水性环氧带锈防锈底面合一漆的试制

分别介绍了水性腰果壳液固化剂与水性环氧树脂乳液的合成，并用此乳液与固化剂合成了水性环氧带锈防锈底面合一漆，讨论了乳化剂的添加量对乳液稳定性及涂膜硬度的影响，固化剂的添加量对漆膜性能的影响，最终确定了乳液与固化剂的最佳配比。此固化剂通用性强，能与多种水性环氧树脂配合使用，且与色漆的配比范围较宽。     

可再生原料在涂料中的应用——腰果壳液改性胺固化剂

简述了腰果壳液的组成和经腰果壳液改性制备的环氧固化剂,其具有低温下快速固化、柔韧性强、高抗冲击性、高附着力、耐盐雾性强、低毒等优异的性能,并介绍了腰果壳液固化剂在溶剂型、无溶剂型和水性环氧涂料中的应用。     

一种高固体分环氧防腐涂料的研制

采用小分子量环氧树脂和大分子量环氧树脂复配作为基料,以腰果壳油改性酚醛胺为固化剂,研制了一种高固体分环氧防腐涂料,并进行了性能检测。讨论了环氧树脂、环氧稀释剂、颜填料、流变助剂和固化剂对涂料性能的影响。     

腰果市场及腰果壳液在涂料中的应用

介绍了腰果壳液的成分、特性 ,探讨了腰果壳液在涂料中的应用 ,并对国内外腰果市场进行了分析     

高附着耐水煮玻璃漆的研制

合成了玻璃环氧底漆,讨论了附着力促进剂、树脂和固化剂种类及用量对涂料性能的影响.结果表明,以1.5%3-缩水甘油醚氧基丙基三甲氧基硅烷为附着力促进剂,以E-20环氧树脂为成膜物、腰果壳油改性酚醛胺为固化剂制成底漆,配合丙烯酸聚氨酯黑面漆,获得了高附着,耐水煮的玻璃漆.     

腰果壳液及其应用

介绍了腰果壳液的萃取方法、成分、特性，探讨了腰果壳液在涂料中的应用，并对国内外腰果市场进行了分析。     

高性能环氧树脂涂料固化剂

通过对几种常用环氧树脂常温固化剂性能的比较和应用结果表明,以天然腰果壳油合成的长链的取代酚醛胺固化剂,具有优异的综合防护性能,是环氧树脂高性能化的一种途径。     

WEC402水性环氧固化剂在水性环氧地坪涂料中的应用

使用WEC4 0 2水性环氧固化剂制备的水性环氧地坪涂料的配方、工艺 ,讨论了固化剂与环氧树脂的配比、颜填料、助剂等对涂料性能的影响。     

腰果壳液的性质及其在摩擦材料工业中的应用

腰果壳液中主要含有腰果酚,利用腰果酚中酚羟基、侧链双键及活泼氢等的化学性质,人们将腰果壳液广泛地应用于材料的各种改性,其中以应用在摩擦材料领域效果最为显著,并主要应用于以下三个方面：1、腰果壳液改性酚醛树脂黏结剂2、腰果树脂黏结剂3、摩擦粉。     

工程机械用水性环氧防锈底漆的制备

采用水性环氧树脂乳液作为基料,水性改性胺作为固化剂以及环保型助剂等配制成双组分水性环氧防锈底漆。讨论了水性环氧固化剂、活性防锈颜料、流变剂及活性稀释剂对水性环氧防锈底漆性能的影响。     

MDI型水性固化剂将开创双组分水性聚氨酯涂料发展新局面

从理论上探讨了MDI型水性固化剂生产的可行性,提出了MDI型水性固化剂的设计思路,针对MDI型水性固化剂应用的困难提出了解决办法。旨在提出MDI型水性固化剂合成新思路,降低水性固化剂成本,促进双组分水性聚氨酯涂料应用。MDI型水性固化剂成功开发与应用,将与脂肪族水性固化剂相互补充和促进,并开创双组分水性聚氨酯涂料局面。     

