB)的光催化降解为目标反应评价其光催化活性,探讨Gd3+/Eu3+共掺杂对TiO2粉体光催化的影响机制。结果表明:Gd3+/Eu3+共掺杂可以显著提高TiO2粉体光催化活性。Gd3+/Eu3+共掺杂在TiO2粉体中产生协同作用,可以抑制TiO2由锐钛矿向金红石相转变,使TiO2的粒径减小。Gd3+/Eu3+共掺杂增大了TiO2粉体的晶格畸变,使TiO2粉体吸收带边蓝移。当Gd3+和Eu3+的质量掺量分别为0.05%和0.4%时,TiO2粉体光催化活性最高,降解率达到95.31%。     

稀土离子(Gd~(3+),Ce~(3+)/Ce~(4+),Eu~(3+))对Tb~(3+)掺杂硅酸盐玻璃发光性能的影响

研究了(Gd3+,Ce3+/Ce4+,Eu3+)对Tb3+掺杂硅酸盐玻璃发光性能的影响.结果表明:Tb3+掺杂硅酸盐玻璃可以发出弱蓝光(400～460 mm)和较强的绿光(480～600mm).Gd3+对Tb3+的发光起敏化作用,可提高TB3+掺杂硅酸盐玻璃的发光强度.在空气中熔制的玻璃中Ce3+和Ce4+同时存在,Ce3+对Tb3+发光起敏化作用;而Ce4+对Tb3+发光起淬灭作用.由于Ce4+比例比较高,CeO2加入导致TB3+发光强度降低,同时也缩短了Tb3+发光余辉.加入Eu2O3时,Eu3+自身发光分散了激发Tb3+发光的能量,使Tb3+的特征发射强度降低.     

Gd~(3+)/Si~(4+)掺杂对LiZnPO_4:Eu~(3+)荧光粉发光性能的影响

采用高温固相法制备了LiZnPO4:Eu3+红色荧光粉,分别研究了Eu3+掺量、Eu3+和Gd3+共掺杂以及SiO2掺杂对材料发光性能的影响。结果表明:在395nm近紫外光激发下,发射光谱峰值位于593nm,属于Eu3+的5D0→7F1辐射跃迁;激发光谱由200~280nm的宽带和310~500nm的一系列尖峰组成,分别对应于O2–→Eu3+电荷迁移带和Eu3+的f→f能级跃迁吸收,主激发峰位于395nm左右,与近紫外发光二极管(NUV-LED)的发射光谱(360~410nm)匹配。Eu3+最佳掺杂摩尔分数为12%,超过12%后发生浓度猝灭现象,浓度猝灭机理为电多极–电多极相互作用。掺杂Gd3+、SiO2使Eu3+在593nm处的发射分别增强了107%、105%。LiZnPO4:Eu3+是适合NUV-LED管芯激发的白光发光二极管用高亮度橙红色荧光粉。     

稀土离子掺杂的氯硼酸锶发光材料的合成及光谱性质

通过高温固相法制备了Sr2B5O9Cl:XEu2+:(0.05-X)Eu3+:YTb3+荧光体,讨论了煅烧温度及掺杂稀土离子Eu3+和Tb3+的浓度对荧光体的发光性能的影响。结果表明,Eu3+和Tb3+的最佳掺入量分别为5%和9%,最佳制备温度是900℃,稀土离子Eu2+、Eu3+和Tb3+掺杂的硼酸锶具有良好的发光性能。     

稀土离子掺杂的氯硼酸锶发光材料的合成及光谱性质

通过高温固相法制备了Sr2B5O9Cl:XEu2+:(0.05-X)Eu3+:YTb3+荧光体,讨论了煅烧温度及掺杂稀土离子Eu3+和Tb3+的浓度对荧光体的发光性能的影响。结果表明,Eu3+和Tb3+的最佳掺入量分别为5%和9%,最佳制备温度是900℃,稀土离子Eu2+、Eu3+和Tb3+掺杂的硼酸锶具有良好的发光性能。     

Eu~(3+)/Tb~(3+)/MoO_4~(2–)掺杂钨酸钙体系荧光粉的结构及其发光性能

采用化学共沉淀法合成了Ca0.75Mg0.2Tb0.02Eu0.03(WO4)1-x(Mo O4)x(x=0~1.0)系列荧光粉,并对荧光粉的晶体结构和发光性能进行了表征。结果表明:不同Mo O42–掺杂量的样品均为四方相Ca0.75Mg0.2Tb0.02Eu0.03(WO4)1-x(Mo O4)x固溶体。在273 nm波长紫外光激发下,随着x的增大,Eu3+离子的发光强度先增强后减弱,当x=0.6时发光强度最强,为未掺杂Mo O42–样品的6倍。Mo O42–共掺杂改变了稀土离子周围的配位环境和局部晶体场的对称性,促进Eu3+离子4f电子的超敏跃迁,提高Eu3+的O2–→Eu3+电荷迁移跃迁,增加基体、Tb3+离子与Eu3+离子之间的能量传递。     

