Luminescence enhancement of BaMgSiO4：Eu^2＋ by adding borate as flux

The luminescence of EU^2＋ in BaMgSiO4 with BaB2O4 as flux was studied. The emission spectrum of the phosphor consisted of two bands, peaking at about 398 nm and 515 nm, which were attributed to the emissions from different Eu^2＋ sites in the lattice. When the BaB2O4 flux was applied, the intensity of the 398 nm emission was not clearly affected, but the intensity of the 515 nm emission was enhanced by about ten times. Gaussian fitting showed that the emission band at around 515 nm could actually be resolved into two bands with peak wavelengths of 499 nm and 521 nm, respectively. The assignments of the emission bands to the cation sites were carried out according to the values of bond valence. The overlapping of the 398 nm emission band on the excitation band of 515 nm emission implied that energy transfer could occur from the luminescent center related to the 398 nm emission to the center related to the 515 nm emission, and the energy transfer process remarkably enhanced the intensity of the 515 nm emission band. The phosphor had strong excitation at around 350-400 nm and emitted a bright green luminescence. Thus it could have applications as a green component in solid-state lighting devices assembled by near-UV Light Emitting Diodes （LED） combined with tricolor phosphors.     

Luminescence and Preparation of LED Phosphor Ca8Mg （ SiO4）4Cl2 ： Eu^2＋

Calcium magnesium chlorosilicate doped by europium, Ca8Mg（SiO4）4Cl2： Eu^2＋, was prepared by the solid state reaction at high temperature. The compound obtained is pure Ca8Mg（SiO4）4Cl2 phase with cubic structure. Its average particle size is 5 μm, and it has good dispersity and morphological form. The excitation spectrum of Ca8Mg（SiO4）4Cl2： Eu^2＋ is a wide band, which covers from 270 to 480 nm. The emission spectrum is also a wide band peaked at 510 nm. The luminescent intensity reaches to the maximum when the concentration of Eu^2 ＋ is 2%. The wavelength of emission and excitation of the phosphor with various Eu^2 ＋ contents keeps constant. This spectrum range matches violet and blue LED chips very well, and its strong luminescence intensity is suitable for a green phosphor of tricolor phosphor of white light LED.     

Synthesis and luminescence properties of Sr3-z（AlxSi1-x）O5-xFx：zCe^3＋phosphors

Sr3-z(Alx,Si1-x)O -5-xFx:zCe3+ phosphors were synthesized by high-temperature solid-state reaction.The structure and luminescence properties of phosphors with various Al/Si ratios and Ce3+ concentrations were characterized using various methods such as X-ray diffraction,photoluminescence excitation and photoluminescence spectra.XRD result displayed that a complete solid solution between Sr3AlO4F and Sr3SiO5 was formed.With the increasing of x value,a broader excitation band and stronger absorption appeared in the blue light region.Moreover,the emission band shifted to a shorter wavelength and the emission intensity reached a maximum at x=0.6.By adjusting the concentration of Ce3+,a widely tunable range of emission wavelength under the excitation of 460 nm was obtained from the green to yellow regions.In addition,the concentration and thermal quenching were also discussed.     

Preparation and Luminescence Properties of the New Long Phosphorescent Phosphors Ba1-x Cax Al2O4 ： Eu^2＋ , Dy^3＋

New long phosphorescent phosphors Ba1-x CaxAl2O4:Eu^2 , Dy^3 with tunable color emission were prepared and studied. The emission spectra show that the tuning range of the color emission of the phosphors is between 498 and 440 nm, which is dependent on x, under the excitation of UV. The wavelength of the afterglow increases with the increasing of x until x equals 0.6. The XRD patterns show that the single phase limit in the phosphors is below x value of 0.4.The Thermolumineseence spectra were measured to investigate the traps created by the doping of Dy^3 .     

Luminescent characteristics of Ba3Y2（BO3）4：Eu^3＋ phosphor for white LED

The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.     

Luminescence properties of a single-host phosphor Bal.8-wSrwLi0.4SiO4： cea＋,Eu2＋,Mn2＋ for WLED

In order to obtain a single-host-white-light phosphor,a series of Ba1.8-w-x-y-zSrwLi0.4-xCexEuyMnzSiO4(BSLS:Ce3+,Eu2+,Mn2+)powder samples were synthesized via high temperature solid-state reaction.The structure and photoluminescence properties were investigated.Under ultraviolet excitation,the emission spectra contained three bands:the 370-470 nm blue band,the 470-570 nm green band and the 570-700 nm red band,which arose from the 5d→4f transitions of Ce3+ and Eu2+,and the 4T1→6A1 transition of Mn2+,respectively.The excitation spectra of the emissions of Ce3+ and Mn2+ ions showed the energy transfer from Ce3+ to Mn2+.White light emission was obtained from the tri-doped samples of appropriate doping concentration under 310-360 nm excitation.     