水性环氧树脂涂料适用期的研讨

研究探讨了水性环氧树脂涂料适用期方面的相关规律与特点。结果表明固化剂乳化型水性环氧树脂涂料的适用期一般较短;其与溶剂型环氧树脂涂料一样,可以用黏度变化来判断其适用期的长短;而对于水性环氧固化剂乳液与水性环氧树脂乳液所组成的水性环氧树脂涂料体系,其适用期较长,并且应以涂膜的性能,如涂膜光泽度的变化来确定。     

水性双组分氟丙烯酸—聚氨酯涂料的研制及性能测试

介绍了水性双组分氟丙烯酸-聚氨酯涂料所用原料及其预处理,水性双组分氟丙烯酸-聚氨酯涂料的羟基组分采用两步法合成:第一步合成了具有大分子表面活性剂性能的水性聚氨酯,在合成的过程中引入了双键和羟基组分;然后采用无皂乳液聚合的方法合成了以氟丙烯酸酯为核、聚氨酯为壳的水性树脂。并列举了采用该树脂与水性固化剂配合研制的清漆的性能指标,该清漆有着非常广泛的用途,讨论了影响涂料性能的各种因素。该双组分清漆水性含氟丙烯酸酯-聚氨酯清漆具有优异的综合性能。     

Studies on Performance of Cured Water-Borne Melamine–Acrylic Emulsion Coatings

In this study, water-borne coating formulations which could be cured quickly were prepared using acrylic emulsion as the major coating constituent and highly reactive melamine resin as curing agent, and further incorporating a variety of additives. Melamine and acrylic types, melamine/acrylic mass ratio in coating formulation, and curing temperature were found to influence the performance of cured coatings. When melamine resin etherified slightly with methanol was used as curing agent, melamine/acrylic mass ratio was 0.45 and the coating formulation was baked at 170°C for 30 s, it was observed that performance of cured coating was the best. FTIR was used to study molecular structural changes of coatings after curing, and to analyze the cure mechanism of the coating. DSC was used to study the range of temperature in which curing occurred. The water-borne coating prepared in this study could be cured quickly when it was applied on decorative paper surface and baked at high temperature. Performance properties of cured coatings were tested according to standard methods, it was observed that dry heat resistance, wet heat resistance, adhesion, pencil hardness, and stain resistance all met standard requirements.     

水性涂料的流变性

介绍了涂料流变性的基本知识以及在涂料性能研究上的应用。基于水性涂料的特点,以最近的研究报道为例,介绍了利用测定其流变特性,在不同结构聚氨酯固化剂存在下,丙烯酸水分散体涂料固化性能与涂膜性质。     

水性环氧涂料用固化剂的探索

水性环氧涂料是水性涂料发展的重要品种之一,水性环氧涂料用固化剂是影响其涂料性能的主要因素之一,因此开发新型水性环氧涂料用固化剂则别具现实意义.文中对水性环氧涂料用固化剂的发展历程作了探讨,并对各类水性环氧涂料用固化剂的特点进行扼要的解说,从中探索出水性胺加成物固化剂是水性环氧涂料用固化剂中最具发展前景的品种.     

双组分水性环氧防腐涂料的研制

采用水性环氧树脂乳液作为环氧防腐涂料基料,水性改性胺作为固化剂,低铅含量防锈颜料、环保型助剂等配制成双组分水性环氧防腐涂料。该涂料达到溶剂型环氧防腐涂料的理化性能要求,同时VOC低,符合国家强制性标准可溶性重金属的限量要求,适用于对环保要求严格的工业钢结构防腐领域。     

水性环氧涂料体系的研究进展

简述了水性环氧涂料体系的发展以及环氧树脂和固化剂的水性化方法,介绍了水性环氧涂料的固化机理和用途。