微波水热法合成Eu~(3+)掺杂的SrMoO_4红色荧光粉

采用微波水热的方法在中性水溶液中合成平均长6μm、中间宽4μm的梭子形SrMoO4基体材料,并研究反应物浓度和Eu3+的掺杂量(摩尔分数3.75%～30%)及EG/H2O体积比等条件对合成的SrMoO4粉体形貌的影响。结果表明:随着Eu3+浓度的增加,形貌向片状结构转变。另外,在掺杂7.5%Eu3+时,采用加入乙二醇(EG)的方法,抑制了片状结构的生成。随着EG比例的增加,颗粒分布趋向均匀,粒径逐渐变小。当EG与H2O体积比为4∶1时,得到了分布均匀、长约0.8μm的梭子状SrMoO4∶Eu3+粉体。荧光光谱分析结果表明,梭子状SrMoO4∶Eu3+(7.5%)粉体能够被近紫外(395 nm)或者蓝光(463 nm)有效地激发,从而发射波长为614 nm的红光。     

Eu~(3+)掺杂Y_2O_3-Al_2O_3-SiO_2玻璃的制备与荧光性能研究

采用高温熔融法制备了Eu3+掺杂Y2O3-Al2O3-SiO2荧光玻璃,探讨了成分对该体系玻璃形成能力的影响,并对不同Eu3+掺杂浓度下的荧光性能进行了研究.结果表明,熔融温度为1500℃条件下,SiO2含量对该体系的玻璃形成能力影响明显,Y/Al摩尔比为3/5时,SiO2含量在52%—68%(摩尔分数)范围内时可以获得玻璃.掺杂Eu3+的Y2O3-Al2O3-SiO2玻璃具有荧光性能,在395nm波长激发下,在588 nm和614 nm处出现明显的发射峰.随着Eu3+掺杂浓度的增加,该荧光玻璃的发射波长不变,但发射强度有所变化;当Eu3+掺杂浓度为1.5%(摩尔分数)时,特征发射峰强度最大.     

白光发光二极管用Eu:(Y_(0.9)La_(0.1))_2O_3透明陶瓷的制备及性能

以Y2O3为原料、La2O3为烧结助剂,采用真空烧结法制备了(Y1-xLax)2O3透明陶瓷。研究了La2O3添加量对Y2O3陶瓷致密化行为的影响,确定La2O3的最佳添加量(摩尔分数)为10.0%。在此基础上制备了不同掺杂量(摩尔分数)的Eu:(Y0.9La0.1)2O3透明荧光陶瓷,研究了Eu3+掺杂浓度对陶瓷显微结构、光学性能及光谱特性的影响。结果表明:随着掺杂量的增加,Eu:(Y0.9La0.1)2O3陶瓷(1 765℃×50 h)的晶粒尺寸变化较小。其中,0.3%Eu:(Y0.9La0.1)2O3陶瓷的晶粒尺寸均匀(约为177.6μm),厚度为1 mm的陶瓷样品在800 nm处的直线透过率为62%。随着Eu3+掺杂浓度的增加,Eu:(Y0.9La0.1)2O3陶瓷的各个激发峰与发射峰强度变强。当激发波长为466 nm时,发射主峰位于红光波段611 nm处,属于Eu3+离子的5D0→7F2跃迁。研究表明Eu:(Y0.9La0.1)2O3透明陶瓷在白光发光二极管上具有潜在的应用价值。     

Sr8Si4O12Cl8:Eu3+,M3+(M3+=Bi3+,Gd3+)中Eu3+的敏化发光

以Na2CO3为电荷补偿剂,采用高温固相法合成了碱土氯硅酸盐Sr8Si4O12Cl8:(Eu3 M3 )(M=Bi3 ,Gd3 )荧光材料.X射线衍射分析结果表明:合成的Sr8Si4O12Cl8:(Eu3 ,M3 )为纯四方相.Eu3 的发射主峰位于614 nm,为5D0→7F2的电偶极跃迁,表明Eu3 处于非中心对称格位,即取代Sr2 的位置.通过对其激发光谱和发射光谱研究,发现敏化剂Bi3 ,Gd3 的掺入对Eu3 的发射具有较强的敏化作用,当Bi3 和Gd3 的掺杂量(摩尔分数)分别为5.0%时,Eu3 的相对发光强度分别提高了29.4%和23.6%.     