A green-yellow emitting β-SreSiO4：Eu^2＋ phosphor for near ultraviolet chip white-light-emitting diode

Sr2SiO4：xEu^2＋ phosphors were synthesized through the solid-state reaction technique. The crystal phase of Sr2SiO4：xEu^2＋ phosphor manipulated by Eu^2＋ concentration was studied. The phase transited from β to α＇ in Sr2SiO4：xEu^2＋ phosphor with increasing europium concentration. The single β phase was formed as x≤005 and changed α＇ phase when x〉0.01. The emission spectrum of the β-Sr2SiO4：Eu^2＋ phosphor consisted of a green-yellow broadband peaking at around 540 nm and a blue band at 470 nm under near ultraviolet excitation. The white LEDs by combining near ultraviolet chips with β-Sr2SiO4：Eu^2＋ phosphors were fabricated. The luminous efficiency （15.7lm/W） was higher than α＇-Sr2SiO4：Eu^2＋ phosphor white LED.     

Photoluminescence Characteristics of Gd2Mo3O9 ： Eu Phosphor Particles by Solid State Reaction Method

Eu^3＋-doped Gd2Mo3O9 was prepared by solid-state reaction method using Na2CO3 as flux and characterized by powder X-ray diffractometry. According to X-ray diffraction, this material belonged to a tetragonal system with space group I41/α. The effects of flux content and sintering temperature on the luminescent properties were investigated with the emission and excitation spectra. The results showed that flux content and sintering temperature had effects on the luminescent properties, the optimized flux content and the best temperature was 3 % and 800 ℃ respectively. The excitation and emission spectra also showed that this phosphor could be effectively excited by C-T band （280 nm）, ultraviolet light 395 nm and blue light 465 nm. The wavelengths at 395 and 465 nm were nicely fitting in with the widely applied output wavelengths of ultraviolet or blue LED chips. Integrated emission intensity of Gd2Mo3O9 ： Eu was twice higher than that of Y2O2S ： Eu^3 ＋ under 395 nm excitation. The Eu^3＋ doped Gd2Mo309 phosphor may be a better candidate in solid-state lighting applications.     

Co-Precipitation Synthesis and Spectral Characteristics of Long Afterglow Phosphor Y2O2 S： Sm^3＋, Mg^2＋ , Ti^4＋

Y2O2S：Sm^3＋, Mg^2＋, Ti^4＋ phosphor was synthesized by co-precipitation method. The crystalline structure of all synthesized phosphors was investigated by XRD. The result showed that all synthesized phosphors had a hexagonal crystal structure, which was the same as Y2O2S. The emission spectrum and excitation spectrum were measured, and the effect of Sm^3 ＋ molar ratio on the spectra was discussed. The emission spectra of the phosphors showed three emission peaks due to typical transitions of Sm^3 ＋ （4G5/2→6HJ ,J = 5/2, 7/2, 9/2）, and the emission peaks at 606 nm was stronger than others. With the increase of Sm^3 ＋ molar ratio, the emission intensity was strengthened. The excitation peaks were ascribed to the representative energy transition 4f→4f of Ti^4＋ phosphor prepared by co-precipitation method was Sm^3＋ ions. The results indicated that the Y2O2S ： Sm^3＋ , Mg^2＋ , an efficient long afterglow phosphor.     

Luminescence properties of Eu2＋ -doped Ba3Si6O12N2 green phosphor： concentration quenching and thermal stability

The efficient Eu2+ -doped Ba3 Si6O12N2 green phosphors were prepared by a traditional solid state reaction method under N2 /H2 atmosphere at a temperature up to 1350 oC for 12h. Photoluminescence (PL) properties showed a broad emission band with a peak of 525 nm and the full width of half-emission maximums (FWHM) of 70 nm under 460 nm light irradiation. The X-ray diffraction patterns (XRD) and scanning electron microscope (SEM) images of the synthesized powder demonstrated its pure phase and excellent crystallization. Quenching concentration in this phosphor was found to be 0.3. The mechanisms of concentration quenching and redshift of emission peak with increasing concentration of Eu2+ were studied. The temperature dependence measurement of this green phosphor revealed excellent thermal quenching property compared to silicate green phosphor. It is believed that Ba3 Si6O12N2 :Eu2+ is an excellent green phosphor for UV or blue chip based white LEDs.     

Effects of crystal field on photoluminescence properties of Ca2Al2SiO7:Eu2+ phosphors

A series of single-phased Ca₂Al₂SiO₇:Eu²⁺ phosphors were synthesized by the solid-state reaction. Their structure and photolumi-nescence properties were investigated by the X-ray powder diffraction （XRD） and excitation and emission spectra in detail. The emission spectra of Ca₂Al₂SiO₇:Eu²⁺ phosphors consisted of blue and green band located at419 and542 nm, respectively. The relative intensities of the blue and green emission changed with Eu²⁺ concentration and were sensitive to the excitation wavelength. The unique photoluminescence property originated from the 4f⁷→4f⁶5d transition of Eu²+ at different energy levels, on which the effect of the crystal field strength was con-sidered to be tailed by adjusting the host composition.     