Modification of Optical Properties of SrAl_2O_4：Eu~（2＋）,Dy~（3＋） Phosphor by Terbium Doping

以尿素为燃料,采用快速燃烧法在650℃合成了Tb3＋掺杂的SrAl2O4：Eu2＋,Dy3＋新型长余辉光致发光材料。研究了Tb3＋掺杂对Eu2＋,Dy3＋共激活的铝酸盐长余辉发光材料的发光特性的影响。X射线衍射分析结果表明：当Tb3＋的掺杂量x=0.17%时,合成的样品结构为单相SrAl2O4单斜晶系。光致发光测试结果表明：样品的激发光谱为峰值位于345nm附近的连续宽带谱,发射光谱为峰值位于510nm左右的连续宽带谱。余辉衰减曲线结果表明：Tb3＋的适量掺杂可以提高铝酸锶的余辉性能。与SrAl2O4：Eu2＋,Dy3＋相比,掺杂Tb3＋有利于形成结晶度良好的固溶体,样品中的晶体细密紧凑,颗粒粒径约为100nm。     

Y_2O_3：Eu~（3＋）@Gd_2O_3核壳结构发光材料的制备与浓度猝灭

采用均相沉淀法制备均匀球形的Y2O3：Eu3＋@Gd2O3核壳结构纳米发光材料,用X射线衍射、红外光谱、扫描电镜、X射线光电子能谱及荧光光谱等表征样品的形貌、结构及发光性能。结果表明：Y2O3：Eu3＋表面成功包覆了Gd2O3,包覆后仍为均匀的球形,包覆层厚度约为5nm;包覆前后样品的猝灭浓度均为7%（摩尔分数）,包覆...     

Ca3MgSi2O8:RE(RE=Eu2+,Ce3+,Tb3+)的发光性能

采用高温固相法在还原气氛下合成了Ca3MgSi2O8:RE(RE=Eu2 ,Ce3 ,Tb3 )系列样品.用荧光光谱仪研究了样品掺杂Eu2 ,Ce3 ,Tb3 后的光谱性质.样品Ca3MgSi2O8:Ce3 在紫外光激发下呈蓝紫色发射;样品Ca3MgSi2O8:Eu2 在紫外光激发下则呈绿色发射.分别讨论了Ce3 ,Eu2 和Ce3 ,Tb3 共激活焦硅酸钙盐在紫外光激发下的光谱特性和其中存在的能量传递机理,发现Ce3 分别对Eu2 和Tb3 有敏化作用.     

Preparation and scintillating properties of sol-gel eu, tb co-doped lu(2)o(3) nanopowders

Nanocrystalline Eu(3+), Tb(3+) co-doped Lu(2)O(3) powders with a maximum size of 25.5 nm were prepared by the sol-gel process, using lutetium, europium and terbium nitrates as precursors, and ethanol as a solvent. Differential thermal analysis (DTA) and infrared spectroscopy (IR) were used to study the chemical changes during the xerogel annealing. After the sol evaporation at 100 °C, the formed gel was annealed from 300 to 900 °C for 30 min under a rich O(2) atmosphere, and the yielded product was analyzed by X-ray diffraction (XRD) to characterize the microstructural behavior and confirm the crystalline structure. The results showed that Lu(2)O(3) nanopowders start to crystallize at 400 °C and that the crystallite size increases along with the annealing temperature. A transmission electron microscopy (TEM) study of samples annealed at 700 and 900 °C was carried out in order to analyze the microstructure, as well as the size, of crystallites. Finally, in regard to scintillating properties, Eu(3+) dopant (5 mol%), Tb(3+) codoped Lu(2)O(3) exhibited a typical red emission at 611 nm (D(°)→(7)F(2)), furthermore, the effect of Tb(3+) molar content (0.01, 0.015 and 0.02% mol) on the Eu(3+) radioluminiscence was analyzed and it was found that the higher emission intensity corresponds to the lower Tb(3+) content.     

Synthesis and Luminescence Properties of Y3Al5O（12）：Eu^（3＋） Phosphors under Vacuum Ultraviolet Excitation

采用凝胶–燃烧法合成了掺Eu3＋的Y3Al5O12（YAG：Eu3＋）荧光粉。分别采用X射线衍射（XRD）、扫描电子显微镜（SEM）、发光光谱等测试手段分析了不同温度下煅烧所得粉体的物相、形貌与发光性质。XRD和SEM结果表明：YAG：Eu3＋的最低合成温度为900℃,并且在该反应过程中没有中间相YAP（YAlO3）和YAM（YAl）的产生。1 100℃合成的晶粒尺寸比较均匀,平均粒径在90 nm左右。发光光谱的测试表明：在592 nm监控下的真空紫外激发光谱由峰值位于147、156、169nm和214nm的系列激发带组成,其分别归属于铝酸根的基质吸收以及Y3＋和Eu3＋的电荷迁移带吸收。在147nm激发下YAG：Eu3＋荧光粉最强发射峰位于592nm处,属于Eu3＋的5D0→7F1跃迁。Eu3＋在基质中的最佳掺杂摩尔分数为4%。     

Sr_3SiO_5：Eu~（2＋）荧光粉相形成的影响因素及发光特性

采用高温固相法制备Sr3SiO5：Eu2＋荧光粉,利用X射线衍射分析方法和光致光谱分析方法研究样品的物相组成、激发光谱和发射光谱。研究摩尔比n（Sr）/n（Si）、助熔剂BaF2质量、煅烧温度及Eu2＋掺量等对样品物相形成和发光性能的影响。结果表明最佳实验参数为：n（Sr）/n（Si）=3、BaF2为1%、煅烧温度为1...     

用于白光LED的Sr_3SiO_5:Eu~(3+)材料制备及发光特性(英文)

采用高温固相法制备了Sr3SiO5:Eu3+材料.测量了Sr3SiO5:Eu3+材料的激发与发射光谱:材料的发射光谱由576、585、611、618nm和650nm几个发射峰组成,分别对应于Eu3+的5D0→7F0、5D0→7F1、5D0→7F2、5D0→7F2和5D0→7F3辐射跃迁.监测618 nm主发射峰时所得激发光谱为一多峰宽谱,主峰分别为400nul和470nm.研究了Eu"浓度对Sr3Si05:Eu3'材料发光强度的影响,结果显示:随Etl3'浓度的增大,发光强度先增大后减小,Eu3+的摩尔分数为3%时,材料的发光强度最大,根据Dexter理论,其浓度猝灭机理为电偶极一偶极跃迁.引入电荷补偿剂Cl-、Li+、Na+和K+时,材料的发光强度均得到了提高,其中Cl-和Li+的提高幅度较明显.     

Electrospinning-derived Tb2(WO4)3:Eu(3+) nanowires: energy transfer and tunable luminescence properties

One-dimensional Tb(2)(WO(4))(3) and Tb(2)(WO(4))(3):Eu(3+) nanowires have been prepared by a combination method of sol-gel process and electrospinning. X-Ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), photoluminescence (PL), low voltage cathodoluminescence (CL) and time-resolved emission spectra as well as kinetic decays were used to characterize the resulting samples. The as-obtained precursor samples present fiber-like morphology with uniform size, and Tb(2)(WO(4))(3) and Tb(2)(WO(4))(3):Eu(3+) nanowires were formed after annealing. Under ultraviolet excitation and low-voltage electron beams excitation into WO(4)(2-) and the f-f transition of Tb(3+), the Tb(2)(WO(4))(3) samples show the characteristic emission of Tb(3+) corresponding to (5)D(4)-(7)F(6, 5, 4, 3) transitions due to an efficient energy transfer from WO(4)(2-) to Tb(3+), while Tb(2)(WO(4))(3):Eu(3+) samples mainly exhibit the characteristic emission of Eu(3+) corresponding to (5)D(0)-(7)F(0, 1, 2) transitions due to an energy transfer occurs from WO(4)(2-) and Tb(3+) to Eu(3+). The increase of Eu(3+) concentration leads to the increase of the energy transfer efficiency from Tb(3+) to Eu(3+). The PL color of Tb(2)(WO(4))(3):x mol% Eu(3+) phosphors can be tuned from green to red easily by changing the doping concentration (x) of Eu(3+), making the materials have potential applications in fluorescent lamps and color display fields.     

四元混配配合物[Ln(x-MBA)2(NO3)(Phen)]2的合成及表征

在酸性介质,乙醇／水混合溶剂中合成得到了三个系列的四元混配配合物[Ln(x-MBA)2(NO3)(Phen)]2(Ln=La、Ce、Pr、Nd、Sm、Eu、Gd、Tb、Er;MBA=CH3C6H4COO^-）。用元素分析、IR、UV、DTA－TG和^1H NMR等方法对配合物进行了表征,测量了三个Eu配合物的荧光光谱和三个Gd配合物的ESR谱。