Luminescence properties of YAl3（BO3）4 phosphors doped with Eu^3＋ ions

YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Doping YAl3（BO3）4： Eu^3＋ phosphors with concentration of Eu^3＋ ions of 0, 2, 5, 8 and 10 mol% were studied and their luminescent properties at room temperature were discussed. The excitation spectrum of Y0.95Eu0.05Al3（BO3）4 was composed of a broad band centered at about 252 nm and a group of lines in the longer wavelength region. In the emission spectra, the peak wavelength was about 614 nm under a 252 nm UV excitation. The optimal doping concentration of Eu^3＋ ions in YAl3（BO3）4： Eu^3＋ phosphors was 8 mol%.     

Phase structure and temperature dependent luminescence properties of Sr2LiSiO4F: Eu2+ and Sr2MgSi2O7: Eu2+ phosphors

Green-emitting Sr2LiSiO4F:Eu2+ and blue-emitting Sr2MgSi2O7:Eu2+ phosphors were synthesized by the conventional high temperature solid-state route,respectively.Their structures and photoluminescenee properties were comparatively investigated.It was found that the mixture phases of Sr2MgSi2O7 and SrF2 were obtained when a part of Sr2+ in Sr2LiSiO4F was replaced by some amount of Mg2+ in order to design the possible SrMgLiSiO4F:Eu2+ phosphor.Based on the photoluminescence analysis,Sr2LiSiO4F:Eu2+ phosphor exhibited a green broad emission band of main peak at 513 nm under the excitation of 365 nm,while the Sr2MgSi2O7:Eu2+ and SrMgLiSiO4F:Eu2+ phosphor showed blue emission centered at 467 nm.The temperature dependent photoluminescence properties and room temperature decay time for the three kinds of phosphors were also discussed in this paper.     

BaEMg（BOa）2：Ce^3＋,Eu^2＋,Na^＋： A potential single-phased two colour borate phosphor for white light-emitting diodes

A two colour phosphor Ba 2 Mg(BO3)2:Ce3+,Eu2+,Na+ was synthesized using solid-state reaction method.Luminescence of Ba2Mg(BO3)2:Ce3+,Eu2+,Na+ showed 416 and 618 nm emission bands attributed to Ce3+ and Eu2+ emission, respectively. Energy transfer occurred from Ce3+ to Eu2+ through a significant overlap of Eu 2+ excitation spectrum with Ce3+ emission spectrum in Ba 2 Mg(BO3)2. They also showed that under the excitation of UV radiation, bluish or yellowish white light was generated by coupling a broad blue emission band and a red emission band.By combining with green phosphor, Ba2Mg(BO3 ):Ce3+,Eu2+,Na+ phosphor showed potential application for white light-emitting diodes (LEDs).     

Luminescent properties of Ca2SiO4：Eu^3＋ red phosphor for trichromatic white light emitting diodes

The luminescent properties of Eu^3＋doped Ca2SiO4 red phosphors synthesized by the flux fusion reaction method were investigated. It was found that the excitation spectrum included two regions： the weak excitation band below 325 nm and strong narrow peaks above 325 nm. The main peak of the excitation band was located at 400 nm. The peaks located at 290 nm were assigned to the combination of the charge transfer transition of O-Eu, peaks above 325 nm （325, 385, 400, 470, 511, and 539 nm） were assigned to the f-f transitions of Eu^3＋. The emission spectrum was dominated by the red peak located at 612 nm due to the electric dipole transition of ^5D0-^7F2. In addition, the effects of the Eu^3＋ content and charge compensators of Li^＋, Na^＋, K^＋, and Cl^- ions on the emission intensity were investigated. The experiment results suggested that the strongest emission was obtained when the concentration of the Eu^3＋ ions was 0.3 mol^-1, and Li^＋ ions gave the best improvement to enhance the emission intensity. Ca2SiO4：Eu^3＋, Li^＋ was thus suitable for low-cost trichromatic white light emitting diodes （WLED） based on UV InGaN chip.     

Colour Centres and Energy Transfer in BaF2-xClx：Eu^2＋ Phosphors

The optical absorption spectra of BaF2-x Clx ：Eu^2＋ after ultraviolet （UV） light excitation were investigated. The differences between the absorption spectra after and before excitation （DAS） were observed. The DAS increase at both the high and the low energy side of F band in BaF2-xClx ： Eu^2 ＋ after 245 nm UV light excitation. The bleach effect of UV light and the absorption of electrons in the valence band may account for the former and the formation of Fa centres （association of F（Cl^-） centres）, whose absorption band matches the HeNe laser better, may explain the latter. In the write-in process, the transfer of electrons is via tunneling, In the readout process, the transfer of electrons captured in F（F^-） and Fa centres is more likely via tunneling, and that of F（Cl^- ） centres is more likely via conduction band.